Objectives. The high revision rates of the DePuy Articular Surface Replacement (ASR) and the DePuy ASR XL (the total hip arthroplasty (THA) version) have led to questions over the viability of metal-on-metal (MoM) hip joints. Some designs of MoM hip joint do, however, have reasonable mid-term performance when implanted in appropriate patients. Investigations into the reasons for implant failure are important to offer help with the choice of implants and direction for future implant designs. One way to assess the performance of explanted hip prostheses is to measure the wear (in terms of material loss) on the joint surfaces. Methods. In this study, a coordinate measuring machine (CMM) was used to measure the wear on five failed cementless Biomet Magnum/ReCap/ Taperloc large head MoM THAs, along with one Biomet ReCap resurfacing joint. Surface roughness measurements were also taken. The reason for revision of these implants was pain and/or adverse reaction to metal debris (ARMD) and/or elevated blood metal ion levels. Results. The mean wear rate of the articulating surfaces of the heads and acetabular components of all six joints tested was found to be 6.1 mm. 3. /year (4.1 to 7.6). The mean wear rate of the femoral head tapers of the five THAs was 0.054 mm. 3. /year (0.021 to 0.128) with a mean maximum wear depth of 5.7 µm (4.3 to 8.5). Conclusion. Although the taper wear was relatively low, the wear from the articulating surfaces was sufficient to provide concern and was potentially large enough to have been the cause of failure of these joints. The authors believe that patients implanted with the ReCap system, whether the resurfacing prosthesis or the THA, should be closely monitored. Cite this article: S. C. Scholes, B. J. Hunt, V. M. Richardson, D. J. Langton, E. Smith, T. J. Joyce. Explant analysis of the Biomet Magnum/ReCap metal-on-metal hip joint. Bone Joint Res 2017;6:113–122. DOI: 10.1302/2046-3758.62.BJR-2016-0130.R2

The peri-prosthetic tissue response to wear debris is complex and influenced by various factors including the size, area and number of particles. We hypothesised that the ‘biologically active area’ of all metal wear particles may predict the type of peri-prosthetic tissue response. . Peri-prosthetic tissue was sampled from 21 patients undergoing revision of a small diameter metal-on-metal (MoM) total hip arthroplasty (THA) for aseptic loosening. An enzymatic protocol was used for tissue digestion and scanning electron microscope was used to characterise particles. Equivalent circle diameters and particle areas were calculated. Histomorphometric analyses were performed on all tissue specimens. Aspirates of synovial fluid were collected for analysis of the cytokine profile analysis, and compared with a control group of patients undergoing primary THA (n = 11) and revision of a failed ceramic-on-polyethylene arthroplasty (n = 6). . The overall distribution of the size and area of the particles in both lymphocyte and non-lymphocyte-dominated responses were similar; however, the subgroup with lymphocyte-dominated peri-prosthetic tissue responses had a significantly larger total number of particles. . 14 cytokines (interleukin (IL)-1ß, IL-2, IL-4, IL-5, IL-6, IL-10, IL-13, IL-17, interferon (IFN)-γ, and IFN-gamma-inducible protein 10), chemokines (macrophage inflammatory protein (MIP)-1α and MIP-1ß), and growth factors (granulocyte macrophage colony stimulating factor (GM-CSF) and platelet derived growth factor) were detected at significantly higher levels in patients with metal wear debris compared with the control group. . Significantly higher levels for IL-1ß, IL-5, IL-10 and GM-CSF were found in the subgroup of tissues from failed MoM THAs with a lymphocyte-dominated peri-prosthetic response compared with those without this response. . These results suggest that the ‘biologically active area’ predicts the type of peri-prosthetic tissue response. The cytokines IL-1ß, IL-5, IL-10, and GM-CSF are associated with lymphocyte-dominated tissue responses from failed small-diameter MoM THA. Cite this article: Bone Joint J 2015;97-B:917–23

Metal-on-metal resurfacing of the hip (MoMHR) has enjoyed a resurgence in the last decade, but is now again in question as a routine option for osteoarthritis of the hip. Proponents of hip resurfacing suggest that its survival is superior to that of conventional hip replacement (THR), and that hip resurfacing is less invasive, is easier to revise than THR, and provides superior functional outcomes. Our argument serves to illustrate that none of these proposed advantages have been realised and new and unanticipated serious complications, such as pseudotumors, have been associated with the procedure. As such, we feel that the routine use of MoMHR is not justified. Cite this article: Bone Joint J 2014;96-B(11 Suppl A):17–21

Objectives. Previous studies have suggested that metal-on-metal (MoM) Pinnacle (DePuy Synthes, Warsaw, Indiana) hip arthroplasties implanted after 2006 exhibit higher failure rates. This was attributed to the production of implants with reduced diametrical clearances between their bearing surfaces, which, it was speculated, were outside manufacturing tolerances. This study aimed to better understand the performance of Pinnacle Systems manufactured before and after this event. Methods. A total of 92 retrieved MoM Pinnacle hips were analyzed, of which 45 were implanted before 2007, and 47 from 2007 onwards. The ‘pre-2007’ group contained 45 implants retrieved from 21 male and 24 female patients, with a median age of 61.3 years (interquartile range (IQR) 57.1 to 65.5); the ‘2007 onwards’ group contained 47 implants retrieved from 19 male and 28 female patients, with a median age of 61.8 years (IQR 58.5 to 67.8). The volume of material lost from their bearing and taper surfaces was measured using coordinate and roundness measuring machines. These outcomes were then compared statistically using linear regression models, adjusting for potentially confounding factors. Results. There was no significant difference between the taper and bearing wear rates of the ‘pre-2007’ and ‘2007 onwards’ groups (p = 0.67 and p = 0.39, respectively). Pinnacles implanted from 2007 onwards were revised after a mean time of 50 months, which was significantly earlier than the ‘pre-2007’ hips (96 months) (p < 0.001). A reduction in the time to revision was present year on year from 2003 to 2011. Conclusion. We found no difference in the wear rate of these implants based on the year of implantation. The ‘pre-2007’ hips had a two-fold greater time to revision than those implanted after 2007; this may be due to the increased surveillance of MoM hips following UK regulatory advice and several high-profile failures. Interestingly, we observed a decreasing trend in the mean time to revision every year from 2003 onwards. Cite this article: S. Bergiers, H. S. Hothi, J. Henckel, A. Eskelinen, J. Skinner, A. Hart. Wear performance of retrieved metal-on-metal Pinnacle hip arthroplasties implanted before and after 2007. Bone Joint Res 2018;7:595–600. DOI: 10.1302/2046-3758.711.BJR-2018-0143.R1

Aims. This study presents the long-term survivorship, risk factors for prosthesis survival, and an assessment of the long-term effects of changes in surgical technique in a large series of patients treated by metal-on-metal (MoM) hip resurfacing arthroplasty (HRA). Patients and Methods. Between November 1996 and January 2012, 1074 patients (1321 hips) underwent HRA using the Conserve Plus Hip Resurfacing System. There were 787 men (73%) and 287 women (27%) with a mean age of 51 years (14 to 83). The underlying pathology was osteoarthritis (OA) in 1003 (75.9%), developmental dysplasia of the hip (DDH) in 136 (10.3%), avascular necrosis in 98 (7.4%), and other conditions, including inflammatory arthritis, in 84 (6.4%). Results. The mean follow-up time was 10.5 years (1 to 20). Using revision for any reason as the endpoint, the overall survivorship at 15 years was 89.4% (95% confidence interval (CI) 86.8 to 91.4). There was a substantial increase between the first and second generation of surgical technique (86.6% vs 90.1%; p = 0.05). Men with idiopathic OA had a 15-year survivorship of 94.5% and women, 82.2% (p = 0.001); gender was not a risk factor after stratification by component size and aetiology. Using revision for excessive wear (ion levels > 7 µg/l associated with symptoms or adverse local tissue reactions) as the endpoint, the 15-year survivorship was 98.5%. Risk factors for revision for all modes of failure were an underlying pathology of hip dysplasia, a contact patch to rim (CPR) distance of 7 mm or less, an age at surgery of 55 years or less, and a femoral component size of 46 mm or less. Specific risk factors for aseptic failure of the femoral component were early surgical technique, a cementless metaphyseal stem, and a body mass index of 24 kg/m. 2. or less. Conclusion. HRA is a viable concept; metal-on-metal bearings are well suited for this procedure when a well-designed device is properly implanted. The best results were obtained in men with OA, but survivorship was better for other underlying pathologies and for women after changes were made to the technique of implantation. Lifetime durability is a possible outcome for many patients despite a high level of activity. Cite this article: Bone Joint J 2018;100-B:1424–33

Aims. Many case reports and small studies have suggested that cobalt ions are a potential cause of cardiac complications, specifically cardiomyopathy, after metal-on-metal (MoM) total hip arthroplasty (THA). The impact of metal ions on the incidence of cardiac disease after MoM THA has not been evaluated in large studies. The aim of this study was to compare the rate of onset of new cardiac symptoms in patients who have undergone MoM THA with those who have undergone metal-on-polyethylene (MoP) THA. Patients and Methods. Data were extracted from the Standard Analytics Files database for patients who underwent MoM THA between 2005 and 2012. Bearing surface was selected using International Classification of Diseases ninth revision codes. Patients with a minimum five-year follow-up were selected. An age and gender-matched cohort of patients who underwent MoP THA served as a comparison group. New diagnoses of cardiac disease were collected during the follow-up period. Comorbidities and demographics were identified and routine descriptive statistics were used. Results. We identified 29 483 patients who underwent MoM THA and 24 175 matched patients who underwent MoP THA. Both groups had a mean Charlson comorbidity index score of 4. There were no statistically significant differences in 30 of 31 pre-existing comorbidities. Patients undergoing MoM THA had a slightly lower incidence of cardiac failure compared with those undergoing MoP THA at three years (6.60% versus 7.06%, odds ratio (OR) 0.93, 95% confidence interval (CI) 0.87 to 0.99) and four years (8.73% versus 9.49%, OR 0.91, 95% CI 0.86 to 0.97) postoperatively, with no difference in the incidence of new cardiac failure in between the groups at five years. There was no statistically significant difference in the incidence of arrhythmia, myocardial infarction and cardiomyopathy at any time between the two groups. Conclusion. MoM THA is not associated with cardiac complications. Initial reports may have represented individual instances of cardiac disease in patients with a failing MoM articulation rather than an emerging epidemiological trend. Cite this article: Bone Joint J 2018;100-B:28–32

We report the clinical and radiological outcome at ten years of 104 primary total hip replacements (100 patients) using the Metasul metal-on-metal bearing. Of these, 52 had a cemented Stuehmer-Weber polyethylene acetabular component with a Metasul bearing and 52 had an uncemented Allofit acetabular component with a Metasul liner. A total of 15 patients (16 hips) died before their follow-up at ten years and three were lost to follow-up. The study group therefore comprised 82 patients (85 hips). The mean Oxford score at ten years was 20.7 (12 to 42). Six of 85 hips required revision surgery. One was performed because of infection, one for aseptic loosening of the acetabular component and four because of unexplained pain. Histological examination showed an aseptic lymphocytic vasculitis associated lesion-type tissue response in two of these. Continued follow-up is advocated in order to monitor the long-term performance of the Metasul bearing and tissue responses to metal debris

Aims . The primary aim of this independent prospective randomised trial was to compare serum metal ion levels for ceramic-on-metal (CoM) and metal-on-metal (MoM) bearing surfaces in total hip arthroplasty (THA). Our one-year results demonstrated elevation in metal ion levels above baseline with no significant difference between the CoM and MoM groups. This paper reviews the five-year data. Patients and Methods. The implants used in each patient differed only in respect to the type of femoral head (ceramic or metal). At five-year follow-up of the 83 enrolled patients, data from 67 (36 CoM, 31 MoM) was available for comparison. Results. The mean serum cobalt (Co) and chromium (Cr) ion levels remained above baseline in both groups (CoM: Co 1.16 μg/l (0.41 to 14.67), Cr 1.05 μg/l (0.16 to 12.58); MoM: Co 2.93 μg/l (0.35 to 30.29), Cr 1.85 μg/l (0.36 to 17.00)) but the increase was significantly less in the CoM cohort (Co difference p = 0.001, Cr difference p = 0.002). These medium-term results, coupled with lower revision rates from national joint registries, suggest that the performance of CoM THA may be superior to that of MoM. . Conclusion. While both bearing combinations have since been withdrawn these results provide useful information for planning clinical surveillance of CoM THAs and warrants continued monitoring. Cite this article: Bone Joint J 2017;99-B:1298–1303

Osteolysis is due to particulate wear debris and is responsible for the long-term failure of total hip replacements. It has stimulated the development of alternative joint surfaces such as metal-on-metal or ceramic-on-ceramic implants. Since 1988 the second-generation metal-on-metal implant Metasul has been used in over 60 000 hips. Analysis of 118 retrieved specimens of the head or cup showed rates of wear of approximately 25 μm for the whole articulation per year in the first year, decreasing to about 5 μm per year after the third. Metal surfaces have a ‘self-polishing’ capacity. Scratches are worn out by further joint movement. Volumetric wear was decreased some 60-fold compared with that of metal-on-polyethylene implants, suggesting that second-generation metal-on-metal prostheses may considerably reduce osteolysis

We have reviewed 42 patients who had revision of metal-on-metal resurfacing procedures, mostly because of problems with the acetabular component. The revisions were carried out a mean of 26.2 months (1 to 76) after the initial operation and most of the patients (30) were female. Malpositioning of the acetabular component resulted in 27 revisions, mostly because of excessive abduction (mean 69.9°; 56° to 98°) or insufficient or excessive anteversion. Seven patients had more than one reason for revision. The mean increase in the diameter of the component was 1.8 mm (0 to 4) when exchange was needed. Malpositioning of the components was associated with metallosis and a high level of serum ions. The results of revision of the femoral component to a component with a modular head were excellent, but four patients had dislocation after revision and four required a further revision

Aims. There are many guidelines that help direct the management of patients with metal-on-metal (MOM) hip arthroplasties. We have undertaken a study to compare the management of patients with MOM hip arthroplasties in different countries. . Methods. Six international tertiary referral orthopaedic centres were invited to participate by organising a multi-disciplinary team (MDT) meeting, consisting of two or more revision hip arthroplasty surgeons and a musculoskeletal radiologist. A full clinical dataset including history, blood tests and imaging for ten patients was sent to each unit, for discussion and treatment planning. Differences in the interpretation of findings, management decisions and rationale for decisions were compared using quantitative and qualitative methods. Results. Overall agreement between the orthopaedic centres and the recommended treatment plans for the ten patients with MOM hip implants was moderate (kappa = 0.6). Full agreement was seen in a third of cases, however split decisions were also seen in a third of cases. Units differed in their interpretation of the significance of the investigation findings and put varying emphasis on serial changes, in the presence of symptoms. Discussion. In conclusion, the management of raised or rising blood metal ions, cystic pseudotumours and peri-acetabular osteolysis led to inconsistency in the agreement between centres. Coordinated international guidance and MDT panel discussions are recommended to improve consensus in decision making. Take home message: A lack of evidence and the subsequent variation in regulator guidance leads to differences in opinions, the clinical impact of which can be reduced through a multi-disciplinary team approach to managing patients with MOM hip implants. Cite this article: Bone Joint J 2016;98-B:179–86

Bioengineering reasons for increased wear and failure of metal-on-metal (MoM) bearings in hip prostheses have been described. Low wear occurs in MoM hips when the centre of the femoral head is concentric with the centre of the acetabular component and the implants are correctly positioned. Translational or rotational malpositioning of the components can lead to the contact-patch of the femoral component being displaced to the rim of the acetabular component, resulting in a ten- to 100-fold increase in wear and metal ion levels. This may cause adverse tissue reactions, loosening of components and failure of the prosthesis

We compared the incidence of pseudotumours after large head metal-on-metal (MoM) total hip arthroplasty (THA) with that after conventional metal-on-polyethylene (MoP) THA and assessed the predisposing factors to pseudotumour formation. . From a previous randomised controlled trial which compared large head (38 mm to 60 mm) cementless MoM THA with conventional head (28 mm) cementless MoP THA, 93 patients (96 THAs: 41 MoM (21 males, 20 females, mean age of 64 years, standard deviation (. sd. ) 4) and 55 MoP (25 males, 30 females, mean age of 65 years, . sd. 5) were recruited after a mean follow-up of 50 months (36 to 64). . The incidence of pseudotumours, measured using a standardised CT protocol was 22 (53.7%) after MoM THA and 12 (21.8%) after MoP THA. Women with a MoM THA were more likely to develop a pseudotumour than those with a MoP THA (15 vs 7, odds ratio (OR) = 13.4, p < 0.001). There was a similar incidence of pseudotumours in men with MoM THAs and those with MoP THAs (7 vs 5, OR = 2.1, p = 0.30). Elevated cobalt levels (≥ 5 microgram/L) were only associated with pseudotumours in women with a MoM THA. There was no difference in mean Oxford and Harris hip scores between patients with a pseudotumour and those without. . Contrary to popular belief, pseudotumours occur frequently around MoP THAs. Women with a MoM THA and an elevated cobalt level are at greatest risk. In this study, pseudotumours had no effect on the functional outcome after either large head MoM or conventional MoP THA. Cite this article: Bone Joint J 2015;97-B:1481–7

Aims. The National Joint Registry for England, Wales and Northern Ireland (NJR) has extended its scope to report on hospital, surgeon and implant performance. Data linkage of the NJR to the London Implant Retrieval Centre (LIRC) has previously evaluated data quality for hip primary procedures, but did not assess revision records. . Methods. We analysed metal-on-metal hip revision procedures performed between 2003 and 2013. A total of 69 929 revision procedures from the NJR and 929 revised pairs of components from the LIRC were included. Results. We were able to link 716 (77.1%) revision procedures on the NJR to the LIRC. This meant that 213 (22.9%) revision procedures at the LIRC could not be identified on the NJR. We found that 349 (37.6%) explants at the LIRC completed the full linkage process to both NJR primary and revision databases. Data completion was excellent (> 99.9%) for revision procedures reported to the NJR. Discussion. This study has shown that only approximately one third of retrieved components at the LIRC, contributed to survival curves on the NJR. We recommend prospective registry-retrieval linkage as a tool to feedback missing and erroneous data to the NJR and improve data quality. Take home message: Prospective Registry – retrieval linkage is a simple tool to evaluate and improve data quality on the NJR. Cite this article: Bone Joint J 2016;98-B:33–9

In a double-blinded randomised controlled trial, 83 patients with primary osteoarthritis of the hip received either a ceramic-on-metal (CoM) or metal-on-metal (MoM) total hip replacement (THR). The implants differed only in the bearing surfaces used. The serum levels of cobalt and chromium and functional outcome scores were compared pre-operatively and at six and 12 months post-operatively. Data were available for 41 CoM and 36 MoM THRs (four patients were lost to follow-up, two received incorrect implants). The baseline characteristics of both cohorts were similar. Femoral head size measured 36 mm in all but two patients who had 28 mm heads. The mean serum cobalt and chromium levels increased in both groups, with no difference noted between groups at six months (cobalt p = 0.67, chromium p = 0.87) and 12 months (cobalt p = 0.76, chromium p = 0.76) post-operatively. Similarly, the mean Oxford hip scores, Western Ontario and McMaster Universities Osteoarthritis index and University of California, Los Angeles activity scores showed comparable improvement at 12 months. Our findings indicate that CoM and MoM couplings are associated with an equivalent increase in serum cobalt and chromium levels, and comparable functional outcome scores at six and 12-months follow-up.

Patients from a randomised trial on resurfacing hip arthroplasty (RHA) (n = 36, 19 males; median age 57 years, 24 to 65) comparing a conventional 28 mm metal-on-metal total hip arthroplasty (MoM THA) (n = 28, 17 males; median age 59 years, 37 to 65) and a matched control group of asymptomatic patients with a 32 mm ceramic-on-polyethylene (CoP) THA (n = 33, 18 males; median age 63 years, 38 to 71) were cross-sectionally screened with metal artefact reducing sequence-MRI (MARS-MRI) for pseudotumour formation at a median of 55 months (23 to 72) post-operatively. MRIs were scored by consensus according to three different classification systems for pseudotumour formation. . Clinical scores were available for all patients and metal ion levels for MoM bearing patients. . Periprosthetic lesions with a median volume of 16 mL (1.5 to 35.9) were diagnosed in six patients in the RHA group (17%), one in the MoM THA group (4%) and six in the CoP group (18%). The classification systems revealed no clear differences between the groups. Solid lesions (n = 3) were exclusively encountered in the RHA group. Two patients in the RHA group and one in the MoM THA group underwent a revision for pseudotumour formation. There was no statistically significant relationship between clinical scoring, metal ion levels and periprosthetic lesions in any of the groups. . Periprosthetic fluid collections are seen on MARS-MRI after conventional CoP THA and RHA and may reflect a soft-tissue collection or effusion. . Currently available MRI classification systems seem to score these collections as pseudotumours, causing an-overestimatation of the incidence of pseudotumours. . Cite this article: Bone Joint J 2015;97-B:1175–82

Aims. We wished to investigate the influence of metal debris exposure on the subsequent immune response and resulting soft-tissue injury following metal-on-metal (MoM) hip arthroplasty. Some reports have suggested that debris generated from the head-neck taper junction is more destructive than equivalent doses from metal bearing surfaces. . Patients and Methods. We investigated the influence of the source and volume of metal debris on chromium (Cr) and cobalt (Co) concentrations in corresponding blood and hip synovial fluid samples and the observed agglomerated particle sizes in excised tissues using multiple regression analysis of prospectively collected data. A total of 199 explanted MoM hips (177 patients; 132 hips female) were analysed to determine rates of volumetric wear at the bearing surfaces and taper junctions. . Results. The statistical modelling suggested that a greater source contribution of metal debris from the taper junction was associated with smaller aggregated particle sizes in the local tissues and a relative reduction of Cr ion concentrations in the corresponding synovial fluid and blood samples. Metal debris generated from taper junctions appears to be of a different morphology, composition and therefore, potentially, immunogenicity to that generated from bearing surfaces. Conclusion. The differences in debris arising from the taper and the articulating surfaces may provide some understanding of the increased incidence of soft-tissue reactions reported in patients implanted with MoM total hip arthroplasties compared with patients with hip resurfacings. Cite this article: Bone Joint J 2016;98-B:925–33

We report the outcome of total hip replacement in 29 failed metal-on-metal resurfacing hip replacements in which the primary surgery was performed between August 1995 and February 2005. The mean length of follow-up was five years (1.7 to 11.7). Of the 29 hip resurfacings, 19 acetabular components and all the femoral components were revised (28 uncemented stems and one cemented stem). There were no deaths and none of the patients was lost to follow-up. None of the hips underwent any further revision. The results of the revision resurfacing group were compared with those of a control group of age-matched patients. In the latter group there were 236 primary total hip replacements and 523 resurfacings performed during the same period by the same surgeons. The outcome of the revision resurfacing group was comparable with that of the stemmed primary hip replacement group but was less good than that of the primary hip resurfacing group. Long-term follow-up is advocated to monitor the outcome of these cases

We evaluated the concentrations of chromium and cobalt ions in blood after metal-on-metal surface replacement arthroplasty using a wrought-forged, high carbon content chromium-cobalt alloy implant in 64 patients. At one year, mean whole blood ion levels were 1.61 μg/L (0.4 to 5.5) for chromium and 0.67 μg/L (0.23 to 2.09) for cobalt. The pre-operative ion levels, component size, female gender and the inclination of the acetabular component were inversely proportional to the values of chromium and/or cobalt ions at one year postoperatively. Other factors, such as age and level of activity, did not correlate with the levels of metal ions. We found that the levels of the ions in the serum were 1.39 and 1.37 times higher for chromium and cobalt respectively than those in the whole blood. The levels of metal ions obtained may be specific to the hip resurfacing implant and reflect its manufacturing process

Objectives. The aims of this piece of work were to: 1) record the background concentrations of blood chromium (Cr) and cobalt (Co) concentrations in a large group of subjects; 2) to compare blood/serum Cr and Co concentrations with retrieved metal-on-metal (MoM) hip resurfacings; 3) to examine the distribution of Co and Cr in the serum and whole blood of patients with MoM hip arthroplasties; and 4) to further understand the partitioning of metal ions between the serum and whole blood fractions. Methods. A total of 3042 blood samples donated to the local transfusion centre were analysed to record Co and Cr concentrations. Also, 91 hip resurfacing devices from patients who had given pre-revision blood/serum samples for metal ion analysis underwent volumetric wear assessment using a coordinate measuring machine. Linear regression analysis was carried out and receiver operating characteristic curves were constructed to assess the reliability of metal ions to identify abnormally wearing implants. The relationship between serum and whole blood concentrations of Cr and Co in 1048 patients was analysed using Bland-Altman charts. This relationship was further investigated in an in vitro study during which human blood was spiked with trivalent and hexavalent Cr, the serum then separated and the fractions analysed. Results. Only one patient in the transfusion group was found to have a blood Co > 2 µg/l. Blood/Serum Cr and Co concentrations were reliable indicators of abnormal wear. Blood Co appeared to be the most useful clinical test, with a concentration of 4.5 µg/l showing sensitivity and specificity for the detection of abnormal wear of 94% and 95%, respectively. Generated metal ions tended to fill the serum compartment preferentially in vivo and this was replicated in the in vitro study when blood was spiked with trivalent Cr and bivalent Co. Conclusions. Blood/serum metal ion concentrations are reliable indicators of abnormal wear processes. Important differences exist however between elements and the blood fraction under study. Future guidelines must take these differences into account