We have carried out a prospective, randomised study designed to compare the long-term stability of the stem of cementless femoral implants with differing surface configurations. A total of 50 hips (46 patients) was randomised into two groups, according to whether the medullary stem had been grit blasted (GB) or coated with hydroxyapatite (HA). Both femoral prostheses were of the same geometrical design. We used Ein Bild Roentgen Analyse femoral component analysis (EBRA-FCA) to assess the stability of the stem. The mean follow-up was for 8.66 years. The mean migration of the stem was 1.26 mm in the HA group compared with 2.57 mm in the GB group (Mann-Whitney U test, p = 0.04). A mixed model ANOVA showed that the development of subsidence was statistically different in the two groups during the first 24 months. After this subsidence increased in both groups with no difference between them. Our results indicate that, with the same design of stem, HA coating enhanced the stability of the femoral stem when compared with GB stems.
We compared and quantified the modes of failure and patterns of wear of 11 Mittelmeier and 11 Ceraver-Ostal retrieved alumina-alumina hip prostheses with reference to the corresponding clinical and radiological histories. Macroscopic wear was assessed using a three-dimensional co-ordinate measuring machine. Talysurf contacting profilometry was used to measure surface roughness on a microscopic scale and SEM to determine mechanisms of wear at the submicron level. The components were classified into one of three categories of wear: low (no visible/measurable wear), stripe (elliptical wear stripe on the heads and larger worn areas on the cups) and severe (macroscopic wear, large volumes of material lost). Overall, the volumetric wear of the alumina-alumina prostheses was substantially less than the widely used metal and ceramic-on-polyethylene combinations. By identifying and eliminating the factors which accelerate wear, it is expected that the lifetime of these devices can be further increased.
Limited success in regenerating large bone defects has been achieved by bridging them with osteoconductive materials. These substitutes lack the osteogenic and osteoinductive properties of bone autograft. A direct approach would be to stimulate osteogenesis in these biomaterials by the addition of fresh bone-marrow cells (BMC). We therefore created osteoperiosteal gaps 2 cm wide in the ulna of adult rabbits and either bridged them with coral alone (CC), coral supplemented with BMC, or left them empty. Coral was chosen as a scaffold because of its good biocompatibility and resorbability. In osteoperiosteal gaps bridged with coral only, the coral was invaded chiefly by fibrous tissue. It was insufficient to produce union after two months. In defects filled with coral and BMC an increase in osteogenesis was observed and the bone surface area was significantly higher compared with defects filled with coral alone. Bony union occurred in six out of six defects filled with coral and BMC after two months. An increase in the resorption of coral was also observed, suggesting that resorbing cells or their progenitors were present in bone marrow and survived the grafting procedure. Our findings have shown that supplementation of coral with BMC increased both the resorption of material and osteogenesis in defects of a clinical significance.
Total hip replacement using an alumina head and socket and a titanium alloy stem is evaluated in a series of patients under 50 years of age. Between April 1977 and December 1986, 86 such replacements were performed in 75 patients, but mainly because patients had difficulty travelling from Africa, only 71 hips were followed up adequately; of these, 56 were primary procedures and 15 revisions. Survivorship analysis showed that 98% of the prostheses were retained for 10 years. On clinical and radiological examination 51 of the 71 hips were stable and acceptable, 15 had radiological changes on the acetabular side, and one on the femoral side; four other cases had clinical and radiological changes suggesting impending failure, possibly because fixation of the socket was inadequate. There were no differences between the results of the primary procedures and those of revisions. In these young patients, the results seem better with alumina-on-alumina hips than with other varieties, possibly because of their remarkably low wear.