We evaluated the efficacy and biocompatibility of porous apatite-wollastonite glass ceramic (AW-GC) as an intramedullary plug in total hip replacement (THR) for up to two years in 22 adult beagle dogs. Cylindrical porous AW-GC rods (70% porosity, mean pore size 200 3m) were prepared. Four dogs were killed at 1, 3, 6 and 12 months each and six at 24 months after implantation.

Radiological evaluation confirmed the efficacy of porous AW-CG as an intramedullary plug. Histological evaluation showed osteoconduction at one month and resorption of the porous AW-GC, which was replaced by newly-formed bone, at 24 months. Our findings indicate that porous AW-GC can be used clinically as an intramedullary plug in THR.

We have developed a new drug delivery system using porous apatite-wollastonite glass ceramic (A-W GC) to treat osteomyelitis. A-W GC (porosity, 70% and 20% to 30%), or porous hydroxyapatite (HA) blocks (porosity 35% to 48%) used as controls, were soaked in mixtures of two antibiotics, isepamicin sulphate (ISP) and cefmetazole (CMZ) under high vacuum.

We evaluated the release concentrations of the antibiotics from the blocks. The bactericidal concentration of ISP from A-W GC was maintained for more than 42 days, but that from HA decreased to below the detection limit after 28 days. The concentrations of CMZ from both materials were lower than those of ISP. An in vivo study using rabbit femora showed that an osseous concentration of ISP was maintained at eight weeks after implantation. Osteoconduction of the A-W GC block was good.

Four patients with infected hip arthroplasties and one with osteomyelitis of the tibia have been treated with the new delivery system with excellent results.

We have developed a bioactive bone cement (BA cement) consisting of Bis-GMA resin and bioactive glass powder. It has high compressive and tensile strengths, a low curing temperature and its bioactivity allows it to bond directly with bone.

We operated on the 18 femora of nine mongrel dogs for intercalary replacement of part of the bone by a metal prosthesis using either PMMA cement or BA cement for fixation. Three dogs were killed at each of 4, 12 and 26 weeks after surgery for the evaluation of fixation strength by a push-out test and for histological examination by Giemsa surface staining and SEM.

Fixation strengths with PMMA cement at 4, 12 and 26 weeks after surgery were 46.8 ± 18.9, 50.0 ± 24.7, and 58.2 ± 28.9 kgf (mean ±SD), respectively. Those with BA cement were 56.8 ± 26.1, 67.2 ± 19.2, and 72.8 ± 22.2 kgf, respectively. Fibrous tissue intervened between bone and PMMA cement but BA cement had bonded directly to bone at 12 and 26 weeks. This suggests that BA cement will be useful in providing long-lasting fixation of implants to bone under weight-bearing conditions.