Aims. The Birmingham Hip Resurfacing (BHR) was introduced in 1997 to address the needs of young active patients using a historically proven large-diameter metal-on-metal (MoM) bearing. A single designer surgeon’s consecutive series of 130 patients (144 hips) was previously reported at five and ten years, reporting three and ten failures, respectively. The aim of this study was to extend the follow-up of this original cohort at 25 years. Methods. The study extends the reporting on the first consecutive 144 resurfacing procedures in 130 patients for all indications. All operations were undertaken between August 1997 and May 1998. The mean age at operation was 52.1 years (SD 9.93; 17 to 76), and included 37 female patients (28.5%). Failure was defined as revision of either component for any reason. Kaplan-Meier survival analysis was performed. Routine follow-up with serum metal ion levels, radiographs, and Oxford Hip Scores (OHSs) was undertaken. Results. Overall implant survival was 83.50% (95% confidence interval (CI) 0.79 to 0.90) at 25 years, and the number at risk was 79. Survival in male patients at 25 years was 89.5% (95% CI 0.83 to 0.96) compared to 66.9% for female patients (95% CI 0.51 to 0.83). Ten additional failures occurred in the period of ten to 25 years. These involved an adverse reaction to metal debris in four patients, a periprosthetic femoral neck fracture affecting five patients, and aseptic loosening in one patient. The median chromium levels were 49.50 nmol/l (interquartile range (IQR) 34 to 70), and the median cobalt serum levels were 42 nmol/l (IQR 24.50 to 71.25). The median OHS at last follow-up was 35 (IQR 10 to 48). During the 25-year study period, 29 patients died. Patient survival at 25 years was 75.10% (95% CI 0.67 to 0.83). Conclusion. This study demonstrates that MoM hip resurfacing using the BHR provides a durable alternative to total hip arthroplasty (THA), particularly in younger male patients with osteoarthritis wishing to maintain a high level of function. These results compare favourably to the best results for THAs. Cite this article: Bone Joint J 2024;106-B(6):540–547

Aims. Hip resurfacing remains a potentially valuable surgical procedure for appropriately-selected patients with optimised implant choices. However, concern regarding high early failure rates continues to undermine confidence in use. A large contributor to failure is adverse local tissue reactions around metal-on-metal (MoM) bearing surfaces. Such phenomena have been well-explored around MoM total hip arthroplasties, but comparable data in equivalent hip resurfacing procedures is lacking. In order to define genetic predisposition, we performed a case-control study investigating the role of human leucocyte antigen (HLA) genotype in the development of pseudotumours around MoM hip resurfacings. Methods. A matched case-control study was performed using the prospectively-collected database at the host institution. In all, 16 MoM hip resurfacing 'cases' were identified as having symptomatic periprosthetic pseudotumours on preoperative metal artefact reduction sequence (MARS) MRI, and were subsequently histologically confirmed as high-grade aseptic lymphocyte-dominated vasculitis-associated lesions (ALVALs) at revision surgery. ‘Controls’ were matched by implant type in the absence of evidence of pseudotumour. Blood samples from all cases and controls were collected prospectively for high resolution genetic a nalysis targeting 11 separate HLA loci. Statistical significance was set at 0.10 a priori to determine the association between HLA genotype and pseudotumour formation, given the small sample size. Results. Using a previously-reported ALVAL classification, the majority of pseudotumour-positive caseswere found to have intermediate-grade group 2 (n = 10; 63%) or group 3 (n = 4; 25%) histological findings. Two further patients (13%) had high-grade group 4 lesions. HLA-DQB1*05:03:01 (p = 0.0676) and HLA-DRB1*14:54:01 (p = 0.0676) alleles were significantly associated with a higher risk of pseudotumour formation, while HLA-DQA1*03:01:01 (p = 0.0240), HLA-DRB1*04:04:01 (p = 0.0453), HLA-C*01:02:01 (p = 0.0453), and HLA-B*27:05:02 (p = 0.0855) were noted to confer risk reduction. Conclusion. These findings confirm the association between specific HLA genotypes and the risk of pseudotumour development around MoM hip resurfacings. Specifically, the two ‘at risk’ alleles (DQB1*05:03:01 and DRB1*14:54:01) may hold clinical value in preoperative screening and prospective surgical decision-making. Cite this article: Bone Jt Open 2023;4(3):182–187

Aims

A recent report from France suggested an association between the use of cobalt-chrome (CoCr) femoral heads in total hip arthroplasties (THAs) and an increased risk of dilated cardiomyopathy and heart failure. CoCr is a commonly used material in orthopaedic implants. If the reported association is causal, the consequences would be significant given the millions of joint arthroplasties and other orthopaedic procedures in which CoCr is used annually. We examined whether CoCr-containing THAs were associated with an increased risk of all-cause mortality, heart outcomes, cancer, and neurodegenerative disorders in a large national database.

Aims. The purpose of this study was to compare two different types of metal-on-metal (MoM) bearing for total hip arthroplasty (THA): one with a large femoral head (38 mm to 52 mm) and the other with a conventional femoral head (28 mm or 32 mm). We compared clinical outcome, blood metal ion levels, and the incidence of pseudotumour in the two groups. Patients and Methods. Between December 2009 and December 2011, 62 patients underwent MoM THA with a large femoral head (Magnum group) and 57 patients an MoM THA with a conventional femoral head (conventional group). Clinical outcome was assessed using the Harris Hip score, University of California, Los Angeles (UCLA) activity score and EuroQol-5D (EQ-5D). Blood metal ion levels were measured and MRI scans were analyzed at a minimum of five years postoperatively. Results. No acetabular component was implanted with more than 50° of inclination in either group. The Harris Hip Score, UCLA activity score, and EQ-5D improved postoperatively in both groups; no significant clinical differences were noted between the groups. The blood cobalt ion levels in the conventional group continued to rise postoperatively to five years while reaching a plateau at two years postoperatively in the Magnum group. At five years, the mean cobalt ion level of 1.16 μg/l (. sd. 1.32) in the Magnum group was significantly lower than the 3.77 μg/l (. sd. 9.80) seen in the conventional group (p = 0.0015). The incidence of moderate to severe pseudotumour was 4.7% in the Magnum group and 20.6% in the conventional group. There were no dislocations in the Magnum group and two in the conventional group. One patient in the Magnum group underwent revision for pseudotumour at 4.7 years postoperatively. Conclusion. At five years, a well-positioned large head MoM THA has a significantly lower level of metal ion release and a lower incidence of moderate to severe pseudotumour than a MoM bearing of conventional size. Cite this article: Bone Joint J 2018;100-B:1018–24

Aims

For this retrospective cohort study, patients aged ≤ 30 years (very young) who underwent total hip arthroplasty (THA) were compared with patients aged ≥ 60 years (elderly) to evaluate the rate of revision arthroplasty, implant survival, the indications for revision, the complications, and the patient-reported outcomes.

Aims . The primary aim of this independent prospective randomised trial was to compare serum metal ion levels for ceramic-on-metal (CoM) and metal-on-metal (MoM) bearing surfaces in total hip arthroplasty (THA). Our one-year results demonstrated elevation in metal ion levels above baseline with no significant difference between the CoM and MoM groups. This paper reviews the five-year data. Patients and Methods. The implants used in each patient differed only in respect to the type of femoral head (ceramic or metal). At five-year follow-up of the 83 enrolled patients, data from 67 (36 CoM, 31 MoM) was available for comparison. Results. The mean serum cobalt (Co) and chromium (Cr) ion levels remained above baseline in both groups (CoM: Co 1.16 μg/l (0.41 to 14.67), Cr 1.05 μg/l (0.16 to 12.58); MoM: Co 2.93 μg/l (0.35 to 30.29), Cr 1.85 μg/l (0.36 to 17.00)) but the increase was significantly less in the CoM cohort (Co difference p = 0.001, Cr difference p = 0.002). These medium-term results, coupled with lower revision rates from national joint registries, suggest that the performance of CoM THA may be superior to that of MoM. . Conclusion. While both bearing combinations have since been withdrawn these results provide useful information for planning clinical surveillance of CoM THAs and warrants continued monitoring. Cite this article: Bone Joint J 2017;99-B:1298–1303

Objectives

Alarm over the reported high failure rates for metal-on-metal (MoM) hip implants as well as their potential for locally aggressive Adverse Reactions to Metal Debris (ARMDs) has prompted government agencies, internationally, to recommend the monitoring of patients with MoM hip implants. Some have advised that a blood ion level >7 µg/L indicates potential for ARMDs. We report a systematic review and meta-analysis of the performance of metal ion testing for ARMDs.

Objectives

This study aimed to characterise and qualitatively grade the severity of the corrosion particles released into the hip joint following taper corrosion.

Objectives

T-cells are considered to play an important role in the inflammatory response causing arthroplasty failure. The study objectives were to investigate the composition and distribution of CD4+ T-cell phenotypes in the peripheral blood (PB) and synovial fluid (SF) of patients undergoing revision surgery for failed metal-on-metal (MoM) and metal-on-polyethylene (MoP) hip arthroplasties, and in patients awaiting total hip arthroplasty.

Dislocation remains among the most common complications of, and reasons for, revision of both primary and revision total hip replacements (THR). Hence, there is great interest in maximising stability to prevent this complication. Head size has been recognised to have a strong influence on the risk of dislocation post-operatively. As femoral head size increases, stability is augmented, secondary to an increase in impingement-free range of movement. Larger head sizes also greatly increase the ‘jump distance’ required for the head to dislocate in an appropriately positioned cup. Level-one studies support the use of larger diameter heads as they decrease the risk of dislocation following primary and revision THR. Highly cross-linked polyethylene has allowed us to increase femoral head size, without a marked increase in wear. However, the thin polyethylene liners necessary to accommodate larger heads may increase the risk of liner fracture and larger heads have also been implicated in causing soft-tissue impingement resulting in groin pain. Larger diameter heads also impart larger forces on the femoral trunnion, which may contribute to corrosion, metal release, and adverse local tissue reactions. Alternative large bearings including large ceramic heads and dual mobility bearings may mitigate some of these risks, and several of these devices have been used with clinical success.

Cite this article: Bone Joint J 2014;96-B(11 Suppl A):23–6.

Large-head metal-on-metal (MoM) total hip replacements (THR) have given rise to concern. Comparative studies of small-head MoM THRs over a longer follow-up period are lacking. Our objective was to compare the incidence of complications such as infection, dislocation, revision, adverse local tissue reactions, mortality and radiological and clinical outcomes in small-head (28 mm) MoM and ceramic-on-polyethylene (CoP) THRs up to 12 years post-operatively.

A prospective cohort study included 3341 THRs in 2714 patients. The mean age was 69.1 years (range 24 to 98) and 1848 (55.3%) were performed in women, with a mean follow-up of 115 months (18 to 201). There were 883 MoM and 2458 CoP bearings. Crude incidence rates (cases/1000 person-years) were: infection 1.3 vs 0.8; dislocation 3.3 vs 3.1 and all-cause revision 4.3 vs 2.2, respectively. There was a significantly higher revision rate after ten years (adjusted hazard ratio 9.4; 95% CI 2.6 to 33.6) in the MoM group, and ten of 26 patients presented with an adverse local tissue reaction at revision. No differences in mortality, osteolysis or clinical outcome were seen.

In conclusion, we found similar results for small-head MoM and CoP bearings up to ten years post-operatively, but after ten years MoM THRs had a higher risk of all-cause revision. Furthermore, the presence of an adverse response to metal debris seen in the small-head MOM group at revision is a cause for concern.

Cite this article: Bone Joint J 2014; 96-B:868–75.

We prospectively assessed the efficacy of a ceramic-on-metal (CoM) hip bearing with uncemented acetabular and femoral components in which cobalt­–chrome acetabular liners and alumina ceramic heads were used.

The cohort comprised 94 total hip replacements (THRs) in 83 patients (38 women and 45 men) with a mean age of 58 years (42 to 70). Minimum follow-up was two years. All patients had pre- and post-operative assessment using the Western Ontario and McMaster Universities osteoarthritis index (WOMAC), Oxford hip score and Short-Form 12 scores. All showed a statistically significant improvement from three months post-operatively onwards (all p < 0.001).

After two years whole blood metal ion levels were measured and chromosomal analysis was performed. The levels of all metal ions were elevated except vanadium. Levels of chromium, cobalt, molybdenum and titanium were significantly higher in patients who underwent bilateral THR compared with those undergoing unilateral THR (p < 0.001). Chromosomal analysis demonstrated both structural and aneuploidy mutations. There were significantly more breaks and losses than in the normal population (p < 0.001). There was no significant difference in chromosomal aberration between those undergoing unilateral and bilateral procedures (all analyses p ≥ 0.62).

The use of a CoM THR is effective clinically in the short-term, with no concerns, but the significance of high metal ion levels and chromosomal aberrations in the long-term remains unclear.

Cite this article: Bone Joint J 2013;95-B:1040–44.

The presence of pseudotumours, which are soft-tissue masses relating to the hip, after metal-on-metal hip resurfacing arthroplasty has been associated with elevated levels of metal ions in serum, suggesting that pseudotumours occur when there is increased wear. We aimed to quantify the wear in vivo of implants revised for pseudotumours (eight) and of a control group of implants (22) revised for other reasons of failure.

We found that the implant group with pseudotumours had a significantly higher rate of median linear wear of the femoral component at 8.1 μm/year (2.75 to 25.4) than the 1.79 μm/year (0.82 to 4.15; p = 0.002) of the non-pseudotumour group. For the acetabular component a significantly higher rate of median linear wear of 7.36 μm/year (1.61 to 24.9) was observed in the pseudotumour group compared with 1.28 μm/year (0.81 to 3.33, p = 0.001) in the other group. Wear of the acetabular component in the pseudotumour group always involved the edge of the implant, indicating that edge-loading had occurred.

Our findings are the first direct evidence that pseudotumour is associated with increased wear at the metal-on-metal articulation. Furthermore, edge-loading with the loss of fluid-film lubrication may be an important mechanism of generation of wear in patients with a pseudotumour.