The role of vacuum mixing on the reduction of porosity and on the clinical performance of cemented total hip replacements remains uncertain. We have used paired femoral constructs prepared with either hand-mixed or vacuum-mixed cement in a cadaver model which simulated intra-operative conditions during cementing of the femoral component. After the cement had cured, the distribution of its porosity was determined, as was the strength of the cement-stem and cement-bone interfaces.

The overall fraction of the pore area was similar for both hand-mixed and vacuum-mixed cement (hand 6%; vacuum 5.7%; paired t-test, p = 0.187). The linear pore fractions at the interfaces were also similar for the two techniques. The pore number-density was much higher for the hand-mixed cement (paired t-test, p = 0.0013). The strength of the cement-stem interface was greater with the hand-mixed cement (paired t-test, p = 0.0005), while the strength of the cement-bone interface was not affected by the conditions of mixing (paired t-test, p = 0.275). The reduction in porosity with vacuum mixing did not affect the porosity of the mantle, but the distribution of the porosity can be affected by the technique of mixing used.

We have assessed the proximal capsular extension of the ankle joint in 18 patients who had a contrast-enhanced MRI ankle arthrogram in order to delineate the capsular attachments.

We noted consistent proximal capsular extensions anterior to the distal tibia and in the tibiofibular recess. The mean capsular extension anterior to the distal tibia was 9.6 mm (4.9 to 27.0) proximal to the anteroinferior tibial margin and 3.8 mm (−2.1 to 9.3) proximal to the dome of the tibial plafond. In the tibiofibular recess, the mean capsular extension was 19.2 mm (12.7 to 38.0) proximal to the anteroinferior tibial margin and 13.4 mm (5.8 to 20.5) proximal to the dome of the tibial plafond.

These areas of proximal capsular extensions run the risk of being traversed during the insertion of finewires for the treatment of fractures of the distal tibia. Surgeons using these techniques should be aware of this anatomy in order to minimise the risk of septic arthritis.

Metal-on-metal (MOM) bearings for hip arthroplasty are increasing in popularity. Concern remains, however, regarding the potential toxicological effects of the metal ions which these bearings release.

The serum levels of cobalt and chromium in 22 patients who had undergone MOM resurfacing arthroplasty were compared with a matched group of 22 patients who had undergone 28 mm MOM total hip arthroplasty (THA).

At a median of 16 months (7 to 56) after resurfacing arthroplasty, we found the median serum levels of cobalt and chromium to be 38 nmol/l (14 to 44) and 53 nmol/l (23 to 165) respectively. These were significantly greater than the levels after 28 mm MOM THA which were 22 nmol/l (15 to 87, p = 0.021) and 19 nmol/l (2 to 58, p < 0.001) respectively.

Since the upper limit for normal patients without implants is typically 5 nmol/l, both groups had significantly raised levels of metal ions. MOM bearings of large diameter, however, result in a greater systemic exposure of cobalt and chromium ions than bearings of small diameter. This may be of relevance for potential long-term side-effects. It is not known to what extent this difference is due to corrosion of the surfaces of the component or of the wear particles produced.

Metal-on-metal (MOM) is a commonly used bearing notable for its ‘suction fit’ when lubricated. In this study, we examined the capacity for MOM bearings to protect against dislocation after total hip replacement (THR).

We undertook a clinical investigation to compare the rate of dislocation of MOM bearings with those of ceramic-on-polyethylene (COP) bearings and found that one MOM bearing dislocated in a series of 109 hips (0.9%) compared with nine of 145 hips (6.2%) in the COP group (p = 0.02).

We also performed an in vitro investigation comparing the peak forces generated during forced separation of the two bearings of the same dimensions at velocities from 1 to 50 cm/s. This revealed that the MOM bearing generated significant resistance to separation at all velocities (maximum mean 24 N), whereas the COP did not (maximum mean 1.9 N, p < 0.001). We conclude that MOM bearings are more stable to dislocation than COP bearings as a result of the interfacial forces provided by a thin, lubricating fluid.

Templates are used in the preoperative planning of many orthopaedic procedures. The magnification of the bones on preoperative radiographs can vary despite using standardised radiological techniques. Templates will give misleading measurements unless this magnification is quantified.

A coin may be used to calculate the magnification, with significant improvement in the accuracy of templating (p = 0.05). A group of patients undergoing uncemented arthroplasty of the hip was at high risk for intraoperative fracture of the femur because the magnification of the radiograph was larger than that of the template.

We have investigated whether the thigh tourniquet used during total knee replacement (TKR) influenced the development of postoperative wound hypoxia and was a cause of delayed wound healing.

We allocated randomly 31 patients (31 TKRs) to one of three groups: 1) no tourniquet; 2) tourniquet inflated at low pressure (about 225 mmHg); and 3) tourniquet inflated to high pressure of about 350 mmHg. Wound oxygenation was measured using transcutaneous oxygen electrodes.

In the first week after surgery, patients with a tourniquet inflated to a high pressure had greater wound hypoxia than those with a low pressure. Those without a tourniquet also had wound hypoxia, but the degree and duration were less pronounced than in either of the groups with a tourniquet.

Use of a tourniquet during TKR can increase postoperative wound hypoxia, especially when inflated to high pressures. Our findings may be relevant to wound healing and the development of wound infection.

A total of 110 total knee replacements (TKRs) was randomised to receive either a cemented or an uncemented prosthesis. Postoperative venography at five to seven days was used to compare the prevalence, site and size of deep-vein thrombosis (DVT). We also compared the findings with those of postoperative venography in a group of patients with cemented total hip replacements (THRs).

The total prevalence of DVT was significantly greater after uncemented (81%) than after cemented TKR (55%). Both knee groups had a significantly higher prevalence of DVT than in cemented hip replacements (32%). We found no difference in the proportion with proximal DVT in the three groups (14%, 15% and 16%). The median length of the thrombi was significantly greater after cemented (26.5 cm) than after uncemented TKR (11 cm) or after cemented THR (7 cm). This difference was mainly due to greater lengths of distal rather than proximal thrombi.

We conclude that the use of cement may affect the formation of DVT after joint replacement, but does not appear to lead to an increased incidence.

We performed routine venography after operation in a consecutive series of 252 patients with total joint arthroplasties in whom no form of routine chemical or mechanical prophylaxis had been used.

The prevalence of deep-vein thrombosis (DVT) was 32% (16% distal, 16% proximal) after total hip replacement and 66% (50% distal, 16% proximal) after total knee replacement (p < 0.001). We did not treat distal DVT. There were only two readmissions within three months of surgery because of thromboembolic disease. There were two deaths within this period, neither of which was due to pulmonary embolism.