Aims

We wanted to evaluate the effects of a bone anabolic agent (bone morphogenetic protein 2 (BMP-2)) on an anti-catabolic background (systemic or local zoledronate) on fixation of allografted revision implants.

Impaction allograft is an established method of securing initial stability of an implant in arthroplasty. Subsequent bone integration can be prolonged, and the volume of allograft may not be maintained. Intermittent administration of parathyroid hormone has an anabolic effect on bone and may therefore improve integration of an implant.

Using a canine implant model we tested the hypothesis that administration of parathyroid hormone may improve osseointegration of implants surrounded by bone graft. In 20 dogs a cylindrical porous-coated titanium alloy implant was inserted into normal cancellous bone in the proximal humerus and surrounded by a circumferential gap of 2.5 mm. Morsellised allograft was impacted around the implant. Half of the animals were given daily injections of human parathyroid hormone (1–34) 5 μg/kg for four weeks and half received control injections. The two groups were compared by mechanical testing and histomorphometry. We observed a significant increase in new bone formation within the bone graft in the parathyroid hormone group. There were no significant differences in the volume of allograft, bone-implant contact or in the mechanical parameters.

These findings suggest that parathyroid hormone improves new bone formation in impacted morsellised allograft around an implant and retains the graft volume without significant resorption. Fixation of the implant was neither improved nor compromised at the final follow-up of four weeks.

We allocated randomly 27 patients undergoing 28 primary uncemented total hip replacements (THR) to receive prosthetic components of similar design with either plasma-sprayed titanium alloy (Ti) coating (n = 13) or hydroxyapatite (HA) coating (n = 15). After some exclusions, 15 of the patients (15 THR; 7 with HA- and 8 with Ti-coating) were followed by roentgen stereophotogrammetric analysis at 3, 6 and 12 months to measure migration of the femoral component. Twenty-six of the patients (26 THR) were followed clinically and by conventional radiography. All the femoral components had migrated at 3 months. From 3 to 12 months, the migration of Ti-coated components continued whereas the HA-coated components had stabilised. At 12 months there was significantly less migration of the HA-coated components (p < 0.05). The maximum subsidence was 0.2 mm in both groups. The Harris hip score was equal in the two groups preoperatively but at follow-up it was better in the HA-coated group (p < 0.05) and visual analogue scale scores showed that they had less pain (p < 0.05).

In previous studies, we have demonstrated a fibrocartilaginous membrane around hydroxyapatite-coated implants subjected to micromovement in contrast to the fibrous connective tissue which predominates around similarly loaded titanium alloy implants. In the present study, in mature dogs, we investigated the effect of immobilising titanium (Ti)- or hydroxyapatite (HA)-coated implants already surrounded by a movement-induced fibrous membrane and compared the results with those of similar implants in which continuous micromovement was allowed to continue. The implants were inserted in the medial femoral condyles of 14 dogs and subjected to 150 microns movements during each gait cycle. After four weeks (when a fibrous membrane had developed), half the implants were immobilised to prevent further micromovement. The dogs were killed at 16 weeks and the results were evaluated by push-out tests and histological analysis. The continuously loaded Ti-coated implants were surrounded by a fibrous membrane, whereas bridges of new bone anchored the HA-coated implants. The immobilised implants were surrounded by bone irrespective of the type of coating. Push-out tests of the continuously loaded implants showed better fixation of those with HA coating (p < 0.001). The immobilised Ti-coated implants had four times stronger fixation than did continuously loaded Ti-coated implants (p < 0.01) but there was no equivalent difference between the two groups of HA-coated implants. The amount of bone ingrowth was greater into immobilised HA-coated implants than into immobilised Ti-coated implants (p < 0.01). Two-thirds of the HA coating had been resorbed after 16 weeks of implantation, but 25% of this resorbed HA had been replaced by bone.(ABSTRACT TRUNCATED AT 250 WORDS)

The reliability of the Catterall grouping of Perthes' disease was examined by determining the agreement between pairs of observers using weighted kappa statistics. Anteroposterior and lateral radiographs of 100 hip joints were grouped independently by four experienced observers. There was a low, and in our opinion, unacceptable degree of inter-observer agreement even when Groups 2 and 3 were combined.