Fracture of the neck of the femur after resurfacing arthroplasty usually leads to failure and conversion to a total hip replacement. We describe an intracapsular fracture of the femoral neck sustained after hip resurfacing which was treated by cannulated screws, resulting in union and retention of the resurfacing implant. The result at follow-up three years later was very satisfactory with a Harris hip score of 99.

Aims

A contact patch to rim (CPR) distance of < 10 mm has been associated with edge-loading and excessive wear. However, not all arthroplasties with a low CPR distance show problems with wear. Therefore, CPR distance may not be the only variable affecting the post-operative metal ion concentrations.

The purpose of this study was twofold: first, to determine whether the five-year results of hip resurfacing arthroplasty (HRA) in Canada justified the continued use of HRA; and second, to identify whether greater refinement of patient selection was warranted.

This was a retrospective cohort study that involved a review of 2773 HRAs performed between January 2001 and December 2008 at 11 Canadian centres. Cox’s proportional hazards models were used to analyse the predictors of failure of HRA. Kaplan–Meier survival analysis was performed to predict the cumulative survival rate at five years. The factors analysed included age, gender, body mass index, pre-operative hip pathology, surgeon’s experience, surgical approach, implant sizes and implant types. The most common modes of failure were also analysed.

The 2773 HRAs were undertaken in 2450 patients: 2127 in men and 646 in women. The mean age at operation was 50.5 years (sd 8.72; 18 to 82) and mean follow-up was 3.4 years (sd 2.1; 2.0 to 10.1). At the last follow-up a total of 101 HRAs (3.6%) required revision. Using revision for all causes of failure as the endpoint, Kaplan–Meier survival analysis showed a cumulative survival of 96.4% (95% confidence interval (CI) 96.1 to 96.9) at five years. With regard to gender, the five-year overall survival was 97.4% in men (95% CI 97.1 to 97.7) and 93.6% in women (95% CI 92.6 to 94.6). Female gender, smaller femoral components, specific implant types and a diagnosis of childhood hip problems were associated with higher rates of failure. The most common cause of failure was fracture of the femoral neck, followed by loosening of the femoral component.

The failure rates of HRA at five years justify the ongoing use of this technique in men. Female gender is an independent predictor of failure, and a higher failure rate at five years in women leads the authors to recommend this technique only in exceptional circumstances for women.

Cite this article: Bone Joint J 2013;95-B:1044–50.

Blood metal ions have been widely used to investigate metal-on-metal hip replacements, but their ability to discriminate between well-functioning and failed hips is not known. The Medicines and Healthcare products Regulatory Agency (MHRA) has suggested a cut-off level of 7 parts per billion (ppb).

We performed a pair-matched, case-control study to investigate the sensitivity and specificity of blood metal ion levels for diagnosing failure in 176 patients with a unilateral metal-on-metal hip replacement. We recruited 88 cases with a pre-revision, unexplained failed hip and an equal number of matching controls with a well-functioning hip. We investigated the 7 ppb cut-off level for the maximum of cobalt or chromium and determined optimal mathematical cut-off levels from receiver-operating characteristic curves.

The 7 ppb cut-off level for the maximum of cobalt or chromium had a specificity of 89% and sensitivity 52% for detecting a pre-operative unexplained failed metal on metal hip replacement. The optimal cut-off level for the maximum of cobalt or chromium was 4.97 ppb and had sensitivity 63% and specificity 86%.

Blood metal ions had good discriminant ability to separate failed from well-functioning hip replacements. The MHRA cut-off level of 7 ppb provides a specific test but has poor sensitivity.

Hip resurfacing has been proposed as an alternative to traditional total hip arthroplasty in young, active patients. Much has been learned following the introduction of metal-on-metal resurfacing devices in the 1990s. The triad of a well-designed device, implanted accurately, in the correct patient has never been more critical than with these implants.

Following Food and Drug Administration approval in 2006, we studied the safety and effectiveness of one hip resurfacing device (Birmingham Hip Resurfacing) at our hospital in a large, single-surgeon series. We report our early to mid–term results in 1333 cases followed for a mean of 4.3 years (2 to 5.7) using a prospective, observational registry. The mean patient age was 53.1 years (12 to 84); 70% were male and 91% had osteoarthritis. Complications were few, including no dislocations, no femoral component loosening, two femoral neck fractures (0.15%), one socket loosening (0.08%), three deep infections (0.23%), and three cases of metallosis (0.23%). There were no destructive pseudotumours.

Overall survivorship at up to 5.7 years was 99.2%. Aseptic survivorship in males under the age of 50 was 100%. We believe this is the largest United States series of a single surgeon using a single resurfacing system.

Cite this article: Bone Joint J 2016;98-B (1 Suppl A):10–13.

Aims

Surgeons have commonly used modular femoral heads and stems from different manufacturers, although this is not recommended by orthopaedic companies due to the different manufacturing processes.

We compared the rate of corrosion and rate of wear at the trunnion/head taper junction in two groups of retrieved hips; those with mixed manufacturers (MM) and those from the same manufacturer (SM).

We retrospectively analysed concentrations of chromium and cobalt ions in samples of synovial fluid and whole blood taken from a group of 92 patients with failed current-generation metal-on-metal hip replacements. We applied acid oxidative digestion to our trace metal analysis protocol, which found significantly higher levels of metal ion concentrations in blood and synovial fluid than a non-digestive method. Patients were subcategorised by mode of failure as either ‘unexplained pain’ or ‘defined causes’. Using this classification, chromium and cobalt ion levels were present over a wider range in synovial fluid and not as strongly correlated with blood ion levels as previously reported. There was no significant difference between metal ion concentrations and manufacturer of the implant, nor femoral head size below or above 50 mm. There was a moderately positive correlation between metal ion levels and acetabular component inclination angle as measured on three-dimensional CT imaging.

Our results suggest that acid digestion of samples of synovial fluid samples is necessary to determine metal ion concentrations accurately so that meaningful comparisons can be made between studies.

The presence of pseudotumours, which are soft-tissue masses relating to the hip, after metal-on-metal hip resurfacing arthroplasty has been associated with elevated levels of metal ions in serum, suggesting that pseudotumours occur when there is increased wear. We aimed to quantify the wear in vivo of implants revised for pseudotumours (eight) and of a control group of implants (22) revised for other reasons of failure.

We found that the implant group with pseudotumours had a significantly higher rate of median linear wear of the femoral component at 8.1 μm/year (2.75 to 25.4) than the 1.79 μm/year (0.82 to 4.15; p = 0.002) of the non-pseudotumour group. For the acetabular component a significantly higher rate of median linear wear of 7.36 μm/year (1.61 to 24.9) was observed in the pseudotumour group compared with 1.28 μm/year (0.81 to 3.33, p = 0.001) in the other group. Wear of the acetabular component in the pseudotumour group always involved the edge of the implant, indicating that edge-loading had occurred.

Our findings are the first direct evidence that pseudotumour is associated with increased wear at the metal-on-metal articulation. Furthermore, edge-loading with the loss of fluid-film lubrication may be an important mechanism of generation of wear in patients with a pseudotumour.

Pseudotumours are a rare complication of hip resurfacing. They are thought to be a response to metal debris which may be caused by edge loading due to poor orientation of the acetabular component. Our aim was to determine the optimal acetabular orientation to minimise the risk of pseudotumour formation.

We matched 31 hip resurfacings revised for pseudotumour formation with 58 controls who had a satisfactory outcome from this procedure. The radiographic inclination and anteversion angles of the acetabular component were measured on anteroposterior radiographs of the pelvis using Einzel-Bild-Roentgen-Analyse software. The mean inclination angle (47°, 10° to 81°) and anteversion angle (14°, 4° to 34°) of the pseudotumour cases were the same (p = 0.8, p = 0.2) as the controls, 46° (29° to 60°) and 16° (4° to 30°) respectively, but the variation was greater. Assuming an accuracy of implantation of ± 10° about a target position, the optimal radiographic position was found to be approximately 45° of inclination and 20° of anteversion. The incidence of pseudotumours inside the zone was four times lower (p = 0.007) than outside the zone.

In order to minimise the risk of pseudotumour formation we recommend that surgeons implant the acetabular component at an inclination of 45° (± 10) and anteversion of 20° (± 10) on post-operative radiographs. Because of differences between the radiographic and the operative angles, this may be best achieved by aiming for an inclination of 40° and an anteversion of 25°.

Lately, concerns have arisen following the use of large metal-on-metal bearings in hip replacements owing to reports of catastrophic soft-tissue reactions resulting in implant failure and associated complications. This review examines the literature and contemporary presentations on current clinical dilemmas in metal-on-metal hip replacement.

We report 17 patients (20 hips) in whom metal-on-metal resurfacing had been performed and who presented with various symptoms and a soft-tissue mass which we termed a pseudotumour. Each patient underwent plain radiography and in some, CT, MRI and ultrasonography were also performed. In addition, histological examination of available samples was undertaken.

All the patients were women and their presentation was variable. The most common symptom was discomfort in the region of the hip. Other symptoms included spontaneous dislocation, nerve palsy, a noticeable mass or a rash. The common histological features were extensive necrosis and lymphocytic infiltration. To date, 13 of the 20 hips have required revision to a conventional hip replacement. Two are awaiting revision.

We estimate that approximately 1% of patients who have a metal-on-metal resurfacing develop a pseudotumour within five years. The cause is unknown and is probably multifactorial. There may be a toxic reaction to an excess of particulate metal wear debris or a hypersensitivity reaction to a normal amount of metal debris. We are concerned that with time the incidence of these pseudotumours may increase. Further investigation is required to define their cause.

Wear of metal-on-metal bearings causes elevated levels of cobalt and chromium in blood and body fluids. Metal-on-metal bearings have two distinct wear phases. In the early phase, the wear rate is high. Later, it decreases and the bearing enters a steady-state phase. It is expected that as the wear rates decline, the level of cobalt detected in plasma will also decrease. We studied the baseline and exercise-related cobalt rise in 21 patients (13 men and eight women) with a mean age of 54 years (38 to 80) who had undergone successful hip resurfacing at a mean of 44 months (10 to 96) earlier. Our results showed that circulating baseline cobalt levels were not significantly correlated with the time since implantation (r = 0.08, p = 0.650). By contrast, the exercise-related cobalt rise was directly correlated with the inclination angle of the acetabular component (r = 0.47, p = 0.032) and inversely correlated with the time since implantation (r = −0.5, p = 0.020).

Inclination of the acetabular component should be kept less than 40° to decrease the production of wear debris.

Metal-on-metal hip resurfacing is commonly performed for osteoarthritis in young active patients. We have observed cystic or solid masses, which we have called inflammatory pseudotumours, arising around these devices. They may cause soft-tissue destruction with severe symptoms and a poor outcome after revision surgery. The aim of this study was to determine the incidence of and risk factors for pseudotumours that are serious enough to require revision surgery.

Since 1999, 1419 metal-on-metal hip resurfacings have been implanted by our group in 1224 patients; 1.8% of the patients had a revision for pseudotumour. In this series the Kaplan-Meier cumulative revision rate for pseudotumour increased progressively with time. At eight years, in all patients, it was 4% (95% confidence interval (CI) 2.2 to 5.8). Factors significantly associated with an increase in revision rate were female gender (p < 0.001), age under 40 (p = 0.003), small components (p = 0.003), and dysplasia (p = 0.019), whereas implant type was not (p = 0.156). These factors were inter-related, however, and on fitting a Cox proportional hazard model only gender (p = 0.002) and age (p = 0.024) had a significant independent influence on revision rate; size nearly reached significance (p = 0.08). Subdividing the cohort according to significant factors, we found that the revision rate for pseudotumours in men was 0.5% (95% CI 0 to 1.1) at eight years wheras in women over 40 years old it was 6% (95% CI 2.3 to 10.1) at eight years and in women under 40 years it was 13.1% at six years (95% CI 0 to 27) (p < 0.001).

We recommend that resurfacings are undertaken with caution in women, particularly those under 40 years of age but they remain a good option in young men. Further work is required to understand the aetiology of pseudotumours so that this complication can be avoided.

Hip simulators have been used for ten years to determine the tribological performance of large-head metal-on-metal devices using traditional test conditions. However, the hip simulator protocols were originally developed to test metal-on-polyethylene devices. We have used patient activity data to develop a more physiologically relevant test protocol for metal-on-metal devices. This includes stop/start motion, a more appropriate walking frequency, and alternating kinetic and kinematic profiles.

There has been considerable discussion about the effect of heat treatments on the wear of metal-on-metal cobalt chromium molybdenum (CoCrMo) devices. Clinical studies have shown a higher rate of wear, levels of metal ions and rates of failure for the heat-treated metal compared to the as-cast metal CoCrMo devices. However, hip simulator studies in vitro under traditional testing conditions have thus far not been able to demonstrate a difference between the wear performance of these implants.

Using a physiologically relevant test protocol, we have shown that heat treatment of metal-on-metal CoCrMo devices adversely affects their wear performance and generates significantly higher wear rates and levels of metal ions than in as-cast metal implants.

Aims

The aims of this study were to compare the diagnostic test characteristics of ultrasound alone, metal artefact reduction sequence MRI (MARS-MRI) alone, and ultrasound combined with MARS-MRI for identifying intra-operative pseudotumours in metal-on-metal hip resurfacing (MoMHR) patients undergoing revision surgery.

Abnormal wear of cobalt-containing metal-on-metal joints is associated with inflammatory pseudotumours. Cobalt ions activate human toll-like receptor 4 (TLR4), which normally responds to bacterial lipopolysaccharide (LPS) in sepsis. Activation of TLR4 by LPS increases the expression of chemokines IL-8 and CXCL10, which recruit leukocytes and activated T-cells, respectively. This study was designed to determine whether cobalt induces a similar inflammatory response to LPS by promoting the expression of IL-8 and CXCL10. A human monocytic cell line, derived from acute monocytic leukaemia, was treated with cobalt ions and expression of IL-8 and CXCL10 measured at mRNA and protein levels. Cobalt-treated macrophages showed a 60-fold increase in IL-8 mRNA, and an eightfold increase in production of the mature chemokine (both p < 0.001); expression of the CXCL10 gene and protein was also significantly increased by cobalt (both p < 0.001). Experiments were also performed in the presence of CLI-095, a TLR4-specific antagonist which abrogated the cobalt-mediated increase in IL-8 and CXCL10 expression.

These findings suggest that cobalt ions induce inflammation similar to that observed during sepsis by the simultaneous activation of two TLR4-mediated signalling pathways. These pathways result in increased production of IL-8 and CXCL10, and may be implicated in pseudotumour formation following metal-on-metal replacement.

Cite this article: Bone Joint J 2014; 96-B:1172–7.

The aim of this study was to evaluate the functional and oncological outcome of extracorporeally irradiated autografts used to reconstruct the pelvis after a P1/2 internal hemipelvectomy.

The study included 18 patients with a primary malignant bone tumour of the pelvis. There were 13 males and five females with a mean age of 24.8 years (8 to 62). Of these, seven had an osteogenic sarcoma, six a Ewing’s sarcoma, and five a chondrosarcoma. At a mean follow-up of 51.6 months (4 to 185), nine patients had died with metastatic disease while nine were free from disease. Local recurrence occurred in three patients all of whom eventually died of their disease. Deep infection occurred in three patients and required removal of their graft in two while the third underwent a hindquarter amputation for extensive flap necrosis.

The mean Musculoskeletal Tumor Society functional score of the 16 patients who could be followed-up for at least 12 months was 77% (50 to 90). Those 15 patients who completed the Toronto Extremity Salvage Score questionnaire had a mean score of 71% (53 to 85).

Extracorporeal irradiation and re-implantation of bone is a valid method of reconstruction after an internal hemipelvectomy. It has an acceptable morbidity and a functional outcome that compares favourably with other available reconstructive techniques.

Cite this article: Bone Joint J 2014;96-B:1404–10