Total hip replacement (THR) is a very common
procedure undertaken in up to 285 000 Americans each year. Patient
satisfaction with THR is very high, with improvements in general
health, quality of life, and function while at the same time very
cost effective. Although the majority of patients have a high degree
of satisfaction with their THR, 27% experience some discomfort,
and up to 6% experience severe chronic pain. Although it can be
difficult to diagnose the cause of the pain in these patients, this
clinical issue should be approached systematically and thoroughly.
A detailed history and clinical examination can often provide the
correct diagnosis and guide the appropriate selection of investigations, which
will then serve to confirm the clinical diagnosis made. Cite this article:
A modular femoral head–neck junction has practical
advantages in total hip replacement. Taper fretting and corrosion
have so far been an infrequent cause of revision. The role of design
and manufacturing variables continues to be debated. Over the past
decade several changes in technology and clinical practice might
result in an increase in clinically significant taper fretting and
corrosion. Those factors include an increased usage of large diameter
(36 mm) heads, reduced femoral neck and taper dimensions, greater
variability in taper assembly with smaller incision surgery, and
higher taper stresses due to increased patient weight and/or physical
activity. Additional studies are needed to determine the role of
taper assembly compared with design, manufacturing and other implant
variables. Cite this article:
Wear debris released from bearing surfaces has been shown to
provoke negative immune responses in the recipient. Excessive wear
has been linked to early failure of prostheses. Analysis using coordinate
measuring machines (CMMs) can provide estimates of total volumetric
material loss of explanted prostheses and can help to understand
device failure. The accuracy of volumetric testing has been debated,
with some investigators stating that only protocols involving hundreds
of thousands of measurement points are sufficient. We looked to
examine this assumption and to apply the findings to the clinical
arena. We examined the effects on the calculated material loss from
a ceramic femoral head when different CMM scanning parameters were
used. Calculated wear volumes were compared with gold standard gravimetric
tests in a blinded study. Objectives
Methods
The rate and mode of early failure in 463 Birmingham hip resurfacings in a two-centre, multisurgeon series were examined. Of the 463 patients two have died and three were lost to follow-up. The mean radiological and clinical follow-up was for 43 months (6 to 90). We have revised 13 resurfacings (2.8%) including seven for pain, three for fracture, two for dislocation and another for sepsis. Of these, nine had macroscopic and histological evidence of metallosis. The survival at five years was 95.8% (95% confidence interval (CI) 94.1 to 96.8) for revision for all causes and 96.9% (95% CI 95.5 to 98.3) for metallosis. The rate of metallosis related revision was 3.1% at five years. Risk factors for metallosis were female gender, a small femoral component, a high abduction angle and obesity. We do not advocate the use of the Birmingham Hip resurfacing procedure in patients with these risk factors.
A total of 219 hips in 192 patients aged between
18 and 65 years were randomised to 28-mm metal-on-metal uncemented
total hip replacements (THRs, 107 hips) or hybrid hip resurfacing
(HR, 112 hips). At a mean follow-up of eight years (6.6 to 9.3)
there was no significant difference between the THR and HR groups
regarding rate of revision (4.0% (4 of 99) Cite this article:
Following the recall of modular neck hip stems
in July 2012, research into femoral modularity will intensify over
the next few years. This review aims to provide surgeons with an
up-to-date summary of the clinically relevant evidence. The development
of femoral modularity, and a classification system, is described.
The theoretical rationale for modularity is summarised and the clinical
outcomes are explored. The review also examines the clinically relevant problems
reported following the use of femoral stems with a modular neck. Joint replacement registries in the United Kingdom and Australia
have provided data on the failure rates of modular devices but cannot
identify the mechanism of failure. This information is needed to
determine whether modular neck femoral stems will be used in the
future, and how we should monitor patients who already have them implanted. Cite this article:
Metal-on-metal (MoM) hip resurfacing was introduced into clinical
practice because it was perceived to be a better alternative to
conventional total hip replacement for young and active patients.
However, an increasing number of reports of complications have arisen
focusing on design and orientation of the components, the generation
of metallic wear particles and serum levels of metallic ions. The
procedure introduced a combination of two elements: large-dimension
components and hard abrasive particles of metal wear. The objective
of our study was to investigate the theory that microseparation
of the articular surfaces draws in a high volume of bursal fluid
and its contents into the articulation, and at relocation under
load would generate high pressures of fluid ejection, resulting
in an abrasive water jet. This theoretical concept using MoM resurfacing components (head
diameter 55 mm) was modelled mathematically and confirmed experimentally
using a material-testing machine that pushed the head into the cup
at a rate of 1000 mm/min until fully engaged.Objectives
Methods
We analysed 54 alumina ceramic-on-ceramic bearings
from total hip replacements retrieved at one centre after a mean
duration of 3.5 years (0.2 to 10.6)
Persistent groin pain after seemingly successful
total hip replacement (THR) appears to have become more common.
Recent studies have indicated a high incidence after metal-on-polyethylene
and metal-on-metal conventional THR and it has been documented in
up to 18% of patients after metal-on-metal resurfacing. There are many
causes, including acetabular loosening, stress fracture, and iliopsoas
tendonitis and impingement. The evaluation of this problem requires
a careful history and examination, plain radiographs and an algorithmic approach
to special diagnostic imaging and tests. Non-operative treatment
is not usually successful. Specific operative treatment depending
on the cause of the pain usually involves revision of the acetabular
component, iliopsoas tenotomy or other procedures, and is usually
successful. Here, an appropriate algorithm is described.
The aims of this piece of work were to: 1) record the background
concentrations of blood chromium (Cr) and cobalt (Co) concentrations
in a large group of subjects; 2) to compare blood/serum Cr and Co
concentrations with retrieved metal-on-metal (MoM) hip resurfacings;
3) to examine the distribution of Co and Cr in the serum and whole
blood of patients with MoM hip arthroplasties; and 4) to further
understand the partitioning of metal ions between the serum and
whole blood fractions. A total of 3042 blood samples donated to the local transfusion
centre were analysed to record Co and Cr concentrations. Also, 91
hip resurfacing devices from patients who had given pre-revision
blood/serum samples for metal ion analysis underwent volumetric
wear assessment using a coordinate measuring machine. Linear regression analysis
was carried out and receiver operating characteristic curves were
constructed to assess the reliability of metal ions to identify
abnormally wearing implants. The relationship between serum and
whole blood concentrations of Cr and Co in 1048 patients was analysed
using Bland-Altman charts. This relationship was further investigated
in an Objectives
Methods
Fibrin glue, also known as fibrin sealant, is now established as a haemostatic agent in surgery, but its role in orthopaedic surgery is neither well known nor clearly defined. Although it was originally used over 100 years ago, concerns about transmission of disease meant that it fell from favour. It is also available as a slow-release drug delivery system and as a substrate for cellular growth and tissue engineering. Consequently, it has the potential to be used in a number of ways in orthopaedic surgery. The purpose of this review is to address its use in surgery of the knee in which it appears to offer great promise.
We systematically reviewed the peer-reviewed literature to relate the survival of hybrid metal-on-metal hip resurfacing arthroplasty devices to a National Institute of Clinical Excellence (NICE) benchmark for choosing a primary total hip replacement, which is a survival rate of 90% at a follow-up of ten years. A total of 29 articles (10 621 resurfaced hips) met the inclusion criteria. The mean follow-up ranged from 0.6 to 10.5 years and the survival of the implant ranged from 84% to 100%. Of the 10 621 hips, 370 were revised (3.5%), with aseptic loosening as the most frequent mode of failure. None of the hip resurfacing arthroplasty implants used to date met the full ten-year NICE benchmark of survival. A total of 13 studies showed satisfactory survival compared with the three-year NICE benchmark.
There have been no large comparative studies of the blood levels of metal ions after implantation of commercially available hip resurfacing devices which have taken into account the effects of femoral size and inclination and anteversion of the acetabular component. We present the results in 90 patients with unilateral articular surface replacement (ASR) hip resurfacings (mean time to blood sampling 26 months) and 70 patients with unilateral Birmingham Hip Resurfacing (BHR) implants (mean time 47 months). The whole blood and serum chromium (Cr) and cobalt (Co) concentrations were inversely related to the size of the femoral component in both groups (p <
0.05). Cr and Co were more strongly influenced by the position of the acetabular component in the case of the ASR, with an increase in metal ions observed at inclinations >
45° and anteversion angles of <
10° and >
20°. These levels were only increased in the BHR group when the acetabular component was implanted with an inclination >
55°. A significant relationship was identified between the anteversion of the BHR acetabular component and the levels of Cr and Co (p <
0.05 for Co), with an increase observed at anteversion angles <
10° and >
20°. The median whole blood and serum Cr concentrations of the male ASR patients were significantly lower than those of the BHR men (p <
0.001). This indicates that reduced diametral clearance may equate to a reduction in metal ion concentrations in larger joints with satisfactory orientation of the acetabular component.
The sternoclavicular joint is vulnerable to the same disease processes as other synovial joints, the most common of which are instability from injury, osteoarthritis, infection and rheumatoid disease. Patients may also present with other conditions, which are unique to the joint, or are manifestations of a systemic disease process. The surgeon should be aware of these possibilities when assessing a patient with a painful, swollen sternoclavicular joint.