We measured the proximal migration of 265 acetabular cups over seven years and correlated the findings with clinical outcome and acetabular revision for aseptic loosening. Cups which eventually became aseptically loose were shown to migrate more rapidly than successful cups. The average proximal migration at two years postoperatively for four groups of cups showed a monotonic relationship to the acetabular revision rate for aseptic loosening at 6.5 years. We conclude that acetabular cups which develop aseptic loosening as evidenced by pain, revision or screw fracture show increased proximal migration by one year, and that the 'migration rate' at two years can be used to predict the acetabular revision rate from aseptic loosening at 6.5 years

In laboratory tests, the ultra-high molecular weight polyethylene used for the acetabular cups of Charnley hip prostheses has a very low wear rate against steel. In the body radiographic measurements indicate that the polyethylene wears more rapidly. In order to investigate this higher wear rate, the sockets of acetabular cups removed at post-mortem have been examined using optical and electron microscopy. It has been shown that a socket wears predominantly on its superior part and that this is a direct consequence of the orientation of the cup in the body and the direction of loading of the hip. In the worn region the femoral head in effect bores out a new socket for itself, a process which is visible with the naked eye after approximately eight years. Electron microscopy shows that the predominant wear mechanism is adhesion, but after about eight years the appearance of surface cracks suggests that surface fatigue is taking place in addition to this. Laboratory wear tests have shown that pure surface fatigue is not sufficient to account for the high clinical wear rate. Other deformation processes are suggested and discussed with regard to the higher clinical wear rate

We examined radiographic polyethylene wear in 233 cemented total hip arthroplasties (201 patients) with either a metal-backed or a non-metal-backed acetabular cup. All patients had identical cemented one-piece titanium femoral stems with a femoral head diameter of 28 mm. The mean linear wear rate was 0.11 mm/yr in metal-backed sockets and 0.08 mm/yr in non-metal-backed sockets (p = 0.0002). The mean volumetric wear rate was 66.2 mm3/yr in the metal-backed sockets and 48.2 mm3/yr in the polyethylene sockets (p = 0.0002). The addition of metal backing to a cemented acetabular cup therefore resulted in a 37% increase in mean polyethylene wear rates which may partially explain the higher failure rate of cemented metal-backed cups. Linear regression analysis also implicated increased follow-up time (log), gross acetabular migration, metal backing and male gender in increasing polyethylene wear. We advocate the use of an all-polyethylene cup in cemented total hip arthroplasty. The increased polyethylene wear must also cause concern about the wear rate of uncemented metal-backed acetabular sockets

Between March 1990 and May 1991 we performed 85 primary total hip replacements in 74 patients using the Landos Atoll hydroxyapatite (HA)-coated cup and the Corail HA-coated stem. The patients were followed up for a mean of ten years. Of the 85 cups, 26 (31%) have already been revised and a further six are radiologically unstable and awaiting revision. Two femoral stems have been revised for infection without loosening. The retrieved acetabular cups were studied by SEM and image-processing techniques to quantify the amount of residual HA on the cup. This was correlated with the clinical variables and modes of failure. The residual HA (as a percentage of the surface) on the loose cups correlated negatively with the duration of implantation (r = −0.732, p < 0.001). Six cups were stable at revision and had more residual HA coating than those which were loose (p < 0.01). The rate of failure of the Landos Atoll HA-coated, smooth hemispherical cup with screw fixation is unacceptably high. Resorption of the HA coating is markedly increased in loose cups compared with stable cups. HA coating cannot substitute for stable mechanical fixation

Fracture of the polyethylene acetabular cup is a rare late complication of total hip replacement. Five cases are reported. In each one this followed a fall, and involved a Muller arthroplasty which had previously been symptomless. It is postulated that ridges or other irregularities of bone, produced by keying holes, could lead to areas of thin cement and potential weakness of support for the cup

1. Prosthetic acetabular cups of the Charnley and McKee-Farrar designs were cemented into cadaveric pelves using different procedures for preparing the acetabulum. 2. The torsional moments needed to loosen these cups were measured. 3. The torsional moments so measured were found to be from about four to more than twenty times higher than the frictional moments measured in independent tests on the two designs of prosthesis. 4. It is argued that late looseness of the acetabular component after total hip replacement, in the absence of infection, seems most likely to be due to thermal damage to the bone occurring at the time of polymerisation of the cement, and to subsequent bone resorption. 5. Surgical preparation of the acetabulum should include removal of all the articular cartilage and cleaning of the acetabular fossa, but the drilling of additional holes in the floor of the acetabulum seems unimportant. 6. The possibility of fatigue fracture in bone as a factor contributing to late loosening is an argument in favour of metal-on-polyethylene prostheses with their lower frictional moments, although the importance of this factor cannot be estimated

Laboratory wear testing of ultra high molecular weight polyethylene from 12 Charnley acetabular cups, removed after periods of up to 17.5 years showed that the large patient-to-patient variations in clinical penetration rate cannot be explained by batch-to-batch variation in the wear resistance of the material. Nor was there any evidence of a time-dependent degradation in wear resistance of the material

We report the long-term radiological results of 58 total hip arthroplasties (THA) using the Charnley offset-bore acetabular socket. Wear was measured at four sites and radiolucent lines and possible migration were recorded. Four cups were retrieved at revision and were examined using light microscopy, SEM and X-ray microanalysis. At a mean follow-up of seven years the mean wear in the DeLee and Charnley zone I was 0.4 mm and in zone II 0.26 mm. The wear rate was 0.06 and 0.04 mm/year, respectively. Progression of radiolucent lines was seen in five cases (8.6%). Three sockets (5.2%) were revised because of aseptic migration at a mean follow-up of 9.8 years and one socket for infection at two years. The offset-bore acetabular cup had excellent wear behaviour and a low migration and revision rate. We recommend that it should be considered in THA since the use of small cups is increasing, particularly in revision cases

We describe a new method for the accurate measurement of the angle of anteversion of an acetabular cup from standard anteroposterior radiographs, and provide the conversion tables required. The effect of the centering of the radiograph is discussed and a method of distinguishing between anteversion and retroversion by using a caudally directed x-ray beam is described

Failure of an acetabular cup is uncommon and has been attributed to wear or creep, trauma or bony irregularities in the acetabulum. We report ten cases in which fracture of the cup occurred at the site of drill holes used to anchor the marker wire. The role of such indentations as stress raisers has not been previously reported; we suggest that deep indentations or grooves should not be placed in the most highly stressed areas and that the cup thickness should allow for predicted wear rates

Ten acetabular cups coated with hydroxyapatite (HA) had originally been inserted in five primary and five revision total hip replacements. The thickness of the HA was 155 ± 35 μm. The cups, which were well-fixed, were retrieved, with their adherent tissue, at reoperation after 0.3 to 5.8 years because of infection (five hips), wear of polyethylene (three hips), and instability (two hips). Undecalcified sections showed a direct contact between bone and osteoid-like tissue which had formed directly onto the HA coating. The area within the threads and their mirror images, as well as the implant-tissue interfaces consisted of similar amounts of bone and soft tissue. Degradation of HA was seen in all hips. The mean thickness of the remaining HA coating was 97 μm (95% CI 94 to 101). The metal interface comprised 66% HA. The HA-tissue interface contained more bone than soft tissue (p = 0.001), whereas the metal-tissue interface included more soft tissue than bone (p = 0.019). Soft tissue at the implant interface and poor replacement of HA by bone may interfere with long-term fixation

Aims

Limited implant survival due to aseptic cup loosening is most commonly responsible for revision total hip arthroplasty (THA). Advances in implant designs and materials have been crucial in addressing those challenges. Vitamin E-infused highly cross-linked polyethylene (VEPE) promises strong wear resistance, high oxidative stability, and superior mechanical strength. Although VEPE monoblock cups have shown good mid-term performance and excellent wear patterns, long-term results remain unclear. This study evaluated migration and wear patterns and clinical and radiological outcomes at a minimum of ten years’ follow-up.

We describe a simple, retroperitoneal approach for the removal of acetabular components that have migrated into the pelvis. The dense fibrous tissue layer which surrounds the implant protects the iliac vessels during removal of the cup by this method.

We reviewed 264 consecutive primary total hip replacements in 244 patients in which the Harris-Galante I porous-coated acetabular component had been used. The mean follow-up was 95 months (69 to 132). In 221 arthroplasties a 32 mm ceramic head had been used, and in the other 43 one of cobalt-chrome alloy. There were 124 women and 120 men with a mean age at operation of 56.8 years (21 to 83).

Survival analysis of the acetabular components was performed using the following definitions of failure: 1) infection; 2) removal because of aseptic loosening; 3) removal for any cause; and 4) a worst-case analysis including removal of the cup or infection or loss to follow-up.

Two well-fixed cups had been removed because of deep infection and three, similarly sound cups had been exchanged at the time of femoral revision. None of the acetabular components had required revision for aseptic loosening. After 11 years survival was 97.7% using the worst-case criterion. Radiological analysis of 187 acetabular components at a mean of 82 months (41 to 132) revealed no case of aseptic loosening. Pelvic osteolysis was seen in only one patient, but was not progressive and showed signs of regression.

The results using these acetabular components are encouraging but the need for regular follow-up remains since complications such as significant wear of the liner, massive osteolysis of the pelvis, aseptic loosening and late infection may increase in the second decade.

We report a high rate of failure of the Ring polyethylene cementless cup caused largely by granulomatous osteolysis. We have reviewed 126 prostheses inserted from 1986 to 1992 at from 11 to 90 months after surgery. There was radiological evidence of osteolytic granulomas adjacent to the external surface of the cup in 32%, appearing on average at three years from operation. In a subgroup of 59 prostheses followed for at least four years the incidence of such changes was 54%. A total of 27 cups (22%) have required revision, 21 for granulomatous loosening at an average follow-up of five years. In the retrieved prostheses there was obvious polyethylene abrasion and histological examination confirmed the presence of polyethylene wear debris. We found no significant correlation of osteolysis with cup size, although smaller cups were predominant among those having revision.

We studied wear in the ultra-high-molecular-weight polyethylene offset bore socket in 54 hips which had had Charnley low-friction arthroplasty. At an average follow-up of 8.1 years, the mean penetration rate was 0.04 mm per year. Correlation between the depth of socket penetration and the incidence of socket migration was confirmed, but socket migration occurred with lower penetration than had been previously reported.

We performed thermal analysis of polyethylene samples obtained from 73 new cups of the Weller hip prosthesis. There were marked individual differences in the degree of their crystallinity, ranging from 37.8% to 67.2% with a mean of 53%. Analysis of polyethylene from removed cups also showed differences in crystallinity in individual cups, with the mean value being higher in the removed implants than in the new ones. This difference in crystallinity between the groups was statistically significant. Marked individual differences in the degree of cup wear may result from these changes.