Objectives. We investigated the reliability of the cobalt-chromium (CoCr) synovial joint fluid ratio (JFR) in identifying the presence of a severe aseptic lymphocyte-dominated vasculitis-associated lesion (ALVAL) response and/or suboptimal taper performance (SOTP) following metal-on-metal (MoM) hip arthroplasty. We then examined the possibility that the CoCr JFR may influence the serum partitioning of Co and Cr. Methods. For part A, we included all revision surgeries carried out at our unit with the relevant data, including volumetric wear analysis, joint fluid (JF) Co and Cr concentrations, and ALVAL grade (n = 315). Receiver operating characteristic curves were constructed to assess the reliability of the CoCr JFR in identifying severe ALVAL and/or SOTP. For part B, we included only patients with unilateral prostheses who had given matched serum and whole blood samples for Co and Cr analysis (n = 155). Multiple regression was used to examine the influence of JF concentrations on the serum partitioning of Co and Cr in the blood. Results. A CoCr JFR > 1 showed a specificity of 83% (77% to 88%) and sensitivity of 63% (55% to 70%) for the detection of severe ALVAL and/or SOTP. In patients with CoCr JFRs > 1, the median blood Cr to serum Cr ratio was 0.99, compared with 0.71 in patients with CoCr JFRs < 1 (p < 0.001). Regression analysis demonstrated that the blood Cr to serum Cr value was positively associated with the JF Co concentration (p = 0.011) and inversely related to the JF Cr concentration (p < 0.001). Conclusion. Elevations in CoCr JFRs are associated with adverse biological (severe ALVAL) or tribocorrosive processes (SOTP). Comparison of serum Cr with blood Cr concentrations may be a useful additional clinical tool to help to identify these conditions. Cite this article: D. J. Langton, S. Natu, C. F. Harrington, J. G. Bowsher, A. V. F. Nargol. Is the synovial fluid cobalt-to-chromium ratio related to the serum partitioning of metal debris following metal-on-metal hip arthroplasty? Bone Joint Res 2019;8:146–155. DOI: 10.1302/2046-3758.83.BJR-2018-0049.R1

Aims. There are limited published data detailing the volumetric material loss from tapers of conventional metal-on-polyethylene (MoP) total hip arthroplasties (THAs). Our aim was to address this by comparing the taper wear rates measured in an explanted cohort of the widely used Exeter THA with those measured in a group of metal-on-metal (MoM) THAs. Patients and Methods. We examined an existing retrieval database to identify all Exeter V40 and Universal MoP THAs. Volumetric wear analysis of the taper surfaces was conducted using previously validated methodology. These values were compared with those obtained from a series of MoM THAs using non-parametric statistical methodology. A number of patient and device variables were accounted for using multiple regression modelling. Results. A total of 95 Exeter MoP and 249 MoM THAs were examined. The median volumetric loss from the MoM cohort was over four times larger than that from the MoP cohort (1.01 mm. 3. vs 0.23 mm. 3. , p < 0.001), despite a significantly shorter median period in vivo for the MoM group (48 months vs 90 months, p < 0.001). Multiple regression modelling indicated that the dominant variables leading to greater female taper material loss were bearing diameter (p < 0.001), larger female taper angles (p < 0.001), and male titanium stem tapers (p < 0.001). Conclusion. Consistent with the long-term clinical success of the device, the volumetric material loss from Exeter femoral head tapers was, in general, small compared with that from larger-diameter MoM head tapers. Cite this article: Bone Joint J 2018;100-B:1310–9

We analysed 54 alumina ceramic-on-ceramic bearings from total hip replacements retrieved at one centre after a mean duration of 3.5 years (0.2 to 10.6) in situ. These implants were obtained from 54 patients (16 men and 38 women) with a mean age of 67 years (33 to 88) who underwent revision for a variety of reasons. Posterior edge loading was found in the majority of these retrievals (32 out of 54). Anterosuperior edge loading occurred less often but produced a higher rate of wear. Stripe wear on the femoral heads had a median volumetric wear rate of 0.2 mm. 3. /year (0 to 7.2). The wear volume on the femoral heads corresponded to the width of edge wear on the matching liner. Anteversion of the acetabular component was found to be a more important determinant than inclination for wear in ceramic bearings. Posterior edge loading may be considered to be a normal occurrence in ceramic-on-ceramic bearings, with minimal clinical consequences. Edge loading should be defined as either anterosuperior or posterior, as each edge loading mechanism may result in different clinical implications

Polyethylene wear debris can cause osteolysis and the failure of total hip arthroplasty. We present the five-year wear rates of a highly cross-linked polyethylene (X3) bearing surface when used in conjunction with a 36 mm ceramic femoral head. This was a prospective study of a cohort of 100 THAs in 93 patients. Pain and activity scores were measured pre- and post-operatively. Femoral head penetration was measured at two months, one year, two years and at five years using validated edge-detecting software (PolyWare Auto). At a mean of 5.08 years (3.93 to 6.01), 85 hips in 78 patients were available for study. The mean age of these patients was 59.08 years (42 to 73, the mean age of males (n = 34) was 59.15 years, and females (n = 44) was 59.02 years). All patients had significant improvement in their functional scores (p < 0.001). The steady state two-dimensional linear wear rate was 0.109 mm/year. The steady state volumetric wear rate was 29.61 mm. 3. /year. No significant correlation was found between rate of wear and age (p = 0.34), acetabular component size (p = 0.12) or clinical score (p = 0.74). Our study shows low steady state wear rates at five years in X3 highly cross-linked polyethylene in conjunction with a 36 mm ceramic femoral head. The linear wear rate was almost identical to the osteolysis threshold of 0.1 mm/year recommended in the literature. Cite this article: Bone Joint J 2015;97-B:1470–4

There are many methods for analysing wear volume in failed polyethylene acetabular components. We compared a radiological technique with three recognised ex vivo methods of measurement. We tested 18 ultra-high-molecular-weight polyethylene acetabular components revised for wear and aseptic loosening, of which 13 had pre-revision radiographs, from which the wear volume was calculated based upon the linear wear. We used a shadowgraph technique on silicone casts of all of the retrievals and a coordinate measuring method on the components directly. For these techniques, the wear vector was calculated for each component and the wear volume extrapolated using mathematical equations. The volumetric wear was also measured directly using a fluid-displacement method. The results of each technique were compared. The series had high wear volumes (mean 1385 mm. 3. ; 730 to 1850) and high wear rates (mean 205 mm. 3. /year; 92 to 363). There were wide variations in the measurements of wear volume between the radiological and the other techniques. Radiograph-derived wear volume correlated poorly with that of the fluid-displacement method, co-ordinate measuring method and shadowgraph methods, becoming less accurate as the wear increased. The mean overestimation in radiological wear volume was 47.7% of the fluid-displacement method wear volume. Fluid-displacement method, coordinate measuring method and shadowgraph determinations of wear volume were all better than that of the radiograph-derived linear measurements since they took into account the direction of wear. However, only radiological techniques can be used in vivo and remain useful for monitoring linear wear in the clinical setting. Interpretation of radiological measurements of acetabular wear must be done judiciously in the clinical setting. In vitro laboratory techniques, in particular the fluid-displacement method, remain the most accurate and reliable methods of assessing the wear of acetabular polyethylene

Polyethylene acetabular cups retrieved at revision surgery were measured by a shadowgraph technique to determine linear wear, and the values were compared with those obtained from radiographs. There was a close correlation between them, although the radiographic measurements slightly underestimated the true wear. Average linear wear rates for surface-replacement components were much greater than those for conventional prostheses with femoral heads up to 32 mm in diameter. Volumetric wear, calculated using a new formula, was found to be less than previously reported in vivo, and similar in magnitude to the results of experimental wear tests in vitro. The volumetric wear rates were greatest for the surface-replacement components and, for conventional components, were found to increase in a linear manner with component diameter

Ultra-high-molecular-weight polyethylene (UHMWPE) components for total joint replacement generate wear particles which cause adverse biological tissue reactions leading to osteolysis and loosening. Sterilisation of UHMWPE components by gamma irradiation in air causes chain scissions which initiate a long-term oxidative process that degrades the chemical and mechanical properties of the polyethylene. Using a tri-pin-on-disc tribometer we studied the effect of ageing for ten years after gamma irradiation in air on the volumetric wear, particle size distribution and the number of particles produced by UHMWPE when sliding against a stainless-steel counterface. The aged and irradiated material produced six times more volumetric wear and 34 times more wear particles per unit load per unit sliding distance than non-sterilised UHMWPE. Our findings indicate that oxidative degradation of polyethylene after gamma irradiation in air with ageing produces more wear

The April 2023 Hip & Pelvis Roundup³⁶⁰ looks at: Do technical errors determine outcomes of operatively managed femoral neck fractures in younger adults?; Single-stage or two-stage revision for hip prosthetic joint infection (INFORM); Fixation better than revision in type B periprosthetic fractures of taper slip stems; Can you maximize femoral head size at the expense of liner thickness?; Plasma D-dimer for periprosthetic joint infection?; How important is in vivo oxidation?; Total hip arthroplasty for HIV patients with osteonecrosis.

This multicentre study analysed 12 alumina ceramic-on-ceramic components retrieved from squeaking total hip replacements after a mean of 23 months in situ (11 to 61). The rates and patterns of wear seen in these squeaking hips were compared with those seen in matched controls using retrieval data from 33 ‘silent’ hip replacements with similar ceramic bearings. All 12 bearings showed evidence characteristic of edge-loading wear. The median rate of volumetric wear was 3.4 mm. 3. /year for the acetabular component, 2.9 mm. 3. /year on the femoral heads and 6.3 mm. 3. /year for head and insert combined. This was up to 45 times greater than that of previously reported silent ceramic-on-ceramic retrievals. The rate of wear seen in ceramic components revised for squeaking hips appears to be much greater than in that seen in retrievals from ‘silent’ hips.

Osteolysis is due to particulate wear debris and is responsible for the long-term failure of total hip replacements. It has stimulated the development of alternative joint surfaces such as metal-on-metal or ceramic-on-ceramic implants. Since 1988 the second-generation metal-on-metal implant Metasul has been used in over 60 000 hips. Analysis of 118 retrieved specimens of the head or cup showed rates of wear of approximately 25 μm for the whole articulation per year in the first year, decreasing to about 5 μm per year after the third. Metal surfaces have a ‘self-polishing’ capacity. Scratches are worn out by further joint movement. Volumetric wear was decreased some 60-fold compared with that of metal-on-polyethylene implants, suggesting that second-generation metal-on-metal prostheses may considerably reduce osteolysis

We compared and quantified the modes of failure and patterns of wear of 11 Mittelmeier and 11 Ceraver-Ostal retrieved alumina-alumina hip prostheses with reference to the corresponding clinical and radiological histories. Macroscopic wear was assessed using a three-dimensional co-ordinate measuring machine. Talysurf contacting profilometry was used to measure surface roughness on a microscopic scale and SEM to determine mechanisms of wear at the submicron level. The components were classified into one of three categories of wear: low (no visible/measurable wear), stripe (elliptical wear stripe on the heads and larger worn areas on the cups) and severe (macroscopic wear, large volumes of material lost). Overall, the volumetric wear of the alumina-alumina prostheses was substantially less than the widely used metal and ceramic-on-polyethylene combinations. By identifying and eliminating the factors which accelerate wear, it is expected that the lifetime of these devices can be further increased

In this prospective, randomised study, we have compared the wear rate of cemented, acetabular polyethylene cups articulating with either a 22 mm or a 32 mm cobalt-chromium head. We evaluated 89 patients who had a total of 484 radiographs. The mean follow-up period was 71.4 months (SD 29.1). All the radiographs were digitised and electronically measured. The linear wear rate was significantly higher during the first two years and decreased after this period to a constant value. We suggest that this is partly due to a ‘run-in’ process caused by irregularities between surfaces of the cup and head and an initial plastic deformation of the polyethylene. The mean volumetric wear was 120.3 mm. 3. /year for the 32 mm head, which was significantly higher than the 41.5 mm. 3. /year for the 22 mm heads. The mean linear wear rate was not significantly different. We were, however, unable to find radiological signs of osteolysis in the patients who had higher wear rates

Aims

The first aim of this study was to evaluate whether preoperative renal function is associated with postoperative changes in whole blood levels of metal ions in patients who have undergone a Birmingham Hip Resurfacing (BHR) arthroplasty with a metal-on-metal bearing. The second aim was to evaluate whether exposure to increased cobalt (Co) and chromium (Cr) levels for ten years adversely affected renal function.

Aims

This study reports the results of 38 total hip arthroplasties (THAs) in 33 patients aged less than 50 years, using the JRI Furlong hydroxyapatite ceramic (HAC)-coated femoral component.

Aims

The aim of this study was to evaluate the performance of first-generation annealed highly cross-linked polyethylene (HXLPE) in cementless total hip arthroplasty (THA).

Aims

In metal-on-metal (MoM) hip arthroplasties and resurfacings, mechanically induced corrosion can lead to elevated serum metal ions, a local inflammatory response, and formation of pseudotumours, ultimately requiring revision. The size and diametral clearance of anatomical (ADM) and modular (MDM) dual-mobility polyethylene bearings match those of Birmingham hip MoM components. If the acetabular component is satisfactorily positioned, well integrated into the bone, and has no surface damage, this presents the opportunity for revision with exchange of the metal head for ADM/MDM polyethylene bearings without removal of the acetabular component.

Aims

The aim of this study was to investigate whether wear and backside deformation of polyethylene (PE) tibial inserts may influence the cement cover of tibial trays of explanted total knee arthroplasties (TKAs).

We examined radiographic polyethylene wear in 233 cemented total hip arthroplasties (201 patients) with either a metal-backed or a non-metal-backed acetabular cup. All patients had identical cemented one-piece titanium femoral stems with a femoral head diameter of 28 mm. The mean linear wear rate was 0.11 mm/yr in metal-backed sockets and 0.08 mm/yr in non-metal-backed sockets (p = 0.0002). The mean volumetric wear rate was 66.2 mm3/yr in the metal-backed sockets and 48.2 mm3/yr in the polyethylene sockets (p = 0.0002). The addition of metal backing to a cemented acetabular cup therefore resulted in a 37% increase in mean polyethylene wear rates which may partially explain the higher failure rate of cemented metal-backed cups. Linear regression analysis also implicated increased follow-up time (log), gross acetabular migration, metal backing and male gender in increasing polyethylene wear. We advocate the use of an all-polyethylene cup in cemented total hip arthroplasty. The increased polyethylene wear must also cause concern about the wear rate of uncemented metal-backed acetabular sockets