Despite the increasing interest and subsequent published literature on hip resurfacing arthroplasty, little is known about the prevalence of its complications and in particular the less common modes of failure. The aim of this study was to identify the prevalence of failure of hip resurfacing arthroplasty and to analyse the reasons for it.

From a multi-surgeon series (141 surgeons) of 5000 Birmingham hip resurfacings we have analysed the modes, prevalence, gender differences and times to failure of any hip requiring revision. To date 182 hips have been revised (3.6%). The most common cause for revision was a fracture of the neck of the femur (54 hips, prevalence 1.1%), followed by loosening of the acetabular component (32 hips, 0.6%), collapse of the femoral head/avascular necrosis (30 hips, 0.6%), loosening of the femoral component (19 hips, 0.4%), infection (17 hips, 0.3%), pain with aseptic lymphocytic vascular and associated lesions (ALVAL)/metallosis (15 hips, 0.3%), loosening of both components (five hips, 0.1%), dislocation (five hips, 0.1%) and malposition of the acetabular component (three hips, 0.1%). In two cases the cause of failure was unknown.

Comparing men with women, we found the prevalence of revision to be significantly higher in women (women = 5.7%; men = 2.6%, p < 0.001). When analysing the individual modes of failure women had significantly more revisions for loosening of the acetabular component, dislocation, infection and pain/ALVAL/metallosis (p < 0.001, p = 0.004, p = 0.008, p = 0.01 respectively).

The mean time to failure was 2.9 years (0.003 to 11.0) for all causes, with revision for fracture of the neck of the femur occurring earlier than other causes (mean 1.5 years, 0.02 to 11.0). There was a significantly shorter time to failure in men (mean 2.1 years, 0.4 to 8.7) compared with women (mean 3.6 years, 0.003 to 11.0) (p < 0.001).

Wear of metal-on-metal bearings causes elevated levels of cobalt and chromium in blood and body fluids. Metal-on-metal bearings have two distinct wear phases. In the early phase, the wear rate is high. Later, it decreases and the bearing enters a steady-state phase. It is expected that as the wear rates decline, the level of cobalt detected in plasma will also decrease. We studied the baseline and exercise-related cobalt rise in 21 patients (13 men and eight women) with a mean age of 54 years (38 to 80) who had undergone successful hip resurfacing at a mean of 44 months (10 to 96) earlier. Our results showed that circulating baseline cobalt levels were not significantly correlated with the time since implantation (r = 0.08, p = 0.650). By contrast, the exercise-related cobalt rise was directly correlated with the inclination angle of the acetabular component (r = 0.47, p = 0.032) and inversely correlated with the time since implantation (r = −0.5, p = 0.020).

Inclination of the acetabular component should be kept less than 40° to decrease the production of wear debris.