Aims

This study reports the results of 38 total hip arthroplasties (THAs) in 33 patients aged less than 50 years, using the JRI Furlong hydroxyapatite ceramic (HAC)-coated femoral component.

Aims

Isolated acetabular liner exchange with a highly crosslinked polyethylene (HXLPE) component is an option to address polyethylene wear and osteolysis following total hip arthroplasty (THA) in the presence of a well-fixed acetabular shell. The liner can be fixed either with the original locking mechanism or by being cemented within the acetabular component. Whether the method used for fixation of the HXLPE liner has any bearing on the long-term outcomes is still unclear.

We analysed in-vivo migration and wear over a long period of all-polyethylene acetabular cups which had not been affected by mechanical loosening. The selection criteria of regular radiological follow-up, good clinical outcome (Charnley score of 5 or 6), continued walking without crutches and no radiological signs of loosening of the acetabular cups were fulfilled by 25 Charnley total hip arthroplasties. Mean migration, measured by the Nunn method, was 0.6 mm in the medial and 0.2 mm in the cranial direction. The mean yearly rate of wear was 0.05 mm and 0.04 mm, with six and two cups having no detectable wear, as measured by the Livermore and Charnley-Cupic methods, respectively. The maximal detected wear was 3.7 mm. There were no changes in the rate of wear with time. Computerised Ein Bild Röntgen Analyse (single-image radiological analysis) measurements of 20 hips indicated plastic deformation of the cups. We conclude that long-term successful cups do not migrate and have a very low rate of wear which was not affected by ageing of the polyethylene. There was no evidence that polyethylene wear alone caused mechanical loosening of the cup but high rates of wear seem to have an adverse prognostic value in terms of the long-term survival of the prosthesis

Aims

The primary objective of this study was to develop a validated classification system for assessing iatrogenic bone trauma and soft-tissue injury during total hip arthroplasty (THA). The secondary objective was to compare macroscopic bone trauma and soft-tissues injury in conventional THA (CO THA) versus robotic arm-assisted THA (RO THA) using this classification system.

Literature surrounding artificial intelligence (AI)-related applications for hip and knee arthroplasty has proliferated. However, meaningful advances that fundamentally transform the practice and delivery of joint arthroplasty are yet to be realized, despite the broad range of applications as we continue to search for meaningful and appropriate use of AI. AI literature in hip and knee arthroplasty between 2018 and 2021 regarding image-based analyses, value-based care, remote patient monitoring, and augmented reality was reviewed. Concerns surrounding meaningful use and appropriate methodological approaches of AI in joint arthroplasty research are summarized. Of the 233 AI-related orthopaedics articles published, 178 (76%) constituted original research, while the rest consisted of editorials or reviews. A total of 52% of original AI-related research concerns hip and knee arthroplasty (n = 92), and a narrative review is described. Three studies were externally validated. Pitfalls surrounding present-day research include conflating vernacular (“AI/machine learning”), repackaging limited registry data, prematurely releasing internally validated prediction models, appraising model architecture instead of inputted data, withholding code, and evaluating studies using antiquated regression-based guidelines. While AI has been applied to a variety of hip and knee arthroplasty applications with limited clinical impact, the future remains promising if the question is meaningful, the methodology is rigorous and transparent, the data are rich, and the model is externally validated. Simple checkpoints for meaningful AI adoption include ensuring applications focus on: administrative support over clinical evaluation and management; necessity of the advanced model; and the novelty of the question being answered.

Cite this article: Bone Joint J 2022;104-B(12):1292–1303.

Aims

This study investigates head-neck taper corrosion with varying head size in a novel hip simulator instrumented to measure corrosion related electrical activity under torsional loads.

Severe leg pain in a patient after total hip replacement was found to be caused by compression of the sciatic nerve by methylmethacrylate cement which had leaked from the acetabulum during fixation of the acetabular cup. The pain persisted for six years but was immediately relieved by removal of the cement mass

We report a case of late dissociation of a one-piece metal-backed acetabular component, associated with a prolific soft-tissue reaction to the polyethylene debris. The polyethylene liner was not visible on the radiographs. The metal-backed shell could not be removed because of bone ingrowth. We recommend that modular systems be utilised in cementless arthroplasty of the hip and that radiographic markers be incorporated in the polyethylene of the acetabular cup

A new method to reconstruct major acetabular floor defects is described. It relies on the placement of special nails into each of the three bones of the hemipelvis. Curved lugs attached to the nails are coalesced using bone cement forming a platform onto which a standard acetabular prosthesis is located. Forty-seven cases are reported with a mean follow-up of 4.4 years (1 to 8). No loosening of an acetabular cup or migration of the device has occurred

Four en-bloc resections for malignant tumours of the hip, the peri-acetabular region and the iliac wing were reconstructed using an irradiated hemipelvic allograft together with a total hip prosthesis. Technical aspects include the use of an anterior Enneking approach which excises the previous biopsy site, division and re-attachment of the iliac crest and fixation of the prosthesis using a modified acetabular cup and three polypropylene artificial ligaments to increase the stability of the joint. Weight-bearing was allowed at three months. The oncological and clinical results were satisfactory after a mean follow-up of 19 months, with walking distances of 500 metres to two kilometres without pain

The Wroblewski golf ball acetabular cup was introduced by surgeons using the trochanteric osteotomy approach for revision total hip replacement (THR) in order to reduce the rate of dislocation. We have routinely used the Ogee long posterior wall (Ogee LPW) and the Wroblewski angle bore cups in THR. Although the new Wroblewski golf ball cup performed well there was a significant early rate of dislocation of 20%. Our rate of dislocation over a period of ten years using the Ogee LPW and Wroblewski angle bore cups had been 0.52%. We present our findings and an investigation as to why the new cup has such a high rate of dislocation when used with the posterior approach. We show that a relatively small change in the design of the acetabular component resulted in significant adverse clinical results

We implanted 203 smooth-stemmed femoral components before January 1988. The femoral component used was anatomically shaped, fluted and made of titanium. Thirty-two hips were revised due to mid-thigh pain, and the femoral implant was found to be loose in all. In the 157 patients with a two-year follow-up, the Merle d'Aubigne and pain scores for completely cementless arthroplasties were similar to those for hybrid prostheses (cemented acetabular cup and cementless femoral stem). Of the 145 cases with two-year radiographic follow-up, 59 had extensive radiolucencies and 22 were unstable. The five-year cumulative survival rate was 77%. Implantation of this stem should be restricted to patients in whom cement fixation is contra-indicated

We selected randomly a consecutive series of 162 patients requiring hip replacement to receive either a cementless, hemispherical, modular, titanium acetabular cup or a cemented, all-polyethylene cup. These replacements were performed by two surgeons in four general hospitals. The same surgical technique was used and a 26 mm metal-head femoral component was used in every case. After exclusions, 115 hips were studied for differences in rates of wear and osteolysis. The mean clinical follow-up was eight years and the mean radiological follow-up, 6.5 years. The cementless cups wore at a mean rate of 0.15 mm per year and the cemented cups at 0.07 mm per year. This difference was significant (p < 0.0001). Our findings in this mid-term study suggest that cementless cups wear more than cemented cups

Polyethylene acetabular cups retrieved at revision surgery were measured by a shadowgraph technique to determine linear wear, and the values were compared with those obtained from radiographs. There was a close correlation between them, although the radiographic measurements slightly underestimated the true wear. Average linear wear rates for surface-replacement components were much greater than those for conventional prostheses with femoral heads up to 32 mm in diameter. Volumetric wear, calculated using a new formula, was found to be less than previously reported in vivo, and similar in magnitude to the results of experimental wear tests in vitro. The volumetric wear rates were greatest for the surface-replacement components and, for conventional components, were found to increase in a linear manner with component diameter

Between February 1975 and August 1976, 195 total hip replacements using Stanmore components were performed; of these, 146 were in 135 patients who had not had previous hip surgery. At review 52 had died, but none of the others was lost to follow-up. Of the 52, two had had a second operation, one for infection and one for recurrent dislocation. In the remaining 83 patients (92 hips) five revisions were necessary: four for aseptic loosening, and one for stem fracture. The remaining 78 patients had little or no pain and little restriction of activity. After a follow-up period of at least nine years, the survival rate of the prosthesis was 95%. There had been migration of the femoral component in five cases and migration of the acetabular cup in one case, but no wear of the acetabular component could be demonstrated

We measured polyethylene wear in 231 porous-coated uncemented acetabular cups. We divided the hips into two groups according to the fixation of the femoral component, by cementing (n = 97) or press-fit (n = 134). Follow-up was from three to five years. The patients in two sub-groups were matched for weight, diagnosis, sex, age and length of follow-up. The linear wear rate of cups articulated with uncemented femoral components (0.22 mm/year) was significantly higher than the wear rate (0.15 mm/year) of cups articulated within cemented femoral components (p < 0.05). These results can be compared with previously reported wear rates of 0.08 mm/year for cemented all-polyethylene cups and 0.11 mm/year for cemented metal-backed cups. The higher wear rates of uncemented arthroplasties could jeopardize the long-term results of this type of hip replacement

We prospectively studied 217 patients who underwent 234 Elite Plus total hip arthroplasties. At a mean of 6.4 (SD 0.7) years post-operatively, 39 patients had died and 22 were either lost to follow-up or had no radiographs available. Clinical (Oxford hip score) and radiological assessments were performed on 156 patients (168 hip arthroplasties) who had a mean age of 67.7 (SD 9.7) years at operation. In the assessed group, 26 of 159 (16.4%) of femoral stems which had not already been revised and 19 of 159 (11.9%) of acetabular cups were definitely loose. In total, 52 of 168 (31%) of hips had either been revised or had definite evidence of loosening of a component. We could not establish any relationship between clinical and radiological outcomes. Despite the fact that the clinical outcome and rate of revision for the Elite Plus appeared to meet international standards, our findings give us cause for concern. We believe that joint registries should include radiological surveillance in order to provide reliable information about medium-term outcomes for hip prostheses

We reviewed the radiographs of 864 Charnley and STH (Zimmer) cemented total hip arthroplasties with a mean follow-up of seven years (maximum 16 years). Survivorship analysis was used to assess the correlation between radiographic performance and the bony containment or the coronal orientation of the acetabular cup. The cup orientation and containment were interrelated; all vertically oriented cups were completely contained, whereas 25% of more horizontal cups were only partially contained. Completely contained cups had significantly lower incidences of complete cement-bone radiolucency (p = 0.02) and of wear (p = 0.09). Vertically oriented cups had a lower incidence of continuous radiolucency than neutrally oriented cups, but this was not statistically significant (p = 0.25). Our results confirm the importance of complete bony containment, and also indicate that it is better to accept vertical orientation and obtain full bony coverage than to have a more horizontal orientation with partial containment

An analysis of 142 dislocations from a multicentre study of 6774 total hip replacements is reported. The incidence of dislocation was 2.1 per cent. Patients with neuromuscular disorder, those in a confused mental state, and those undergoing revision operations are at special risk. The commonest surgical error, present in nearly half the patients, was placing the acetabular cup too vertically or too anteverted. A less common fault was placing the femoral component too anteverted. Neither the original pathology nor the approach to the hip appeared to affect the likelihood of dislocation. The dislocations were divided into early and late, single and recurrent, and the success rate of treatment is described in these groups. One hundred and eleven patients (78.2 per cent) eventually obtained stability. Of those with a single dislocation, 62 per cent remained stable after a single manipulation. Thirty-four per cent of the patients required an open operation to achieve stability and it is suggested that, in many cases, open reduction alone is not enough; the mechanical fault needs to be corrected

We examined stainless-steel, cobalt-chrome, titanium and alumina and zirconia ceramic femoral heads retrieved at revision surgery. All the heads had articulated against ultra-high-molecular-weight-polyethylene (UHMWPE) acetabular cups. We studied the simulation of third-body damage and the wear of UHMWPE against the various materials used for the heads. The surfaces of the retrieved heads were analysed using a two-dimensional contacting profilometer. Third-body damage was characterised by the mean height of the scratches above the mean line (R. pm. ). The alumina ceramic and zirconia ceramic retrieved heads were found to have significantly less damage. In laboratory studies the ceramics were also more resistant to simulated third-body damage than the metal alloys. We studied the wear of UHMWPE against the damaged counterfaces in simple configuration tests. The damaged ceramics produced less polyethylene wear than the damaged metal counterfaces. The wear factor of UHMWPE against the damaged materials was dependent on the amount of damage to the counterface (R. p. ). Our study has shown the benefit of using the harder and more damage-resistant ceramic materials for femoral heads