The Journal of Bone & Joint Surgery British Volume
Vol. 76-B, Issue 3 | Pages 423 - 427
1 May 1994
Amstutz H Grigoris P Safran M Grecula M Campbell P Schmalzried T

Cemented Ti-6Al-4V components were used to resurface ten femoral heads in nine young adult patients with osteonecrosis of the femoral head (average age 32 years; range 20 to 51). There were eight hips at Ficat stage III and two at stage IV. Five hips have maintained satisfactory function for an average period of 11.2 years (10 to 12.2) with no radiographic evidence of component loosening or osteolysis; five have been revised after an average period of 7.8 years (3.3 to 10.3) for pain caused by deterioration of the acetabular cartilage. No component required revision for loosening and the specimens retrieved at revision showed no evidence of osteolysis despite burnishing of the titanium bearing surface and the presence of particulate titanium debris in the tissues.


The Journal of Bone & Joint Surgery British Volume
Vol. 76-B, Issue 1 | Pages 1 - 3
1 Jan 1994
Dorey F Grigoris P Amstutz H


The Journal of Bone & Joint Surgery British Volume
Vol. 75-B, Issue 2 | Pages 254 - 258
1 Mar 1993
Kabo J Gebhard J Loren G Amstutz H

Polyethylene acetabular cups retrieved at revision surgery were measured by a shadowgraph technique to determine linear wear, and the values were compared with those obtained from radiographs. There was a close correlation between them, although the radiographic measurements slightly underestimated the true wear. Average linear wear rates for surface-replacement components were much greater than those for conventional prostheses with femoral heads up to 32 mm in diameter. Volumetric wear, calculated using a new formula, was found to be less than previously reported in vivo, and similar in magnitude to the results of experimental wear tests in vitro. The volumetric wear rates were greatest for the surface-replacement components and, for conventional components, were found to increase in a linear manner with component diameter.