Vancomycin-supplemented allografts provide biological restoration of bone stock and sound fixation with a low incidence of re-infection. Experimental incorporation of these grafts is similar to allografts without vancomycin. However, the underlying biology remains unknown.

We report the first histological observations of vancomycin-supplemented impacted bone allografts in two reconstructions performed 14 and 20 months after revision surgery because of a periprosthetic fracture.

Areas of active bone remodelling (creeping substitution), as well as calcified bone trabeculae and graft particles embedded in dense fibrous tissue, were observed with osteoid and fibroconnective tissue surrounding polymethylmethacrylate particles.

These pathological findings are similar to those reported in allografts without vancomycin and support the hypothesis that high levels of vancomycin do not affect the incorporation of bone graft.

Two Durasul highly crosslinked polyethylene liners were exchanged during revision surgery four and five years after implantation, respectively. The retrieved liners were evaluated macroscopically and surface analysis was performed using optical and electron microscopy. A sample of each liner was used to determine the oxidation of the material by Fourier transform infrared spectroscopy. Samples of the capsule were examined histologically.

The annual wear rate was found to be 0.010 and 0.015 mm/year, respectively. Surface analysis showed very little loss of material caused by wear. Histological evaluation revealed a continuous neosynovial lining with single multinucleated foreign-body giant cells. Our findings showed no unexpected patterns of wear on the articulating surfaces up to five years after implantation and no obvious failure of material.

Few independent studies have reported the outcome of resurfacing arthroplasty of the hip. The aim of this study was to report the five-year clinical outcome and seven-year survival of an independent series.

A total of 610 Birmingham Hip Resurfacing arthroplasties were performed in 532 patients with a mean age of 51.8 years (16.5 to 81.6). They were followed for between two and eight years; 107 patients (120 hips) had been followed up for more than five years. Two patients were lost to follow-up. At a minimum of five years’ follow-up, 79 of 85 hips (93%) had an excellent or good outcome according to the Harris hip score. The mean Oxford hip score was 16.1 points (sd 7.7) and the mean University of California Los Angeles activity score was 6.6 points (sd 1.9). There were no patients with definite radiological evidence of loosening or of narrowing of the femoral neck exceeding 10% of its width. There were 23 revisions (3.8%), giving an overall survival of 95% (95% confidence interval 85.3 to 99.2) at seven years. Fractured neck of femur in 12 hips was the most common indication for revision, followed by aseptic loosening in four. In three hips (three patients) (0.5%), failure was possibly related to metal debris.

Considering that these patients are young and active these results are good, and support the use of resurfacing. Further study is needed to address the early failures, particularly those related to fracture and metal debris.

Platelet-rich plasma is a new inductive therapy which is being increasingly used for the treatment of the complications of bone healing, such as infection and nonunion. The activator for platelet-rich plasma is a mixture of thrombin and calcium chloride which produces a platelet-rich gel.

We analysed the antibacterial effect of platelet-rich gel in vitro by using the platelet-rich plasma samples of 20 volunteers. In vitro laboratory susceptibility to platelet-rich gel was determined by the Kirby-Bauer disc-diffusion method. Baseline antimicrobial activity was assessed by measuring the zones of inhibition on agar plates coated with selected bacterial strains.

Zones of inhibition produced by platelet-rich gel ranged between 6 mm and 24 mm (mean 9.83 mm) in diameter. Platelet-rich gel inhibited the growth of Staphylococcus aureus and was also active against Escherichia coli. There was no activity against Klebsiella pneumoniae, Enterococcus faecalis, and Pseudomonas aeruginosa. Moreover, platelet-rich gel seemed to induce the in vitro growth of Ps. aeruginosa, suggesting that it may cause an exacerbation of infections with this organism. We believe that a combination of the inductive and antimicrobial properties of platelet-rich gel can improve the treatment of infected delayed healing and nonunion.

This is a longitudinal study of the daily urinary output and the concentrations in whole blood of cobalt and chromium in patients with metal-on-metal resurfacings over a period of four years.

Twelve-hour urine collections and whole blood specimens were collected before and periodically after a Birmingham hip resurfacing in 26 patients. All ion analyses were carried out using a high-resolution inductively-coupled plasma mass spectrometer. Clinical and radiological assessment, hip function scoring and activity level assessment revealed excellent hip function.

There was a significant early increase in urinary metal output, reaching a peak at six months for cobalt and one year for chromium post-operatively. There was thereafter a steady decrease in the median urinary output of cobalt over the following three years, although the differences are not statistically significant. The mean whole blood levels of cobalt and chromium also showed a significant increase between the pre-operative and one-year post-operative periods. The blood levels then decreased to a lower level at four years, compared with the one-year levels. This late reduction was statistically significant for chromium but not for cobalt.

The effects of systemic metal ion exposure in patients with metal-on-metal resurfacing arthroplasties continue to be a matter of concern. The levels in this study provide a baseline against which the in vivo wear performance of newer bearings can be compared.

Ciprofloxacin hydrochloride-loaded microspheres were prepared by a spray-drying method using pectin and chitosan. The effects of different polymers and drug ratios were investigated.

The most appropriate carriers were selected by in vitro testing. A rat methicillin-resistant Staphylococcus aureus osteomyelitis model was used to evaluate the effects of the loaded microspheres.

The drug was released rapidly from the pectin carrier but this was more sustained in the chitosan formulation.

Chitosan microspheres loaded with ciprofloxacin hydrochloride were more effective for the treatment of osteomyelitis than equivalent intramuscular antibiotics.

We present the histological findings of bone retrieved from beneath the femoral components of failed metal-on-metal hip resurfacing arthroplasties. Of a total of 377 patients who underwent resurfacing arthroplasty, 13 required revision; for fracture of the femoral neck in eight, loosening of a component in three and for other reasons in two. None of these cases had shown histological evidence of osteonecrosis in the femoral bone at the time of the initial implantation.

Bone from the remnant of the femoral head showed changes of osteonecrosis in all but one case at revision. In two cases of fracture which occurred within a week of implantation, the changes were compatible with early necrosis of the edge of the fracture. In the remaining six fractures, there were changes of established osteonecrosis. In all but one of the non-fracture cases, patchy osteonecrosis was seen.

We conclude that histological evidence of osteonecrosis is a common finding in failed resurfaced hips. Given that osteonecrosis is extensive in resurfaced femoral heads which fail by fracture, it is likely to play a role in the causation of these fractures.

We examined the mechanical properties of Vicryl (polyglactin 910) mesh in vitro and assessed its use in vivo as a novel biomaterial to attach tendon to a hydroxyapatite-coated metal implant, the interface of which was augmented with autogenous bone and marrow graft. This was compared with tendon re-attachment using a compressive clamp device in an identical animal model. Two- and four-ply sleeves of Vicryl mesh tested to failure under tension reached 5.13% and 28.35% of the normal ovine patellar tendon, respectively. Four-ply sleeves supported gait in an ovine model with 67.05% weight-bearing through the operated limb at 12 weeks, without evidence of mechanical failure.

Mesh fibres were visible at six weeks but had been completely resorbed by 12 weeks, with no evidence of chronic inflammation. The tendon-implant neoenthesis was predominantly an indirect type, with tendon attached to the bone-hydroxyapatite surface by perforating collagen fibres.

Despite worldwide clinical use of bio-absorbable devices for internal fixation in orthopaedic surgery, the degradation behaviour and tissue replacement of these implants are not fully understood.

In a long-term experimental study, we have determined the patterns of tissue restoration 36 and 54 months after implantation of polyglycolic acid and poly-laevo-lactic acid screws in the distal femur of the rabbit.

After 36 months in the polyglycolic acid group the specimens showed no remaining polymer and loose connective tissue occupied 80% of the screw track. Tissue restoration remained poor at 54 months, the amounts of trabecular bone and haematopoietic elements being significantly lower than those in the intact control group. The amount of trabecular bone within the screw track at 54 months in the polyglycolic acid group was less than in the empty drill holes (p = 0.04). In the poly-laevo-lactic acid group, polymeric material was present in abundance after 54 months, occupying 60% of the cross-section of the core area of the screw track.

When using absorbable internal fixation implants we should recognise that the degradation of the devices will probably not be accompanied by the restoration of normal trabecular bone.

Previous research has shown an increase in chromosomal aberrations in patients with worn implants. The type of aberration depended on the type of metal alloy in the prosthesis. We have investigated the metal-specific difference in the level of DNA damage (DNA stand breaks and alkali labile sites) induced by culturing human fibroblasts in synovial fluid retrieved at revision arthroplasty.

All six samples from revision cobalt-chromium metal-on-metal and four of six samples from cobalt-chromium metal-on-polyethylene prostheses caused DNA damage. By contrast, none of six samples from revision stainless-steel metal-on-polyethylene prostheses caused significant damage. Samples of cobalt-chromium alloy left to corrode in phosphate-buffered saline also caused DNA damage and this depended on a synergistic effect between the cobalt and chromium ions.

Our results further emphasise that epidemiological studies of orthopaedic implants should take account of the type of metal alloy used.

We have studied cellular and vascular changes in different stages of full thickness tears of the rotator cuff. We examined biopsies from the supraspinatus tendon in 40 patients with chronic rotator cuff tears who were undergoing surgery and compared them with biopsies from four uninjured subscapularis tendons. Morphological and immunocytochemical methods using monoclonal antibodies directed against leucocytes, macrophages, mast cells, proliferative and vascular markers were used.

Histological changes indicative of repair and inflammation were most evident in small sized rotator cuff tears with increased fibroblast cellularity and intimal hyperplasia, together with increased expression of leucocyte and vascular markers. These reparative and inflammatory changes diminished as the size of the rotator cuff tear increased. Marked oedema and degeneration was seen in large and massive tears, which more often showed chondroid metaplasia and amyloid deposition. There was no association between the age of the patient and the duration of symptoms. In contrast, large and massive tears showed no increase in the number of inflammatory cells and blood vessels.

Small sized rotator cuff tears retained the greatest potential to heal, showing increased fibroblast cellularity, blood vessel proliferation and the presence of a significant inflammatory component. Tissue from large and massive tears is of such a degenerative nature that it may be a significant cause of re-rupture after surgical repair and could make healing improbable in this group.