The aim of this study was to obtain detailed long-term data on the cement-bone interface in patients with cemented stems, implanted using the constrained fixation technique. A total of eight stems were removed together with adjacent bone during post-mortem examinations of patients with well-functioning prostheses. Specimens were cut at four defined levels, contact radiographs were obtained for each level, and slices were prepared for histological analysis. Clinical data, clinical radiographs, contact radiographs and histological samples were examined for signs of loosening and remodelling. The mean radiological follow-up was 9.6 years and all stems were well-fixed, based on clinical and radiological criteria. Contact radiographs revealed an incomplete cement mantle but a complete filling of the medullary canal for all implants. Various amounts of polyethylene particles were evident at the cement-bone interface of seven stems, with no accompanying inflammatory reaction. Cortical atrophy and the formation of an ‘inner cortex’ were confirmed in six of eight stems by contact radiographs and histology, but were only visible on two clinical radiographs.

Our results confirm that a complete cement mantle is not essential for the survival of Müller straight stems into the mid term, and support our hypothesis that no benefit to long-term survival can be expected from modern cementing techniques.

The original forged Müller straight stem (CoNiCr) has shown excellent ten- to 15-year results. We undertook a long-term survival analysis with special emphasis on radiological changes within a 20-year period of follow-up.

In all, 165 primary total hip replacements, undertaken between July 1984 and June 1987 were followed prospectively. Clinical follow-up included a standardised clinical examination, and radiological assessment was based on a standardised anteroposterior radiograph of the pelvis, which was studied for the presence of osteolysis, debonding and cortical atrophy.

Survival of the stem with revision for any reason was 81% (95% confidence interval (CI), 76 to 86) at 20 years and for aseptic loosening 87% (95% CI, 82 to 90). At the 20-year follow-up, 15 of the surviving 36 stems showed no radiological changes. Debonding (p = 0.005), osteolysis (p = 0.003) and linear polyethylene wear (p = 0.016) were associated with aseptic loosening, whereas cortical atrophy was not associated with failure (p = 0.008).

The 20-year results of the Müller straight stem are comparable to those of other successful cemented systems with similar follow-up. Radiological changes are frequently observed, but with a low incidence of progression, and rarely result in revision. Cortical atrophy appears to be an effect of ageing and not a sign of loosening of the femoral component.

We analysed in-vivo migration and wear over a long period of all-polyethylene acetabular cups which had not been affected by mechanical loosening. The selection criteria of regular radiological follow-up, good clinical outcome (Charnley score of 5 or 6), continued walking without crutches and no radiological signs of loosening of the acetabular cups were fulfilled by 25 Charnley total hip arthroplasties.

Mean migration, measured by the Nunn method, was 0.6 mm in the medial and 0.2 mm in the cranial direction. The mean yearly rate of wear was 0.05 mm and 0.04 mm, with six and two cups having no detectable wear, as measured by the Livermore and Charnley-Cupic methods, respectively. The maximal detected wear was 3.7 mm. There were no changes in the rate of wear with time. Computerised Ein Bild Röntgen Analyse (single-image radiological analysis) measurements of 20 hips indicated plastic deformation of the cups.

We conclude that long-term successful cups do not migrate and have a very low rate of wear which was not affected by ageing of the polyethylene. There was no evidence that polyethylene wear alone caused mechanical loosening of the cup but high rates of wear seem to have an adverse prognostic value in terms of the long-term survival of the prosthesis.