We have prospectively studied the wear of enhanced ultra-high molecular-weight polyethylene (Hylamer) in combination with a zirconia femoral head of 22.225 mm diameter on a cemented, triple-tapered, collarless, polished stem, the C Stem. The 71 patients who underwent total hip arthroplasty had a mean follow-up of six years (3 to 8). No patient died or was lost to follow-up. The clinical results were excellent with 96% of patients satisfied. There were no revisions. Two cups were considered to be loose radiologically. One was avulsed from the cement in a skiing accident, with a periprosthetic fracture of the femur, but has remained stable for more than seven years. One femur shows radiological appearances which are compatible with a healing infection. One femoral component is at risk of loosening. The mean rate of penetration of the cup was 0.22 mm/year (0.06 to 0.55). Our results appear to be within the guidelines set by the National Institute of Clinical Excellence. We have discontinued the use of Hylamer despite excellent clinical results and no revisions to date because the high initial rates of penetration did not settle to the expected low levels within the anticipated time

We report the findings from independent prospective clinical and laboratory-based joint-simulator studies of the performance of ceramic femoral heads of 22.225 mm diameter in cross-linked polyethylene (XLP) acetabular cups. We found remarkable qualitative and quantitative agreement between the clinical and simulator results for the wear characteristics with time, and confirmed that ceramic femoral heads penetrate the XLP cups at only about half the rate of otherwise comparable metal heads. In the clinical study, 19 hips in 17 patients were followed for an average of 77 months. In the hip-joint simulator a similar prosthesis was tested for 7.3 million cycles. Both clinical and simulator results showed relatively high rates of penetration over the first 18 months or 1.5 million cycles, followed by a very much lower wear thereafter. Once an initial bedding-in of 0.2 mm to 0.4 mm had taken place the subsequent rates of penetration were very small. The initial clinical wear during bedding-in averaged 0.29 mm/year; subsequent progression was an order of magnitude lower at about 0.022 mm/year, lower than the 0.07 mm/year in metal-to-UHMWP Charnley LFAs. Our results show the excellent tribological features of alumina-ceramic-to-XLP implants, and also confirm the value of well-designed joint simulators for the evaluation of total joint replacements

We present the results of 62 consecutive acetabular revisions using impaction bone grafting and a cemented polyethylene acetabular component in 58 patients (13 men and 45 women) after a mean follow-up of 27 years (25 to 30). All patients were prospectively followed. The mean age at revision was 59.2 years (23 to 82).

We performed Kaplan–Meier (KM) analysis and also a Competing Risk (CR) analysis because with long-term follow-up, the presence of a competing event (i.e. death) prevents the occurrence of the endpoint of re-revision.

A total of 48 patients (52 hips) had died or had been re-revised at final review in March 2011. None of the deaths were related to the surgery. The mean Harris hip score of the ten surviving hips in ten patients was 76 points (45 to 99).

The KM survivorship at 25 years for the endpoint ‘re-revision for any reason’ was 58.0% (95% confidence interval (CI) 38 to 73) and for ‘re-revision for aseptic loosening’ 72.1% (95% CI 51 to 85). With the CR analysis we calculated the KM analysis overestimates the failure rate with respectively 74% and 93% for these endpoints. The current study shows that acetabular impaction bone grafting revisions provide good clinical results at over 25 years.

Cite this article: Bone Joint J 2015;97-B:1338–44.

We used radiostereometric analysis to compare wear rates between uncemented porous sockets and cemented all-polyethylene sockets in a series of 102 hips randomised for either a Harris-Galante or a Charnley cup. Wear was evaluated in 95 hips at a mean of five years (2 to 7). All hips had a cemented, 22 mm head mono-bloc Charnley stem.

The mean annual wear rate was 0.09 mm in the Charnley sockets and 0.10 mm in the Harris-Galante sockets, with no statistically significant differences in wear, migration or rotation.

We conclude that, up to five years, the wear characteristics of the modular and porous Harris-Galante socket resemble that of the Charnley socket.

The results of using the Ring uncemented polyethylene-to-metal (UPM) prosthesis in patients with protrusio acetabuli or dysplasia are reported. Fifty-four cases of protrusio were analysed and a modified method of measuring the deformity is described; after operation, remodelling of the medial wall had improved, on average, by 29.6%. For the dysplastic acetabulum the main difficulty is the lack of lateral support for the cup. In order to test the hypothesis that this support improves with an uncemented prosthesis, 38 hips with an average follow-up of 31 months were studied. Lateral support, measured radiographically, showed an average increase of 21%. The remodelling effect may be attributed to the biomechanical design of the prosthesis.

Most published randomised controlled trials which compare the rates of wear of conventional and cross-linked (XL) polyethylene (PE) in total hip arthroplasty (THA) have described their use with a cementless acetabular component.

We conducted a prospective randomised study to assess the rates of penetration of two distinct types of PE in otherwise identical cemented all-PE acetabular components.

A total of 100 consecutive patients for THA were randomised to receive an acetabular component which had been either highly XL then remelted or moderately XL then annealed.

After a minimum of eight years follow-up, 38 hips in the XL group and 30 hips in the annealed group had complete data (mean follow-up of 9.1 years (7.6 to 10.7) and 8.7 years (7.2 to 10.2), respectively). In the XL group, the steady state rate of penetration from one year onwards was -0.0002 mm/year (sd 0.108): in the annealed group it was 0.1382 mm/year (sd 0.129) (Mann–Whitney U test, p < 0.001). No complication specific to either material was recorded.

These results show that the yearly linear rate of femoral head penetration can be significantly reduced by using a highly XLPE cemented acetabular component.

Cite this article: Bone Joint J 2015;97-B:1458–62.

We report the long-term clinical and radiological outcomes of the Aequalis total shoulder replacement with a cemented all-polyethylene flat-back keeled glenoid component implanted for primary osteoarthritis between 1991 and 2003 in nine European centres. A total of 226 shoulders in 210 patients were retrospectively reviewed at a mean of 122.7 months (61 to 219) or at revision. Clinical outcome was assessed using the Constant score, patient satisfaction score and range of movement. Kaplan-Meier survivorship analysis was performed with glenoid revision for loosening and radiological glenoid loosening (sd) as endpoints. The Constant score was found to improve from a mean of 26.8 (sd 10.3) pre-operatively to 57.6 (sd 20.0) post-operatively (p < 0.001). Active forward flexion improved from a mean of 85.3° (sd 27.4) pre-operatively to 125° (sd 37.3) postoperatively (p < 0.001). External rotation improved from a mean of 7° (sd 6.5) pre-operatively to 30.3° (sd 21.8°) post-operatively (p < 0.001). Survivorship with revision of the glenoid component as the endpoint was 99.1% at five years, 94.5% at ten years and 79.4% at 15 years. Survivorship with radiological loosening as the endpoint was 99.1% at five years, 80.3% at ten years and 33.6% at 15 years.

Younger patient age and the curettage technique for glenoid preparation correlated with loosening. The rate of glenoid revision and radiological loosening increased with duration of follow-up, but not until a follow-up of five years. Therefore, we recommend that future studies reporting radiological outcomes of new glenoid designs should report follow-up of at least five to ten years.