Retrieval studies of total hip replacements with highly cross-linked ultra-high-molecular-weight polyethylene liners have shown much less surface damage than with conventional ultra-high-molecular-weight polyethylene liners. A recent revision hip replacement for recurrent dislocation undertaken after only five months revealed a highly cross-linked polyethylene liner with a large area of visible delamination. In order to determine the cause of this unusual surface damage, we analysed the bearing surfaces of the cobalt-chromium femoral head and the acetabular liner with scanning electron microscopy, energy dispersive x-ray spectroscopy and optical profilometry. We concluded that the cobalt-chromium modular femoral head had scraped against the titanium acetabular shell during the course of the dislocations and had not only roughened the surface of the femoral head but also transferred deposits of titanium onto it. The largest deposits were 1.6 μm to 4.3 μm proud of the surrounding surface and could lead to increased stresses in the acetabular liner and therefore cause accelerated wear and damage.

This case illustrates that dislocations can leave titanium deposits on cobalt-chromium femoral heads and that highly cross-linked ultra-high-molecular-weight polyethylene remains susceptible to surface damage.

Ultra-high-molecular-weight polyethylene sterilised in the absence of air and highly cross-linked polyethylene have been used to avoid osteolysis and loosening in total hip replacement. Our prospective randomised study has assessed the results using two different polyethylenes associated with the same prosthetic design. We assessed 45 Allofit acetabular components with a Sulene-polyethylene liner of conventional polyethylene gamma sterilised with nitrogen and 45 Allofit acetabular components with a Durasul-polyethylene liner sterilised in ethylene oxide, both matched with an Alloclassic stem with a 28 mm modular femoral head. The prostheses were implanted between May 1999 and December 2001. The mean follow-up was for 66.3 months (60 to 92). The linear penetration of the femoral head was estimated at 6 weeks, at 6 and 12 months and annually thereafter from standardised digitised radiographs using image-analysis software.

There was no loosening of any prosthetic component. There were no radiolucent lines or osteolysis. The mean rate of penetration calculated from regression analysis during the first five years was 38 μm/year (sd 2) for the Sulene group and 6 μm/year (sd 1) for the Durasul group (p = 0.00002). The rate of penetration of the Durasul group was 15.7% of that of the Sulene group.

Aims

The aim of this study was to compare early functional and health related quality of life outcomes (HRQoL) in patients who have undergone total hip arthroplasty (THA) using a bone conserving short stem femoral component and those in whom a conventional length uncemented component was used. Outcome was assessed using a validated performance based outcome instrument as well as patient reported outcome measures (PROMs).

In this prospective study we studied the effect of the inclination angle of the acetabular component on polyethylene wear and component migration in cemented acetabular sockets using radiostereometric analysis.

A total of 120 patients received either a cemented Reflection All-Poly ultra-high-molecular-weight polyethylene or a cemented Reflection All-Poly highly cross-linked polyethylene acetabular component, combined with either cobalt–chrome or Oxinium femoral heads. Femoral head penetration and migration of the acetabular component were assessed with repeated radiostereometric analysis for two years. The inclination angle was measured on a standard post-operative anteroposterior pelvic radiograph. Linear regression analysis was used to determine the relationship between the inclination angle and femoral head penetration and migration of the acetabular component.

We found no relationship between the inclination angle and penetration of the femoral head at two years’ follow-up (p = 0.9). Similarly, our data failed to reveal any statistically significant correlation between inclination angle and migration of these cemented acetabular components (p = 0.07 to p = 0.9).

The August 2014 Hip & Pelvis Roundup³⁶⁰ looks at: Serial MRIs best for pseudotumour surveillance; Is ultrasound good enough for MOM follow-up?; Does weight loss in obese patients help?; Measuring acetabular anteversion on plain films; Two-stage one-stage too many in fungal hip revisions? and 35 is the magic number in arthroplasty.

The creep and wear behaviour of highly cross-linked polyethylene and standard polyethylene liners were examined in a prospective, double-blind randomised, controlled trial using radiostereometric analysis.

We randomised 54 patients to receive hip replacements with either highly cross-linked polyethylene or standard liners and determined the three-dimensional penetration of the liners over three years.

After three years the mean total penetration was 0.35 mm (SD 0.14) for the highly cross-linked polyethylene group and 0.45 mm (SD 0.19) for the standard group. The difference was statistically significant (p = 0.0184). From the pattern of penetration it was possible to discriminate creep from wear. Most (95%) of the creep occurred within six months of implantation and nearly all within the first year. There was no difference in the mean degree of creep between the two types of polyethylene (highly cross-linked polyethylene 0.26 mm, SD 0.17; standard 0.27 mm, SD 0.2; p = 0.83). There was, however, a significant difference (p = 0.012) in the mean wear rate (highly cross-linked polyethylene 0.03 mm/yr, SD 0.06; standard 0.07 mm/yr, SD 0.05). Creep and wear occurred in significantly different directions (p = 0.01); creep was predominantly proximal whereas wear was anterior, proximal and medial.

We conclude that penetration in the first six months is creep-dominated, but after one year virtually all penetration is due to wear. Highly cross-linked polyethylene has a 60% lower rate of wear than standard polyethylene and therefore will probably perform better in the long term.