Radiostereometric analysis (RSA) can detect early micromovement in unstable implant designs which are likely subsequently to have a high failure rate. In 2010, the Articular Surface Replacement (ASR) was withdrawn because of a high failure rate. In 19 ASR femoral components, the mean micromovement over the first two years after implantation was 0.107 mm (sd 0.513) laterally, 0.055 mm (sd 0.204) distally and 0.150 mm (sd 0.413) anteriorly. The mean backward tilt around the x-axis was -0.08° (sd 1.088), mean internal rotation was 0.165° (sd 0.924) and mean varus tilt 0.238° (sd 0.420). The baseline to two-year varus tilt was statistically significant from zero movement, but there was no significant movement from one year onwards.

We conclude that the ASR femoral component achieves initial stability and that early migration is not the mode of failure for this resurfacing arthroplasty.

A 70-year-old man with an uncemented metal-on-polyethylene total hip prosthesis underwent revision arthroplasty 33 months later because of pain, swelling and recurrent dislocation. There appeared to be corrosion and metal release from the prosthetic head, resulting in pseudotumour formation and severe local soft-tissue destruction. The corrosion occurred at the junction between the titanium-molybdenum-zirconium-iron taper and the cobalt-chrome-molybdenum head, but the mechanism was unproven.

We analysed 54 alumina ceramic-on-ceramic bearings from total hip replacements retrieved at one centre after a mean duration of 3.5 years (0.2 to 10.6) in situ. These implants were obtained from 54 patients (16 men and 38 women) with a mean age of 67 years (33 to 88) who underwent revision for a variety of reasons. Posterior edge loading was found in the majority of these retrievals (32 out of 54). Anterosuperior edge loading occurred less often but produced a higher rate of wear. Stripe wear on the femoral heads had a median volumetric wear rate of 0.2 mm³/year (0 to 7.2). The wear volume on the femoral heads corresponded to the width of edge wear on the matching liner. Anteversion of the acetabular component was found to be a more important determinant than inclination for wear in ceramic bearings. Posterior edge loading may be considered to be a normal occurrence in ceramic-on-ceramic bearings, with minimal clinical consequences. Edge loading should be defined as either anterosuperior or posterior, as each edge loading mechanism may result in different clinical implications.

This systematic review of the literature summarises the clinical experience with ceramic-on-ceramic hip bearings over the past 40 years and discusses the concerns that exist in relation to the bearing combination. Loosening, fracture, liner chipping on insertion, liner canting and dissociation, edge-loading and squeaking have all been reported, and the relationship between these issues and implant design and surgical technique is investigated. New design concepts are introduced and analysed with respect to previous clinical experience.

We compared the medium-term clinical and radiological results of hybrid total hip replacement (THR) with metal-on-metal Birmingham hip resurfacing (BHR) in two groups of 54 young patients matched for age, gender, body mass index and pre-operative levels of activity.

The clinical outcome was assessed by the University of California, Los Angeles (UCLA) activity score, the Oxford Hip Score (OHS) and the EuroQol scores. Radiologically, all hips were assessed for migration and osteolysis, the hybrid THRs for polyethylene wear and the BHRs for a pedestal sign. The mean follow-up of the patients with a hybrid THR was ten years and for those with a BHR, nine years. Four patients with a hybrid THR and one with a BHR had died. In each group five were lost to follow-up. The revision rate of the hybrid THRs was 16.7% (9 of 54) and of the BHRs 9.3% (5 of 54) (p = 0.195). Radiographs of a further eight hybrid THRs demonstrated wear and osteolysis, and they await revision (p = 0.008). Of the unrevised BHRs 90% had radiological changes, of which approximately 50% had progressed over the previous four years. All hybrid THRs demonstrated linear polyethylene wear with a mean of 1.24 mm (0.06 to 3.03). The BHRs recorded superior OHS (p = 0.013), UCLA (p = 0.008), and EuroQol visual analogue scores (p = 0.009).

After nine years, patients with BHRs remained more active and had a lower rate of revision than those with hybrid THRs. Both groups demonstrated progressive radiological changes at medium-term follow-up.

We present the 10- to 17-year results of 112 computer-assisted design computer-assisted manufacture femoral components. The total hip replacements were performed between 1992 and 1998 in 111 patients, comprising 53 men and 58 women. Their mean age was 46.2 years (24.6 to 62.2) with a mean follow-up of 13 years (10 to 17). The mean Harris Hip Score improved from 42.4 (7 to 99) to 90.3 (38 to 100), the mean Oxford Hip Score from 43.1 (12 to 59) to 18.2 (12 to 51) and the mean Western Ontario MacMasters University Osteoarthritis Index score from 57.0 (7 to 96) to 11.9 (0 to 85). There was one revision due to failure of the acetabular component but no failures of the femoral component. There were no revisions for aseptic loosening. The worst-case survival in this cohort of custom femoral components at 13.2 years follow-up was 98.2% (95% confidence interval 95 to 99). Overall survival of this series of total hip replacements was 97.3% (95% confidence interval 95 to 99).

These results are comparable with the best medium- to long-term results for femoral components used in primary total hip replacement with any means of fixation.

We performed 96 Birmingham resurfacing arthroplasties of the hip in 71 consecutive patients with avascular necrosis of the femoral head. A modified neck-capsule-preserving approach was used which is described in detail. The University of California, Los Angeles outcome score, the radiological parameters and survival rates were assessed. The mean follow-up was for 5.4 years (4.0 to 8.1). All the patients remained active with a mean University of California, Los Angeles activity score of 6.86 (6 to 9). Three hips failed, giving a cumulative survival rate of 95.4%. With failure of the femoral component as the endpoint, the cumulative survival rate was 98.0%. We also describe the combined abduction-valgus angle of the bearing couple, which is the sum of the inclination angle of the acetabular component and the stem-shaft angle, as an index of the optimum positioning of the components in the coronal plane.

Using a modified surgical technique, it is possible to preserve the femoral head in avascular necrosis by performing hip resurfacing in patients with good results.

Resurfacing arthroplasties of the hip are being undertaken with increasing frequency and the complications associated with this procedure are well documented. We have encountered a further problem with a fracture of the centralising peg of the femoral component in a prosthesis which had been in situ for three years.

We have reviewed our experience of the removal of deep extremity orthopaedic implants in children to establish the nature, rate and risk of complications associated with this procedure. A retrospective review was performed of 801 children who had 1223 implants inserted and subsequently removed over a period of 17 years. Bivariate analysis of possible predictors including clinical factors, complications associated with implant insertion and indications for removal and the complications encountered at removal was performed. A logistical regression model was then constructed using those predictors which were significantly associated with surgical complications from the bivariate analyses. Odds ratios estimated in the logistical regression models were converted to risk ratios.

The overall rate of complications after removal of the implant was 12.5% (100 complications in 801 patients), with 48 (6.0%) major and 52 (6.5%) minor. Children with a complication after insertion of the initial implant or with a non-elective indication for removal, a neuromuscular disease associated with a seizure disorder or a neuromuscular disease in those unable to walk, had a significantly greater chance of having a major complication after removal of the implant. Children with all four of these predictors were 14.6 times more likely to have a major complication.

We used a biodegradable mesh to convert an acetabular defect into a contained defect in six patients at total hip replacement. Their mean age was 61 years (46 to 69). The mean follow-up was 32 months (19 to 50). Before clinical use, the strength retention and hydrolytic in vitro degradation properties of the implants were studied in the laboratory over a two-year period. A successful clinical outcome was determined by the radiological findings and the Harris hip score.

All the patients had a satisfactory outcome and no mechanical failures or other complications were observed. No protrusion of any of the impacted grafts was observed beyond the mesh. According to our preliminary laboratory and clinical results the biodegradable mesh is suitable for augmenting uncontained acetabular defects in which the primary stability of the implanted acetabular component is provided by the host bone. In the case of defects of the acetabular floor this new application provides a safe method of preventing graft material from protruding excessively into the pelvis and the mesh seems to tolerate bone-impaction grafting in selected patients with primary and revision total hip replacement.

Despite the increasing interest and subsequent published literature on hip resurfacing arthroplasty, little is known about the prevalence of its complications and in particular the less common modes of failure. The aim of this study was to identify the prevalence of failure of hip resurfacing arthroplasty and to analyse the reasons for it.

From a multi-surgeon series (141 surgeons) of 5000 Birmingham hip resurfacings we have analysed the modes, prevalence, gender differences and times to failure of any hip requiring revision. To date 182 hips have been revised (3.6%). The most common cause for revision was a fracture of the neck of the femur (54 hips, prevalence 1.1%), followed by loosening of the acetabular component (32 hips, 0.6%), collapse of the femoral head/avascular necrosis (30 hips, 0.6%), loosening of the femoral component (19 hips, 0.4%), infection (17 hips, 0.3%), pain with aseptic lymphocytic vascular and associated lesions (ALVAL)/metallosis (15 hips, 0.3%), loosening of both components (five hips, 0.1%), dislocation (five hips, 0.1%) and malposition of the acetabular component (three hips, 0.1%). In two cases the cause of failure was unknown.

Comparing men with women, we found the prevalence of revision to be significantly higher in women (women = 5.7%; men = 2.6%, p < 0.001). When analysing the individual modes of failure women had significantly more revisions for loosening of the acetabular component, dislocation, infection and pain/ALVAL/metallosis (p < 0.001, p = 0.004, p = 0.008, p = 0.01 respectively).

The mean time to failure was 2.9 years (0.003 to 11.0) for all causes, with revision for fracture of the neck of the femur occurring earlier than other causes (mean 1.5 years, 0.02 to 11.0). There was a significantly shorter time to failure in men (mean 2.1 years, 0.4 to 8.7) compared with women (mean 3.6 years, 0.003 to 11.0) (p < 0.001).

Second-generation metal-on-metal bearings were introduced as a response to the considerable incidence of wear-induced failures associated with conventional replacements, especially in young patients. We present the results at ten years of a consecutive series of patients treated using a metal-on-metal hip resurfacing. A distinct feature of the bearings used in our series was that they had been subjected to double-heat treatments during the post-casting phase of their manufacture. In the past these bearings had not been subjected to thermal treatments, making this a unique metal-on-metal bearing which had not been used before in clinical practice.

We report the outcome of 184 consecutive hips (160 patients) treated using a hybrid-fixed metal-on-metal hip resurfacing during 1996. Patients were invited for a clinicoradiological follow-up at a minimum of ten years. The Oxford hip score and anteroposterior and lateral radiographs were obtained. The mean age at operation was 54 years (21 to 75). A series of 107 consecutive hips (99 patients) who received the same prosthesis, but subjected to a single thermal treatment after being cast, between March 1994 and December 1995, were used as a control group for comparison.

In the 1994 to 1995 group seven patients (seven hips) died from unrelated causes and there were four revisions (4%) for osteolysis and aseptic loosening. In the 1996 group nine patients died at a mean of 6.9 years after operation because of unrelated causes. There were 30 revisions (16%) at a mean of 7.3 years (1.2 to 10.9), one for infection at 1.2 years and 29 for osteolysis and aseptic loosening. Furthermore, in the latter group there were radiological signs of failure in 27 (24%) of the 111 surviving hips.

The magnitude of the problem of osteolysis and aseptic loosening in the 1996 cohort did not become obvious until five years after the operation. Our results indicate that double-heat treatments of metal-on-metal bearings can lead to an increased incidence of wear-induced osteolysis.

In a randomised study, 28 patients with a mean age of 62.2 years (32 to 81) with osteoarthritis or avascular necrosis of the hip received either a ceramic-on-ceramic or a metal-on-metal total hip replacement. Apart from the liners the acetabular and femoral components were made of Ti-Al-Nb alloy. The serum aluminium and cobalt levels were measured before, and at one year after surgery.

The 15 patients in the ceramic-on-ceramic group had a median pre-operative aluminium level of 1.3 μg/l (0.25 to 8.4) and a cobalt level below the detection limit. At one year the aluminium level was 1.1 μg/l (0.25 to 2.3) and the cobalt level was 0.4 μg/l (0.15 to 0.7). The 13 patients in the metal-on-metal group had a median pre-operative aluminium level of 1.9 μg/l (0.25 to 4.4) and a cobalt level below the detection limit. At one year the median aluminium level was 0.9 μg/l (0.25 to 3.9) whereas the cobalt level was 1.4 μg/l (0.5 to 10.5). This increase in the cobalt level at one year was significant (p < 0.001).

Our findings indicate that ceramic-on-ceramic bearings do not cause elevated levels of serum aluminium in the first post-operative year.

A total of 20 pairs of fresh-frozen cadaver femurs were assigned to four alignment groups consisting of relative varus (10° and 20°) and relative valgus (10° and 20°), 75 composite femurs of two neck geometries were also used. In both the cadaver and the composite femurs, placing the component in 20° of valgus resulted in a significant increase in load to failure. Placing the component in 10° of valgus had no appreciable effect on increasing the load to failure except in the composite femurs with varus native femoral necks. Specimens in 10° of varus were significantly weaker than the neutrally-aligned specimens.

The results suggest that retention of the intact proximal femoral strength occurs at an implant angulation of ≥ 142°. However, the benefit of extreme valgus alignment may be outweighed in clinical practice by the risk of superior femoral neck notching, which was avoided in this study.

We report the survival at five years of 144 consecutive metal-on-metal resurfacings of the hip implanted between August 1997 and May 1998. Failure was defined as revision of either the acetabular or femoral component for any reason during the study period. The survival at the end of five years was 98% overall and 99% for aseptic revisions only. The mean age of the patients at implantation was 52.1 years.

Three femoral components failed during the first two years, two were infected and one fractured. A single stage revision was carried out in each case. No other revisions were performed or are impending. No patients were lost to follow-up. Four died from unrelated causes during the study period.

This study confirms that hip resurfacing using a metal-on-metal bearing of known provenance can provide a solution in the medium term for the younger more active adult who requires surgical intervention for hip disease.

Metal-on-metal hip resurfacing was performed for developmental dysplasia in 96 hips in 85 patients, 78 in women and 18 in men, with a mean age at the time of surgery of 43 years (14 to 65). These cases were matched for age, gender, operating surgeon and date of operation with a group of patients with primary osteoarthritis who had been treated by resurfacing, to provide a control group of 96 hips (93 patients). A clinical and radiological follow-up study was performed. The dysplasia group were followed for a mean of 4.4 years (2.0 to 8.5) and the osteoarthritis group for a mean of 4.5 years (2.2 to 9.4). Of the dysplasia cases, 17 (18%) were classified as Crowe grade III or IV.

There were five (5.2%) revisions in the dysplasia group and none in the osteoarthritic patients. Four of the failures were due to acetabular loosening and the other sustained a fracture of the neck of femur. There was a significant difference in survival between the two groups (p = 0.02). The five-year survival was 96.7% (95% confidence interval 90.0 to 100) for the dysplasia group and 100% (95% confidence interval 100 to 100) for the osteoarthritic group. There was no significant difference in the median Oxford hip score between the two groups at any time during the study.

The medium-term results of metal-on-metal hip resurfacing in all grades of developmental dysplasia are encouraging, although they are significantly worse than in a group of matched patients with osteoarthritis treated in the same manner.

The effects of the method of fixation and interface conditions on the biomechanics of the femoral component of the Birmingham hip resurfacing arthroplasty were examined using a highly detailed three-dimensional computer model of the hip. Stresses and strains in the proximal femur were compared for the natural femur and for the femur resurfaced with the Birmingham hip resurfacing. A comparison of cemented versus uncemented fixation showed no advantage of either with regard to bone loading. When the Birmingham hip resurfacing femoral component was fixed to bone, proximal femoral stresses and strains were non-physiological. Bone resorption was predicted in the inferomedial and superolateral bone within the Birmingham hip resurfacing shell. Resorption was limited to the superolateral region when the stem was not fixed. The increased bone strain observed adjacent to the distal stem should stimulate an increase in bone density at that location. The remodelling of bone seen during revision of failed Birmingham hip resurfacing implants appears to be consistent with the predictions of our finite element analysis.

We report an independent prospective review of the first 230 Birmingham hip resurfacings in 212 patients at a mean follow-up of five years (4 to 6).

Two patients, one with a loose acetabular component and the other with suspected avascular necrosis of the femoral head, underwent revision. There were two deaths from unrelated causes and one patient was lost to follow-up. The survivorship with the worst-case scenario was 97.8% (95% confidence interval 95.8 to 99.5). The mean Harris hip score improved significantly (paired t-test, p < 0.05) from 62.54 (8 to 92) pre-operatively to 97.7 (61 to 100) at a mean of three years (2.1 to 4.3), then deteriorated slightly to a mean of 95.2 (47 to 100) at a mean of five years. The mean flexion improved from 91.5° (25° to 140°) to 110.4° (80° to 145°) at a mean of three years with no further improvement at five years (111.2°; 70° to 160°).

On radiological review at five years, one patient had a progressive lucent line around the acetabular component and six had progressive lucent lines around the femoral component. A total of 18 femoral components (8%) had migrated into varus and those with lucent lines present migrated a mean of 3.8° (1.02° to 6.54°) more than the rest. Superolateral notching of the femoral neck and reactive sclerosis at the tip of the peg of the femoral component were associated with the presence of lucent lines (chi-squared test, p < 0.05), but not with migration of the femoral component, and are of unknown significance.

Our results with the Birmingham hip resurfacing continue to be satisfactory at a mean follow-up of five years.

In an attempt to increase the life of cementless prostheses, an hydroxyapatite-coated implant which releases a bisphosphonate has been suggested as a drug-delivery system. Our in vitro study was designed to determine the maximum dose to which osteoblasts could be safely exposed.

Our findings demonstrated that zoledronate did not impair the proliferation of human osteoblasts when used at concentrations below 1 μm. Murine cells can be exposed to concentrations as high as 10 μm.

A concentration of 0.01% of titanium particles did not impair the proliferation of either cell line. Zoledronate affected the alkaline phosphatase activity of murine osteoblasts through a chelation phenomenon. The presence of titanium particles strongly decreased the alkaline phosphatase activity of murine osteoblasts. We did not detect any synergic effect of zoledronate and titanium particles on the behaviour of both human and murine osteoblasts.