Aims. Hip resurfacing remains a potentially valuable surgical procedure for appropriately-selected patients with optimised implant choices. However, concern regarding high early failure rates continues to undermine confidence in use. A large contributor to failure is adverse local tissue reactions around metal-on-metal (MoM) bearing surfaces. Such phenomena have been well-explored around MoM total hip arthroplasties, but comparable data in equivalent hip resurfacing procedures is lacking. In order to define genetic predisposition, we performed a case-control study investigating the role of human leucocyte antigen (HLA) genotype in the development of pseudotumours around MoM hip resurfacings. Methods. A matched case-control study was performed using the prospectively-collected database at the host institution. In all, 16 MoM hip resurfacing 'cases' were identified as having symptomatic periprosthetic pseudotumours on preoperative metal artefact reduction sequence (MARS) MRI, and were subsequently histologically confirmed as high-grade aseptic lymphocyte-dominated vasculitis-associated lesions (ALVALs) at revision surgery. ‘Controls’ were matched by implant type in the absence of evidence of pseudotumour. Blood samples from all cases and controls were collected prospectively for high resolution genetic a nalysis targeting 11 separate HLA loci. Statistical significance was set at 0.10 a priori to determine the association between HLA genotype and pseudotumour formation, given the small sample size. Results. Using a previously-reported ALVAL classification, the majority of pseudotumour-positive caseswere found to have intermediate-grade group 2 (n = 10; 63%) or group 3 (n = 4; 25%) histological findings. Two further patients (13%) had high-grade group 4 lesions. HLA-DQB1*05:03:01 (p = 0.0676) and HLA-DRB1*14:54:01 (p = 0.0676) alleles were significantly associated with a higher risk of pseudotumour formation, while HLA-DQA1*03:01:01 (p = 0.0240), HLA-DRB1*04:04:01 (p = 0.0453), HLA-C*01:02:01 (p = 0.0453), and HLA-B*27:05:02 (p = 0.0855) were noted to confer risk reduction. Conclusion. These findings confirm the association between specific HLA genotypes and the risk of pseudotumour development around MoM hip resurfacings. Specifically, the two ‘at risk’ alleles (DQB1*05:03:01 and DRB1*14:54:01) may hold clinical value in preoperative screening and prospective surgical decision-making. Cite this article: Bone Jt Open 2023;4(3):182–187

Aims. The Birmingham Hip Resurfacing (BHR) was introduced in 1997 to address the needs of young active patients using a historically proven large-diameter metal-on-metal (MoM) bearing. A single designer surgeon’s consecutive series of 130 patients (144 hips) was previously reported at five and ten years, reporting three and ten failures, respectively. The aim of this study was to extend the follow-up of this original cohort at 25 years. Methods. The study extends the reporting on the first consecutive 144 resurfacing procedures in 130 patients for all indications. All operations were undertaken between August 1997 and May 1998. The mean age at operation was 52.1 years (SD 9.93; 17 to 76), and included 37 female patients (28.5%). Failure was defined as revision of either component for any reason. Kaplan-Meier survival analysis was performed. Routine follow-up with serum metal ion levels, radiographs, and Oxford Hip Scores (OHSs) was undertaken. Results. Overall implant survival was 83.50% (95% confidence interval (CI) 0.79 to 0.90) at 25 years, and the number at risk was 79. Survival in male patients at 25 years was 89.5% (95% CI 0.83 to 0.96) compared to 66.9% for female patients (95% CI 0.51 to 0.83). Ten additional failures occurred in the period of ten to 25 years. These involved an adverse reaction to metal debris in four patients, a periprosthetic femoral neck fracture affecting five patients, and aseptic loosening in one patient. The median chromium levels were 49.50 nmol/l (interquartile range (IQR) 34 to 70), and the median cobalt serum levels were 42 nmol/l (IQR 24.50 to 71.25). The median OHS at last follow-up was 35 (IQR 10 to 48). During the 25-year study period, 29 patients died. Patient survival at 25 years was 75.10% (95% CI 0.67 to 0.83). Conclusion. This study demonstrates that MoM hip resurfacing using the BHR provides a durable alternative to total hip arthroplasty (THA), particularly in younger male patients with osteoarthritis wishing to maintain a high level of function. These results compare favourably to the best results for THAs. Cite this article: Bone Joint J 2024;106-B(6):540–547

The aim of this study was to establish the natural course of unrevised asymptomatic pseudotumours after metal-on-metal (MoM) hip resurfacing during a six- to 12-month follow-up period. We used repeated metal artefact reduction sequence (MARS)-magnetic resonance imaging (MRI), serum metal ion analysis and clinical examination to study 14 unrevised hips (mean patient age 52.7 years, 46 to 68, 5 female, 7 male) with a pseudotumour and 23 hips (mean patient age 52.8 years, 38 to 69, 7 female, 16 male) without a pseudotumour. The mean post-operative time to the first MARS-MRI scan was 4.3 years (2.2 to 8.3), and mean time between the first and second MARS-MRI scan was eight months (6 to 12). At the second MRI scan, the grade of severity of the pseudotumour had not changed in 35 hips. One new pseudotumour (Anderson C2 score, moderate) was observed, and one pseudotumour was downgraded from C2 (moderate) to C1 (mild). In general, the characteristics of the pseudotumours hardly changed. Repeated MARS-MRI scans within one year in patients with asymptomatic pseudotumours after MoM hip resurfacing showed little or no variation. In 23 patients without pseudotumour, one new asymptomatic pseudotumour was detected. This is the first longitudinal study on the natural history of pseudotumours using MARS-MRI scans in hip resurfacing, and mirrors recent results for 28 mm diameter MoM total hip replacement. Cite this article: Bone Joint J 2013;95-B:1626–31

Objectives. We have encountered patients who developed large joint fluid collections with massive elevations in chromium (Cr) and cobalt (Co) concentrations following metal-on-metal (MoM) hip arthroplasties. In some cases, retrieval analysis determined that these ion concentrations could not be explained simply by the wear rates of the components. We hypothesized that these effects may be associated with aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL). Patients and Methods. We examined the influence of the ALVAL grade on synovial fluid Co and Cr concentrations following adjustment for patient and device variables, including volumetric wear rates. Initially restricting the analysis to include only patients with one MoM hip resurfacing device, we performed multiple regression analyses of prospectively collected data. We then repeated the same statistical approach using results from a larger cohort with different MoM designs, including total hip arthroplasties. Results. In the resurfacing cohort (n = 76), the statistical modelling indicated that the presence of severe ALVAL and a large fluid collection were associated with greater joint fluid Co concentrations after adjustment for volumetric wear rates (p = 0.005). These findings were replicated in the mixed implant group (n = 178), where the presence of severe ALVAL and a large fluid collection were significantly associated with greater fluid Co concentrations (p < 0.001). Conclusion. The development of severe ALVAL is associated with elevations in metal ion concentrations far beyond those expected from the volumetric loss from the prosthetic surfaces. This finding may aid the understanding of the sequence of events leading to soft-tissue reactions following MoM hip arthroplasties. Cite this article: D. J. Langton, R. P. Sidaginamale, T. J. Joyce, J. G. Bowsher, J. P. Holland, D. Deehan, A. V. F. Nargol, S. Natu. Aseptic lymphocyte-dominated vasculitis-associated lesions are related to changes in metal ion handling in the joint capsules of metal-on-metal hip arthroplasties. Bone Joint Res 2018;7:388–396. DOI: 10.1302/2046-3758.76.BJR-2018-0037

Aims

The aims of the study were to report for a cohort aged younger than 40 years: 1) indications for HRA; 2) patient-reported outcomes in terms of the modified Harris Hip Score (HHS); 3) dislocation rate; and 4) revision rate.

Aims

Large-diameter metal-on-metal (MoM) total hip arthroplasty (THA) has demonstrated unexpected high failure rates and pseudotumour formation. The purpose of this prospective cohort study is to report ten-year results in order to establish revision rate, prevalence of pseudotumour formation, and relation with whole blood cobalt levels.

Aims

We investigated whether blood metal ion levels could effectively identify patients with bilateral Birmingham Hip Resurfacing (BHR) implants who have adverse reactions to metal debris (ARMD).

Aims

Cardiac magnetic resonance (CMR) was used to assess whether cardiac function or tissue composition was affected in patients with well-functioning metal-on-metal hip resurfacing arthroplasties (MoMHRA) when compared with a group of controls, and to assess if metal ion levels correlated with any of the functional or structural parameters studied.

The presence of pseudotumours, which are soft-tissue masses relating to the hip, after metal-on-metal hip resurfacing arthroplasty has been associated with elevated levels of metal ions in serum, suggesting that pseudotumours occur when there is increased wear. We aimed to quantify the wear in vivo of implants revised for pseudotumours (eight) and of a control group of implants (22) revised for other reasons of failure.

We found that the implant group with pseudotumours had a significantly higher rate of median linear wear of the femoral component at 8.1 μm/year (2.75 to 25.4) than the 1.79 μm/year (0.82 to 4.15; p = 0.002) of the non-pseudotumour group. For the acetabular component a significantly higher rate of median linear wear of 7.36 μm/year (1.61 to 24.9) was observed in the pseudotumour group compared with 1.28 μm/year (0.81 to 3.33, p = 0.001) in the other group. Wear of the acetabular component in the pseudotumour group always involved the edge of the implant, indicating that edge-loading had occurred.

Our findings are the first direct evidence that pseudotumour is associated with increased wear at the metal-on-metal articulation. Furthermore, edge-loading with the loss of fluid-film lubrication may be an important mechanism of generation of wear in patients with a pseudotumour.

In this paper, we will consider the current role of metal-on-metal bearings by looking at three subtypes of MoM hip arthroplasty separately: Hip resurfacing, large head (> 36 mm) MoM THA and MoM THA with traditional femoral head sizes.

We undertook a retrospective cohort study to determine clinical outcomes following the revision of metal-on-metal (MoM) hip replacements for adverse reaction to metal debris (ARMD), and to identify predictors of time to revision and outcomes following revision. Between 1998 and 2012 a total of 64 MoM hips (mean age at revision of 57.8 years; 46 (72%) female; 46 (72%) hip resurfacings and 18 (28%) total hip replacements) were revised for ARMD at one specialist centre. At a mean follow-up of 4.5 years (1.0 to 14.6) from revision for ARMD there were 13 hips (20.3%) with post-operative complications and eight (12.5%) requiring re-revision.

The Kaplan–Meier five-year survival rate for ARMD revision was 87.9% (95% confidence interval 78.9 to 98.0; 19 hips at risk). Excluding re-revisions, the median absolute Oxford hip score (OHS) following ARMD revision using the percentage method (0% best outcome and 100% worst outcome) was 18.8% (interquartile range (IQR) 7.8% to 48.3%), which is equivalent to 39/48 (IQR 24.8/48 to 44.3/48) when using the modified OHS. Histopathological response did not affect time to revision for ARMD (p = 0.334) or the subsequent risk of re-revision (p = 0.879). Similarly, the presence or absence of a contralateral MoM hip bearing did not affect time to revision for ARMD (p = 0.066) or the subsequent risk of re-revision (p = 0.178).

Patients revised to MoM bearings had higher rates of re-revision (five of 16 MoM hips re-revised; p = 0.046), but those not requiring re-revision had good functional results (median absolute OHS 14.6% or 41.0/48). Short-term morbidity following revision for ARMD was comparable with previous reports. Caution should be exercised when choosing bearing surfaces for ARMD revisions.

Cite this article: Bone Joint J 2014;96-B:1600–9.

We measured the orientation of the acetabular and femoral components in 45 patients (33 men, 12 women) with a mean age of 53.4 years (30 to 74) who had undergone revision of metal-on-metal hip resurfacings. Three-dimensional CT was used to measure the inclination and version of the acetabular component, femoral version and the horizontal femoral offset, and the linear wear of the removed acetabular components was measured using a roundness machine.

We found that acetabular version and combined version of the acetabular and femoral components were weakly positively correlated with the rate of wear. The acetabular inclination angle was strongly positively correlated with the rate of wear. Femoral version was weakly negatively correlated with the rate of wear. Application of a threshold of > 5 μm/year for the rate of wear in order to separate the revisions into low or high wearing groups showed that more high wearing components were implanted outside Lewinnek’s safe zone, but that this was mainly due to the inclination of the acetabular component, which was the only parameter that significantly differed between the groups.

We were unable to show that excess version of the acetabular component alone or combined with femoral version was associated with an increase in the rate of wear based on our assessment of version using CT.

Aims

Our first aim was to determine whether there are significant changes in the level of metal ions in the blood at mid-term follow-up, in patients with an Articular Surface Replacement (ASR) arthroplasty. Secondly, we sought to identify risk factors for any increases.

Aims

To determine ten-year failure rates following 36 mm metal-on-metal (MoM) Pinnacle total hip arthroplasty (THA), and identify predictors of failure.

Objectives

The high revision rates of the DePuy Articular Surface Replacement (ASR) and the DePuy ASR XL (the total hip arthroplasty (THA) version) have led to questions over the viability of metal-on-metal (MoM) hip joints. Some designs of MoM hip joint do, however, have reasonable mid-term performance when implanted in appropriate patients. Investigations into the reasons for implant failure are important to offer help with the choice of implants and direction for future implant designs. One way to assess the performance of explanted hip prostheses is to measure the wear (in terms of material loss) on the joint surfaces.

We sought to establish the incidence of joint failure secondary to adverse reaction to metal debris (ARMD) following metal-on-metal hip resurfacing in a large, three surgeon, multicentre study involving 4226 hips with a follow-up of 10 to 142 months. Three implants were studied: the Articular Surface Replacement; the Birmingham Hip Resurfacing; and the Conserve Plus. Retrieved implants underwent analysis using a co-ordinate measuring machine to determine volumetric wear. There were 58 failures associated with ARMD. The median chromium and cobalt concentrations in the failed group were significantly higher than in the control group (p < 0.001). Survival analysis showed a failure rate in the patients with Articular Surface Replacement of 9.8% at five years, compared with < 1% at five years for the Conserve Plus and 1.5% at ten years for the Birmingham Hip Resurfacing. Two ARMD patients had relatively low wear of the retrieved components. Increased wear from the metal-on-metal bearing surface was associated with an increased rate of failure secondary to ARMD. However, the extent of tissue destruction at revision surgery did not appear to be dose-related to the volumetric wear.

Aims

The aims of this study were to compare the diagnostic test characteristics of ultrasound alone, metal artefact reduction sequence MRI (MARS-MRI) alone, and ultrasound combined with MARS-MRI for identifying intra-operative pseudotumours in metal-on-metal hip resurfacing (MoMHR) patients undergoing revision surgery.

Plasma levels of cobalt and chromium ions and Metal Artefact Reduction Sequence (MARS)-MRI scans were performed on patients with 209 consecutive, unilateral, symptomatic metal-on-metal (MoM) hip arthroplasties. There was wide variation in plasma cobalt and chromium levels, and MARS-MRI scans were positive for adverse reaction to metal debris (ARMD) in 84 hips (40%). There was a significant difference in the median plasma cobalt and chromium levels between those with positive and negative MARS-MRI scans (p < 0.001). Compared with MARS-MRI as the potential reference standard for the diagnosis of ARMD, the sensitivity of metal ion analysis for cobalt or chromium with a cut-off of > 7 µg/l was 57%. The specificity was 65%, positive predictive value was 52% and the negative predictive value was 69% in symptomatic patients. A lowered threshold of > 3.5 µg/l for cobalt and chromium ion levels improved the sensitivity and negative predictive value to 86% and 74% but at the expense of specificity (27%) and positive predictive value (44%).

Metal ion analysis is not recommended as a sole indirect screening test in the surveillance of symptomatic patients with a MoM arthroplasty. The investigating clinicians should have a low threshold for obtaining cross-sectional imaging in these patients, even in the presence of low plasma metal ion levels.

Persistent groin pain after seemingly successful total hip replacement (THR) appears to have become more common. Recent studies have indicated a high incidence after metal-on-polyethylene and metal-on-metal conventional THR and it has been documented in up to 18% of patients after metal-on-metal resurfacing. There are many causes, including acetabular loosening, stress fracture, and iliopsoas tendonitis and impingement. The evaluation of this problem requires a careful history and examination, plain radiographs and an algorithmic approach to special diagnostic imaging and tests. Non-operative treatment is not usually successful. Specific operative treatment depending on the cause of the pain usually involves revision of the acetabular component, iliopsoas tenotomy or other procedures, and is usually successful. Here, an appropriate algorithm is described.

Objectives

The aims of this piece of work were to: 1) record the background concentrations of blood chromium (Cr) and cobalt (Co) concentrations in a large group of subjects; 2) to compare blood/serum Cr and Co concentrations with retrieved metal-on-metal (MoM) hip resurfacings; 3) to examine the distribution of Co and Cr in the serum and whole blood of patients with MoM hip arthroplasties; and 4) to further understand the partitioning of metal ions between the serum and whole blood fractions.