Aims. We have previously demonstrated raised cobalt and chromium levels in patients with larger diameter femoral heads, following metal-on-polyethylene uncemented total hip arthroplasty. Further data have been collected, to see whether these associations have altered with time and to determine the long-term implications for these patients and our practice. Methods. Patients from our previous study who underwent Trident-Accolade primary total hip arthroplasties using a metal-on-polyethylene bearing in 2009 were reviewed. Patients were invited to have their cobalt and chromium levels retested, and were provided an Oxford Hip Score. Serum ion levels were then compared between groups (28 mm, 36 mm, and 40 mm heads) and over time. Results. Metal ion levels were repeated in 33 patients. When comparing the results of serum metal ion levels over time, regardless of head size, there was a significant increase in both cobalt and chromium levels (p < 0.001). Two patients with larger head sizes had undergone revision arthroplasty with evidence of trunnion damage at surgery. Two patients within the 40 mm subgroup had metal ion levels above the MHRA (Medicines and Healthcare Products Regulatory Agency) threshold for detailed investigation. The increase in cobalt and chromium, when comparing the 36 mm and 40 mm groups with those of the 28 mm group, was not significant (36 mm vs 28 mm; p = 0.092/p = 0.191; 40 mm vs 28 mm; p = 0.200/p = 0.091, respectively). There was no difference, between femoral head sizes, when comparing outcome as measured by the Oxford Hip Score. Conclusion. This study shows an increase in cobalt and chromium levels over time for all modular femoral head sizes in patients with metal-on-polyethylene bearings, with two patients demonstrating ion levels above the MHRA threshold for failure, and a further two patients requiring revision surgery. These results may have clinical implications regarding longer term follow-up of patients and future implant choice, particularly among younger patients. Cite this article: Bone Joint J 2020;102-B(7):832–837

Objectives. The use of ceramic femoral heads in total hip arthroplasty (THA) has increased due to their proven low bearing wear characteristics. Ceramic femoral heads are also thought to reduce wear and corrosion at the head-stem junction with titanium (Ti) stems when compared with metal heads. We sought to evaluate taper damage of ceramic compared with metal heads when paired with cobalt chromium (CoCr) alloy stems in a single stem design. Methods. This retrieval study involved 48 total hip arthroplasties (THAs) with CoCr V40 trunnions paired with either CoCr (n = 21) or ceramic (n = 27) heads. The taper junction of all hips was evaluated for fretting/corrosion damage and volumetric material loss using a roundness-measuring machine. We used linear regression analysis to investigate taper damage differences after adjusting for potential confounding variables. Results. We measured median taper material loss rates of 0.210 mm. 3. /year (0.030 to 0.448) for the metal head group and 0.084 mm. 3. /year (0.059 to 0.108) for the ceramic group. The difference was not significant (p = 0.58). Moreover, no significant correlation between material loss and implant or patient factors (p > 0.05) was found. Conclusions. Metal heads did not increase taper damage on CoCr trunnions compared with ceramic heads from the same hip design. The amount of material released at the taper junctions was very low when compared with available data regarding CoCr/Ti coupling in metal-on-metal bearings. Cite this article: A. Di Laura, H. Hothi, J. Henckel, I. Swiatkowska, M. H. L. Liow, Y-M. Kwon, J. A. Skinner, A. J. Hart. Retrieval analysis of metal and ceramic femoral heads on a single CoCr stem design. Bone Joint Res 2017;6:–350. DOI: 10.1302/2046-3758.65.BJR-2016-0325.R1

Aims. Reverse total shoulder arthroplasty (RTSA) using trabecular metal (TM)-backed glenoid implants has been introduced with the aim to increase implant survival. Only short-term reports on the outcomes of TM-RTSA have been published to date. We aim to present the seven-year survival of TM-backed glenoid implants along with minimum five-year clinical and radiological outcomes. Methods. All consecutive elective RTSAs performed at a single centre between November 2008 and October 2014 were reviewed. Patients who had primary TM-RTSA for rotator cuff arthropathy and osteoarthritis with deficient cuff were included. A total of 190 shoulders in 168 patients (41 male, 127 female) were identified for inclusion at a mean of 7.27 years (SD 1.4) from surgery. The primary outcome was survival of the implant with all-cause revision and aseptic glenoid loosening as endpoints. Secondary outcomes were clinical, radiological, and patient-related outcomes with a five-year minimum follow-up. Results. The implant was revised in ten shoulders (5.2%) with a median time to revision of 21.2 months (interquartile range (IQR) 9.9 to 41.8). The Kaplan-Meier survivorship estimate at seven years was 95.9% (95% confidence interval (CI) 91.7 to 98; 35 RTSAs at risk) for aseptic mechanical failure of the glenoid and 94.8% (95% CI 77.5 to 96.3; 35 RTSAs at risk) for all-cause revision. Minimum five-year clinical and radiological outcomes were available for 103 and 98 RTSAs respectively with a median follow-up time of six years (IQR 5.2 to 7.0). Median postoperative Oxford Shoulder Score was 38 (IQR 31 to 45); median Constant and Murley score was 60 (IQR 47.5 to 70); median forward flexion 115° (IQR 100° to 125°); median abduction 95° (IQR 80° to 120°); and external rotation 25° (IQR 15° to 40°) Scapular notching was seen in 62 RTSAs (63.2%). Conclusion. We present the largest and longest-term series of TM-backed glenoid implants demonstrating 94.8% all-cause survivorship at seven years. Specifically pertaining to glenoid loosening, survival of the implant increased to 95.9%. In addition, we report satisfactory minimum five-year clinical and radiological outcomes. Cite this article: Bone Joint J 2021;103-B(8):1333–1338

Aims. Our first aim was to determine whether there are significant changes in the level of metal ions in the blood at mid-term follow-up, in patients with an Articular Surface Replacement (ASR) arthroplasty. Secondly, we sought to identify risk factors for any increases. Patients and Methods. The study involved 435 patients who underwent unilateral, metal-on-metal (MoM) hip resurfacing (HRA) or total hip arthroplasty (THA). These patients all had one measurement of the level of metal ions in the blood before seven years had passed post-operatively (early evaluation) and one after seven years had passed post-operatively (mid-term evaluation). Changes in ion levels were tested using a Wilcoxon signed-rank test. We identified subgroups at the highest risk of increase using a multivariable linear logistic regression model. Results. There were significant increases in the levels of metal ions for patients who underwent both MoM HRA (Chromium (Cr): 0.5 parts per billion (ppb); Cobalt (Co): 1.1 ppb) and MoM THA (Cr: 0.5 ppb; Co: 0.7 ppb). In a multivariable model considering MoM HRAs, the change in the levels of metal ions was influenced by female gender (Co: Odds Ratio (OR) 1.42; p = 0.002 and Cr: OR 1.08; p = 0.006). The change was found to be irrespective of the initial level for the MoM HRAs, whereas there was a negative relationship between the initial level and the change in the level for those with a MoM THA (Co: OR -0.43; p <  0.001 and Cr: OR -0.14; p = 0.033). Conclusion. The levels of metal ions in the blood increase significantly over the period until mid-term follow-up in patients with both a MoM HRA and those with a MoM THA. We recommend that the levels of metal ions be measured most frequently for women with a MoM HRA. While those with a MoM THA appear to stabilise at a certain level, the accuracy of this trend is not yet clear. Vigilant follow-up is still recommended. . Cite this article: Bone Joint J 2017;99-B(4 Supple B):33–40

Aims

The tibial component of total knee arthroplasty can either be an all-polyethylene (AP) implant or a metal-backed (MB) implant. This study aims to compare the five-year functional outcomes of AP tibial components to MB components in patients aged over 70 years. Secondary aims are to compare quality of life, implant survivorship, and cost-effectiveness.

Aims

Taper corrosion has been widely reported to be problematic for modular total hip arthroplasty implants. A simple and systematic method to evaluate taper damage with sufficient resolution is needed. We introduce a semiquantitative grading system for modular femoral tapers to characterize taper corrosion damage.

Aims. Total knee arthroplasty is an established treatment for knee osteoarthritis with excellent long-term results, but there remains controversy about the role of uncemented prostheses. We present the long-term results of a randomized trial comparing an uncemented tantalum metal tibial component with a conventional cemented component of the same implant design. Methods. Patients under the age of 70 years with symptomatic osteoarthritis of the knee were randomized to receive either an uncemented tantalum metal tibial monoblock component or a standard cemented modular component. The mean age at time of recruitment to the study was 63 years (50 to 70), 46 (51.1%) knees were in male patients, and the mean body mass index was 30.4 kg/m. 2. (21 to 36). The same cruciate retaining total knee system was used in both groups. All patients received an uncemented femoral component and no patients had their patella resurfaced. Patient outcomes were assessed preoperatively and postoperatively using the modified Oxford Knee Score, Knee Society Score, and 12-Item Short-Form Health Survey questionnaire (SF-12) score. Radiographs were analyzed using the American Knee Society Radiograph Evaluation score. Operative complications, reoperations, or revision surgery were recorded. A total of 90 knees were randomized and at last review 77 knees were assessed. In all, 11 patients had died and two were lost to follow-up. Results. At final review all patients were between 11 and 15 years following surgery. In total, 41 of the knees were cemented and 36 uncemented. There were no revisions in the cemented group and one revision in the uncemented group for fracture. The uncemented group reported better outcomes with both statistically and clinically significant (p = 0.001) improvements in knee-specific Oxford and Knee Society scores compared with the cemented group. The global SF-12 scores demonstrated no statistical difference (p = 0.812). Uncemented knees had better radiological analysis compared with the cemented group (p < 0.001). Conclusion. Use of an uncemented trabecular metal tibial implant can afford better long-term clinical outcomes when compared to cemented tibial components of a matched design. However, both have excellent survivorship up to 15 years after implantation. Cite this article: Bone Joint J 2020;102-B(8):1025–1032

Aims

The use of cementless total knee arthroplasty (TKA) components has increased during the past decade. The initial design of cementless metal-backed patellar components had shown high failure rates due to many factors. The aim of this study was to evaluate the clinical results of a second-generation cementless, metal-backed patellar component of a modern design.

We report a systematic review and meta-analysis of the peer-reviewed literature focusing on metal sensitivity testing in patients undergoing total joint replacement (TJR). Our purpose was to assess the risk of developing metal hypersensitivity post-operatively and its relationship with outcome and to investigate the advantages of performing hypersensitivity testing. We undertook a comprehensive search of the citations quoted in PubMed and EMBASE: 22 articles (comprising 3634 patients) met the inclusion criteria. The frequency of positive tests increased after TJR, especially in patients with implant failure or a metal-on-metal coupling. The probability of developing a metal allergy was higher post-operatively (odds ratio (OR) 1.52 (95% confidence interval (CI) 1.06 to 2.31)), and the risk was further increased when failed implants were compared with stable TJRs (OR 2.76 (95% CI 1.14 to 6.70)). Hypersensitivity testing was not able to discriminate between stable and failed TJRs, as its predictive value was not statistically proven. However, it is generally thought that hypersensitivity testing should be performed in patients with a history of metal allergy and in failed TJRs, especially with metal-on-metal implants and when the cause of the loosening is doubtful

Aims. The aims of this study were to evaluate wear on the surface of cobalt-chromium (CoCr) femoral components used in total knee arthroplasty (TKA) and compare the wear of these components with that of ceramic femoral components. Methods. Optical profilometry was used to evaluate surface roughness and to examine the features created by the wear process in a knee wear simulator. We developed a method of measuring surface changes on five CoCr femoral components and quantifying the loss of material from the articular surface during the wear process. We also examined the articular surface of three ceramic femoral components from a previous test for evidence of surface damage, and compared it with that of CoCr components. Results. We found that the surface roughness of CoCr components rapidly increased during the first 1,000 wear cycles, then reached a steady state, but material loss from the surface continued at a rate of 1,778,000 μm. 3. per million cycles as carbides were removed from its matrix. These carbides formed third-body wear particles, leading to the formation of new scratches even as older scratches were worn away. In contrast, no scratching, loss of material, or other surface damage, when evaluated with one nanometer resolution, was found on the surface of the ceramic components after a 15 M wear cycle test. Conclusion. This study showed wear and loss of CoCr material from scratching and microabrasive wear in TKA. The material loss from the surface continued in a linear relationship with increasing cycles. We also found the absence of scratching and roughening of ceramic femoral components in simulated wear, suggesting an advantage in wear rate and avoiding metal sensitivity. This may have implications in the management of persistent pain after TKA. Cite this article: Bone Joint J 2021;103-B(6 Supple A):94–101

Aims

Reverse total shoulder arthroplasty (rTSA) can be used in complex cases when the glenoid requires reconstruction. In this study, a baseplate with composite bone autograft and a central trabecular titanium peg was implanted, and its migration was assessed for two years postoperatively using radiostereometric analysis (RSA).

The purpose of this study was to evaluate whether concerns about the release of metal ions in metal-on-metal total hip replacements (THR) should be extended to patients with metal-bearing total disc replacements (TDR). Cobalt and chromium levels in whole blood and serum were measured in ten patients with a single-level TDR after a mean follow-up of 34.5 months (13 to 61) using inductively-coupled plasma mass spectrometry. These metal ion levels were compared with pre-operative control levels in 81 patients and with metal ion levels 12 months after metal-on-metal THR (n = 21) and resurfacing hip replacement (n = 36). Flexion-extension radiographs were used to verify movement of the TDR. Cobalt levels in whole blood and serum were significantly lower in the TDR group than in either the THR (p = 0.007) or the resurfacing group (p < 0.001). Both chromium levels were also significantly lower after TDR versus hip resurfacing (p < 0.001), whereas compared with THR this difference was only significant for serum levels (p = 0.008). All metal ion levels in the THR and resurfacing groups were significantly higher than in the control group (p < 0.001). In the TDR group only cobalt in whole blood appeared to be significantly higher (p < 0.001). The median range of movement of the TDR was 15.5° (10° to 22°). These results suggest that there is minimal cause for concern about high metal ion concentrations after TDR, as the levels appear to be only moderately elevated. However, spinal surgeons using a metal-on-metal TDR should still be aware of concerns expressed in the hip replacement literature about toxicity from elevated metal ion levels, and inform their patients appropriately

Metaphyseal bone loss is common with revision total knee replacement (RTKR). Using the Anderson Orthopaedic Research Institute (AORI) classification, type 2-B and type 3 defects usually require large metal blocks, bulk structural allograft or highly porous metal cones. Tibial and femoral trabecular metal metaphyseal cones are a unique solution for large bone defects. These cones substitute for bone loss, improve metaphyseal fixation, help correct malalignment, restore the joint line and may permit use of a shorter stem. The technique for insertion involves sculpturing of the remaining bone with a high speed burr and rasp, followed by press-fit of the cone into the metaphysis. The fixation and osteoconductive properties of the porous cone outer surface allow ingrowth and encourage long-term biological fixation. The revision knee component is then cemented into the porous cone inner surface, which provides superior fixation compared with cementing into native but deficient metaphyseal bone. The advantages of the cone compared with allograft include: technical ease, biological fixation, no resorption, and possibly a lower risk of infection. The disadvantages include: difficult extraction and relatively short-term follow-up. Several studies using cones report promising short-term results for the reconstruction of large bone defects in RTKR. Cite this article: Bone Joint J 2014;96-B(11 Suppl A):118–21

Aims

The aim of this study was to evaluate the incidence of liner malseating in two commonly used dual-mobility (DM) designs. Secondary aims included determining the risk of dislocation, survival, and clinical outcomes.

Aims

One of the main causes of tibial revision surgery for total knee arthroplasty is aseptic loosening. Therefore, stable fixation between the tibial component and the cement, and between the tibial component and the bone, is essential. A factor that could influence the implant stability is the implant design, with its different variations. In an existing implant system, the tibial component was modified by adding cement pockets. The aim of this experimental in vitro study was to investigate whether additional cement pockets on the underside of the tibial component could improve implant stability. The relative motion between implant and bone, the maximum pull-out force, the tibial cement mantle, and a possible path from the bone marrow to the metal-cement interface were determined.

Aims. We wished to investigate the influence of metal debris exposure on the subsequent immune response and resulting soft-tissue injury following metal-on-metal (MoM) hip arthroplasty. Some reports have suggested that debris generated from the head-neck taper junction is more destructive than equivalent doses from metal bearing surfaces. . Patients and Methods. We investigated the influence of the source and volume of metal debris on chromium (Cr) and cobalt (Co) concentrations in corresponding blood and hip synovial fluid samples and the observed agglomerated particle sizes in excised tissues using multiple regression analysis of prospectively collected data. A total of 199 explanted MoM hips (177 patients; 132 hips female) were analysed to determine rates of volumetric wear at the bearing surfaces and taper junctions. . Results. The statistical modelling suggested that a greater source contribution of metal debris from the taper junction was associated with smaller aggregated particle sizes in the local tissues and a relative reduction of Cr ion concentrations in the corresponding synovial fluid and blood samples. Metal debris generated from taper junctions appears to be of a different morphology, composition and therefore, potentially, immunogenicity to that generated from bearing surfaces. Conclusion. The differences in debris arising from the taper and the articulating surfaces may provide some understanding of the increased incidence of soft-tissue reactions reported in patients implanted with MoM total hip arthroplasties compared with patients with hip resurfacings. Cite this article: Bone Joint J 2016;98-B:925–33

We retrospectively analysed concentrations of chromium and cobalt ions in samples of synovial fluid and whole blood taken from a group of 92 patients with failed current-generation metal-on-metal hip replacements. We applied acid oxidative digestion to our trace metal analysis protocol, which found significantly higher levels of metal ion concentrations in blood and synovial fluid than a non-digestive method. Patients were subcategorised by mode of failure as either ‘unexplained pain’ or ‘defined causes’. Using this classification, chromium and cobalt ion levels were present over a wider range in synovial fluid and not as strongly correlated with blood ion levels as previously reported. There was no significant difference between metal ion concentrations and manufacturer of the implant, nor femoral head size below or above 50 mm. There was a moderately positive correlation between metal ion levels and acetabular component inclination angle as measured on three-dimensional CT imaging. Our results suggest that acid digestion of samples of synovial fluid samples is necessary to determine metal ion concentrations accurately so that meaningful comparisons can be made between studies