Aims. This study reports the ten-year wear rates, incidence of osteolysis, clinical outcomes, and complications of a multicentre randomized controlled trial comparing oxidized zirconium (OxZr) versus cobalt-chrome (CoCr) femoral heads with
Aims. We propose a state-of-the-art temporary spacer, consisting of a cobalt-chrome (CoCr) femoral component and a gentamicin-eluting
We describe a cohort of patients with a high rate of mid-term failure following Kinemax Plus total knee replacement inserted between 1998 and 2001. This implant has been recorded as having a survival rate of 96% at ten years. However, in our series the survival rate was 75% at nine years. This was also significantly lower than that of subsequent consecutive series of PFC Sigma knee replacements performed by the same surgeon. No differences were found in the clinical and radiological parameters between the two groups. At revision the most striking finding was polyethylene wear. An independent analysis of the polyethylene components was therefore undertaken. Scanning electron microscopy revealed type 2 fusion defects in the
It has been suggested that the wear of
Oxidised zirconium (OxZi) has been developed
as an alternative bearing surface for femoral heads in total hip arthroplasty
(THA). This study has investigated polyethylene wear, functional
outcomes and complications, comparing OxZi and cobalt–chrome (CoCr)
as part of a three-arm, multicentre randomised controlled trial.
Patients undergoing THA from four institutions were prospectively
randomised into three groups. Group A received a CoCr femoral head
and highly cross-linked polyethylene (XLPE) liner; Group B received
an OxZi femoral head and XLPE liner; Group C received an OxZi femoral
head and
Periprosthetic joint infection (PJI) remains an extremely challenging complication. We have focused on this issue more over the last decade than previously, but there are still many unanswered questions. We now have a workable definition that everyone should align to, but we need to continue to focus on identifying the organisms involved. Surgical strategies are evolving and care is becoming more patient-centred. There are some good studies under way. There are, however, still numerous problems to resolve, and the challenge of PJI remains a major one for the orthopaedic community. This annotation provides some up-to-date thoughts about where we are, and the way forward. There is still scope for plenty of research in this area. Cite this article:
The aim of this study was to compare the migration of the femoral component, five years postoperatively, between patients with a highly cross-linked polyethylene (HXLPE) insert and those with a conventional polyethylene (PE) insert in an uncemented Triathlon fixed insert cruciate-retaining total knee arthroplasty (TKA). Secondary aims included clinical outcomes and patient-reported outcome measures (PROMs). We have previously reported the migration and outcome of the tibial components in these patients. A double-blinded randomized controlled trial was conducted including 96 TKAs. The migration of the femoral component was measured with radiostereometry (RSA) at three and six months and one, two, and five years postoperatively. PROMs were collected preoperatively and at all periods of follow-up.Aims
Methods
Isolated acetabular liner exchange with a highly crosslinked polyethylene (HXLPE) component is an option to address polyethylene wear and osteolysis following total hip arthroplasty (THA) in the presence of a well-fixed acetabular shell. The liner can be fixed either with the original locking mechanism or by being cemented within the acetabular component. Whether the method used for fixation of the HXLPE liner has any bearing on the long-term outcomes is still unclear. Data were retrieved for all patients who underwent isolated acetabular component liner exchange surgery with a HXLPE component in our institute between August 2000 and January 2015. Patients were classified according to the fixation method used (original locking mechanism (n = 36) or cemented (n = 50)). Survival and revision rates were compared. A total of 86 revisions were performed and the mean duration of follow-up was 13 years.Aims
Methods
The primary outcome was investigating differences in wear, as measured by femoral head penetration, between cross-linked vitamin E-diffused polyethylene (vE-PE) and cross-linked polyethylene (XLPE) acetabular component liners and between 32 and 36 mm head sizes at the ten-year follow-up. Secondary outcomes included acetabular component migration and patient-reported outcome measures (PROMs) such as the EuroQol five-dimension questionnaire, 36-Item Short-Form Health Survey, Harris Hip Score, and University of California, Los Angeles Activity Scale (UCLA). A single-blinded, multi-arm, 2 × 2 factorial randomized controlled trial was undertaken. Patients were recruited between May 2009 and April 2011. Radiostereometric analyses (RSAs) were performed from baseline to ten years. Of the 220 eligible patients, 116 underwent randomization, and 82 remained at the ten-year follow-up. Eligible patients were randomized into one of four interventions: vE-PE acetabular liner with either 32 or 36 mm femoral head, and XLPE acetabular liner with either 32 or 36 mm femoral head. Parameters were otherwise identical except for acetabular liner material and femoral head size.Aims
Methods
The aim of this study was to evaluate the performance of first-generation annealed highly cross-linked polyethylene (HXLPE) in cementless total hip arthroplasty (THA). We retrospectively evaluated 29 patients (35 hips) who underwent THA between December 2000 and February 2002. The survival rate was estimated using the Kaplan-Meier method. Hip joint function was evaluated using the Japanese Orthopaedic Association (JOA) score. Two-dimensional polyethylene wear was estimated using Martell’s Hip Analysis Suite. We calculated the wear rates between years 1 and 5, 5 and 10, 10 and 15, and 15 and final follow-up.Aims
Methods
The aims of this study were to evaluate wear on the surface of cobalt-chromium (CoCr) femoral components used in total knee arthroplasty (TKA) and compare the wear of these components with that of ceramic femoral components. Optical profilometry was used to evaluate surface roughness and to examine the features created by the wear process in a knee wear simulator. We developed a method of measuring surface changes on five CoCr femoral components and quantifying the loss of material from the articular surface during the wear process. We also examined the articular surface of three ceramic femoral components from a previous test for evidence of surface damage, and compared it with that of CoCr components.Aims
Methods
We present the results, in terms of survival, clinical outcome, and radiological appearance at 20 years, in a cohort of 225 cemented Exeter Universal femoral components (Stryker, Newbury, UK) implanted in 207 patients, at a district general hospital. All patients in this study had a total hip arthroplasty (THA) using an Exeter Universal femoral component with a cemented (n = 215) or cementless (n = 10) acetabular component. Clinical and radiological data were collected prospectively at one year, five years, and every five years thereafter. Patients lost to radiological and clinical follow-up (five) were cross-referenced with National Joint Registry (NJR) data and general practitioner (GP) records to assess whether they had undergone revision for any reason.Aims
Methods
The creep and wear behaviour of highly cross-linked polyethylene and standard polyethylene liners were examined in a prospective, double-blind randomised, controlled trial using radiostereometric analysis. We randomised 54 patients to receive hip replacements with either highly cross-linked polyethylene or standard liners and determined the three-dimensional penetration of the liners over three years. After three years the mean total penetration was 0.35 mm (SD 0.14) for the highly cross-linked polyethylene group and 0.45 mm (SD 0.19) for the standard group. The difference was statistically significant (p = 0.0184). From the pattern of penetration it was possible to discriminate creep from wear. Most (95%) of the creep occurred within six months of implantation and nearly all within the first year. There was no difference in the mean degree of creep between the two types of polyethylene (highly cross-linked polyethylene 0.26 mm, SD 0.17; standard 0.27 mm, SD 0.2; p = 0.83). There was, however, a significant difference (p = 0.012) in the mean wear rate (highly cross-linked polyethylene 0.03 mm/yr, SD 0.06; standard 0.07 mm/yr, SD 0.05). Creep and wear occurred in significantly different directions (p = 0.01); creep was predominantly proximal whereas wear was anterior, proximal and medial. We conclude that penetration in the first six months is creep-dominated, but after one year virtually all penetration is due to wear. Highly cross-linked polyethylene has a 60% lower rate of wear than standard polyethylene and therefore will probably perform better in the long term.
A retrospective longitudinal study was conducted to compare directly volumetric wear of retrieved polyethylene inserts to predicted volumetric wear modelled from individual gait mechanics of total knee arthroplasty (TKA) patients. In total, 11 retrieved polyethylene tibial inserts were matched with gait analysis testing performed on those patients. Volumetric wear on the articular surfaces was measured using a laser coordinate measure machine and autonomous reconstruction. Knee kinematics and kinetics from individual gait trials drove computational models to calculate medial and lateral tibiofemoral contact paths and forces. Sliding distance along the contact path, normal forces and implantation time were used as inputs to Archard’s equation of wear to predict volumetric wear from gait mechanics. Measured and modelled wear were compared for each component.Aims
Methods
The aim of this study was to evaluate the surface damage, the density of crosslinking, and oxidation in retrieved antioxidant-stabilized highly crosslinked polyethylene (A-XLPE) tibial inserts from total knee arthroplasty (TKA), and to compare the results with a matched cohort of standard remelted highly crosslinked polyethylene (XLPE) inserts. A total of 19 A-XLPE tibial inserts were retrieved during revision TKA and matched to 18 retrieved XLPE inserts according to the demographics of the patients, with a mean length of implantation of 15 months (1 to 42). The percentage areas of PE damage on the articular surfaces and the modes of damage were measured. The density of crosslinking of the PE and oxidation were measured at loaded and unloaded regions on these surfaces.Aims
Materials and Methods
The aim of this study was to describe temporal trends and survivorship of total hip arthroplasty (THA) in very young patients, aged ≤ 20 years. A descriptive observational study was undertaken using data from the National Joint Registry (NJR) for England, Wales, Northern Ireland and the Isle of Man between April 2003 and March 2017. All patients aged ≤ 20 years at the time of THA were included and the primary outcome was revision surgery. Descriptive statistics were used to summarize the data and Kaplan–Meier estimates calculated for the cumulative implant survival.Aims
Patients and Methods
This study aimed to evaluate implant survival of reverse hybrid
total hip arthroplasty (THA) at medium-term follow-up. A consecutive series of 1082 THAs in 982 patients with mean follow-up
of 7.9 years (5 to 11.3) is presented. Mean age was 69.2 years (21
to 94). Of these, 194 (17.9%) were in patients under 60 years, 663
(61.3%) in female patients and 348 (32.2%) performed by a trainee.
Head size was 28 mm in 953 hips (88.1%) or 32 mm in 129 hips (11.9%).
Survival analysis was performed and subgroups compared using log
rank tests.Aims
Patients and Methods
We sought to establish whether an oxidised zirconium (OxZr) femoral
component causes less loss of polyethylene volume than a cobalt
alloy (CoCr) femoral component in total knee arthroplasty. A total of 20 retrieved tibial inserts that had articulated with
OxZr components were matched with 20 inserts from CoCr articulations
for patient age, body mass index, length of implantation, and revision
diagnosis. Changes in dimensions of the articular surfaces were compared
with those of pristine inserts using laser scanning. The differences
in volume between the retrieved and pristine surfaces of the two
groups were calculated and compared.Aims
Materials and Methods
The aim of this systematic review was to report the rate of dislocation
following the use of dual mobility (DM) acetabular components in
primary and revision total hip arthroplasty (THA). A systematic review of the literature according to the Preferred
Reporting Items for Systematic Reviews and Meta-analyses guidelines
was performed. A comprehensive search of Pubmed/Medline, Cochrane
Library and Embase (Scopus) was conducted for English articles between
January 1974 and March 2016 using various combinations of the keywords “dual
mobility”, “dual-mobility”, “tripolar”, “double-mobility”, “double
mobility”, “hip”, “cup”, “socket”. The following data were extracted
by two investigators independently: demographics, whether the operation
was a primary or revision THA, length of follow-up, the design of
the components, diameter of the femoral head, and type of fixation
of the acetabular component.Aims
Materials and Methods
The leading indication for revision total hip
arthroplasty (THA) remains aseptic loosening owing to wear. The younger,
more active patients currently undergoing THA present unprecedented
demands on the bearings. Ceramic-on-ceramic (CoC) bearings have
consistently shown the lowest rates of wear. The recent advances,
especially involving alumina/zirconia composite ceramic, have led
to substantial improvements and good results Alumina/zirconia composite ceramics are extremely hard, scratch
resistant and biocompatible. They offer a low co-efficient of friction
and superior lubrication and lower rates of wear compared with other
bearings. The major disadvantage is the risk of fracture of the
ceramic. The new composite ceramic has reduced the risk of fracture
of the femoral head to 0.002%. The risk of fracture of the liner
is slightly higher (0.02%). Assuming that the components are introduced without impingement,
CoC bearings have major advantages over other bearings. Owing to
the superior hardness, they produce less third body wear and are
less vulnerable to intra-operative damage. The improved tribology means that CoC bearings are an excellent
choice for young, active patients requiring THA. Cite this article: