We made a semiquantitative study of the comparative histology of pseudomembranes from 12 loose cemented ceramic-ceramic and 18 metal-polyethylene total hip replacements. We found no significant difference in cellular reaction between the two groups, but there was a major difference in the origin of the particulate debris. In the metal-polyethylene group, polyethylene of articular origin was predominant, while in the ceramic-ceramic group the cellular reaction appeared to be a response to zirconia ceramic particles used to opacify cement used for fixation.

Isolation and characterisation of the debris showed that the zirconia particles formed the greatest proportion (76%) in ceramic-ceramic hips, while alumina debris of articular origin formed only 12%.

Our study has indicated that aseptic loosening of ceramic cups is not due to a response to debris generated at the articular interface, but to mechanical factors which lead to fragmentation of the cement.

Fifty-three of 55 consecutive elbow replacements for post-traumatic arthritis were followed for a minimum of two years (mean 6.3, range 2 to 14.4). The patients presented difficult management problems, having undergone an average of two previous operations per joint; 22 joints had suffered prior complications; 18 had less than 50 degrees of flexion and six were flail. One of three versions of the Coonrad prosthesis was employed in all. During the follow-up period, 10 patients underwent 14 revision procedures for aseptic loosening; 38 elbows are currently without progressive radiolucent lines. In two patients an elbow had to be resected, one for deep infection and the other for bone resorption following a foreign-body reaction to titanium. The current design of the Coonrad prosthesis offers a reliable option for the treatment of post-traumatic arthritis but should be used only in carefully selected patients over the age of 60 years.

Total hip replacement was performed in 27 hips of patients who had sickle cell anaemia with avascular necrosis of the femoral head. The disease was bilateral in 11 patients. Considerable medical problems were encountered although most of the patients had exchange transfusion before surgery (86%), which prevented postoperative sickle cell crises in all but two cases. At the primary operation hard sclerotic bone was seen in nine femora with complete obliteration of the femoral canal. There were four femoral fractures, three following perforation of the shaft due to this hard bone. There was a very high morbidity due to loosening in both cemented and uncemented prostheses. With a rate of 59% over a cumulative 5.5 year period, revision was being performed at an average of only 43 months. Surgeons should be aware of these problems.

1. Seventy-seven operations on the patella have been reviewed.

2. There is no evidence that arthritic changes in the femoral condyles are an inevitable sequel of complete excision of the patella.

3. There is a direct relationship between the severity of symptoms after complete excision of the patella and the extent of ossification in the quadriceps tendon.

4. Patello-femoral arthritis after partial excision of the patella may be due to faulty realignment of the patellar ligament and consequent tilting of the patellar remnant towards the femoral condyles.

Mobile-bearing (MB) total knee replacement (TKR) was introduced to reduce the risk of aseptic loosening and wear of polyethylene inserts. However, no consistent clinical advantages of mobile- over fixed-bearing (FB) TKR have been found. In this study we evaluated whether mobile bearings have an advantage over fixed bearings with regard to revision rates and clinical outcome scores. Furthermore, we determined which modifying variables affected the outcome.

A systematic search of the literature was conducted to collect clinical trials comparing MB and FB in primary TKR. The primary outcomes were revision rates for any reason, aseptic loosening and wear. Secondary outcomes included range of movement, Knee Society score (KSS), Oxford knee score (OKS), Short-Form 12 (SF-12) score and radiological parameters. Meta-regression techniques were used to explore factors modifying the observed effect.

Our search yielded 1827 publications, of which 41 studies met our inclusion criteria, comprising over 6000 TKRs. Meta-analyses showed no clinically relevant differences in terms of revision rates, clinical outcome scores or patient-reported outcome measures between MB and FB TKRs. It appears that theoretical assumptions of superiority of MB over FB TKR are not borne out in clinical practice.

Cite this article: Bone Joint J 2013;95-B:1209–16.

We evaluated the impact of pre-coating the tibial component with polymethylmethacrylate (PMMA) on implant survival in a cohort of 16 548 primary NexGen total knee replacements (TKRs) in 14 113 patients. In 13 835 TKRs a pre-coated tray was used while in 2713 TKRs the non-pre-coated version of the same tray was used. All the TKRs were performed between 2001 and 2009 and were cemented. TKRs implanted with a pre-coated tibial component had a lower cumulative survival than those with a non-pre-coated tibial component (p = 0.01). After adjusting for diagnosis, age, gender, body mass index, American Society of Anesthesiologists grade, femoral coupling design, surgeon volume and hospital volume, pre-coating was an independent risk factor for all-cause aseptic revision (hazard ratio 2.75, p = 0.006). Revision for aseptic loosening was uncommon for both pre-coated and non-pre-coated trays (rates of 0.12% and 0%, respectively). Pre-coating with PMMA does not appear to be protective of revision for this tibial tray design at short-term follow-up.

Cite this article: Bone Joint J 2013;95-B:367–70.

Isolated dislocations of the navicular are rare injuries; we present our experience of six cases in which the navicular was dislocated without fracture. All patients had complex injuries, with considerable disruption of the midfoot. Five patients had open reduction and stabilisation with Kirschner wires. One developed subluxation and deformity of the midfoot because of inadequate stabilisation of the lateral column, and there was one patient with ischaemic necrosis. We believe that the navicular cannot dislocate in isolation because of the rigid bony supports around it; there has to be significant disruption of both longitudinal columns of the foot. Most commonly, an abduction/pronation injury causes a midtarsal dislocation, and on spontaneous reduction the navicular may dislocate medially. This mechanism is similar to a perilunate dislocation. Stabilisation of both medial and lateral columns of the foot may sometimes be essential for isolated dislocations. In spite of our low incidence of ischaemic necrosis, there is always a likelihood of this complication.

Aseptic loosening is seen in a significant proportion of cemented total hip replacements (THR). In a small subgroup of patients who suffer early loosening polyethylene debris is unlikely to be responsible. We recently reported one case of allergic contact dermatitis to N,N-dimethylparatoluidine (DMT), an accelerator used in bone cement. We have therefore investigated this using skin-patch tests to a variety of substances including metals, polyethylene and the separated individual components of Simplex cement.

We studied 70 patients, 15 with aseptic loosening less than two years after THR, 25 with satisfactory long-term cemented fixation, five with infected loosening of cemented THRs and 25 awaiting hip arthroplasty. We found seven positive reactions to DMT, all of them in patients with the rapid onset of aseptic loosening.

Allergy to DMT is recognised in the dental profession in respect of the ‘denture sore mouth’ syndrome, and could also be an occupational hazard since some industrial glues contain DMT. Our results suggest the need for awareness of possible previous dental or occupational exposure to the constituents of bone cement. We recommend the use of skin-patch testing in high-risk cases.

We report complications from the use of modular components in 20 hip replacements in 18 patients. Fifteen complications (in 13 patients) were related to failure of a modular interface after operation. Femoral head detachment from its trunnion was seen in 6 hips from trauma (3), reduction of a dislocation (2), and normal activity (1). In one case the base of the trunnion fractured below an extra-long modular head. In seven other hips the modular polyethylene liner dislodged from its shell, causing severe damage to the shell in four cases with extensive metallosis. In one other hip an asymmetrical polyethylene liner rotated, resulting in impingement of the femoral component and recurrent dislocation. Operative errors were seen in five cases: implantation of a trial acetabular component in one; and mismatching between the size of the femoral head and the acetabular component in the others. Surgeons who use hip replacements with modular components should be aware of the potential for operative error and of the importance of early treatment for postoperative mechanical failure.

We report the results of cementless total joint replacement in 18 patients with old tuberculosis of the hip, performed, on average, 34 years after the onset of infection. Mean follow-up was 3.5 years. Only seven of the patients had antituberculous drugs during or after the operation. Using the Mayo hip score, 15 patients had excellent or good results and two had a fair rating. One patient had the prosthesis removed more than one year postoperatively for late haematogenous staphylococcal infection and had a poor rating. All the patients had relief of hip-related pain. Despite the absence of any reactivation of tuberculosis in our series, we recommend the use of specific prophylaxis.

Several radiological methods of measuring anteversion of the acetabular component after total hip replacement (THR) have been described. These studies used different definitions and reference planes to compare methods, allowing for misinterpretation of the results. We compared the reliability and accuracy of five current methods using plain radiographs (those of Lewinnek, Widmer, Liaw, Pradhan, and Woo and Morrey) with CT measurements, using the same definition and reference plane. We retrospectively studied the plain radiographs and CT scans in 84 hips of 84 patients who underwent primary THR. Intra- and inter-observer reliability were high for the measurement of inclination and anteversion with all methods on plain radiographs and CT scans. The measurements of inclination on plain radiographs were similar to the measurements using CT (p = 0.043). The mean difference between CT measurements was 0.6° (-5.9° to 6.8°).

Measurements using Widmer’s method were the most similar to those using CT (p = 0.088), with a mean difference between CT measurements of -0.9° (-10.4° to 9.1°), whereas the other four methods differed significantly from those using CT (p < 0.001).

This study has shown that Widmer’s method is the best for evaluating the anteversion of the acetabular component on plain radiographs.

Cite this article: Bone Joint J 2014; 96-B:597–603.

Components from 73 failed knee replacements (TKRs) consisting of rotating-platform, mobile-bearing and fixed-bearing implants were examined to assess the patterns of wear. The patterns were divided into low-grade (burnishing, abrasion and cold flow) and high-grade (scratching, pitting/metal embedding and delamination) to assess the severity of the wear of polyethylene.

The rotating-platform group had a higher incidence of low-grade wear on the upper surface compared with the fixed-bearing group. By contrast, high-grade wear comprising scratching, pitting and third-body embedding was seen on the lower surface. Linear regression analysis showed a significant correlation of the wear scores between the upper and lower surfaces of the tibial insert (R² = 0.29, p = 0.04) for the rotating-platform group, but no significant correlation was found for the fixed-bearing counterpart.

This suggests that high-grade wear patterns on the upper surface are reduced with the rotating-platform design. However, the incidence of burnishing, pitting/third-body embedding and scratching wear patterns on the lower surface was higher compared with that in the fixed-bearing knee.

Peri-prosthetic fracture after joint replacement in the lower limb is associated with significant morbidity. The primary aim of this study was to investigate the incidence of peri-prosthetic fracture after total hip replacement (THR) and total knee replacement (TKR) over a ten-year period using a population-based linked dataset.

Between 1 April 1997 and 31 March 2008, 52 136 primary THRs, 8726 revision THRs, 44 511 primary TKRs, and 3222 revision TKRs were performed. Five years post-operatively, the rate of fracture was 0.9% after primary THR, 4.2% after revision THR, 0.6% after primary TKR and 1.7% after revision TKR. Comparison of survival analysis for all primary and revision arthroplasties showed peri-prosthetic fractures were more likely in females, patients aged > 70 and after revision arthroplasty.

Female patients aged > 70 should be warned of a significantly increased risk of peri-prosthetic fracture after hip or knee replacement. The use of adjuvant medical treatment to reduce the effect of peri-prosthetic osteoporosis may be a direction of research for these patients.

Between January 1984 and January 1986, 131 porous-coated anatomic total hip replacements were performed in 119 consecutive patients. Of these, 100 patients (110 hips) who were alive at a minimum of 18 years after replacement were included in the study. The mean age of the patients at surgery was 48.4 years and that of surviving patients at the latest follow-up was 67.8 years. The mean duration of the clinical and radiological follow-up was 19.4 years (18 to 20).

The mean Harris hip score initially improved from 55 points before to 95 points at two years after operation, but subsequently decreased to 91 points after six years, 87 points after 11.2 years, and 85 points after 19.4 years. At the final follow-up, 23 hips (18%) of the entire cohort and 21% of survivors had undergone revision because of loosening or osteolysis of the acetabular component and eight hips (6%) of the entire cohort and 7% of survivors for loosening or osteolysis of the femoral component. Only four femoral components (4%) were revised for isolated aseptic loosening without osteolysis and two (2%) for recurrent dislocation. On the basis of these long-term results, the porous-coated anatomic femoral component survived for a minimum of 18 years after operation while the acetabular component was less durable. The findings identify the principles of uncemented joint replacement which can be applied to current practice.

Our study has determined the response of C-reactive protein (CRP) after total knee replacement (TKR). The peak level occurs on the second postoperative day and is significantly greater than that after total hip replacement (THR). The level returns to normal at similar times after both procedures. The physiological response to TKR as measured by the area under the CRP/ time curve is significantly greater than that after THR. Rising CRP levels after the third postoperative day may indicate a complication of surgery such as infection.

Our aim was to analyse the influence of the size, shape and number of particles on the pathogenesis of osteolysis. We obtained peri-implant tissues from 18 patients having revision surgery for aseptically loosened Freeman total knee replacements (10), Charnley total hip replacements (3) and Imperial College/London Hospital double-cup surface hip replacements (5). The size and shape of the polyethylene particles were characterised using SEM and their concentration was calculated. The results were analysed with reference to the presence of radiological osteolysis.

The concentration of polyethylene particles in 6 areas with osteolysis was significantly higher than that in 12 areas without osteolysis. There were no significant differences between the size and shape of the particles in these two groups.

We conclude that the most critical factor in the pathogenesis of osteolysis is the concentration of polyethylene particles accumulated in the tissue.