Bioengineering reasons for increased wear and failure of metal-on-metal (MoM) bearings in hip prostheses have been described. Low wear occurs in MoM hips when the centre of the femoral head is concentric with the centre of the acetabular component and the implants are correctly positioned. Translational or rotational malpositioning of the components can lead to the contact-patch of the femoral component being displaced to the rim of the acetabular component, resulting in a ten- to 100-fold increase in wear and metal ion levels. This may cause adverse tissue reactions, loosening of components and failure of the prosthesis.

Dislocation is one of the most common causes of patient and surgeon dissatisfaction following hip replacement and to treat it, the causes must first be understood. Patient factors include age greater than 70 years, medical comorbidities, female gender, ligamentous laxity, revision surgery, issues with the abductors, and patient education. Surgeon factors include the annual quantity of procedures and experience, the surgical approach, adequate restoration of femoral offset and leg length, component position, and soft-tissue or bony impingement. Implant factors include the design of the head and neck region, and so-called skirts on longer neck lengths. There should be offset choices available in order to restore soft-tissue tension. Lipped liners aid in gaining stability, yet if improperly placed may result in impingement and dislocation. Late dislocation may result from polyethylene wear, soft-tissue destruction, trochanteric or abductor disruption and weakness, or infection. Understanding the causes of hip dislocation facilitates prevention in a majority of instances. Proper pre-operative planning includes the identification of patients with a high offset in whom inadequate restoration of offset will reduce soft-tissue tension and abductor efficiency. Component position must be accurate to achieve stability without impingement. Finally, patient education cannot be over-emphasised, as most dislocations occur early, and are preventable with proper instructions.

Cite this article: Bone Joint J 2013;95-B, Supple A:67–9.

Previous research has shown an increase in chromosomal aberrations in patients with worn implants. The type of aberration depended on the type of metal alloy in the prosthesis. We have investigated the metal-specific difference in the level of DNA damage (DNA stand breaks and alkali labile sites) induced by culturing human fibroblasts in synovial fluid retrieved at revision arthroplasty.

All six samples from revision cobalt-chromium metal-on-metal and four of six samples from cobalt-chromium metal-on-polyethylene prostheses caused DNA damage. By contrast, none of six samples from revision stainless-steel metal-on-polyethylene prostheses caused significant damage. Samples of cobalt-chromium alloy left to corrode in phosphate-buffered saline also caused DNA damage and this depended on a synergistic effect between the cobalt and chromium ions.

Our results further emphasise that epidemiological studies of orthopaedic implants should take account of the type of metal alloy used.

Cementless femoral stems are currently preferred for total hip replacement (THR) in the United States. Improvements in stem design, instrumentation and surgical technique have made this technology highly successful, reproducible, and applicable to the vast majority of patients requiring a THR. However, there are ongoing developments in some aspects of stem design that influence clinical results, the incidence of complications and their inherent adaptability in accommodating the needs of individual patients. Here we examine some of these design features.

Cite this article: Bone Joint J 2013;95-B, Supple A:53–6.

Surface hip replacement (SHR) is generally used in younger, active patients as an alternative conventional total hip replacement in part because of the ability to preserve femoral bone. This major benefit of surface replacement will only hold true if revision procedures of SHRs are found to provide good clinical results.

A retrospective review of SHR revisions between 2007 and 2012 was presented, and the type of revision and aetiologies were recorded. There were 55 SHR revisions, of which 27 were in women. At a mean follow-up of 2.3 years (0.72 to 6.4), the mean post-operative Harris hip score (HHS) was 94.8 (66 to 100). Overall 23 were revised for mechanical reasons, nine for impingement, 13 for metallosis, nine for unexplained pain and one for sepsis. Of the type of revision surgery performed, 14 were femoral-only revisions; four were acetabular-only revisions, and 37 were complete revisions.

We did not find that clinical scores were significantly different between gender or different types of revisions. However, the mean post-operative HHS was significantly lower in patients revised for unexplained pain compared with patients revised for mechanical reasons (86.9 (66 to 100) versus 99 (96 to 100); p = 0.029). There were two re-revisions for infection in the entire cohort.

Based on the overall clinical results, we believe that revision of SHR can have good or excellent results and warrants a continued use of the procedure in selected patients. Close monitoring of these patients facilitates early intervention, as we believe that tissue damage may be related to the duration of an ongoing problem. There should be a low threshold to revise a surface replacement if there is component malposition, rising metal ion levels, or evidence of soft-tissue abnormalities.

Cite this article: Bone Joint J 2013;95-B, Supple A:88–91.

Total hip replacement (THR) after acetabular fracture presents unique challenges to the orthopaedic surgeon. The majority of patients can be treated with a standard THR, resulting in a very reasonable outcome. Technical challenges however include infection, residual pelvic deformity, acetabular bone loss with ununited fractures, osteonecrosis of bone fragments, retained metalwork, heterotopic ossification, dealing with the sciatic nerve, and the difficulties of obtaining long-term acetabular component fixation. Indications for an acute THR include young patients with both femoral head and acetabular involvement with severe comminution that cannot be reconstructed, and the elderly, with severe bony comminution. The outcomes of THR for established post-traumatic arthritis include excellent pain relief and functional improvements. The use of modern implants and alternative bearing surfaces should improve outcomes further.

Cite this article: Bone Joint J 2013;95-B, Supple A:11–16.

Metal artefact reduction (MAR) MRI is now widely considered to be the standard for imaging metal-on-metal (MoM) hip implants. The Medicines and Healthcare Products Regulatory Agency (MHRA) has recommended cross-sectional imaging for all patients with symptomatic MoM bearings. This paper describes the natural history of MoM disease in a 28 mm MoM total hip replacement (THR) using MAR MRI. Inclusion criteria were patients with MoM THRs who had not been revised and had at least two serial MAR MRI scans. All examinations were reported by an experienced observer and classified as A (normal), B (infection) or C1–C3 (mild, moderate, severe MoM-related abnormalities). Between 2002 and 2011 a total of 239 MRIs were performed on 80 patients (two to four scans per THR); 63 initial MRIs (61%) were normal. On subsequent MRIs, six initially normal scans (9.5%) showed progression to a disease state; 15 (15%) of 103 THRs with sequential scans demonstrated worsening disease on subsequent imaging.

Most patients with a MoM THR who do not undergo early revision have normal MRI scans. Late progression (from normal to abnormal, or from mild to more severe MoM disease) is not common and takes place over several years.

Cite this article: Bone Joint J 2013;95-B:1035–9.

The August 2013 Hip & Pelvis Roundup³⁶⁰ looks at: are we getting it right first time?; tantalum augments in revision hip surgery; lower wear in dual mobility?; changing faces changes outcomes; synovial fluid aspiration in MOM hips; taper disease: the new epidemic of hip surgery; the super-obese and THR; and whether well fixed stems can remain in infected hips

We investigated the role of ion release in the assessment of fixation of the implant after total knee replacement and hypothesised that ion monitoring could be a useful parameter in the diagnosis of prosthetic loosening. We enrolled 59 patients with unilateral procedures and measured their serum aluminium, titanium, chromium and cobalt ion levels, blinded to the clinical and radiological outcome which was considered to be the reference standard. The cut-off levels for detection of the ions were obtained by measuring the levels in 41 healthy blood donors who had no implants. Based on the clinical and radiological evaluation the patients were divided into two groups with either stable (n = 24) or loosened (n = 35) implants.

A significant increase in the mean level of Cr ions was seen in the group with failed implants (p = 0.001). The diagnostic accuracy was 71% providing strong evidence of failure when the level of Cr ions exceeded the cut-off value. The possibility of distinguishing loosening from other causes of failure was demonstrated by the higher diagnostic accuracy of 83%, when considering only patients with failure attributable to loosening.

Measurement of the serum level of Cr ions may be of value for detecting failure due to loosening when the diagnosis is in doubt. The other metal ions studies did not have any diagnostic value.

We sought to establish the incidence of joint failure secondary to adverse reaction to metal debris (ARMD) following metal-on-metal hip resurfacing in a large, three surgeon, multicentre study involving 4226 hips with a follow-up of 10 to 142 months. Three implants were studied: the Articular Surface Replacement; the Birmingham Hip Resurfacing; and the Conserve Plus. Retrieved implants underwent analysis using a co-ordinate measuring machine to determine volumetric wear. There were 58 failures associated with ARMD. The median chromium and cobalt concentrations in the failed group were significantly higher than in the control group (p < 0.001). Survival analysis showed a failure rate in the patients with Articular Surface Replacement of 9.8% at five years, compared with < 1% at five years for the Conserve Plus and 1.5% at ten years for the Birmingham Hip Resurfacing. Two ARMD patients had relatively low wear of the retrieved components. Increased wear from the metal-on-metal bearing surface was associated with an increased rate of failure secondary to ARMD. However, the extent of tissue destruction at revision surgery did not appear to be dose-related to the volumetric wear.

We describe the findings at six years in an ongoing prospective clinicoradiological and metal ion study in a cohort of 26 consecutive male patients with unilateral Birmingham Hip Resurfacing arthroplasties with one of two femoral head sizes (50 mm and 54 mm). Their mean age was 52.9 years (29 to 67). We have previously shown an early increase in the 24-hour urinary excretion of metal ions, reaching a peak at six months (cobalt) and one year (chromium) after operation. Subsequently there is a decreasing trend in excretion of both cobalt and chromium. The levels of cobalt and chromium in whole blood also show a significant increase at one year, followed by a decreasing trend until the sixth year.

We reviewed the literature on the currently available choices of bearing surface in total hip replacement (THR). We present a detailed description of the properties of articulating surfaces review the understanding of the advantages and disadvantages of existing bearing couples. Recent technological developments in the field of polyethylene and ceramics have altered the risk of fracture and the rate of wear, although the use of metal-on-metal bearings has largely fallen out of favour, owing to concerns about reactions to metal debris. As expected, all bearing surface combinations have advantages and disadvantages. A patient-based approach is recommended, balancing the risks of different options against an individual’s functional demands.

Cite this article: Bone Joint J 2014;96-B:147–56.

We report the results of revision total knee replacement (TKR) in 26 patients with major metaphyseal osteolytic defects using 29 trabecular metal cones in conjunction with a rotating hinged total knee prosthesis. The osteolytic defects were types II and III (A or B) according to the Anderson Orthopaedic Research Institute (AORI) classification. The mean age of the patients was 72 years (62 to 84) and there were 15 men and 11 women. In this series patients had undergone a mean of 2.34 previous total knee arthroplasties. The main objective was to restore anatomy along with stability and function of the knee joint to allow immediate full weight-bearing and active knee movement. Outcomes were measured using Knee Society scores, Oxford knee scores, range of movement of the knee and serial radiographs. Patients were followed for a mean of 36 months (24 to 49). The mean Oxford knee clinical scores improved from 12.83 (10 to 15) to 35.20 (32 to 38) (p < 0.001) and mean American Knee Society scores improved from 33.24 (13 to 36) to 81.12 (78 to 86) (p < 0.001). No radiolucent lines suggestive of loosening were seen around the trabecular metal cones, and by one year all the radiographs showed good osteo-integration. There was no evidence of any collapse or implant migration. Our early results confirm the findings of others that trabecular metal cones offer a useful way of managing severe bone loss in revision TKR.

Cite this article: Bone Joint J 2013;95-B:1069–74.

The practice of removing a well-fixed cementless femoral component is associated with high morbidity. Ceramic bearing couples are low wearing and their use minimises the risk of subsequent further revision due to the production of wear debris. A total of 165 revision hip replacements were performed, in which a polyethylene-lined acetabular component was revised to a new acetabular component with a ceramic liner, while retaining the well-fixed femoral component. A titanium sleeve was placed over the used femoral trunnion, to which a ceramic head was added. There were 100 alumina and 65 Delta bearing couples inserted.

The mean Harris hip score improved significantly from 71.3 (9.0 to 100.0) pre-operatively to 91.0 (41.0 to 100.0) at a mean follow up of 4.8 years (2.1 to 12.5) (p < 0.001). No patients reported squeaking of the hip.

There were two fractures of the ceramic head, both in alumina bearings. No liners were seen to fracture. No fractures were observed in components made of Delta ceramic. At 8.3 years post-operatively the survival with any cause of failure as the endpoint was 96.6% (95% confidence interval (CI) 85.7 to 99.3) for the acetabular component and 94.0% (95% CI 82.1 to 98.4) for the femoral component.

The technique of revising the acetabular component in the presence of a well-fixed femoral component with a ceramic head placed on a titanium sleeve over the used trunnion is a useful adjunct in revision hip practice. The use of Delta ceramic is recommended.

Cite this article: Bone Joint J 2013;95-B:333–8.

A moderator and panel of five experts led an interactive session in discussing five challenging and interesting patient case presentations involving surgery of the hip. The hip pathologies reviewed included failed open reduction internal fixation of subcapital femoral neck fracture, bilateral hip disease, evaluation of pain after metal-on-metal hip arthroplasty, avascular necrosis, aseptic loosening secondary to osteolysis and polyethylene wear, and management of ceramic femoral head fracture.

In a double-blinded randomised controlled trial, 83 patients with primary osteoarthritis of the hip received either a ceramic-on-metal (CoM) or metal-on-metal (MoM) total hip replacement (THR). The implants differed only in the bearing surfaces used. The serum levels of cobalt and chromium and functional outcome scores were compared pre-operatively and at six and 12 months post-operatively.

Data were available for 41 CoM and 36 MoM THRs (four patients were lost to follow-up, two received incorrect implants). The baseline characteristics of both cohorts were similar. Femoral head size measured 36 mm in all but two patients who had 28 mm heads. The mean serum cobalt and chromium levels increased in both groups, with no difference noted between groups at six months (cobalt p = 0.67, chromium p = 0.87) and 12 months (cobalt p = 0.76, chromium p = 0.76) post-operatively. Similarly, the mean Oxford hip scores, Western Ontario and McMaster Universities Osteoarthritis index and University of California, Los Angeles activity scores showed comparable improvement at 12 months.

Our findings indicate that CoM and MoM couplings are associated with an equivalent increase in serum cobalt and chromium levels, and comparable functional outcome scores at six and 12-months follow-up.

The painful subluxed or dislocated hip in adults with cerebral palsy presents a challenging problem. Prosthetic dislocation and heterotopic ossification are particular concerns. We present the first reported series of 19 such patients (20 hips) treated with hip resurfacing and proximal femoral osteotomy. The pre-operative Gross Motor Function Classification System (GMFCS) was level V in 13 (68%) patients, level IV in three (16%), level III in one (5%) and level II in two (11%). The mean age at operation was 37 years (13 to 57).

The mean follow-up was 8.0 years (2.7 to 11.6), and 16 of the 18 (89%) contactable patients or their carers felt that the surgery had been worthwhile. Pain was relieved in 16 of the 18 surviving hips (89%) at the last follow-up, and the GMFCS level had improved in seven (37%) patients. There were two (10%) early dislocations; three hips (15%) required revision of femoral fixation, and two hips (10%) required revision, for late traumatic fracture of the femoral neck and extra-articular impingement, respectively. Hence there were significant surgical complications in a total of seven hips (35%). No hips required revision for instability, and there were no cases of heterotopic ossification.

We recommend hip resurfacing with proximal femoral osteotomy for the treatment of the painful subluxed or dislocated hip in patients with cerebral palsy.