We sought to determine whether cobalt-chromium alloy (CoCr) femoral
stem tapers (trunnions) wear more than titanium (Ti) alloy stem
tapers (trunnions) when used in a large diameter (LD) metal-on-metal
(MoM) hip arthroplasty system. We performed explant analysis using validated methodology to
determine the volumetric material loss at the taper surfaces of
explanted LD CoCr MoM hip arthroplasties used with either a Ti alloy
(n = 28) or CoCr femoral stem (n = 21). Only 12/14 taper constructs
with a rough male taper surface and a nominal included angle close
to 5.666° were included. Multiple regression modelling was undertaken
using taper angle, taper roughness, bearing diameter (horizontal
lever arm) as independent variables. Material loss was mapped using
a coordinate measuring machine, profilometry and scanning electron
microscopy.Aims
Patients and Methods
The aim of this study was to evaluate the long-term clinical
and radiographic outcomes of the Birmingham Interlocking Pelvic
Osteotomy (BIPO). In this prospective study, we report the mid- to long-term clinical
outcomes of the first 100 consecutive patients (116 hips; 88 in
women, 28 in men) undergoing BIPO, reflecting the surgeon’s learning
curve. Failure was defined as conversion to hip arthroplasty. The
mean age at operation was 31 years (7 to 57). Three patients (three
hips) were lost to follow-up.Aims
Patients and Methods
This study aimed to characterise and qualitatively grade the severity of the corrosion particles released into the hip joint following taper corrosion. The 26 cases examined were CoC/ABG Modular (n = 13) and ASR/SROM (n = 13). Blood serum metal ion levels were collected before and after revision surgery. The haematoxylin and eosin tissue sections were graded on the presence of fibrin exudates, necrosis, inflammatory cells and corrosion products. The corrosion products were identified based on visible observation and graded on abundance. Two independent observers blinded to the clinical patient findings scored all cases. Elemental analysis was performed on corrosion products within tissue sections. X-Ray diffraction was used to identify crystalline structures present in taper debris.Objectives
Methods