The early failure and revision of bimodular primary total hip arthroplasty prostheses requires the identification of the risk factors for material loss and wear at the taper junctions through taper wear analysis. Deviations in taper geometries between revised and pristine modular neck tapers were determined using high resolution tactile measurements. A new algorithm was developed and validated to allow the quantitative analysis of material loss, complementing the standard visual inspection currently used.

The algorithm was applied to a sample of 27 retrievals (in situ from 2.9 to 38.1 months) of the withdrawn Rejuvenate modular prosthesis. The mean wear volumes on the flat distal neck piece taper was 3.35 mm³ (0.55 to 7.57), mainly occurring in a characteristic pattern in areas with high mechanical loading. Wear volume tended to increase with time to revision (r² = 0.423, p = 0.001). Implant and patient specific data (offset, stem size, patient’s mass, age and body mass index) did not correlate with the amount of material loss observed (p >  0.078). Bilaterally revised implants showed higher amounts of combined total material loss and similar wear patterns on both sides. The consistent wear pattern found in this study has not been reported previously, suggesting that the device design and materials are associated with the failure of this prosthesis.

Cite this article: Bone Joint J 2015;97-B:1350–7.

Following the recall of modular neck hip stems in July 2012, research into femoral modularity will intensify over the next few years. This review aims to provide surgeons with an up-to-date summary of the clinically relevant evidence. The development of femoral modularity, and a classification system, is described. The theoretical rationale for modularity is summarised and the clinical outcomes are explored. The review also examines the clinically relevant problems reported following the use of femoral stems with a modular neck.

Joint replacement registries in the United Kingdom and Australia have provided data on the failure rates of modular devices but cannot identify the mechanism of failure. This information is needed to determine whether modular neck femoral stems will be used in the future, and how we should monitor patients who already have them implanted.

Cite this article: Bone Joint J 2013;95-B:1011–21.

Objectives

The use of ceramic femoral heads in total hip arthroplasty (THA) has increased due to their proven low bearing wear characteristics. Ceramic femoral heads are also thought to reduce wear and corrosion at the head-stem junction with titanium (Ti) stems when compared with metal heads. We sought to evaluate taper damage of ceramic compared with metal heads when paired with cobalt chromium (CoCr) alloy stems in a single stem design.