We made a semiquantitative study of the comparative histology of pseudomembranes from 12 loose cemented ceramic-ceramic and 18 metal-polyethylene total hip replacements. We found no significant difference in cellular reaction between the two groups, but there was a major difference in the origin of the particulate debris. In the metal-polyethylene group, polyethylene of articular origin was predominant, while in the ceramic-ceramic group the cellular reaction appeared to be a response to zirconia ceramic particles used to opacify cement used for fixation.

Isolation and characterisation of the debris showed that the zirconia particles formed the greatest proportion (76%) in ceramic-ceramic hips, while alumina debris of articular origin formed only 12%.

Our study has indicated that aseptic loosening of ceramic cups is not due to a response to debris generated at the articular interface, but to mechanical factors which lead to fragmentation of the cement.

Our study has determined the response of C-reactive protein (CRP) after total knee replacement (TKR). The peak level occurs on the second postoperative day and is significantly greater than that after total hip replacement (THR). The level returns to normal at similar times after both procedures. The physiological response to TKR as measured by the area under the CRP/ time curve is significantly greater than that after THR. Rising CRP levels after the third postoperative day may indicate a complication of surgery such as infection.

We revised seven alumina-blasted cementless hip prostheses (Ti-alloy stems, cp Ti threaded sockets) with low- or high-carbon Co-alloy bearings at a mean of 20.1 months after implantation because of pain and loosening. Histological examination of the retrieved periprosthetic tissues from two cases in which the implant was stable and three in which the socket was loose showed macrophages with basophilic granules containing metal and alumina wear particles and lymph-cell infiltrates. In one of the two cases of stem loosening the thickened neocapsule also contained definite lymphatic follicles and gross lymphocyte/plasma-cell infiltrates. Spectrometric determination of the concentration of elements in periprosthetic tissues from six cases was compared with that of joint capsules from five control patients undergoing primary hip surgery. In the revisions the mean concentration of implant-relevant elements was 693.85 μg/g dry tissue. In addition to Cr (15.2%), Co (4.3%), and Ti (10.3%), Al was predominant (68.1%) and all concentrations were significantly higher (p < 0.001) than those in the control tissues. The annual rates of linear wear were calculated for six implants. The mean value was 11.1 μm (heads 6.25 μm, inserts 4.82 μm). SEM/EDXA showed numerous fine scratches and deep furrows containing alumina particles in loosened sockets, and stems showed contamination with adhering or impacted alumina particles of between 2 and 50 μm in size.

From a prospective, cross-sectional survey of 402 patients who had a total hip (THR) or a total knee (TKR) replacement for idiopathic osteoarthritis (OA) at a major centre, we determined the prevalence of these replacements for idiopathic OA in their 1171 siblings and 376 spouses. Using spouses as controls, the relative risk of THR in siblings was 1.86 (95% CI 0.93 to 3.69). The relative risk for TKR in siblings v spouses was 4.8 (95% CI 0.64 to 36.4) whereas the risk for the combined outcome measure of THR or TKR was 2.32 (95% CI 1.22 to 4.43) when siblings and spouses over 64 years of age were compared. Using a threshold liability model (Falconer), the heritability of end-stage OA of the hip was estimated at 27%. The increased risks of joint replacement for severe, idiopathic OA which we found in siblings suggest that genetic influences are important in end-stage OA of the hip and knee

We have studied the effect of hydroxyapatite (HA) coating in 15 ovariectomised and 15 normal rats which had had a sham procedure. Twenty-four weeks after operation, HA-coated implants were inserted into the intramedullary canal of the right femur and uncoated implants into the left femur. The prostheses were removed four weeks after implantation. Twelve specimens in each group had mechanical push-out tests. Sagittal sections of the other three were evaluated by SEM. The bone mineral density (BMD) of the dissected left tibia was measured by dual-energy x-ray absorptiometry. The difference in BMD between the control and ovariectomised tibiae was 35.01 mg/cm. 2. (95% CI, 26.60 to 43.42). The push-out strength of the HA-coated implants was higher than that of the uncoated implants in both groups (p < 0.0001), but the HA-coated implants of the ovariectomised group had a reduction in push-out strength of 40.3% compared with the control group (p < 0.0001). Our findings suggest that HA-coated implants may improve the fixation of a cementless total hip prosthesis but that the presence of osteoporosis may limit the magnitude of this benefit

Our aim was to determine if the serum levels of bone-resorbing cytokines (IL-1β, TNF-α, IL-6, GM-CSF) are altered in patients with aseptic loosening of a total hip prosthesis, and if such levels are influenced by the type of implant. We determined cytokine levels in sera from 35 patients before revision for failed total hip arthroplasty and compared them with those in 25 healthy donors. We also assessed the soluble receptor of interleukin-2 (sIL-2r) in serum as an indication of a specific immune reaction against the implant. Our findings showed that the sIL-2r and TNF-α serum level did not change. The IL-6 level was not significantly altered, but was higher in patients with TiAlV prostheses than in those with a CrCoMo implant and in patients with cemented prostheses. The IL-1β level was found to be higher in those with a TiAlV cemented prosthesis than in the control group (p = 0.0001) and other groups of patients (p = 0.003 v uncemented TiAlV, p = 0.01 v cemented CrCoMo, p = 0.001 v uncemented CrCoMo). The GM-CSF level significantly increased in patients compared with healthy subjects (p = 0.008), and it was higher in those with cemented than with uncemented implants (p = 0.01). Only patients with cementless CrCoMo prostheses had levels of GM-CSF similar to those of the control group. The highest GM-CSF concentrations were observed in patients treated with non-steroidal anti-inflammatory drugs (NSAIDs) in the last months before revision (p = 0.04). In addition, when massive osteolysis was observed, the level of GM-CSF tended to decrease to that of the control group

High-intensity narrow-spectrum (HINS) light is a novel violet-blue light inactivation technology which kills bacteria through a photodynamic process, and has been shown to have bactericidal activity against a wide range of species. Specimens from patients with infected hip and knee arthroplasties were collected over a one-year period (1 May 2009 to 30 April 2010). A range of these microbial isolates were tested for sensitivity to HINS-light. During testing, suspensions of the pathogens were exposed to increasing doses of HINS-light (of 123mW/cm² irradiance). Non-light exposed control samples were also used. The samples were then plated onto agar plates and incubated at 37°C for 24 hours before enumeration. Complete inactivation (greater than 4-log₁₀ reduction) was achieved for all of the isolates. The typical inactivation curve showed a slow initial reaction followed by a rapid period of inactivation. The doses of HINS-light required ranged between 118 and 2214 J/cm². Gram-positive bacteria were generally found to be more susceptible than Gram-negative.

As HINS-light uses visible wavelengths, it can be safely used in the presence of patients and staff. This unique feature could lead to its possible use in the prevention of infection during surgery and post-operative dressing changes.

Cite this article: Bone Joint J 2015;97-B:283–8.

A cadaver study using six pairs of lower limbs was conducted to investigate the accuracy of computer navigation and standard instrumentation for the placement of the Birmingham Hip Resurfacing femoral component. The aim was to place all the femoral components with a stem-shaft angle of 135°.

The mean stem-shaft angle obtained in the standard instrumentation group was 127.7° (120° to 132°), compared with 133.3° (131° to 139°) in the computer navigation group (p = 0.03). The scatter obtained with computer-assisted navigation was approximately half that found using the conventional jig.

Computer navigation was more accurate and more consistent in its placement of the femoral component than standard instrumentation. We suggest that image-free computer-assisted navigation may have an application in aligning the femoral component during hip resurfacing.

The complications of impaction bone grafting in revision hip replacement includes fracture of the femur and subsidence of the prosthesis. In this in vitro study we aimed to investigate whether the use of vibration, combined with a perforated tamp during the compaction of morsellised allograft would reduce peak loads and hoop strains in the femur as a surrogate marker of the risk of fracture and whether it would also improve graft compaction and prosthetic stability.

We found that the peak loads and hoop strains transmitted to the femoral cortex during graft compaction and subsidence of the stem in subsequent mechanical testing were reduced. This innovative technique has the potential to reduce the risk of intra-operative fracture and to improve graft compaction and therefore prosthetic stability.