The early failure and revision of bimodular primary total hip arthroplasty prostheses requires the identification of the risk factors for material loss and wear at the taper junctions through taper wear analysis. Deviations in taper geometries between revised and pristine modular neck tapers were determined using high resolution tactile measurements. A new algorithm was developed and validated to allow the quantitative analysis of material loss, complementing the standard visual inspection currently used.

The algorithm was applied to a sample of 27 retrievals (in situ from 2.9 to 38.1 months) of the withdrawn Rejuvenate modular prosthesis. The mean wear volumes on the flat distal neck piece taper was 3.35 mm³ (0.55 to 7.57), mainly occurring in a characteristic pattern in areas with high mechanical loading. Wear volume tended to increase with time to revision (r² = 0.423, p = 0.001). Implant and patient specific data (offset, stem size, patient’s mass, age and body mass index) did not correlate with the amount of material loss observed (p >  0.078). Bilaterally revised implants showed higher amounts of combined total material loss and similar wear patterns on both sides. The consistent wear pattern found in this study has not been reported previously, suggesting that the device design and materials are associated with the failure of this prosthesis.

Cite this article: Bone Joint J 2015;97-B:1350–7.

The long term biological effects of wear products following total hip arthroplasty (THA) are unclear. However, the indications for THA are expanding, with increasingly younger patients undergoing the procedure.

This prospective, randomised study compared two groups of patients undergoing THA after being randomised to receive one of two different bearing surfaces: metal-on-polyethylene (MoP) n = 22 and metal-on-metal (MoM) n = 23. We investigated the relationship between three variables: bearing surface (MoP vs MoM), whole blood levels of chromium (Cr) and cobalt (Co) and chromosomal aberrations in peripheral lymphocyte pre-operatively and at one, two and five years post-surgery.

Our results demonstrated significantly higher mean cobalt and chromium (Co and Cr) blood levels in the MoM group at all follow-up points following surgery (p < 0.01), but there were no significant differences in the chromosomal aberration indices between MoM and MoP at two or five years (two years: p = 0.56, p = 0.08, p = 0.91, p = 0.51 and five years: p = 0.086, p = 0.73, p = 0.06, p = 0.34) for translocations, breaks, loss and gain of chromosomes respectively. Regression analysis showed a strong linear relationship between Cr levels and the total chromosomal aberration indices in the MoM group (R² = 0.90016), but this was not as strong for Co (R² = 0.68991). In the MoP group, the analysis revealed a poor relationship between Cr levels and the total chromosomal aberration indices (R² = 0.23908) but a slightly stronger relationship for Co (R² = 0.64292). Across both groups, Spearman’s correlation detected no overall association between Co and Cr levels and each of the studied chromosomal aberrations. There remains no clear indication which THA bearing couple is the most biocompatible, especially in young active patients. While THA continues to be very successful at alleviating pain and restoring function, the long-term biological implications of the procedure still require further scrutiny.

Cite this article: Bone Joint J 2015;97-B:1183–91.

Following the recall of modular neck hip stems in July 2012, research into femoral modularity will intensify over the next few years. This review aims to provide surgeons with an up-to-date summary of the clinically relevant evidence. The development of femoral modularity, and a classification system, is described. The theoretical rationale for modularity is summarised and the clinical outcomes are explored. The review also examines the clinically relevant problems reported following the use of femoral stems with a modular neck.

Joint replacement registries in the United Kingdom and Australia have provided data on the failure rates of modular devices but cannot identify the mechanism of failure. This information is needed to determine whether modular neck femoral stems will be used in the future, and how we should monitor patients who already have them implanted.

Cite this article: Bone Joint J 2013;95-B:1011–21.

Aims

We present a case series of ten metal-on-polyethylene total hip arthroplasties (MoP THAs) with delayed dislocation associated with unrecognised adverse local tissue reaction due to corrosion at the trunnion and pseudotumour formation.

Aims

Surgeons have commonly used modular femoral heads and stems from different manufacturers, although this is not recommended by orthopaedic companies due to the different manufacturing processes.

We compared the rate of corrosion and rate of wear at the trunnion/head taper junction in two groups of retrieved hips; those with mixed manufacturers (MM) and those from the same manufacturer (SM).

Adverse reaction to wear and corrosion debris is a cause for concern in total hip arthroplasty (THA). Modular junctions are a potential source of such wear products and are associated with secondary pseudotumour formation.

We present a consecutive series of 17 patients treated at our unit for this complication following metal-on-highly cross-linked polyethylene (MoP) THA. We emphasise the risk of misdiagnosis as infection, and present the aggregate laboratory results and pathological findings in this series.

The clinical presentation was pain, swelling or instability. Solid, cystic and mixed soft-tissue lesions were noted on imaging and confirmed intra-operatively. Corrosion at the head–neck junction was noted in all cases. No bacteria were isolated on multiple pre- and intra-operative samples yet the mean erythrocyte sedimentation rate was 49 (9 to 100) and C-reactive protein 32 (0.6 to 106) and stromal polymorphonuclear cell counts were noted in nine cases.

Adverse soft–tissue reactions can occur in MoP THA owing to corrosion products released from the head–neck junction. The diagnosis should be carefully considered when investigating pain after THA. This may avoid the misdiagnosis of periprosthetic infection with an unidentified organism and mitigate the unnecessary management of these cases with complete single- or two-stage exchange.

Cite this article: Bone Joint J 2015;97-B:1024–1030.

Objectives

Malalignment of the tibial component could influence the long-term survival of a total knee arthroplasty (TKA). The object of this study was to investigate the biomechanical effect of varus and valgus malalignment on the tibial component under stance-phase gait cycle loading conditions.

Objectives

To quantify and compare peri-acetabular bone mineral density (BMD) between a monoblock acetabular component using a metal-on-metal (MoM) bearing and a modular titanium shell with a polyethylene (PE) insert. The secondary outcome was to measure patient-reported clinical function.

Symptomatic cobalt toxicity from a failed total hip replacement is a rare but devastating complication. It has been reported following revision of fractured ceramic components, as well as in patients with failed metal-on-metal articulations. Potential clinical findings include fatigue, weakness, hypothyroidism, cardiomyopathy, polycythaemia, visual and hearing impairment, cognitive dysfunction, and neuropathy. We report a case of an otherwise healthy 46-year-old patient, who developed progressively worsening symptoms of cobalt toxicity beginning approximately six months following synovectomy and revision of a fractured ceramic-on-ceramic total hip replacement to a metal-on-polyethylene bearing. The whole blood cobalt levels peaked at 6521 µg/l. The patient died from cobalt-induced cardiomyopathy. Implant retrieval analysis confirmed a loss of 28.3 g mass of the cobalt–chromium femoral head as a result of severe abrasive wear by ceramic particles embedded in the revision polyethylene liner. Autopsy findings were consistent with heavy metal-induced cardiomyopathy.

We recommend using new ceramics at revision to minimise the risk of wear-related cobalt toxicity following breakage of ceramic components.

Cite this article: Bone Joint J 2013;95-B:31–7.

Complications involving the patellofemoral joint, caused by malrotation of the femoral component during total knee replacement, are an important cause of persistent pain and failure leading to revision surgery. The aim of this study was to determine and quantify the influence of femoral component malrotation on patellofemoral wear, and to determine whether or not there is a difference in the rate of wear of the patellar component when articulated against oxidised zirconium (OxZr) and cobalt-chrome (CoCr) components. An in vitro method was used to simulate patellar maltracking for both materials. Both rates of wear and changes in height on the patellar articular surface were measured. The mean rates of wear measured were very small compared to standard tibiofemoral wear rates. When data for each femoral component material were pooled, the mean rate of wear was 0.19 mm³/Mcycle (sd 0.21) for OxZr and 0.34 mm³/Mcycle (sd 0.335) for CoCr. The largest change in height on each patella varied from -0.05 mm to -0.33 mm over the different configurations.

The results suggest that patellar maltracking due to an internally rotated femoral component leads to an increased mean patellar wear. Although not statistically significant, the mean wear production may be lower for OxZr than for CoCr components.

Metal-on-metal hip arthroplasty gained significant favor in the first decade of the millennium. However, the past several years have seen increasing reports of failure, pseudotumor and other adverse reactions. This study presents the results of a single center’s 15-year experience with metal-on-metal total hip arthroplasty as strong evidence that metal-on-metal is going, going, gone.

We present a case of early retrieval of an Oxinium femoral head and corresponding polyethylene liner where there was significant surface damage to the head and polyethylene. The implants were retrieved at the time of revision surgery to correct leg-length discrepancy just 48 hours after the primary hip replacement. Appropriate analysis of the retrieved femoral head demonstrated loss of the Oxinium layer with exposure of the underlying substrate and transfer of titanium from the acetabular shell at the time of a reduction of the index total hip replacement. In addition, the level of damage to the polyethylene was extensive despite only 48 hours in situ.

The purpose of this report is to highlight the care that is required at the time of reduction, especially with these hard femoral counter-faces such as Oxinium. To our knowledge, the damage occurring at the time of reduction has not been previously reported following the retrieval of an otherwise well-functioning hip replacement.

Second-generation metal-on-metal bearings were introduced as a response to the considerable incidence of wear-induced failures associated with conventional replacements, especially in young patients. We present the results at ten years of a consecutive series of patients treated using a metal-on-metal hip resurfacing. A distinct feature of the bearings used in our series was that they had been subjected to double-heat treatments during the post-casting phase of their manufacture. In the past these bearings had not been subjected to thermal treatments, making this a unique metal-on-metal bearing which had not been used before in clinical practice.

We report the outcome of 184 consecutive hips (160 patients) treated using a hybrid-fixed metal-on-metal hip resurfacing during 1996. Patients were invited for a clinicoradiological follow-up at a minimum of ten years. The Oxford hip score and anteroposterior and lateral radiographs were obtained. The mean age at operation was 54 years (21 to 75). A series of 107 consecutive hips (99 patients) who received the same prosthesis, but subjected to a single thermal treatment after being cast, between March 1994 and December 1995, were used as a control group for comparison.

In the 1994 to 1995 group seven patients (seven hips) died from unrelated causes and there were four revisions (4%) for osteolysis and aseptic loosening. In the 1996 group nine patients died at a mean of 6.9 years after operation because of unrelated causes. There were 30 revisions (16%) at a mean of 7.3 years (1.2 to 10.9), one for infection at 1.2 years and 29 for osteolysis and aseptic loosening. Furthermore, in the latter group there were radiological signs of failure in 27 (24%) of the 111 surviving hips.

The magnitude of the problem of osteolysis and aseptic loosening in the 1996 cohort did not become obvious until five years after the operation. Our results indicate that double-heat treatments of metal-on-metal bearings can lead to an increased incidence of wear-induced osteolysis.

Objectives

Up to 40% of unicompartmental knee arthroplasty (UKA) revisions are performed for unexplained pain which may be caused by elevated proximal tibial bone strain. This study investigates the effect of tibial component metal backing and polyethylene thickness on bone strain in a cemented fixed-bearing medial UKA using a finite element model (FEM) validated experimentally by digital image correlation (DIC) and acoustic emission (AE).

Retrieval studies of total hip replacements with highly cross-linked ultra-high-molecular-weight polyethylene liners have shown much less surface damage than with conventional ultra-high-molecular-weight polyethylene liners. A recent revision hip replacement for recurrent dislocation undertaken after only five months revealed a highly cross-linked polyethylene liner with a large area of visible delamination. In order to determine the cause of this unusual surface damage, we analysed the bearing surfaces of the cobalt-chromium femoral head and the acetabular liner with scanning electron microscopy, energy dispersive x-ray spectroscopy and optical profilometry. We concluded that the cobalt-chromium modular femoral head had scraped against the titanium acetabular shell during the course of the dislocations and had not only roughened the surface of the femoral head but also transferred deposits of titanium onto it. The largest deposits were 1.6 μm to 4.3 μm proud of the surrounding surface and could lead to increased stresses in the acetabular liner and therefore cause accelerated wear and damage.

This case illustrates that dislocations can leave titanium deposits on cobalt-chromium femoral heads and that highly cross-linked ultra-high-molecular-weight polyethylene remains susceptible to surface damage.

Objectives

The cytotoxicity induced by cobalt ions (Co²⁺) and cobalt nanoparticles (Co-NPs) which released following the insertion of a total hip prosthesis, has been reported. However, little is known about the underlying mechanisms. In this study, we investigate the toxic effect of Co²⁺ and Co-NPs on liver cells, and explain further the potential mechanisms.

During open reduction of an irreducible anterior dislocation of a total hip replacement with an Oxinium femoral head, it was observed that the head had been significantly damaged. Gross and scanning electron microscopic examination revealed cracking, gouging, and delamination of the surface. Because of the risk which this poses for damaging the polyethylene acetabular liner, it is strongly recommended that patients with this type of prosthetic head be carefully monitored after a dislocation.

Large ceramic femoral heads offer several advantages that are potentially advantageous to patients undergoing both primary and revision total hip replacement. Many high-quality studies have demonstrated the benefit of large femoral heads in reducing post-operative instability. Ceramic femoral heads may also offer an advantage in reducing polyethylene wear that has been reported in vitro and is starting to become clinically apparent in mid-term clinical outcome studies. Additionally, the risk of taper corrosion at a ceramic femoral head–neck junction is clearly lower than when using a metal femoral head. With improvements in the material properties of both modern ceramic femoral heads and polyethylene acetabular liners that have reduced the risk of mechanical complications, large ceramic heads have gained popularity in recent years.

Cite this article: Bone Joint J 2013;95-B, Supple A:63–6.

Despite many claims of good wear properties following total knee replacement (TKR) with an oxidised zirconium (OxZr) femoral component, there are conflicting clinical results. We hypothesised that there would be no difference in either the mid-term clinical and radiological outcomes or the characteristics of the polyethylene wear particles (weight, size and shape) in patients using an OxZr or cobalt-chrome (CoCr) femoral component. In all 331 patients underwent bilateral TKR, receiving an OxZr femoral component in one knee and a CoCr femoral component in the other. The mean follow-up was 7.5 years (6 to 8). Following aspiration, polyethylene wear particles were analysed using thermogravimetric methods and scanning electron microscopy. At the most recent follow-up, the mean Knee Society score, Western Ontario and McMaster Universities Osteoarthritis Index score, range of movement and satisfaction score were not significantly different in the two groups. The mean weight, size, aspect ratio and roundness of the aspirated wear particles were similar for each femoral component. Survivorship of the femoral, tibial and patellar components was 100% in both groups.

In the absence of evidence of an advantage in the medium term we cannot justify the additional expense of an OxZr femoral component.