A silver-containing hydroxyapatite (Ag-HA) coating has been developed using thermal spraying technology. We evaluated the osteoconductivity of this coating on titanium (Ti) implants in rat tibiae in relation to bacterial infection in joint replacement.

At 12 weeks, the mean affinity indices of bone formation of a Ti, an HA, a 3%Ag-HA and a 50%Ag-HA coating were 97.3%, 84.9%, 81.0% and 40.5%, respectively. The mean affinity indices of bone contact of these four coatings were 18.8%, 83.7%, 77.2% and 40.5%, respectively. The indices of bone formation and bone contact around the implant of the 3%Ag-HA coating were similar to those of the HA coating, and no significant differences were found between them (bone formation, p = 0.99; bone contact, p = 0.957). However, inhibition of bone formation was observed with the 50%Ag-HA coating.

These results indicate that the 3%Ag-HA coating has low toxicity and good osteoconductivity, and that the effect of silver toxicity on osteoconductivity depends on the dose.

We have assessed the proximal capsular extension of the ankle joint in 18 patients who had a contrast-enhanced MRI ankle arthrogram in order to delineate the capsular attachments.

We noted consistent proximal capsular extensions anterior to the distal tibia and in the tibiofibular recess. The mean capsular extension anterior to the distal tibia was 9.6 mm (4.9 to 27.0) proximal to the anteroinferior tibial margin and 3.8 mm (−2.1 to 9.3) proximal to the dome of the tibial plafond. In the tibiofibular recess, the mean capsular extension was 19.2 mm (12.7 to 38.0) proximal to the anteroinferior tibial margin and 13.4 mm (5.8 to 20.5) proximal to the dome of the tibial plafond.

These areas of proximal capsular extensions run the risk of being traversed during the insertion of finewires for the treatment of fractures of the distal tibia. Surgeons using these techniques should be aware of this anatomy in order to minimise the risk of septic arthritis.