We retrospectively reviewed 175 patients (191 hips) who had undergone primary cemented total hip replacement between November 1992 and November 1995 using a collarless polished double-tapered femoral component after a minimum of ten years (mean 11.08; 10 to 12.8). All stems were implanted using contemporary cementing techniques with a distal cement restrictor, pressurised lavage, retrograde cementing with a gun and proximal pressurisation. Clinical outcome was assessed using the Harris Hip score. Radiological analysis was performed on calibrated plain radiographs taken in two planes. Complete radiological data on 110 patients (120 hips) and clinical follow-up on all the surviving 111 patients (122 hips) was available. The fate of all the hips was known.

At final follow-up, the mean Harris Hip score was 86 (47 to 100), and 87 of 116 patients (75%) had good or excellent scores. Survival with revision of the stem for aseptic loosening as the endpoint was 100%; and survival with revision of the stem for any reason was 95.9% (95% confidence interval 87.8 to 96.8) at ten years. All the stems subsided vertically at the stem-cement interface in a predictable pattern, at an overall mean rate of 0.18 mm per year (0.02 to 2.16), but with a mean rate of 0.80 mm (0.02 to 2.5) during the first year. The mean total subsidence was 1.95 mm (0.21 to 24). Only three stems loosened at the cement-bone interface. There was excellent preservation of proximal femoral bone stock. There was a high incidence of Brooker III and IV heterotopic ossification affecting 25 patients (22%).

The collarless polished tapered stem has an excellent clinical and radiological outcome at a minimum of ten years’ follow-up. The pattern and magnitude of subsidence of the stem within the cement mantle occurred in a predictable pattern, consistent with the design philosophy.

Polymethylmethacrylate remains one of the most enduring materials in orthopaedic surgery. It has a central role in the success of total joint replacement and is also used in newer techniques such as percutaneous vertebroplasty and kyphoplasty.

This article describes the current uses and limitations of polymethylmethacrylate in orthopaedic surgery. It focuses on its mechanical and chemical properties and links these to its clinical performance. The behaviour of antibiotic-loaded bone cement are discussed, together with areas of research that are now shedding light upon the behaviour of this unique biomaterial.

Peri-prosthetic femoral fracture after total hip replacement (THR) is associated with a poor outcome and high mortality. However, little is known about its long-term incidence after uncemented THR.

We retrospectively reviewed a consecutive series of 326 patients (354 hips) who had received a CLS Spotorno replacement with an uncemented, straight, collarless tapered titanium stem between January 1985 and December 1989. The mean follow-up was 17 years (15 to 20). The occurrence of peri-prosthetic femoral fracture during follow-up was noted. Kaplan-Meier survival analysis was used to estimate the cumulative incidence of fracture.

At the last follow-up, 86 patients (89 hips) had died and eight patients (eight hips) had been lost to follow-up. A total of 14 fractures in 14 patients had occurred. In ten hips, the femoral component had to be revised and in four the fracture was treated by open reduction and internal fixation. The cumulative incidence of peri-prosthetic femoral fracture was 1.6% (95% confidence interval 0.7 to 3.8) at ten years and 4.5% (95% confidence interval 2.6 to 8.0) at 17 years after the primary THR. There was no association between the occurrence of fracture and gender or age at the time of the primary replacement.

Our findings indicate that peri-prosthetic femoral fracture is a significant mode of failure in the long term after the insertion of an uncemented CLS Spotorno stem. Revision rates for this fracture rise in the second decade. Further research is required to investigate the risk factors involved in the occurrence of late peri-prosthetic femoral fracture after the implantation of any uncemented stem, and to assess possible methods of prevention.

Because the femoral head/neck junction is preserved in hip resurfacing, patients may be at greater risk of impingement, leading to abnormal wear patterns and pain. We assessed femoral head/neck offset in 63 hips undergoing metal-on-metal hip resurfacing and in 56 hips presenting with non-arthritic pain secondary to femoroacetabular impingement. Most hips undergoing resurfacing (57%; 36) had an offset ratio ≤ 0.15 pre-operatively and required greater correction of offset at operation than the rest of the group. In the non-arthritic hips the mean offset ratio was 0.137 (0.04 to 0.23), with the offset ratio correlating negatively to an increasing α angle. An offset ratio ≤ 0.15 had a 9.5-fold increased relative risk of having an α angle ≥ 50.5°. Most hips undergoing resurfacing have an abnormal femoral head/neck offset, which is best assessed in the sagittal plane.

Our aim in this prospective study was to compare the bone mineral density (BMD) around cementless acetabular and femoral components which were identical in geometry and had the same alumina modular femoral head, but differed in regard to the material of the acetabular liners (alumina ceramic or polyethylene) in 50 patients (100 hips) who had undergone bilateral simultaneous primary total hip replacement. Dual energy X-ray absorptiometry scans of the pelvis and proximal femur were obtained at one week, at one year, and annually thereafter during the five-year period of the study.

At the final follow-up, the mean BMD had increased significantly in each group in acetabular zone I of DeLee and Charnley (20% (15% to 26%), p = 0.003), but had decreased in acetabular zone II (24% (18% to 36%) in the alumina group and 25% (17% to 31%) in the polyethylene group, p = 0.001). There was an increase in the mean BMD in zone III of 2% (0.8% to 3.2%) in the alumina group and 1% (0.6% to 2.2%) in the polyethylene group (p = 0.315). There was a decrease in the mean BMD in the calcar region (femoral zone 7) of 15% (8% to 24%) in the alumina group and 14% (6% to 23%) in the polyethylene group (p < 0.001). The mean bone loss in femoral zone 1 of Gruen et al was 2% (1.1% to 3.1%) in the alumina group and 3% (1.3% to 4.3%) in the polyethylene group (p = 0.03), and in femoral zone 6, the mean bone loss was 15% (9% to 27%) in the alumina group and 14% (11% to 29%) in the polyethylene group compared with baseline values. There was an increase in the mean BMD on the final scans in femoral zones 2 (p = 0.04), 3 (p = 0.04), 4 (p = 0.12) and 5 (p = 0.049) in both groups.

There was thus no significant difference in the bone remodelling of the acetabulum and femur five years after total hip replacement in those two groups where the only difference was in the acetabular liner.

We investigated 219 revisions of total hip replacement (THR) in 211 patients using a collarless double-taper cemented femoral component. The mean age of the patients was 72 years (30 to 90). The 137 long and 82 standard length stems were analysed separately. The mean follow-up was six years (2 to 18), and no patient was lost to follow-up.

Survival of the long stems to re-revision for aseptic loosening at nine years was 98% (95% confidence interval (CI) 94 to 100), and for the standard stems was 93% (95% CI 85 to 100). At five years, one long stem was definitely loose radiologically and one standard stem was probably loose. Pre-operative femoral bone deficiency did not influence the results for the long stems, and corrective femoral osteotomy was avoided, as were significant subsidence, major stress shielding and persistent thigh pain.

Because of these reliable results, cemented long collarless double-taper femoral components are recommended for routine revision THR in older patients.

We describe the survivorship of the Exeter femoral component in a District General Hospital. Between 1994 and 1996, 230 Exeter Universal cemented femoral components were implanted in 215 patients who were reviewed at a mean of 11.2 years (10 to 13). We used one acetabular implant, the Elite Ogee component, in 218 of the 230 hips.

During the period of this study 76 patients (79 hips) died. Of the remaining 139 patients (151 hips), 121 were able to attend for radiological analysis at a minimum of ten years. One patient was lost to follow-up.

No femoral component was revised for aseptic loosening. Three hips were revised for deep infection and six acetabular components required revision, four for loosening and two for recurrent dislocation. Taking the ‘worst-case scenario’ including the one patient lost to follow-up, the overall survival rate was 94.4% at 13 years.

Our results confirm excellent medium-term results for the Exeter Universal femoral component, implanted in a general setting. The excellent survival of this femoral component, when used in combination with the Ogee acetabular component, suggests that this is a successful pairing.

We describe three cases of fracture of the titanium JRI-Furlong hydroxyapatite-ceramic (HAC)-coated femoral component. We have examined previous case reports of failure of this stem and conclude that fracture may occur in two places, namely at the neck-shoulder junction and at the conical-distal cylindrical junction. These breakages are the result of fatigue in a metallurgically-proven normal femoral component. All the cases of failure of the femoral component have occurred in patients with a body mass index of more than 25 in whom a small component, either size 9 or 10, had been used.

In patients with a body mass index above normal size 9 components should be avoided and the femoral canal should be reamed sufficiently to accept a large femoral component to ensure that there is adequate metaphyseal fixation.

This study reviewed the results of a cementless anatomical femoral component to give immediate post-operative stability, and with a narrow distal section in order not to contact the femoral cortex in the diaphysis, ensuring exclusively metaphyseal loading.

A total of 471 patients (601 hips) who had a total hip replacement between March 1995 and February 2002 were included in the study. There were 297 men and 174 women. The mean age at the time of operation was 52.7 years (28 to 63). Clinical and radiological evaluation were performed at each follow-up. Bone densitometry was carried out on all patients two weeks after operation and at the final follow-up examination. The mean follow-up was 8.8 years (5 to 12).

The mean pre-operative Harris hip score was 41 points (16 to 54), which improved to a mean of 96 (68 to 100) at the final follow-up. No patient complained of thigh pain at any stage. No acetabular or femoral osteolysis was observed and no hip required revision for aseptic loosening of either component. Deep infection occurred in two hips (0.3%) which required revision. One hip (0.2%) required revision of the acetabular component for recurrent dislocation. Bone mineral densitometry revealed a minimal bone loss in the proximal femur.

This cementless anatomical femoral component with metaphyseal loading but without distal fixation produced satisfactory fixation and encourages proximal femoral loading.

The outcome of a cemented hip arthroplasty is partly dependent on the type of cement which is used. The production of an interface gap between the stem and the cement mantle as a result of shrinkage of the cement, may be a factor involved. Palacos R, Palacos LV (both with gentamicin), CMW 1, CMW 2, CMW Endurance (CMWE) and Simplex were prepared under vacuum and allowed to cure overnight in similar cylinders. The next day this volume was determined by the displacement of water. Shrinkage varied between 3.82% and 7.08% with CMWE having the lowest and Palacos LV the highest. This could be a factor to consider when choosing a cement for a shape-closed stem.

We describe the results at five years of a prospective study of a new tri-tapered polished, cannulated, cemented femoral stem implanted in 51 patients (54 hips) with osteoarthritis. The mean age and body mass index of the patients was 74 years and 27.9, respectively. Using the anterolateral approach, half of the stems were implanted by a consultant orthopaedic surgeon and half by six different registrars. There were three withdrawals from the study because of psychiatric illness, a deep infection and a recurrent dislocation. Five deaths occurred prior to five-year follow-up and one patient withdrew from clinical review.

In the remaining 51 hips the mean pre-operative Oxford hip score was 47 points which decreased to 19 points at five years (45 hips). Of the stems 49 (98%) were implanted within 1° of neutral in the femoral canal. The mean migration of the stem at five years was 1.9 mm and the survivorship for aseptic loosening was 100%. There was no significant difference in outcome between the consultant and registrar groups. At five years, the results were comparable with those of other polished, tapered, cemented stems. Long-term surveillance continues.

We have investigated the role of the penetration of saline on the shear strength of the cement-stem interface for stems inserted at room temperature and those preheated to 37°C using a variety of commercial bone cements. Immersion in saline for two weeks at 37°C reduced interfacial strength by 56% to 88% after insertion at room temperature and by 28% to 49% after preheating of the stem. The reduction in porosity as a result of preheating ranged from 71% to 100%. Increased porosity correlated with a reduction in shear strength after immersion in saline (r = 0.839, p < 0.01) indicating that interfacial porosity may act as a fluid conduit.

We carried out a clinical and radiological review of 103 cementless primary hip arthroplasties with a tapered rectangular grit-blasted titanium press-fit femoral component and a threaded conical titanium acetabular component at a mean follow-up of 14.4 years (10.2 to 17.1).

The mean Harris hip score at the last follow-up was 89.2 (32 to 100). No early loosening and no fracture of the implant were found. One patient needed revision surgery because of a late deep infection. In 11 hips (10.7%), the reason for revision was progressive wear of the polyethylene liner. Exchange of the acetabular component because of aseptic loosening without detectable liner wear was carried out in three hips (2.9%).

After 15 years the survivorship with aseptic loosening as the definition for failure was 95.6% for the acetabular component and 100% for the femoral component.