We compared the incidence of pseudotumours after large head metal-on-metal (MoM) total hip arthroplasty (THA) with that after conventional metal-on-polyethylene (MoP) THA and assessed the predisposing factors to pseudotumour formation.

From a previous randomised controlled trial which compared large head (38 mm to 60 mm) cementless MoM THA with conventional head (28 mm) cementless MoP THA, 93 patients (96 THAs: 41 MoM (21 males, 20 females, mean age of 64 years, standard deviation (sd) 4) and 55 MoP (25 males, 30 females, mean age of 65 years, sd 5) were recruited after a mean follow-up of 50 months (36 to 64).

The incidence of pseudotumours, measured using a standardised CT protocol was 22 (53.7%) after MoM THA and 12 (21.8%) after MoP THA. Women with a MoM THA were more likely to develop a pseudotumour than those with a MoP THA (15 vs 7, odds ratio (OR) = 13.4, p < 0.001). There was a similar incidence of pseudotumours in men with MoM THAs and those with MoP THAs (7 vs 5, OR = 2.1, p = 0.30). Elevated cobalt levels (≥ 5 microgram/L) were only associated with pseudotumours in women with a MoM THA. There was no difference in mean Oxford and Harris hip scores between patients with a pseudotumour and those without.

Contrary to popular belief, pseudotumours occur frequently around MoP THAs. Women with a MoM THA and an elevated cobalt level are at greatest risk. In this study, pseudotumours had no effect on the functional outcome after either large head MoM or conventional MoP THA.

Cite this article: Bone Joint J 2015;97-B:1481–7.

We have investigated the use of a conically-shaped cement plug made of Polyactive (PA), a biodegradable copolymer. The flexibility and hydrogel properties were thought to facilitate occlusion of the femoral canal even when it was oval or irregular in shape. The function of the plug was first compared with that of the Thackray polyethylene model in 16 artificial plastic femora.

The maximum intramedullary pressure achieved during cementing was ten times higher with the biodegradable model. Migration or leakage of cement did not occur when the diameter of the femoral canal was equal to or smaller than the diameter of the plug. We also showed that the biodegradable properties of this implant were such that it did not require removal during revision.

The new plug was tested in a pilot clinical trial. At two years only two out of 21 patients had evidence of migration or leakage of cement, probably due to a mismatch in the size of plug and femoral canal. There were no local changes in the femur.