We have reviewed 70 patients with bilateral simultaneous total hip arthroplasties to determine the rate of failure and to compare polyethylene wear and osteolysis between an implant with a cobalt-chrome head and Hylamer liner with that of a zirconia head and Hylamer liner. The mean thickness of the polyethylene liner was 11.0 mm (8.8 to 12.2) in the hip with a zirconia head and 10.7 mm (8.8 to 12.2) in that with a cobalt-chrome head. At follow-up at 6.4 years no acetabular or femoral component had been revised for aseptic loosening and no acetabular or femoral component was loose according to radiological criteria in both the cemented and cementless groups. The mean rate of linear wear and annual wear rate were highest in the 22 mm zirconia femoral head (1.25 mm (SD 1.05) and 0.21 mm (SD 0.18), respectively) and lowest in the 22 mm cobalt-chrome femoral head (0.70 mm (SD 0.39) and 0.12 mm (SD 0.07), respectively). The mean volumetric wear was highest in the 28 mm zirconia femoral head (730.79 mm. 3. ) and lowest in the 22 mm cobalt-chrome femoral head (264.67 mm. 3. ), but if the results were compared by size of the femoral head and type of material there was no statistical difference (p > 0.05). Sequential measurements of annual wear showed that the zirconia femoral head had a relatively higher rate of penetration than the cobalt-chrome head over the first three years; thereafter the rate of wear was reduced and compared favourably with that of cobalt-chrome heads. There was a statistically significant relationship between the wear of the polyethylene liner and the age of the patient, male gender and the degree of abduction angle of the cup, but not diagnosis, weight, hip score, range of movement, or amount of anteversion. Osteolysis was identified on both sides of the acetabulum in six patients (9%). Of 12 hips with acetabular osteolysis, six had a 28 mm cobalt-chrome femoral head and the remaining six a 28 mm zirconia head. Osteolysis was observed in zones 1A and 7A of the femur in two hips (3%) with a 28 mm zirconia head (cemented hip) and in four (6%) with a 28 mm cobalt-chrome femoral head (cementless hip). Our findings suggest that although the performance of a zirconia femoral head with a Hylamer liner was not statistically different from that of a cobalt-chrome femoral head and Hylamer liner, there was a trend for the zirconia head to be worse than the cobalt-chrome femoral head

The long-term biological effects of wear debris are unknown. We have investigated whether there is any evidence of cumulative mutagenic damage in peripheral blood lymphocytes of patients undergoing revision arthroplasty of predominantly metal-on-plastic total hip replacements compared with those at primary arthroplasty. There was a threefold increase in aneuploidy and a twofold increase in chromosomal translocations which could not be explained by the confounding variables of smoking, gender, age and diagnostic radiographs. In the patients with TiVaAl prostheses there was a fivefold increase in aneuploidy but no increase in chromosomal translocations. By contrast, in patients with cobalt-chrome prostheses there was a 2.5-fold increase in aneuploidy and a 3.5-fold increase in chromosomal translocations. In six patients with stainless-steel prostheses there was no increase in either aneuploidy or chromosomal translocations. Our results suggest that future epidemiological studies of the putative long-term risks of joint replacement should take into account the type of alloy used in the prosthesis

We examined stainless-steel, cobalt-chrome, titanium and alumina and zirconia ceramic femoral heads retrieved at revision surgery. All the heads had articulated against ultra-high-molecular-weight-polyethylene (UHMWPE) acetabular cups. We studied the simulation of third-body damage and the wear of UHMWPE against the various materials used for the heads. The surfaces of the retrieved heads were analysed using a two-dimensional contacting profilometer. Third-body damage was characterised by the mean height of the scratches above the mean line (R. pm. ). The alumina ceramic and zirconia ceramic retrieved heads were found to have significantly less damage. In laboratory studies the ceramics were also more resistant to simulated third-body damage than the metal alloys. We studied the wear of UHMWPE against the damaged counterfaces in simple configuration tests. The damaged ceramics produced less polyethylene wear than the damaged metal counterfaces. The wear factor of UHMWPE against the damaged materials was dependent on the amount of damage to the counterface (R. p. ). Our study has shown the benefit of using the harder and more damage-resistant ceramic materials for femoral heads

Objectives

Taper junctions between modular hip arthroplasty femoral heads and stems fail by wear or corrosion which can be caused by relative motion at their interface. Increasing the assembly force can reduce relative motion and corrosion but may also damage surrounding tissues. The purpose of this study was to determine the effects of increasing the impaction energy and the stiffness of the impactor tool on the stability of the taper junction and on the forces transmitted through the patient’s surrounding tissues.

We implanted titanium and carbon fibre-reinforced plastic (CFRP) femoral prostheses of the same dimensions into five prosthetic femora. An abductor jig was attached and a 1 kN load applied. This was repeated with five control femora. Digital image correlation was used to give a detailed two-dimensional strain map of the medial cortex of the proximal femur. Both implants caused stress shielding around the calcar. Distally, the titanium implant showed stress shielding, whereas the CFRP prosthesis did not produce a strain pattern which was statistically different from the controls. There was a reduction in strain beyond the tip of both the implants.

This investigation indicates that use of the CFRP stem should avoid stress shielding in total hip replacement.

Wear of polyethylene is associated with aseptic loosening of orthopaedic implants and has been observed in hip and knee prostheses and anatomical implants for the shoulder. The reversed shoulder prostheses have not been assessed as yet. We investigated the volumetric polyethylene wear of the reversed and anatomical Aequalis shoulder prostheses using a mathematical musculoskeletal model. Movement and joint stability were achieved by EMG-controlled activation of the muscles. A non-constant wear factor was considered. Simulated activities of daily living were estimated from in vivo recorded data.

After one year of use, the volumetric wear was 8.4 mm³ for the anatomical prosthesis, but 44.6 mm³ for the reversed version. For the anatomical prosthesis the predictions for contact pressure and wear were consistent with biomechanical and clinical data. The abrasive wear of the polyethylene in reversed prostheses should not be underestimated, and further analysis, both experimental and clinical, is required.

An experimental sheep model was used for impaction allografting of 12 hemiarthroplasty femoral components placed into two equal-sized groups. In group 1, a 50:50 mixture of ApaPore hydroxyapatite bone-graft substitute and allograft was used. In group 2, ApaPore and allograft were mixed in a 90:10 ratio. Both groups were killed at six months. Ground reaction force results demonstrated no significant differences (p > 0.05) between the two groups at 8, 16 and 24 weeks post-operatively, and all animals remained active. The mean bone turnover rates were significantly greater in group 1, at 0.00206 mm/day, compared to group 2 at 0.0013 mm/day (p < 0.05). The results for the area of new bone formation demonstrated no significant differences (p > 0.05) between the two groups. No significant differences were found between the two groups in thickness of the cement mantle (p > 0.05) and percentage ApaPore-bone contact (p > 0.05).

The results of this animal study demonstrated that a mixture of ApaPore allograft in a 90:10 ratio was comparable to using a 50:50 mixture.

The effects of the method of fixation and interface conditions on the biomechanics of the femoral component of the Birmingham hip resurfacing arthroplasty were examined using a highly detailed three-dimensional computer model of the hip. Stresses and strains in the proximal femur were compared for the natural femur and for the femur resurfaced with the Birmingham hip resurfacing. A comparison of cemented versus uncemented fixation showed no advantage of either with regard to bone loading. When the Birmingham hip resurfacing femoral component was fixed to bone, proximal femoral stresses and strains were non-physiological. Bone resorption was predicted in the inferomedial and superolateral bone within the Birmingham hip resurfacing shell. Resorption was limited to the superolateral region when the stem was not fixed. The increased bone strain observed adjacent to the distal stem should stimulate an increase in bone density at that location. The remodelling of bone seen during revision of failed Birmingham hip resurfacing implants appears to be consistent with the predictions of our finite element analysis.