Metal-on-metal total hip replacement has been targeted at younger patients with anticipated long-term survival, but the effect of the production of metal ions is a concern because of their possible toxicity to cells. We have reviewed the results of the use of the Ultima hybrid metal-on-metal total hip replacement, with a cemented polished tapered femoral component with a 28 mm diameter and a cobalt-chrome (CoCr) modular head, articulating with a 28 mm CoCr acetabular bearing surface secured in a titanium alloy uncemented shell. Between 1997 and 2004, 545 patients with 652 affected hips underwent replacement using this system. Up to 31 January 2008, 90 (13.8%) hips in 82 patients had been revised. Pain was the sole reason for revision in 44 hips (48.9%) of which 35 had normal plain radiographs. Peri-prosthetic fractures occurred in 17 hips (18.9%) with early dislocation in three (3.3%) and late dislocation in 16 (17.8%). Infection was found in nine hips (10.0%). At operation, a range of changes was noted including cavities containing cloudy fluid under pressure, necrotic soft tissues with avulsed tendons and denuded osteonecrotic upper femora. Corrosion was frequently observed on the retrieved cemented part of the femoral component. Typically, the peri-operative findings confirmed those found on pre-operative metal artefact reduction sequence MRI and histological examination showed severe necrosis. Metal artefact reduction sequence MRI proved to be useful when investigating these patients with pain in the absence of adverse plain radiological features

We studied the tapered interface between the head and the neck of 139 modular femoral components of hip prostheses which had been removed for a variety of reasons. In 91 the same alloy had been used for the head and the stem; none of them showed evidence of corrosion. In contrast, there was definite corrosion in 25 of the 48 prostheses in which the stem was of titanium alloy and the head of cobalt-chrome. This corrosion was time-dependent: no specimens were corroded after less than nine months in the body, but all which had been in place for more than 40 months were damaged. We discuss the factors which may influence the rate of these changes and present evidence that they were due to galvanically-accelerated crevice corrosion, which was undetected in previous laboratory testing of this type of prosthesis

In a post-mortem study, we compared subjects with metal implants with and without visible wear with an age-matched control group to determine the extent and effects of dissemination of wear debris. In subjects with stainless-steel and cobalt-chrome prostheses metal was found in local and distant lymph nodes, bone marrow, liver and spleen. The levels were highest in subjects with loose, worn joint prostheses and the main source of the debris was the matt coating. Metal levels were also raised in subjects with implants without visible wear and, to a less extent, in those with dynamic hip screws. Necrosis of lymph nodes was seen in those cases with the most wear, and potential damage to more distant organs such as the bone marrow, liver and spleen in the long term cannot be discounted. The consequences for the immune system and the role of metal dissemination in the possible induction of neoplasia are discussed

We implanted cylinders of cobalt-chrome or titanium, with smooth or porous surfaces, into rabbit bones which had been inoculated with suspensions of Staphylococcus aureus in various doses. The bacterial concentration required to produce infection of porous-coated titanium implants was 2.5 times smaller than that necessary to infect implants with polished surfaces. Porous-coated cobalt-chromium implants required bacterial concentrations that were 40 times smaller than those needed to infect implants with polished surfaces, and 15 times smaller than those required to infect porous-coated titanium implants. The other advantages and disadvantages of the various implants, such as improved osseointegration, larger ion-release surfaces, surface wear and relative stiffness, must be weighed against the higher infection rates in the porous-coated implants, and particularly in the cobalt-chromium implants

We investigated the fixation of fully-threaded cementless acetabular prostheses in 20 patients with osteoarthritis, measuring the migration of the cup using roentgen stereophotogrammetric analysis (RSA). All the cups migrated proximally, 13 moved laterally or medially, and nine moved anteriorly or posteriorly in the first two postoperative years, the average migration being 1.1 to 1.4 mm in either direction. Rotatory movements of up to 5.7 degrees were found in nine of the 13 hips where this analysis could be performed. Movements of cobalt-chrome (12) and titanium alloy (8) cups did not differ significantly. Seventeen of the 20 patients had some pain two years after the operation. The migration of the prostheses indicates that 'osseointegration' had not occurred. The combination of this with persistent pain suggests that the long-term results will be unfavourable

We have studied 27 tibial prostheses retrieved from knee replacements after 1 to 9 years. In 22 the femoral components were of cobalt-chrome, in five polyacetal. The design of the components gave a nominal contact area of 320 mm2 on each condyle. The tibial component was of high-density polyethylene (HDP) at least 6 mm thick, and not heat-treated. In the metal/HDP prostheses the average wear rate was 0.025 mm/year. The relative wear on the medial and lateral sides was related to the leg axis. None of the retrieved prostheses showed any severe disruption of their surface. The polyacetal/HDP prostheses showed similar wear with a statistically insignificant trend towards slower penetration. We conclude that the rate of wear of HDP in a conforming tibiofemoral bearing with a fixed tibial component at least 6 mm thick and not heat-treated is slow enough to be safe in clinical practice

Ten uncemented total hip replacements were performed in 1975 using an implant in which the cobalt-chrome femoral stem was coated to give a porous surface. In all but one case a high-density polyethylene head was used. The radiological changes in the upper femoral shafts were assessed between three and nine years later. Seven showed extensive stress-relieving changes, loss of calcar, stress fractures at the root of the lesser trochanter with subsequent detachment, and osteoporosis followed by avulsion of the greater trochanter. In these seven patients the lower part of the stem appeared to be soundly embedded, although in only one was there evidence of bony incorporation. It is suggested that if the fixation of a fully coated implant of this sort remains sound, gross atrophy of the upper femoral shaft develops after five years. This atrophy, associated with an implant which can be removed only at the expense of further bone destruction, presents substantial problems if revision is needed

The Norwegian Arthroplasty Register has shown that several designs of uncemented femoral stems give good or excellent survivorship. The overall findings for uncemented total hip replacement however, have been disappointing because of poor results with the use of metal-backed acetabular components. In this study, we exclusively investigated the medium-to long-term performance of primary uncemented metal-backed acetabular components. A total of 9113 primary uncemented acetabular components were implanted in 7937 patients between 1987 and 2007. These were included in a prospective, population-based observational study. All the implants were modular and metal-backed with ultra-high-molecular-weight polyethylene liners. The femoral heads were made of stainless steel, cobalt-chrome (CoCr) alloy or alumina ceramic. In all, seven different designs of acetabular component were evaluated by the Kaplan-Meier survivorship method and Cox regression analysis. Most acetabular components performed well up to seven years. When the endpoint was revision of the acetabular component because of aseptic loosening, the survival ranged between 87% and 100% at ten years. However, when the endpoint was revision for any reason, the survival estimates were 81% to 92% for the same implants at ten years. Aseptic loosening, wear, osteolysis and dislocation were the main reasons for the relatively poor overall performance of the acetabular components. Prostheses with alumina heads performed slightly better than those with stainless steel or CoCr alloy in subgroups. Whereas most acetabular components performed well at seven years, the survivorship declined with longer follow-up. Fixation was generally good. None of the metal-backed uncemented acetabular components with ultra-high-molecular-weight polyethylene liners in our study had satisfactory long-term results because of high rates of wear, osteolysis, aseptic loosening and dislocation

Aims

Orthopaedic and reconstructive surgeons are faced with large defects after the resection of malignant tumours of the sacrum. Spinopelvic reconstruction is advocated for resections above the level of the S1 neural foramina or involving the sacroiliac joint. Fixation may be augmented with either free vascularized fibular flaps (FVFs) or allograft fibular struts (AFSs) in a cathedral style. However, there are no studies comparing these reconstructive techniques.

We examined stainless-steel, cobalt-chrome, titanium and alumina and zirconia ceramic femoral heads retrieved at revision surgery. All the heads had articulated against ultra-high-molecular-weight-polyethylene (UHMWPE) acetabular cups. We studied the simulation of third-body damage and the wear of UHMWPE against the various materials used for the heads. The surfaces of the retrieved heads were analysed using a two-dimensional contacting profilometer. Third-body damage was characterised by the mean height of the scratches above the mean line (R. pm. ). The alumina ceramic and zirconia ceramic retrieved heads were found to have significantly less damage. In laboratory studies the ceramics were also more resistant to simulated third-body damage than the metal alloys. We studied the wear of UHMWPE against the damaged counterfaces in simple configuration tests. The damaged ceramics produced less polyethylene wear than the damaged metal counterfaces. The wear factor of UHMWPE against the damaged materials was dependent on the amount of damage to the counterface (R. p. ). Our study has shown the benefit of using the harder and more damage-resistant ceramic materials for femoral heads

Total hip replacement using porous-coated cobalt-chrome femoral implants designed for biological fixation has been evaluated in 307 patients after two years and in 89 patients after five years. Histological study of 11 retrieved specimens showed bone ingrowth in nine and fibrous tissue fixation in two. Fixation by bone ingrowth occurred in 93% of the cases in which a press fit of the stem at the isthmus was achieved, but in only 69% of those without a press fit. The clinical results at two years were excellent. The incidence of pain and limp was much lower when there was either a press fit of the stem or radiographic evidence of bone ingrowth. Factors such as age, sex, and the disease process did not influence the clinical results. Most cases showed only slight resorptive remodelling of the upper femur, but in a few cases with a larger, more rigid stem, more extensive bone loss occurred. The results after five years showed no deterioration with time. Fixation by the ingrowth of bone or of fibrous tissue both appeared to be stable, but bone ingrowth gave better clinical results

We reviewed 264 consecutive primary total hip replacements in 244 patients in which the Harris-Galante I porous-coated acetabular component had been used. The mean follow-up was 95 months (69 to 132). In 221 arthroplasties a 32 mm ceramic head had been used, and in the other 43 one of cobalt-chrome alloy. There were 124 women and 120 men with a mean age at operation of 56.8 years (21 to 83). Survival analysis of the acetabular components was performed using the following definitions of failure: 1) infection; 2) removal because of aseptic loosening; 3) removal for any cause; and 4) a worst-case analysis including removal of the cup or infection or loss to follow-up. Two well-fixed cups had been removed because of deep infection and three, similarly sound cups had been exchanged at the time of femoral revision. None of the acetabular components had required revision for aseptic loosening. After 11 years survival was 97.7% using the worst-case criterion. Radiological analysis of 187 acetabular components at a mean of 82 months (41 to 132) revealed no case of aseptic loosening. Pelvic osteolysis was seen in only one patient, but was not progressive and showed signs of regression. The results using these acetabular components are encouraging but the need for regular follow-up remains since complications such as significant wear of the liner, massive osteolysis of the pelvis, aseptic loosening and late infection may increase in the second decade

Aims

To establish our early clinical results of a new total knee arthroplasty (TKA) tibial component introduced in 2013 and compare it to other designs in use at our hospital during the same period.

Aims

To report the mid-term results of a modified self-growing rod (SGR) technique for the treatment of idiopathic and neuromuscular early-onset scoliosis (EOS).

1. The probable greatest bending moment applied to a plated or nailed fracture of the tibia during restricted weight-bearing is estimated to be, in men, up to about 79 Newton metres (58 poundsforce feet). The maximum twisting moment is estimated to be about 29 Newton metres (22 poundsforce feet). 2. Twenty-two human tibiae were loaded in three-point bending and broke at bending moments of from 57·9 to 294 Newton metres (42·7 to 216 poundsforce feet) if they had not previously been drilled; tibiae which had holes made through both cortices with a c. 3-millimetre (⅛-inch) drill broke at from 32·4 to 144 Newton metres (23·8 to 106 poundsforce feet). Tibiae loaded in torsion broke at twisting moments of from 27·5 to 892 Newton metres (20·2 to 65·8 poundsforce feet) when not drilled, 23·6 to 77·5 Newton metres (l7·3 to 57·1 poundsforce feet) when drilled. 3. When bent so as to open the fracture site, the 14-centimetre Stamm was the strongest of all the single plates tested (reaching its elastic limit at a bending moment of 17·6 Newton metres (13 poundsforce feet) and 5 degrees total angulation at 22·6 Newton metres (16·6 poundsforce feet)), while the Venable was the weakest (elastic limit 4·9 Newton metres (3·6 poundsforce feet) and 5 degrees at 7·9 Newton metres (5·8 poundsforce feet)). A 13-millimetre Küntscher nail reached its elastic limit at 42·2 Newton metres (31·1 poundsforce feet) and 5 degrees total angulation at 49 Newton metres (36 poundsforce feet). 4. In torsion the 15-centimetre Hicks was the strongest ofthe plates (elastic limit 27·5 Newton metres (20·2 poundsforce feet) and 5 degrees rotation at 16·7 Newton metres (l2·3 poundsforce feet)). 5. Küntscher nails in bones provided no dependable strength in torsion. 6. In both bending and torsion, a preparation of one Venable plate on each of the two anterior surfaces was stronger than any single plate, and was as strong as the weaker drilled tibiae. 7. The three currently available metallic materials (stainless steel, cobalt-chrome and titanium) have static mechanical properties so similar that the choice between them can be made on other grounds. 8. The highest load applied to a screw during bending tests was about half that needed to pull a screw out of even a thin-walled tibia. 9. Screws beyond four for one plate are mechanically redundant at the moment of implantation but may be necessary as an insurance against subsequent deterioration in strength. 10. Countersinks in plates are a source of significant weakness, and should preferably be as shallow as possible. 11. An unoccupied screw hole in the centre of a plate is a source of serious weakness. 12. Only the strongest implants tested were strong enough to withstand the bending or twisting moments to be expected in restricted weight-bearing. In two-plate preparations a danger is introduced by the fact that these moments are similar to those required to Ireak a drilled tibia

Aims

To evaluate the histopathological examination of peri-implant tissue samples as a technique in the diagnosis of postoperative spinal implant infection (PSII).

Aims

We have previously demonstrated raised cobalt and chromium levels in patients with larger diameter femoral heads, following metal-on-polyethylene uncemented total hip arthroplasty. Further data have been collected, to see whether these associations have altered with time and to determine the long-term implications for these patients and our practice.

Aims

Biofilm formation is intrinsic to prosthetic joint infection (PJI). In the current study, we evaluated the effects of silver-containing hydroxyapatite (Ag-HA) coating and vancomycin (VCM) on methicillin-resistant Staphylococcus aureus (MRSA) biofilm formation.