Osteoarthritis of the medial compartment of the knee often shows a specific pattern of anterior wear. Review of our revisions from a series of medial metal-backed Brigham unicondylar knee replacements performed between 1983 and 1989 showed that this wear pattern was common on the tibial polyethylene surface. We reviewed these cases retrospectively to compare the pattern of preoperative erosion with the wear of the prosthesis. In all 14 knees with severe anterior wear in a unicompartmental replacement, the prearthroplasty radiographs showed similar patterns, suggesting that the implanted tibial component may continue to be subjected to the same localised stresses that precipitated the failure of the original articular cartilage. Many tibial components implanted during the 1980s had an unacceptably thin anterior rim of polyethylene and it seems that greater thickness is essential at the anterior and peripheral margins of the tibial plateau.

Ten cases are described of catastrophic failure of the polyethylene liner of three different designs of uncemented acetabular component. Failure occurred as a result of either 'wearthrough' to the metal backing, liner fracture or a combination of both, at a mean of 4.6 years after implantation (2 to 7.6). At revision there was metallosis in all hips and osteolysis of the femur or the pelvis in six. Catastrophic failure was seen only in cups with a minimum polyethylene thickness of less than 5 mm.