There is increasing global awareness of adverse reactions to metal debris and elevated serum metal ion concentrations following the use of second generation metal-on-metal total hip arthroplasties. The high incidence of these complications can be largely attributed to corrosion at the head-neck interface. Severe corrosion of the taper is identified most commonly in association with larger diameter femoral heads. However, there is emerging evidence of varying levels of corrosion observed in retrieved components with smaller diameter femoral heads. This same mechanism of galvanic and mechanically-assisted crevice corrosion has been observed in metal-on-polyethylene and ceramic components, suggesting an inherent biomechanical problem with current designs of the head-neck interface. We provide a review of the fundamental questions and answers clinicians and researchers must understand regarding corrosion of the taper, and its relevance to current orthopaedic practice. Cite this article: Bone Joint J 2016;98-B:579–84

Aims. This study investigates head-neck taper corrosion with varying head size in a novel hip simulator instrumented to measure corrosion related electrical activity under torsional loads. Methods. In all, six 28 mm and six 36 mm titanium stem-cobalt chrome head pairs with polyethylene sockets were tested in a novel instrumented hip simulator. Samples were tested using simulated gait data with incremental increasing loads to determine corrosion onset load and electrochemical activity. Half of each head size group were then cycled with simulated gait and the other half with gait compression only. Damage was measured by area and maximum linear wear depth. Results. Overall, 36 mm heads had lower corrosion onset load (p = 0.009) and change in open circuit potential (OCP) during simulated gait with (p = 0.006) and without joint movement (p = 0.004). Discontinuing gait’s joint movement decreased corrosion currents (p = 0.042); however, wear testing showed no significant effect of joint movement on taper damage. In addition, 36 mm heads had greater corrosion area (p = 0.050), but no significant difference was found for maximum linear wear depth (p = 0.155). Conclusion. Larger heads are more susceptible to taper corrosion; however, not due to frictional torque as hypothesized. An alternative hypothesis of taper flexural rigidity differential is proposed. Further studies are necessary to investigate the clinical significance and underlying mechanism of this finding. Cite this article: Bone Jt Open 2021;2(11):1004–1016

Aims. Dual mobility implants in total hip arthroplasty are designed to increase the functional head size, thus decreasing the potential for dislocation. Modular dual mobility (MDM) implants incorporate a metal liner (e.g. cobalt-chromium alloy) in a metal shell (e.g. titanium alloy), raising concern for mechanically assisted crevice corrosion at the modular liner-shell connection. We sought to examine fretting and corrosion on MDM liners, to analyze the corrosion products, and to examine histologically the periprosthetic tissues. Methods. A total of 60 retrieved liners were subjectively scored for fretting and corrosion. The corrosion products from the three most severely corroded implants were removed from the implant surface, imaged using scanning electron microscopy, and analyzed using Fourier-transform infrared spectroscopy. Results. Fretting was present on 88% (53/60) of the retrieved liners, and corrosion was present on 97% (58/60). Fretting was most often found on the lip of the taper at the transition between the lip and the dome regions. Macrophages and particles reflecting an innate inflammatory reaction to corrosion debris were noted in six of the 48 cases for which periprosthetic tissues were examined, and all were associated with retrieved components that had high corrosion scores. Conclusion. Our results show that corrosion occurs at the interface between MDM liners and shells and that it can be associated with reactions in the local tissues, suggesting continued concern that this problem may become clinically important with longer-term use of these implants. Cite this article: Bone Joint J 2021;103-B(7):1238–1246

Aims. This study aims to enhance understanding of clinical and radiological consequences and involved mechanisms that led to corrosion of the Precice Stryde (Stryde) intramedullary lengthening nail in the post market surveillance era of the device. Between 2018 and 2021 more than 2,000 Stryde nails have been implanted worldwide. However, the outcome of treatment with the Stryde system is insufficiently reported. Methods. This is a retrospective single-centre study analyzing outcome of 57 consecutive lengthening procedures performed with the Stryde nail at the authors’ institution from February 2019 until November 2020. Macro- and microscopic metallographic analysis of four retrieved nails was conducted. To investigate observed corrosion at telescoping junction, scanning electron microscopy (SEM) and energy dispersive x-ray spectroscopy (EDX) were performed. Results. Adjacent to the nail’s telescoping junction, osteolytic changes were observed in bi-planar radiographs of 20/57 segments (35%) after a mean of 9.5 months (95% confidence interval 7.2 to 11.9) after surgery. A total of 8/20 patients with osseous alterations (40%) reported rest and ambulation pain of the lengthened segment during consolidation. So far, 24 Stryde nails were retrieved and in 20 (83%) macroscopic corrosion was observed at the nail’s telescoping junction. Before implant removal 11/20 radiographs (55%) of lengthened segments with these 20 nails revealed osteolysis. Implant retrieval analysis by means of SEM showed pitting and crevice corrosion. EDX detected chromium as the main metallic element of corrosion. Conclusion. Patients are exposed to the risk of implant-related osteolysis of unclear short- and long-term clinical consequences. The authors advocate in favour of an early implant removal after osseous consolidation. Cite this article: Bone Joint Res 2021;10(7):425–436

Objectives. This study aimed to characterise and qualitatively grade the severity of the corrosion particles released into the hip joint following taper corrosion. Methods. The 26 cases examined were CoC/ABG Modular (n = 13) and ASR/SROM (n = 13). Blood serum metal ion levels were collected before and after revision surgery. The haematoxylin and eosin tissue sections were graded on the presence of fibrin exudates, necrosis, inflammatory cells and corrosion products. The corrosion products were identified based on visible observation and graded on abundance. Two independent observers blinded to the clinical patient findings scored all cases. Elemental analysis was performed on corrosion products within tissue sections. X-Ray diffraction was used to identify crystalline structures present in taper debris. Results. The CoC/ABG Modular patients had a mean age of 64.6 years (49.4 to 76.5) and ASR/SROM patients had a mean age of 58.2 years (33.3 to 85.6). The mean time in situ for CoC/ABG was 4.9 years (2 to 6.4) and ASR/SROM was 6.1 years (2.5 to 8.1). The blood serum metal ion concentrations reduced following revision surgery with the exception of Cr levels within CoC/ABG. The grading of tissue sections showed that the macrophage response and metal debris were significantly higher for the ASR/SROM patients (p < 0.001). The brown/red particles were significantly higher for ASR/SROM (p < 0.001). The taper debris contained traces of titanium oxide, chromium oxide and aluminium nitride. Conclusion. This study characterised and qualitatively graded the severity of the corrosion particles released into the hip joint from tapers that had corrosion damage. Cite this article: S. Munir, R. A. Oliver, B. Zicat, W. L. Walter, W. K. Walter, W. R. Walsh. The histological and elemental characterisation of corrosion particles from taper junctions. Bone Joint Res 2016;5:370–378. DOI: 10.1302/2046-3758.59.2000507

Aims. To report our experience with trunnion corrosion following metal-on-polyethylene total hip arthroplasty, in particular to report the spectrum of presentation and determine the mean time to presentation. Patients and Methods. We report the presenting symptoms and signs, intraoperative findings, and early results and complications of operative treatment in nine patients with a mean age of 74 years (60 to 86). The onset of symptoms was at a mean of seven years (3 to 18) after index surgery. Results. Patients presented with a variety of symptoms including pain, limp and rash. The preoperative mean serum cobalt level was 7.1 ppb (2.2 to 12.8) and mean serum chromium level was 2.2 ppb (0.5 to 5.2). Metal artifact reduction sequence (MARS) MRI showed fluid collection and possible pseudotumour formation in five hips, fluid collection in two hips, and synovitis/debris in one hip, with no MRI in one patient. Acetabular revision was performed in three patients, six patients underwent liner and head exchange only. The postoperative metal levels decreased in all patients: mean cobalt 0.5 ppb (0 to 1.8) and mean chromium 0.9 ppb (0 to 2.6) at a mean of five months (3 to 8) postoperatively. Seven patients had good pain relief and no complications at one year. There were two major complications requiring reoperation: acute infection at six weeks, for which the patient required two-stage reimplantation; and recurrent dislocation, for which the patient was revised to a dual mobility component. Conclusion. Trunnion corrosion in metal-on-polyethylene THA has a range of presenting symptoms, and may present later than previously described. A high index of suspicion is warranted, and serum cobalt and chromium levels are recommended for diagnosis. Patients should be counselled about possible postoperative complications. Cite this article: Bone Joint J 2018;100-B:898–902

Aims. To present a surgically relevant update of trunnionosis. . Materials and Methods. Systematic review performed April 2017. Results. Trunnionosis accounts for approximately 2% of the revision total hip arthroplasty (THA) burden. Thinner (reduced flexural rigidity) and shorter trunnions (reduced contact area at the taper junction) may contribute to mechanically assisted corrosion, exacerbated by high offset implants. The contribution of large heads and mixed metallurgy is discussed. Conclusion. Identifying causative risk factors is challenging due to the multifactorial nature of this problem. Cite this article: Bone Joint J 2018;100-B(1 Supple A):44–9

The aim of this study was to assess the effect of frictional torque and bending moment on fretting corrosion at the taper interface of a modular femoral component and to investigate whether different combinations of material also had an effect. The combinations we examined were 1) cobalt–chromium (CoCr) heads on CoCr stems 2) CoCr heads on titanium alloy (Ti) stems and 3) ceramic heads on CoCr stems. In test 1 increasing torque was imposed by offsetting the stem in the anteroposterior plane in increments of 0 mm, 4 mm, 6 mm and 8 mm when the torque generated was equivalent to 0 Nm, 9 Nm, 14 Nm and 18 Nm. In test 2 we investigated the effect of increasing the bending moment by offsetting the application of axial load from the midline in the mediolateral plane. Increments of offset equivalent to head + 0 mm, head + 7 mm and head + 14 mm were used. Significantly higher currents and amplitudes were seen with increasing torque for all combinations of material. However, Ti stems showed the highest corrosion currents. Increased bending moments associated with using larger offset heads produced more corrosion: Ti stems generally performed worse than CoCr stems. Using ceramic heads did not prevent corrosion, but reduced it significantly in all loading configurations. Cite this article: Bone Joint J 2015;97-B:463–72

1. A total of 564 metal components from 109 patients have been examined. 2. Corrosion was detected on 228 components. 3. Most implants were removed for reasons other than corrosion. 4. In at least twelve cases corrosion was the reason for removal of the implant. 5. No corrosion of cobalt-chromium-molybdenum implants has been detected by the methods described in this paper. 6. Corrosion of ferrous alloy implants occurs in the human body. 7. The most common site for corrosion is the junction between components of implants. 8. The most corrosion-resistant type of ferrous alloy for implant uses is 18/8/Mo steel, which falls within specification En58.J of the British Standards Institute, and specification 316/317 of the American Iron and Steel Institute. 9. About 13 per cent of components removed (and by no means only when something was amiss) showed "face" corrosion when all the components of the implant were made of 18/8/Mo steel. 10. Four per cent of 18/8/Mo components of implants showed corrosion at sites other than the interface between components. 11. On the basis of corrosion resistance it is preferable to use cobalt-chromium-molybdenum alloys for implants that are to be left in the body for an indefinite period. 12. The corrosion resistance of the high alloy steels examined (18/8, 18/8/Ti, 18/8/Mo) does not appear to be related to hardness. 13. The marking of components, either by punching or by electrolytic methods, has not predisposed to corrosion. 14. All hollow 18/8/Mo implants should have a clean and metallurgically satisfactory internal surface. 15. The figures in this report do not permit a full statistical survey of corrosion in surgical implants because it has not been possible to examine a satisfactorily random sample. Many patients cannot be followed up and others die with the implant still in the body

A 70-year-old man with an uncemented metal-on-polyethylene total hip prosthesis underwent revision arthroplasty 33 months later because of pain, swelling and recurrent dislocation. There appeared to be corrosion and metal release from the prosthetic head, resulting in pseudotumour formation and severe local soft-tissue destruction. The corrosion occurred at the junction between the titanium-molybdenum-zirconium-iron taper and the cobalt-chrome-molybdenum head, but the mechanism was unproven

Aims. Surgeons have commonly used modular femoral heads and stems from different manufacturers, although this is not recommended by orthopaedic companies due to the different manufacturing processes. We compared the rate of corrosion and rate of wear at the trunnion/head taper junction in two groups of retrieved hips; those with mixed manufacturers (MM) and those from the same manufacturer (SM). . Materials and Methods. We identified 151 retrieved hips with large-diameter cobalt-chromium heads; 51 of two designs that had been paired with stems from different manufacturers (MM) and 100 of seven designs paired with stems from the same manufacturer (SM). We determined the severity of corrosion with the Goldberg corrosion score and the volume of material loss at the head/stem junction. We used multivariable statistical analysis to determine if there was a significant difference between the two groups. . Results. We found no significant difference in the corrosion scores of the two groups. The median rate of material loss at the head/stem junction for the MM and SM groups were 0.39 mm. 3. /year (0.00 to 4.73) and 0.46 mm. 3. /year (0.00 to 6.71) respectively; this difference was not significant after controlling for confounding factors (p = 0.06). . Conclusion. The use of stems with heads of another manufacturer does not appear to affect the amount of metal lost from the surfaces between these two components at total hip arthroplasty. Other surgical, implant and patient factors should be considered when determining the mechanisms of failure of large diameter metal-on-metal hip arthroplasties. Cite this article: Bone Joint J 2016;98-B:917–24

Aims. Head-taper corrosion is a cause of failure in total hip arthroplasty (THA). Recent reports have described an increasing number of V40 taper failures with adverse local tissue reaction (ALTR). However, the real incidence of V40 taper damage and its cause remain unknown. The aim of this study was to evaluate the long-term incidence of ALTR in a consecutive series of THAs using a V40 taper and identify potentially related factors. Methods. Between January 2006 and June 2007, a total of 121 patients underwent THA using either an uncemented (Accolade I, made of Ti. 12. Mo. 6. Zr. 2. Fe; Stryker, USA) or a cemented (ABG II, made of cobalt-chrome-molybdenum (CoCrMo); Stryker) femoral component, both with a V40 taper (Stryker). Uncemented acetabular components (Trident; Stryker) with crosslinked polyethylene liners and CoCr femoral heads of 36 mm diameter were used in all patients. At a mean folllow-up of 10.8 years (SD 1.1), 94 patients (79%) were eligible for follow-up (six patients had already undergone a revision, 15 had died, and six were lost to follow-up). A total of 85 THAs in 80 patients (mean age 61 years (24 to 75); 47 (56%) were female) underwent clinical and radiological evaluation, including the measurement of whole blood levels of cobalt and chrome. Metal artifact reduction sequence MRI scans of the hip were performed in 71 patients. Results. A total of 20 ALTRs were identified on MRI, with an incidence of 26%. Patients with ALTR had significantly higher median Co levels compared with those without ALTR (2.96 μg/l (interquartile range (IQR) 1.35 to 4.98) vs 1.44 μg/l (IQR 0.79 to 2.5); p = 0.019). Radiological evidence of osteolysis was also significantly associated with ALTR (p = 0.014). Median Cr levels were not significantly higher in those with ALTR compared with those without one (0.97 μg/l (IQR 0.72 to 1.9) v 0.67 μg/l (IQR 0.5 to 1.19; p = 0.080). BMI, sex, age, type of femoral component, head length, the inclination of the acetabular component, and heterotopic ossification formation showed no significant relationship with ALTR. Conclusion. Due to the high incidence of local ALTR in our cohort after more than ten years postoperatively, we recommend regular follow-up investigation even in asymptomatic patients with V40 taper and metal heads. As cobalt levels correlate with ALTR occurrence, routine metal ion screening and consecutive MRI investigation upon elevation could be discussed. Cite this article: Bone Joint J 2022;104-B(7):852–858

We present a series of 35 patients (19 men and 16 women) with a mean age of 64 years (36.7 to 75.9), who underwent total hip replacement using the ESKA dual-modular short stem with metal on-polyethylene bearing surfaces. This implant has a modular neck section in addition to the modular head. Of these patients, three presented with increasing post-operative pain due to pseudotumour formation that resulted from corrosion at the modular neck-stem junction. These patients underwent further surgery and aseptic lymphocytic vaculitis associated lesions were demonstrated on histological analysis. Retrieval analysis of two modular necks showed corrosion at the neck-stem taper. Blood cobalt and chromium levels were measured at a mean of nine months (3 to 28) following surgery. These were compared with the levels in seven control patients (three men and four women) with a mean age of 53.4 years (32.1 to 64.1), who had an identical prosthesis and articulation but with a prosthesis that had no modularity at neck-stem junction. The mean blood levels of cobalt in the study group were raised at 50.75 nmol/l (5 to 145) compared with 5.6 nmol/l (2 to 13) in control patients. Corrosion at neck-stem tapers has been identified as an important source of metal ion release and pseudotumour formation requiring revision surgery. Finite element modelling of the dual modular stem demonstrated high stresses at the modular stem-neck junction. Dual modular cobalt-chrome hip prostheses should be used with caution due to these concerns

Adverse reaction to wear and corrosion debris is a cause for concern in total hip arthroplasty (THA). Modular junctions are a potential source of such wear products and are associated with secondary pseudotumour formation. . We present a consecutive series of 17 patients treated at our unit for this complication following metal-on-highly cross-linked polyethylene (MoP) THA. We emphasise the risk of misdiagnosis as infection, and present the aggregate laboratory results and pathological findings in this series. The clinical presentation was pain, swelling or instability. Solid, cystic and mixed soft-tissue lesions were noted on imaging and confirmed intra-operatively. Corrosion at the head–neck junction was noted in all cases. No bacteria were isolated on multiple pre- and intra-operative samples yet the mean erythrocyte sedimentation rate was 49 (9 to 100) and C-reactive protein 32 (0.6 to 106) and stromal polymorphonuclear cell counts were noted in nine cases. . Adverse soft–tissue reactions can occur in MoP THA owing to corrosion products released from the head–neck junction. The diagnosis should be carefully considered when investigating pain after THA. This may avoid the misdiagnosis of periprosthetic infection with an unidentified organism and mitigate the unnecessary management of these cases with complete single- or two-stage exchange. Cite this article: Bone Joint J 2015;97-B:1024–1030

Cemented titanium stems in hip arthroplasty are associated with proximal cement-stem debonding and early failure. This was well publicised with the 3M Capital hip. However, corrosion in this setting has been reported with only one stem design and is less widely accepted. We present a series of 12 cemented titanium Furlong Straight Stems which required revision at a mean of 78 months for thigh pain. At revision the stems were severely corroded in a pattern which was typical of crevice corrosion. Symptoms were eliminated after revision to an all-stainless steel femoral prosthesis of the same design. We discuss the likely causes for the corrosion. The combination of a titanium stem and cement appears to facilitate crevice corrosion

Tribocorrosion at the head–neck taper interface – so-called ‘taperosis’ – may be a source of metal ions and particulate debris in metal-on-polyethylene total hip arthroplasty (THA). We examined the effect of femoral head length on fretting and corrosion in retrieved head–neck tapers in vivo for a minimum of two years (mean 8.7 years; 2.6 to 15.9). A total of 56 femoral heads ranging from 28 mm to 3 mm to 28 mm + 8 mm, and 17 femoral stems featuring a single taper design were included in the study. Fretting and corrosion were scored in three horizontally oriented concentric zones of each taper by stereomicroscopy. Head length was observed to affect fretting (p = 0.03), with 28 mm + 8 mm femoral heads showing greater total fretting scores than all other head lengths. The central zone of the femoral head bore taper was subject to increased fretting damage (p = 0.01), regardless of head length or stem offset. High-offset femoral stems were associated with greater total fretting of the bore taper (p = 0.04). Increased fretting damage is seen with longer head lengths and high-offset femoral stems, and occurs within a central concentric zone of the femoral head bore taper. Further investigation is required to determine the effect of increased head size, and variations in head–neck taper design. Cite this article: Bone Joint J 2015; 97-B:911–16

We examined 108 uncemented femoral stems with modular femoral heads which had been retrieved for reasons other than loosening. There were detectable amounts of wear and corrosion in 10 of 29 (34.5%) mixed-alloy components and 7 of 79 (9%) single-alloy components after a mean implantation time of 25 months. We found no correlation between the presence or extent of corrosion or surface damage and any of time in situ, initial diagnosis, reason for removal, age, or weight. Stems with wear and corrosion were less likely to show histological bony ingrowth. The interface between the head and stem of modular total hip components is a possible source of ion release and wear debris, but wear and corrosion were totally absent in most specimens. This suggests that this problem could be avoided, and that further research is required to develop manufacturing methods which would minimise such changes

We studied the tapered interface between the head and the neck of 139 modular femoral components of hip prostheses which had been removed for a variety of reasons. In 91 the same alloy had been used for the head and the stem; none of them showed evidence of corrosion. In contrast, there was definite corrosion in 25 of the 48 prostheses in which the stem was of titanium alloy and the head of cobalt-chrome. This corrosion was time-dependent: no specimens were corroded after less than nine months in the body, but all which had been in place for more than 40 months were damaged. We discuss the factors which may influence the rate of these changes and present evidence that they were due to galvanically-accelerated crevice corrosion, which was undetected in previous laboratory testing of this type of prosthesis

Nine uncemented hip prostheses of modular design were revised because of late infection (2 cases), femoral stem loosening or fracture (2), loosening of threaded cups (3) and protrusion of bipolar cups (2). At surgery we found tissue discoloration and macroscopic corrosion in four of the nine prostheses, located at the head-neck junction. Histological examination in most cases showed extensive necrosis associated with metal particles, indicating metal toxicity. Metallographic examination of the prosthetic heads revealed structural imperfections and inhomogeneity of the metal. We suggest that the crevice between the head and neck is a potential site of corrosion in modular designs

Aims. We present a case series of ten metal-on-polyethylene total hip arthroplasties (MoP THAs) with delayed dislocation associated with unrecognised adverse local tissue reaction due to corrosion at the trunnion and pseudotumour formation. . Methods. The diagnosis was not suspected in nine of the ten patients (six female/four male; mean age 66 years), despite treatment in a specialist unit (mean time from index surgery to revision was 58 months, 36 to 84). It was identified at revision surgery and subsequently confirmed by histological examination of resected tissue. Pre-operative assessment and culture results ruled out infection. A variety of treatment strategies were used, including resection of the pseudotumour and efforts to avoid recurrent dislocation. . Results. The rate of complications was high and included three deep infections, two patients with recurrent dislocation, and one recurrent pseudotumour. . Conclusion. This series (mean follow-up of 76 months following index procedure and 19 months following revision THA) demonstrates that pseudotumour is an infrequent but important contributor to delayed instability following MoP THA. It is easy to overlook in the differential diagnosis, especially if the alignment of the components is less than optimal, leading to an assumption that malalignment is the cause of the dislocation. The instability is likely to be multifactorial and the revision surgery is complex. Take home message: Due to the high complication rate associated with revision in this cohort, the diagnosis should be borne in mind when counselling patients regarding the risks of revision surgery. . Cite this article: Bone Joint J 2016;98-B:187–93