We report the five-year outcome of a randomised controlled trial which used radiostereometric analysis (RSA) to assess the influence of surface oxidised zirconium (OxZr, Oxinium) on polyethylene wear in vivo.

A total of 120 patients, 85 women and 35 men with a mean age of 70 years (59 to 80) who were scheduled for primary cemented total hip arthroplasty were randomly allocated to four study groups. Patients were blinded to their group assignment and received either a conventional polyethylene (CPE) or a highly cross-linked (HXL) acetabular component of identical design. On the femoral side patients received a 28 mm head made of either cobalt-chromium (CoCr) or OxZr.

The proximal head penetration (wear) was measured with repeated RSA examinations over five years. Clinical outcome was measured using the Harris hip score.

There was no difference in polyethylene wear between the two head materials when used with either of the two types of acetabular component (p = 0.3 to 0.6). When comparing the two types of polyethylene there was a significant difference in favour of HXLPE, regardless of the head material used (p < 0.001).

In conclusion, we found no advantage of OxZr over CoCr in terms of polyethylene wear after five years of follow-up. Our findings do not support laboratory results which have shown a reduced rate of wear with OxZr. They do however add to the evidence on the better resistance to wear of HXLPE over CPE.

Cite this article: Bone Joint J 2015;97-B:1463–9.

Oxidised zirconium (OxZi) has been developed as an alternative bearing surface for femoral heads in total hip arthroplasty (THA). This study has investigated polyethylene wear, functional outcomes and complications, comparing OxZi and cobalt–chrome (CoCr) as part of a three-arm, multicentre randomised controlled trial. Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and highly cross-linked polyethylene (XLPE) liner; Group B received an OxZi femoral head and XLPE liner; Group C received an OxZi femoral head and ultra-high molecular weight polyethylene (UHMWPE) liner. At five years, 368 patients had no statistically significant differences in short-form-36 (p = 0.176 mental, p = 0.756 physical), Western Ontario and McMaster Universities Osteoarthritis Index (p = 0.847), pain scores (p = 0.458) or complications. The mean rate of linear wear was 0.028 mm/year (standard deviation (. sd) 0.010). for Group A, 0.023 mm/year (. sd. 0.010) for Group B, and 0.09 mm/year (. sd. 0.045) for Group C. Penetration was significantly higher in the UHMWPE liner group compared with both XLPE liner groups (p < 0.001) but no significant difference was noted between CoCr and OxZi when articulating with XLPE (p = 0.153). In this, the largest randomised study of this bearing surface, it appears that using a XLPE acetabular liner is more important in reducing THA component wear than the choice of femoral head bearing, at mid-term follow-up. There is a non-significant trend towards lower wear, coupling OxZi rather than CoCr with XLPE but long-term analysis is required to see if this observation changes with time and becomes significant. Cite this article: Bone Joint J 2015;97-B:883–9

Aims

To present a surgically relevant update of trunnionosis.