Objectives. The use of ceramic femoral heads in total hip arthroplasty (THA) has increased due to their proven low bearing wear characteristics. Ceramic femoral heads are also thought to reduce wear and corrosion at the head-stem junction with titanium (Ti) stems when compared with metal heads. We sought to evaluate taper damage of ceramic compared with metal heads when paired with cobalt chromium (CoCr) alloy stems in a single stem design. Methods. This retrieval study involved 48 total hip arthroplasties (THAs) with CoCr V40 trunnions paired with either CoCr (n = 21) or ceramic (n = 27) heads. The taper junction of all hips was evaluated for fretting/corrosion damage and volumetric material loss using a roundness-measuring machine. We used linear regression analysis to investigate taper damage differences after adjusting for potential confounding variables. Results. We measured median taper material loss rates of 0.210 mm. 3. /year (0.030 to 0.448) for the metal head group and 0.084 mm. 3. /year (0.059 to 0.108) for the ceramic group. The difference was not significant (p = 0.58). Moreover, no significant correlation between material loss and implant or patient factors (p > 0.05) was found. Conclusions. Metal heads did not increase taper damage on CoCr trunnions compared with ceramic heads from the same hip design. The amount of material released at the taper junctions was very low when compared with available data regarding CoCr/Ti coupling in metal-on-metal bearings. Cite this article: A. Di Laura, H. Hothi, J. Henckel, I. Swiatkowska, M. H. L. Liow, Y-M. Kwon, J. A. Skinner, A. J. Hart.
This study compared component wear rates and pre-revision blood metal ions levels in two groups of failed metal-on-metal hip arthroplasties: hip resurfacing and modular total hip replacement (THR). There was no significant difference in the median rate of linear wear between the groups for both acetabular (p = 0.4633) and femoral (p = 0.0872) components. There was also no significant difference in the median linear wear rates when failed hip resurfacing and modular THR hips of the same type (ASR and Birmingham hip resurfacing (BHR)) were compared. Unlike other studies of well-functioning hips, there was no significant difference in pre-revision blood metal ion levels between hip resurfacing and modular THR. Edge loading was common in both groups, but more common in the resurfacing group (67%) than in the modular group (57%). However, this was not significant (p = 0.3479). We attribute this difference to retention of the neck in resurfacing of the hip, leading to impingement-type edge loading. This was supported by visual evidence of impingement on the femur. These findings show that failed metal-on-metal hip resurfacing and modular THRs have similar component wear rates and are both associated with raised pre-revision blood levels of metal ions.
Acetabular edge-loading was a cause of increased wear rates in metal-on-metal hip arthroplasties, ultimately contributing to their failure. Although such wear patterns have been regularly reported in retrieval analyses, this study aimed to determine their in vivo location and investigate their relationship with acetabular component positioning. 3D CT imaging was combined with a recently validated method of mapping bearing surface wear in retrieved hip implants. The asymmetrical stabilizing fins of Birmingham hip replacements (BHRs) allowed the co-registration of their acetabular wear maps and their computational models, segmented from CT scans. The in vivo location of edge-wear was measured within a standardized coordinate system, defined using the anterior pelvic plane.Aims
Methods
The main advantage of 3D-printed, off-the-shelf acetabular implants is the potential to promote enhanced bony fixation due to their controllable porous structure. In this study we investigated the extent of osseointegration in retrieved 3D-printed acetabular implants. We compared two groups, one made via 3D-printing (n = 7) and the other using conventional techniques (n = 7). We collected implant details, type of surgery and removal technique, patient demographics, and clinical history. Bone integration was assessed by macroscopic visual analysis, followed by sectioning to allow undecalcified histology on eight sections (~200 µm) for each implant. The outcome measures considered were area of bone attachment (%), extent of bone ingrowth (%), bone-implant contact (%), and depth of ingrowth (%), and these were quantified using a line-intercept method.Aims
Methods
Aims. The aim of this study was to evaluate fretting and corrosion in retrieved oxidized zirconium (OxZr; OXINIUM, Smith & Nephew, Memphis, Tennessee) femoral heads and compare the results with those from a matched cohort of cobalt-chromium (CoCr) femoral heads. Patients and Methods. A total of 28 OxZr femoral heads were retrieved during revision total hip arthroplasty (THA) and matched to 28 retrieved CoCr heads according to patient demographics. The mean age at index was 56 years (46 to 83) in the OxZr group and 70 years (46 to 92) in the CoCr group. Fretting and corrosion scores of the female taper of the heads were measured according to the modified Goldberg scoring method. Results. The OxZr-retrieved femoral heads showed significantly lower mean corrosion scores than the CoCr heads (1.3 (1 to 2.75) vs 2.1 (1 to 4); p < 0.01). Mean fretting scores were also significantly lower in the OxZr cohort when compared with the CoCr cohort (1.3 (1 to 2) vs 1.5 (1 to 2.25); p = 0.02). OxZr heads had more damage in the proximal region compared with the distal region of the head. Location had no impact on damage of CoCr heads. A trend towards increased corrosion in large heads was seen only in the CoCr heads, although this was not statistically significant. Conclusion.
Aims. We evaluated a large database with mechanical failure of a single uncemented modular femoral component, used in revision hip arthroplasty, as the end point and compared them to a control group treated with the same implant. Patient- and implant-specific risk factors for implant failure were analyzed. . Methods. All cases of a fractured uncemented modular revision femoral component from one manufacturer until April 2017 were identified and the total number of implants sold until April 2017 was used to calculate the fracture rate. The manufacturer provided data on patient demographics, time to failure, and implant details for all notified fractured devices. Patient- and implant-specific risk factors were evaluated using a logistic regression model with multiple imputations and compared to data from a previously published reference group, where no fractures had been observed. The results of a
Objectives. We have encountered patients who developed large joint fluid collections with massive elevations in chromium (Cr) and cobalt (Co) concentrations following metal-on-metal (MoM) hip arthroplasties. In some cases,
We present a series of 35 patients (19 men and
16 women) with a mean age of 64 years (36.7 to 75.9), who underwent
total hip replacement using the ESKA dual-modular short stem with
metal on-polyethylene bearing surfaces. This implant has a modular
neck section in addition to the modular head. Of these patients,
three presented with increasing post-operative pain due to pseudotumour
formation that resulted from corrosion at the modular neck-stem
junction. These patients underwent further surgery and aseptic lymphocytic
vaculitis associated lesions were demonstrated on histological
Symptomatic cobalt toxicity from a failed total
hip replacement is a rare but devastating complication. It has been reported
following revision of fractured ceramic components, as well as in
patients with failed metal-on-metal articulations. Potential clinical
findings include fatigue, weakness, hypothyroidism, cardiomyopathy,
polycythaemia, visual and hearing impairment, cognitive dysfunction,
and neuropathy. We report a case of an otherwise healthy 46-year-old
patient, who developed progressively worsening symptoms of cobalt
toxicity beginning approximately six months following synovectomy
and revision of a fractured ceramic-on-ceramic total hip replacement
to a metal-on-polyethylene bearing. The whole blood cobalt levels
peaked at 6521 µg/l. The patient died from cobalt-induced cardiomyopathy.
Implant
This study reports the ten-year wear rates, incidence of osteolysis, clinical outcomes, and complications of a multicentre randomized controlled trial comparing oxidized zirconium (OxZr) versus cobalt-chrome (CoCr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) and highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA). Patients undergoing primary THA were recruited from four institutions and prospectively allocated to the following treatment groups: Group A, CoCr femoral head with XLPE liner; Group B, OxZr femoral head with XLPE liner; and Group C, OxZr femoral head with UHMWPE liner. All study patients and assessors recording outcomes were blinded to the treatment groups. The outcomes of 262 study patients were analyzed at ten years’ follow-up.Aims
Methods
This study investigates head-neck taper corrosion with varying head size in a novel hip simulator instrumented to measure corrosion related electrical activity under torsional loads. In all, six 28 mm and six 36 mm titanium stem-cobalt chrome head pairs with polyethylene sockets were tested in a novel instrumented hip simulator. Samples were tested using simulated gait data with incremental increasing loads to determine corrosion onset load and electrochemical activity. Half of each head size group were then cycled with simulated gait and the other half with gait compression only. Damage was measured by area and maximum linear wear depth.Aims
Methods
The Exeter V40 cemented polished tapered stem system has demonstrated excellent long-term outcomes. This paper presents a systematic review of the existing literature and reports on a large case series comparing implant fractures between the Exeter V40 series; 125 mm and conventional length stem systems. A systematic literature search was performed adhering to the Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) criteria. In parallel, we performed a retrospective single centre study of Exeter V40 femoral stem prosthetic fractures between April 2003 and June 2020.Aims
Methods
The optimum clearance between the bearing surfaces of hip arthroplasties is unknown. Theoretically, to minimize wear, it is understood that clearances must be low enough to maintain optimal contact pressure and fluid film lubrication, while being large enough to allow lubricant recovery and reduce contact patch size. This study aimed to identify the relationship between diametrical clearance and volumetric wear, through the analysis of retrieved components. A total of 81 metal-on-metal Pinnacle hips paired with 12/14 stems were included in this study. Geometrical analysis was performed on each component, using coordinate and roundness measuring machines. The relationship between their as-manufactured diametrical clearance and volumetric wear was investigated. The Mann-Whitney U test and unpaired Aims
Methods
The aim of this study was to develop a novel computational model for estimating head/stem taper mechanics during different simulated assembly conditions. Finite element models of generic cobalt-chromium (CoCr) heads on a titanium stem taper were developed and driven using dynamic assembly loads collected from clinicians. To verify contact mechanics at the taper interface, comparisons of deformed microgroove characteristics (height and width of microgrooves) were made between model estimates with those measured from five retrieved implants. Additionally, these models were used to assess the role of assembly technique—one-hit versus three-hits—on the taper interlock mechanical behaviour.Aims
Methods
This combined clinical and in vitro study aimed to determine the incidence of liner malseating in modular dual mobility (MDM) constructs in primary total hip arthroplasties (THAs) from a large volume arthroplasty centre, and determine whether malseating increases the potential for fretting and corrosion at the modular metal interface in malseated MDM constructs using a simulated corrosion chamber. For the clinical arm of the study, observers independently reviewed postoperative radiographs of 551 primary THAs using MDM constructs from a single manufacturer over a three-year period, to identify the incidence of MDM liner-shell malseating. Multivariable logistic regression analysis was performed to identify risk factors including age, sex, body mass index (BMI), cup design, cup size, and the MDM case volume of the surgeon. For the in vitro arm, six pristine MDM implants with cobalt-chrome liners were tested in a simulated corrosion chamber. Three were well-seated and three were malseated with 6° of canting. The liner-shell couples underwent cyclic loading of increasing magnitudes. Fretting current was measured throughout testing and the onset of fretting load was determined by analyzing the increase in average current.Aims
Methods
Modular dual-mobility constructs reduce the risk of dislocation after revision total hip arthroplasty (THA). However, questions about metal ions from the cobalt-chromium (CoCr) liner persist, and are particularly germane to patients being revised for adverse local tissue reactions (ALTR) to metal. We determined the early- to mid-term serum Co and Cr levels after modular dual-mobility components were used in revision and complex primary THAs, and specifically included patients revised for ALTR. Serum Co and Cr levels were measured prospectively in 24 patients with a modular dual-mobility construct and a ceramic femoral head. Patients with CoCr heads or contralateral THAs with CoCr heads were excluded. The mean age was 63 years (35 to 83), with 13 patients (54%) being female. The mean follow-up was four years (2 to 7). Indications for modular dual-mobility were prosthetic joint infection treated with two-stage exchange and subsequent reimplantation (n = 8), ALTR revision (n = 7), complex primary THA (n = 7), recurrent instability (n = 1), and periprosthetic femoral fracture (n = 1). The mean preoperative Co and Cr in patients revised for an ALTR were 29.7 μg/l (2 to 146) and 21.5 μg/l (1 to 113), respectively.Aims
Patients and Methods
Previous studies have suggested that metal-on-metal (MoM) Pinnacle (DePuy Synthes, Warsaw, Indiana) hip arthroplasties implanted after 2006 exhibit higher failure rates. This was attributed to the production of implants with reduced diametrical clearances between their bearing surfaces, which, it was speculated, were outside manufacturing tolerances. This study aimed to better understand the performance of Pinnacle Systems manufactured before and after this event. A total of 92 retrieved MoM Pinnacle hips were analyzed, of which 45 were implanted before 2007, and 47 from 2007 onwards. The ‘pre-2007’ group contained 45 implants retrieved from 21 male and 24 female patients, with a median age of 61.3 years (interquartile range (IQR) 57.1 to 65.5); the ‘2007 onwards’ group contained 47 implants retrieved from 19 male and 28 female patients, with a median age of 61.8 years (IQR 58.5 to 67.8). The volume of material lost from their bearing and taper surfaces was measured using coordinate and roundness measuring machines. These outcomes were then compared statistically using linear regression models, adjusting for potentially confounding factors.Objectives
Methods
Modular dual mobility (DM) prostheses in which a cobalt-chromium liner is inserted into a titanium acetabular shell ( This was a prospective study of patients between 18 and 65 years of age, with a body mass index (BMI) < 35 kg/m2 and University of California at Los Angeles (UCLA) activity score > 6, who received a modular cobalt-chromium acetabular liner, highly crosslinked polyethylene mobile bearing, and cementless titanium femoral stem for their primary THA. Patients with a history of renal disease and metal hardware elsewhere in the body were excluded. A total of 43 patients (30 male, 13 female; mean age 52.6 years (Aims
Patients and Methods
To present a surgically relevant update of trunnionosis. Systematic review performed April 2017.Aims
Materials and Methods
There are limited published data detailing the volumetric material loss from tapers of conventional metal-on-polyethylene (MoP) total hip arthroplasties (THAs). Our aim was to address this by comparing the taper wear rates measured in an explanted cohort of the widely used Exeter THA with those measured in a group of metal-on-metal (MoM) THAs. We examined an existing retrieval database to identify all Exeter V40 and Universal MoP THAs. Volumetric wear analysis of the taper surfaces was conducted using previously validated methodology. These values were compared with those obtained from a series of MoM THAs using non-parametric statistical methodology. A number of patient and device variables were accounted for using multiple regression modelling.Aims
Patients and Methods
To report our experience with trunnion corrosion following metal-on-polyethylene
total hip arthroplasty, in particular to report the spectrum of
presentation and determine the mean time to presentation. We report the presenting symptoms and signs, intraoperative findings,
and early results and complications of operative treatment in nine
patients with a mean age of 74 years (60 to 86). The onset of symptoms
was at a mean of seven years (3 to 18) after index surgery.Aims
Patients and Methods
Our aim in this study was to describe a continuing review of
11 total hip arthroplasties using 22.225 mm Alumina ceramic femoral
heads on a Charnley flanged femoral component, articulating against
a silane crosslinked polyethylene. Nine patients (11 THAs) were reviewed at a mean of 27.5 years
(26 to 28) post-operatively. Outcome was assessed using the d’Aubigne
and Postel, and Charnley scores and penetration was recorded on
radiographs. In addition, the oxidation of a 29-year-old shelf-aged
acetabular component was analysed.Aims
Patients and Methods
We aimed to determine the effect of surgical approach on the
histology of the femoral head following resurfacing of the hip. We performed a histological assessment of the bone under the
femoral component taken from retrieval specimens of patients having
revision surgery following resurfacing of the hip. We compared the
number of empty lacunae in specimens from patients who had originally
had a posterior surgical approach with the number in patients having alternative
surgical approaches.Objectives
Methods
Adverse reaction to wear and corrosion debris
is a cause for concern in total hip arthroplasty (THA). Modular junctions
are a potential source of such wear products and are associated
with secondary pseudotumour formation. We present a consecutive series of 17 patients treated at our
unit for this complication following metal-on-highly cross-linked
polyethylene (MoP) THA. We emphasise the risk of misdiagnosis as
infection, and present the aggregate laboratory results and pathological
findings in this series. The clinical presentation was pain, swelling or instability.
Solid, cystic and mixed soft-tissue lesions were noted on imaging
and confirmed intra-operatively. Corrosion at the head–neck junction
was noted in all cases. No bacteria were isolated on multiple pre-
and intra-operative samples yet the mean erythrocyte sedimentation
rate was 49 (9 to 100) and C-reactive protein 32 (0.6 to 106) and
stromal polymorphonuclear cell counts were noted in nine cases. Adverse soft–tissue reactions can occur in MoP THA owing to corrosion
products released from the head–neck junction. The diagnosis should
be carefully considered when investigating pain after THA. This
may avoid the misdiagnosis of periprosthetic infection with an unidentified
organism and mitigate the unnecessary management of these cases
with complete single- or two-stage exchange. Cite this article:
Tribocorrosion at the head–neck taper interface
– so-called ‘taperosis’ – may be a source of metal ions and particulate
debris in metal-on-polyethylene total hip arthroplasty (THA). We examined the effect of femoral head length on fretting and
corrosion in retrieved head–neck tapers Head length was observed to affect fretting (p = 0.03), with
28 mm + 8 mm femoral heads showing greater total fretting scores
than all other head lengths. The central zone of the femoral head
bore taper was subject to increased fretting damage (p = 0.01),
regardless of head length or stem offset. High-offset femoral stems
were associated with greater total fretting of the bore taper (p
= 0.04). Increased fretting damage is seen with longer head lengths and
high-offset femoral stems, and occurs within a central concentric
zone of the femoral head bore taper. Further investigation is required
to determine the effect of increased head size, and variations in
head–neck taper design. Cite this article:
Dislocation remains among the most common complications
of, and reasons for, revision of both primary and revision total
hip replacements (THR). Hence, there is great interest in maximising
stability to prevent this complication. Head size has been recognised
to have a strong influence on the risk of dislocation post-operatively.
As femoral head size increases, stability is augmented, secondary
to an increase in impingement-free range of movement. Larger head
sizes also greatly increase the ‘jump distance’ required for the
head to dislocate in an appropriately positioned cup. Level-one
studies support the use of larger diameter heads as they decrease
the risk of dislocation following primary and revision THR. Highly cross-linked
polyethylene has allowed us to increase femoral head size, without
a marked increase in wear. However, the thin polyethylene liners
necessary to accommodate larger heads may increase the risk of liner
fracture and larger heads have also been implicated in causing soft-tissue
impingement resulting in groin pain. Larger diameter heads also
impart larger forces on the femoral trunnion, which may contribute
to corrosion, metal release, and adverse local tissue reactions.
Alternative large bearings including large ceramic heads and dual
mobility bearings may mitigate some of these risks, and several
of these devices have been used with clinical success. Cite this article:
This study reports the mid-term results of a large-bearing hybrid metal-on-metal total hip replacement in 199 hips (185 patients) with a mean follow-up of 62 months (32 to 83). Two patients died of unrelated causes and 13 were lost to follow-up. In all, 17 hips (8.5%) have undergone revision, and a further 14 are awaiting surgery. All revisions were symptomatic. Of the revision cases, 14 hips showed evidence of adverse reactions to metal debris. The patients revised or awaiting revision had significantly higher whole blood cobalt ion levels (p = 0.001), but no significant difference in acetabular component size or position compared with the unrevised patients. Wear analysis (n = 5) showed increased wear at the trunnion-head interface, normal levels of wear at the articulating surfaces and evidence of corrosion on the surface of the stem. The cumulative survival rate, with revision for any reason, was 92.4% (95% confidence interval 87.4 to 95.4) at five years. Including those awaiting surgery, the revision rate would be 15.1% with a cumulative survival at five years of 89.6% (95% confidence interval 83.9 to 93.4). This hybrid metal-on-metal total hip replacement series has shown an unacceptably high rate of failure, with evidence of high wear at the trunnion-head interface and passive corrosion of the stem surface. This raises concerns about the use of large heads on conventional 12/14 tapers.
We conducted a retrospective study to assess
the prevalence of adverse reactions to metal debris (ARMD) in patients
operated on at our institution with metal-on-metal (MoM) total hip
replacements with 36 mm heads using a Pinnacle acetabular shell.
A total of 326 patients (150 males, 175 hips; 176 females, 203 hips)
with a mean age of 62.7 years (28 to 85) and mean follow-up of 7.5
years (0.1 to 10.8) participating in our in-depth modern MoM follow-up
programme were included in the study, which involved recording whole
blood cobalt and chromium ion measurements, Oxford hip scores (OHS)
and plain radiographs of the hip and targeted cross-sectional imaging. Elevated
blood metal ion levels (>
5 parts per billion) were seen in 32 (16.1%)
of the 199 patients who underwent unilateral replacement. At 23
months after the start of our modern MoM follow-up programme, 29
new cases of ARMD had been revealed. Hence, the nine-year survival
of this cohort declined from 96% (95% CI 95 to 98) with the old
surveillance routine to 86% (95% CI 82 to 90) following the new
protocol. Although ARMD may not be as common in 36 mm MoM THRs as
in those with larger heads, these results support the Medicines
and Healthcare Products Regulatory Agency guidelines on regular
reviews and further investigations, and emphasise the need for specific
a follow-up programme for patients with MoM THRs. Cite this article:
The issues surrounding raised levels of metal
ions in the blood following large head metal-on-metal total hip replacement
(THR), such as cobalt and chromium, have been well documented. Despite
the national popularity of uncemented metal-on-polyethylene (MoP)
THR using a large-diameter femoral head, few papers have reported
the levels of metal ions in the blood following this combination.
Following an isolated failure of a 44 mm Trident–Accolade uncemented
THR associated with severe wear between the femoral head and the
trunnion in the presence of markedly elevated levels of cobalt ions
in the blood, we investigated the relationship between modular femoral head
diameter and the levels of cobalt and chromium ions in the blood
following this THR. A total of 69 patients received an uncemented Trident–Accolade
MoP THR in 2009. Of these, 43 patients (23 men and 20 women, mean
age 67.0 years) were recruited and had levels of cobalt and chromium
ions in the blood measured between May and June 2012. The patients
were then divided into three groups according to the diameter of
the femoral head used: 12 patients in the 28 mm group (controls),
18 patients in the 36 mm group and 13 patients in the 40 mm group.
A total of four patients had identical bilateral prostheses in situ
at phlebotomy: one each in the 28 mm and 36 mm groups and two in
the 40 mm group. There was a significant increase in the mean levels of cobalt
ions in the blood in those with a 36 mm diameter femoral head compared
with those with a 28 mm diameter head (p = 0.013). The levels of
cobalt ions in the blood were raised in those with a 40 mm diameter
head but there was no statistically significant difference between
this group and the control group (p = 0.152). The levels of chromium
ions in the blood were normal in all patients. The clinical significance of this finding is unclear, but we
have stopped using femoral heads with a diameter of ≤ 36 mm, and
await further larger studies to clarify whether, for instance, this
issue particularly affects this combination of components. Cite this article:
Squeaking arising from a ceramic-on-ceramic (CoC)
total hip replacement (THR) may cause patient concern and in some
cases causes patients to seek revision surgery. We performed a meta-analysis
to determine the incidence of squeaking and the incidence of revision
surgery for squeaking. A total of 43 studies including 16 828 CoC
THR that reported squeaking, or revision for squeaking, were entered
into the analysis. The incidence of squeaking was 4.2% and the incidence
of revision for squeaking was 0.2%. The incidence of squeaking in
patients receiving the Accolade femoral stem was 8.3%, and the incidence
of revision for squeaking in these patients was 1.3%. Cite this article:
We conducted a systematic review and meta-analysis of randomised controlled trials comparing cross-linked with conventional polyethylene liners for total hip replacement in order to determine whether these liners reduce rates of wear, radiological evidence of osteolysis and the need for revision. The MEDLINE, EMBASE and COCHRANE databases were searched from their inception to May 2010 for all trials involving the use of cross-linked polyethylene in total hip replacement. Eligibility for inclusion in the review included the random allocation of treatments, the use of cross-linked and conventional polyethylene, and radiological wear as an outcome measure. The pooled mean differences were calculated for bedding-in, linear wear rate, three-dimensional linear wear rate, volumetric wear rate and total linear wear. Pooled risk ratios were calculated for radiological osteolysis and revision hip replacement. A search of the literature identified 194 potential studies, of which 12 met the inclusion criteria. All reported a significant reduction in radiological wear for cross-linked polyethylene. The pooled mean differences for linear rate of wear, three-dimensional linear rate of wear, volumetric wear rate and total linear wear were all significantly reduced for cross-linked polyethylene. The risk ratio for radiological osteolysis was 0.40 (95% confidence interval 0.27 to 0.58; I2 = 0%), favouring cross-linked polyethylene. The follow-up was not long enough to show a difference in the need for revision surgery.
Noise generation has been reported with ceramic-on-ceramic
articulations in total hip replacement (THR). This study evaluated
208 consecutive Delta Motion THRs at a mean follow-up of 21 months
(12 to 35). There were 141 women and 67 men with a mean age of 59
years (22 to 84). Patients were reviewed clinically and radiologically,
and the incidence of noise was determined using a newly described
assessment method. Noise production was examined against range of
movement, ligamentous laxity, patient-reported outcome scores, activity
level and orientation of the acetabular component. There were 143
silent hips (69%), 22 (11%) with noises other than squeaking, 17
(8%) with unreproducible squeaking and 26 (13%) with reproducible
squeaking. Hips with reproducible squeaking had a greater mean range
of movement (p <
0.001) and mean ligament laxity (p = 0.004), smaller
median head size (p = 0.01) and decreased mean acetabular component
inclination (p = 0.02) and anteversion angle (p = 0.02) compared
with the other groups. There was no relationship between squeaking
and age (p = 0.13), height (p = 0.263), weight (p = 0.333), body
mass index (p = 0.643), gender (p = 0.07) or patient outcome score
(p = 0.422). There were no revisions during follow-up. Despite the
surprisingly high incidence of squeaking, all patients remain satisfied
with their hip replacement. Cite this article:
We analysed 54 alumina ceramic-on-ceramic bearings
from total hip replacements retrieved at one centre after a mean
duration of 3.5 years (0.2 to 10.6)
We report a case of a male patient presenting
with bilateral painful but apparently well-positioned and -fixed
large-diameter metal-on-metal hip replacements four years post-operatively.
Multiple imaging modes revealed a thick-walled, cystic expansile
mass in communication with the hip joint (a pseudotumour). Implant
retrieval analysis and tissue culture eliminated high bearing wear
or infection as causes for the soft-tissue reaction, but noted marked corrosion
of the modular neck taper adaptor and corrosion products in the
tissues. Therefore, we believe corrosion products from the taper
caused by mismatch of the implant components led to pseudotumour
formation requiring revision.
Lately, concerns have arisen following the use of large metal-on-metal bearings in hip replacements owing to reports of catastrophic soft-tissue reactions resulting in implant failure and associated complications. This review examines the literature and contemporary presentations on current clinical dilemmas in metal-on-metal hip replacement.
We prospectively assessed the efficacy of a ceramic-on-metal
(CoM) hip bearing with uncemented acetabular and femoral components
in which cobalt–chrome acetabular liners and alumina ceramic heads
were used. The cohort comprised 94 total hip replacements (THRs) in 83 patients
(38 women and 45 men) with a mean age of 58 years (42 to 70). Minimum
follow-up was two years. All patients had pre- and post-operative
assessment using the Western Ontario and McMaster Universities osteoarthritis
index (WOMAC), Oxford hip score and Short-Form 12 scores. All showed
a statistically significant improvement from three months post-operatively
onwards (all p <
0.001). After two years whole blood metal ion levels were measured and
chromosomal analysis was performed. The levels of all metal ions
were elevated except vanadium. Levels of chromium, cobalt, molybdenum
and titanium were significantly higher in patients who underwent
bilateral THR compared with those undergoing unilateral THR (p <
0.001).
Chromosomal analysis demonstrated both structural and aneuploidy
mutations. There were significantly more breaks and losses than
in the normal population (p <
0.001). There was no significant
difference in chromosomal aberration between those undergoing unilateral
and bilateral procedures (all analyses p ≥ 0.62). The use of a CoM THR is effective clinically in the short-term,
with no concerns, but the significance of high metal ion levels
and chromosomal aberrations in the long-term remains unclear. Cite this article:
Despite the increasing interest and subsequent published literature on hip resurfacing arthroplasty, little is known about the prevalence of its complications and in particular the less common modes of failure. The aim of this study was to identify the prevalence of failure of hip resurfacing arthroplasty and to analyse the reasons for it. From a multi-surgeon series (141 surgeons) of 5000 Birmingham hip resurfacings we have analysed the modes, prevalence, gender differences and times to failure of any hip requiring revision. To date 182 hips have been revised (3.6%). The most common cause for revision was a fracture of the neck of the femur (54 hips, prevalence 1.1%), followed by loosening of the acetabular component (32 hips, 0.6%), collapse of the femoral head/avascular necrosis (30 hips, 0.6%), loosening of the femoral component (19 hips, 0.4%), infection (17 hips, 0.3%), pain with aseptic lymphocytic vascular and associated lesions (ALVAL)/metallosis (15 hips, 0.3%), loosening of both components (five hips, 0.1%), dislocation (five hips, 0.1%) and malposition of the acetabular component (three hips, 0.1%). In two cases the cause of failure was unknown. Comparing men with women, we found the prevalence of revision to be significantly higher in women (women = 5.7%; men = 2.6%, p <
0.001). When analysing the individual modes of failure women had significantly more revisions for loosening of the acetabular component, dislocation, infection and pain/ALVAL/metallosis (p <
0.001, p = 0.004, p = 0.008, p = 0.01 respectively). The mean time to failure was 2.9 years (0.003 to 11.0) for all causes, with revision for fracture of the neck of the femur occurring earlier than other causes (mean 1.5 years, 0.02 to 11.0). There was a significantly shorter time to failure in men (mean 2.1 years, 0.4 to 8.7) compared with women (mean 3.6 years, 0.003 to 11.0) (p <
0.001).
Between 1986 and 1991 we implanted 331 consecutive Furlong hydroxyapatite-coated femoral components of a total hip replacement in 291 patients. A cemented acetabular prosthesis was used in 217 hips and a hydroxyapatite-coated component in 114. We describe the long-term clinical and radiological survival of the femoral component at a mean follow-up of 17.5 years (15 to 21). Only two patients (0.68%) were lost to follow-up. With revision of the femoral component for any reason as the endpoint, the survival at a mean of 17 years was 97.4% (95% confidence interval 94.1 to 99.5), and with revision for aseptic loosening as the endpoint it was 100%. The survival at a maximum of 21 years with revision of the femoral component for any reason as the endpoint was 97.4% (95% confidence interval 81.0 or 99.5). These results compare favourably with the best long-term results of cemented or uncemented femoral components used in total hip replacement.
Early failure associated with adverse reactions to metal debris is an emerging problem after hip resurfacing but the exact mechanism is unclear. We analysed our entire series of 660 metal-on-metal resurfacings (Articular Surface Replacement (ASR) and Birmingham Hip Resurfacing (BHR)) and large-bearing ASR total hip replacements, to establish associations with metal debris-related failures. Clinical and radiological outcomes, metal ion levels, explant studies and lymphocyte transformation tests were performed. A total of 17 patients (3.4%) were identified (all ASR bearings) with adverse reactions to metal debris, for which revision was required. This group had significantly smaller components, significantly higher acetabular component anteversion, and significantly higher whole concentrations of blood and joint chromium and cobalt ions than asymptomatic patients did (all p <
0.001). Post-revision lymphocyte transformation tests on this group showed no reactivity to chromium or cobalt ions. Explants from these revisions had greater surface wear than retrievals for uncomplicated fractures. The absence of adverse reactions to metal debris in patients with well-positioned implants usually implies high component wear. Surgeons must consider implant design, expected component size and acetabular component positioning in order to reduce early failures when performing large-bearing metal-on-metal hip resurfacing and replacement.
Two Durasul highly crosslinked polyethylene liners were exchanged during revision surgery four and five years after implantation, respectively. The retrieved liners were evaluated macroscopically and surface analysis was performed using optical and electron microscopy. A sample of each liner was used to determine the oxidation of the material by Fourier transform infrared spectroscopy. Samples of the capsule were examined histologically. The annual wear rate was found to be 0.010 and 0.015 mm/year, respectively. Surface analysis showed very little loss of material caused by wear. Histological evaluation revealed a continuous neosynovial lining with single multinucleated foreign-body giant cells. Our findings showed no unexpected patterns of wear on the articulating surfaces up to five years after implantation and no obvious failure of material.
Resurfacing arthroplasty of the hip is being used increasingly as an alternative to total hip replacement, especially for young active patients. There is concern about necrosis of the femoral head after resurfacing which can result in fracture and loosening. Most systems use a cemented femoral component, with the potential for thermal necrosis of the cancellous bone of the reamed femoral head. We used thermal probes to record temperatures close to the cement-bone interface during resurfacing arthroplasty. The maximum temperature recorded at the cement-bone interface in four cases was approximately 68°C which was higher than that reported to kill osteocytes. A modified surgical technique using insertion of a suction cannula into the lesser trochanter, generous pulsed lavage and early reduction of the joint significantly reduced the maximum recorded cancellous bone temperature to approximately 36°C in five cases (p = 0.014). We recommend the modified technique since it significantly reduces temperatures at the cement-bone interface.
The dysplasia cup, which was devised as an adjunct to the Birmingham Hip Resurfacing system, has a hydroxyapatite-coated porous surface and two supplementary neutralisation screws to provide stable primary fixation, permit early weight-bearing, and allow incorporation of morcellised autograft without the need for structural bone grafting. A total of 110 consecutive dysplasia resurfacing arthroplasties in 103 patients (55 men and 48 women) performed between 1997 and 2000 was reviewed with a minimum follow-up of six years. The mean age at operation was 47.2 years (21 to 62) and 104 hips (94%) were Crowe grade II or III. During the mean follow-up of 7.8 years (6 to 9.6), three hips (2.7%) were converted to a total hip replacement at a mean of 3.9 years (2 months to 8.1 years), giving a cumulative survival of 95.2% at nine years (95% confidence interval 89 to 100). The revisions were due to a fracture of the femoral neck, a collapse of the femoral head and a deep infection. There was no aseptic loosening or osteolysis of the acetabular component associated with either of the revisions performed for failure of the femoral component. No patient is awaiting a revision. The median Oxford hip score in 98 patients with surviving hips at the final review was 13 and the 10th and the 90th percentiles were 12 and 23, respectively.
We present the histological findings of bone retrieved from beneath the femoral components of failed metal-on-metal hip resurfacing arthroplasties. Of a total of 377 patients who underwent resurfacing arthroplasty, 13 required revision; for fracture of the femoral neck in eight, loosening of a component in three and for other reasons in two. None of these cases had shown histological evidence of osteonecrosis in the femoral bone at the time of the initial implantation. Bone from the remnant of the femoral head showed changes of osteonecrosis in all but one case at revision. In two cases of fracture which occurred within a week of implantation, the changes were compatible with early necrosis of the edge of the fracture. In the remaining six fractures, there were changes of established osteonecrosis. In all but one of the non-fracture cases, patchy osteonecrosis was seen. We conclude that histological evidence of osteonecrosis is a common finding in failed resurfaced hips. Given that osteonecrosis is extensive in resurfaced femoral heads which fail by fracture, it is likely to play a role in the causation of these fractures.
The Cambridge Cup has been designed to replace the horseshoe-shaped articular cartilage of the acetabulum and the underlying subchondral bone. It is intended to provide physiological loading with minimal resection of healthy bone. The cup has been used in 50 women with displaced, subcapital fractures of the neck of the femur. In 24 cases, the cup was coated with hydroxyapatite. In 26, the coating was removed before implantation in order to simulate the effect of long-term resorption. The mean Barthel index and the Charnley-modified Merle d’Aubigné scores recovered to their levels before fracture. We reviewed 30 women at two years, 21 were asymptomatic and nine reported minimal pain. The mean scores deteriorated slightly after five years reflecting the comorbidity of advancing age. Patients with the hydroxyapatite-coated components remained asymptomatic, with no wear or loosening. The uncoated components migrated after four years and three required revision. This trial shows good early results using a novel, hydroxyapatite-coated, physiological acetabular component.