Aims. There are limited published data detailing the volumetric material loss from tapers of conventional metal-on-polyethylene (MoP) total hip arthroplasties (THAs). Our aim was to address this by comparing the taper wear rates measured in an explanted cohort of the widely used Exeter THA with those measured in a group of metal-on-metal (MoM) THAs. Patients and Methods. We examined an existing retrieval database to identify all Exeter V40 and Universal MoP THAs. Volumetric wear analysis of the taper surfaces was conducted using previously validated methodology. These values were compared with those obtained from a series of MoM THAs using non-parametric statistical methodology. A number of patient and device variables were accounted for using multiple regression modelling. Results. A total of 95 Exeter MoP and 249 MoM THAs were examined. The median volumetric loss from the MoM cohort was over four times larger than that from the MoP cohort (1.01 mm. 3. vs 0.23 mm. 3. , p < 0.001), despite a significantly shorter median period in vivo for the MoM group (48 months vs 90 months, p < 0.001). Multiple regression modelling indicated that the dominant variables leading to greater female taper material loss were bearing diameter (p < 0.001), larger female taper angles (p < 0.001), and male titanium stem tapers (p < 0.001). Conclusion. Consistent with the long-term clinical success of the device, the volumetric material loss from Exeter femoral head tapers was, in general, small compared with that from larger-diameter MoM head tapers. Cite this article: Bone Joint J 2018;100-B:1310–9

Complications involving the patellofemoral joint, caused by malrotation of the femoral component during total knee replacement, are an important cause of persistent pain and failure leading to revision surgery. The aim of this study was to determine and quantify the influence of femoral component malrotation on patellofemoral wear, and to determine whether or not there is a difference in the rate of wear of the patellar component when articulated against oxidised zirconium (OxZr) and cobalt-chrome (CoCr) components. An in vitro method was used to simulate patellar maltracking for both materials. Both rates of wear and changes in height on the patellar articular surface were measured. The mean rates of wear measured were very small compared to standard tibiofemoral wear rates. When data for each femoral component material were pooled, the mean rate of wear was 0.19 mm. 3. /Mcycle (. sd. 0.21) for OxZr and 0.34 mm. 3. /Mcycle (. sd. 0.335) for CoCr. The largest change in height on each patella varied from -0.05 mm to -0.33 mm over the different configurations. The results suggest that patellar maltracking due to an internally rotated femoral component leads to an increased mean patellar wear. Although not statistically significant, the mean wear production may be lower for OxZr than for CoCr components

Aims. Distal radial fractures are the most common fracture sustained by the adult population. Most can be treated using cast immobilization without the need for surgery. The aim of this study was to assess the feasibility of a definitive trial comparing the commonly used fibreglass cast immobilization with an alternative product called Woodcast. Woodcast is a biodegradable casting material with theoretical benefits in terms of patient comfort as well as benefits to the environment. Methods. This was a multicentre, two-arm, open-label, parallel-group randomized controlled feasibility trial. Patients with a fracture of the distal radius aged 16 years and over were recruited from four centres in the UK and randomized (1:1) to receive a Woodcast or fibreglass cast. Data were collected on participant recruitment and retention, clinical efficacy, safety, and patient acceptability. Results. Over an eight-month period, 883 patients were screened, 271 were found to be eligible, and 120 were randomized. Patient-reported outcome measures were available for 116 (97%) of participants at five weeks and 99 (83%) at three months. Clinical outcomes and patient acceptability were similar between the two interventions and no serious adverse events were reported in either intervention arm. Conclusion. Both interventions were deemed efficacious and safe in the cohort studied. This study showed that a definitive study comparing Woodcast and fibreglass was feasible in terms of patient recruitment and retention. Cite this article: Bone Joint J 2020;102-B(1):48–54

We reviewed the literature on the currently available choices of bearing surface in total hip replacement (THR). We present a detailed description of the properties of articulating surfaces review the understanding of the advantages and disadvantages of existing bearing couples. Recent technological developments in the field of polyethylene and ceramics have altered the risk of fracture and the rate of wear, although the use of metal-on-metal bearings has largely fallen out of favour, owing to concerns about reactions to metal debris. As expected, all bearing surface combinations have advantages and disadvantages. A patient-based approach is recommended, balancing the risks of different options against an individual’s functional demands.

Cite this article: Bone Joint J 2014;96-B:147–56.

In a prospective, randomised study on the repair of tears of the rotator cuff we compared the clinical results of two suture techniques for which different suture materials were used. We prospectively randomised 100 patients with tears of the rotator cuff into two groups. Group 1 had transosseous repair with No. 3 Ethibond using modified Mason-Allen sutures and group 2 had transosseous repair with 1.0 mm polydioxanone cord using modified Kessler sutures. After 24 to 30 months the patients were evaluated clinically using the Constant score and by ultrasonography. Of the 100 patients, 92 completed the study. No significant statistical difference was seen between the two groups: Constant score, 91% vs 92%; rate of further tear, 18% vs 22%; and revision, 4% vs 4%. In cases of further tear the outcome in group 2 did not differ from that for the intact repairs (91% vs 91%), but in group 1 it was significantly worse (94% vs 77%, p = 0.005). Overall, seven patients had complications which required revision surgery, in four for pain (two in each group) and in three for infection (two in group 1 and one in group 2)

The early failure and revision of bimodular primary total hip arthroplasty prostheses requires the identification of the risk factors for material loss and wear at the taper junctions through taper wear analysis. Deviations in taper geometries between revised and pristine modular neck tapers were determined using high resolution tactile measurements. A new algorithm was developed and validated to allow the quantitative analysis of material loss, complementing the standard visual inspection currently used. The algorithm was applied to a sample of 27 retrievals (in situ from 2.9 to 38.1 months) of the withdrawn Rejuvenate modular prosthesis. The mean wear volumes on the flat distal neck piece taper was 3.35 mm. 3. (0.55 to 7.57), mainly occurring in a characteristic pattern in areas with high mechanical loading. Wear volume tended to increase with time to revision (r² = 0.423, p = 0.001). Implant and patient specific data (offset, stem size, patient’s mass, age and body mass index) did not correlate with the amount of material loss observed (p >  0.078). Bilaterally revised implants showed higher amounts of combined total material loss and similar wear patterns on both sides. The consistent wear pattern found in this study has not been reported previously, suggesting that the device design and materials are associated with the failure of this prosthesis. Cite this article: Bone Joint J 2015;97-B:1350–7

The Fairbank Collection in the Radiology Department of the Royal National Orthopaedic Hospital contains details of 15 patients in the section labelled "Metaphysial Dysplasia and Dysostosis". This material has been reviewed, long-term follow-up of the patients carried out and the diagnosis revised, where indicated, according to current concepts. Of the 15 patients, all children, seven had recognisable bone dysplasias. The remaining eight, all listed under the heading "metaphysial fragility", had the characteristic radiographic features of "battered" babies

Aims

Calcium sulphate (CaSO₄) is a resorbable material that can be used simultaneously as filler of a dead space and as a carrier for the local application of antibiotics. Our aim was to describe the systemic exposure and the wound fluid concentrations of vancomycin in patients treated with vancomycin-loaded CaSO₄ as an adjunct to the routine therapy of bone and joint infections.

It has been suggested that the wear of ultra-high molecular weight polyethylene (UHMWPE) in total hip replacement is substantially reduced when the femoral head is ceramic rather than metal. However, studies of alumina and zirconia ceramic femoral heads on the penetration of an UHMWPE liner in vivo have given conflicting results.

The purpose of this study was to examine the surface characteristics of 30 alumina and 24 zirconia ceramic femoral heads and to identify any phase transformation in the zirconia heads. We also studied the penetration rate of alumina and zirconia heads into contemporary UHMWPE liners. The alumina heads had been implanted for a mean of 11.3 years (8.1 to 16.2) and zirconia heads for a mean of 9.8 years (7.5 to 15).

The mean surface roughness values of the explanted alumina heads (Ra 40.12 nm and Rpm 578.34 nm) were similar to those for the explanted zirconia heads (Ra 36.21 nm and Rpm 607.34 nm). The mean value of the monoclinic phase of two control zirconia heads was 1% (0.8% to 1.5%) and 1.2% (0.9% to 1.3%), respectively. The mean value of the monoclinic phase of 24 explanted zirconia heads was 7.3% (1% to 26%).

In the alumina group, the mean linear penetration rate of the UMWPE liner was 0.10 mm/yr (0.09 to 0.12) in hips with low Ra and Rpm values (13.22 nm and 85.91 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.13 mm/yr (0.07 to 0.23) in hips with high Ra and Rpm values (198.72 nm and 1329 nm, respectively). This difference was significant (p = 0.041).

In the zirconia head group, the mean linear penetration rate of the UHMWPE liner was 0.09 mm/yr (0.07 to 0.14) in hips with low Ra and Rpm values (12.78 nm and 92.99 nm, respectively). The mean linear penetration rate of the UHMWPE liner was 0.12 mm/yr (0.08 to 0.22) in hips with high Ra and Rpm values (199.21 nm and 1381 nm, respectively). This difference was significant (p = 0.039).

The explanted zirconia heads which had a minimal phase transformation had similar surface roughness and a similar penetration rate of UHMWPE liner as the explanted alumina head.

We studied the biomechanical behaviour of three sliding fixation devices for trochanteric femoral fractures. These were a titanium alloy sideplate and lag screw, a titanium alloy sideplate and dome plunger with cement augmentation, and a stainless-steel sideplate and lag screw. We used 18 mildly osteoporotic cadaver femora, randomly assigned to one of the three fixation groups. Four displacement and two strain gauges were fixed to each specimen, and each femur was first tested intact (control), then as a two-part fracture and then as a four-part intertrochanteric fracture. A range of physiological loads was applied to determine load-bearing, load-sharing and head displacement. The four-part-fracture specimens were subsequently tested to failure to determine maximum fixation strengths and modes of failure. The dome-plunger group failed at a load 50% higher than that of the stainless-steel lag-screw group (p < 0.05) and at a load 20% higher than that of the titanium-alloy lag-screw group (NS). All 12 lag-screw specimens failed by cut-out through the femoral head or neck, but none of the dome-plunger group showed movement within the femoral head when tested to failure. Strain-gauge analysis showed that the dome plunger produced considerably less strain in the inferior neck and calcar region than either of the lag screws. Inferior displacement of the femoral head was greatest for the dome-plunger group, and was due to sliding of the plunger. The dome plunger with cement augmentation was able to support higher loads and did not fail by cut-out through the femoral head.(ABSTRACT TRUNCATED AT 250 WORDS)

The shallow lateral recesses of the trefoil shape of the lumbar spinal canal have been implicated in the production of the spinal stenosis syndrome. In the present study, 485 skeletons of South African Blacks and Whites were examined in order to establish the incidence and possible genesis of the trefoil configuration. The overall incidence was 14 per cent, with little variation between the sexes or races. The incidence was not related to increasing age, measured stenosis of the spinal canal or osteophytosis. Of 74 trefoil-shaped vertebrae, 68 (92 per cent) were found at the fifth lumbar level. It is suggested that the trefoil configuration is a common non-pathological condition, usually of the fifth lumbar vertebral canal, and is probably a developmental variation of normal anatomy.

Aims. The aims of this study were to evaluate wear on the surface of cobalt-chromium (CoCr) femoral components used in total knee arthroplasty (TKA) and compare the wear of these components with that of ceramic femoral components. Methods. Optical profilometry was used to evaluate surface roughness and to examine the features created by the wear process in a knee wear simulator. We developed a method of measuring surface changes on five CoCr femoral components and quantifying the loss of material from the articular surface during the wear process. We also examined the articular surface of three ceramic femoral components from a previous test for evidence of surface damage, and compared it with that of CoCr components. Results. We found that the surface roughness of CoCr components rapidly increased during the first 1,000 wear cycles, then reached a steady state, but material loss from the surface continued at a rate of 1,778,000 μm. 3. per million cycles as carbides were removed from its matrix. These carbides formed third-body wear particles, leading to the formation of new scratches even as older scratches were worn away. In contrast, no scratching, loss of material, or other surface damage, when evaluated with one nanometer resolution, was found on the surface of the ceramic components after a 15 M wear cycle test. Conclusion. This study showed wear and loss of CoCr material from scratching and microabrasive wear in TKA. The material loss from the surface continued in a linear relationship with increasing cycles. We also found the absence of scratching and roughening of ceramic femoral components in simulated wear, suggesting an advantage in wear rate and avoiding metal sensitivity. This may have implications in the management of persistent pain after TKA. Cite this article: Bone Joint J 2021;103-B(6 Supple A):94–101

Aims. The survival of humeral hemiarthroplasties in patients with relatively intact glenoid cartilage could theoretically be extended by minimizing the associated postoperative glenoid erosion. Ceramic has gained attention as an alternative to metal as a material for hemiarthroplasties because of its superior tribological properties. The aim of this study was to assess the in vitro wear performance of ceramic and metal humeral hemiarthroplasties on natural glenoids. Methods. Intact right cadaveric shoulders from donors aged between 50 and 65 years were assigned to a ceramic group (n = 8, four male cadavers) and a metal group (n = 9, four male cadavers). A dedicated shoulder wear simulator was used to simulate daily activity by replicating the relevant joint motion and loading profiles. During testing, the joint was kept lubricated with diluted calf serum at room temperature. Each test of wear was performed for 500,000 cycles at 1.2 Hz. At intervals of 125,000 cycles, micro-CT scans of each glenoid were taken to characterize and quantify glenoid wear by calculating the change in the thickness of its articular cartilage. Results. At the completion of the wear test, the total thickness of the cartilage had significantly decreased in both the ceramic and metal groups, by 27% (p = 0.019) and 29% (p = 0.008), respectively. However, the differences between the two were not significant (p = 0.606) and the patterns of wear in the specimens were unpredictable. No significant correlation was found between cartilage wear and various factors, including age, sex, the size of the humeral head, joint mismatch, the thickness of the native cartilage, and the surface roughness (all p > 0.05). Conclusion. Although ceramic has better tribological properties than metal, we did not find evidence that its use in hemiarthroplasty of the shoulder in patients with healthy cartilage is a better alternative than conventional metal humeral heads. Cite this article: Bone Joint J 2024;106-B(11):1273–1283

Aims. The primary outcome was investigating differences in wear, as measured by femoral head penetration, between cross-linked vitamin E-diffused polyethylene (vE-PE) and cross-linked polyethylene (XLPE) acetabular component liners and between 32 and 36 mm head sizes at the ten-year follow-up. Secondary outcomes included acetabular component migration and patient-reported outcome measures (PROMs) such as the EuroQol five-dimension questionnaire, 36-Item Short-Form Health Survey, Harris Hip Score, and University of California, Los Angeles Activity Scale (UCLA). Methods. A single-blinded, multi-arm, 2 × 2 factorial randomized controlled trial was undertaken. Patients were recruited between May 2009 and April 2011. Radiostereometric analyses (RSAs) were performed from baseline to ten years. Of the 220 eligible patients, 116 underwent randomization, and 82 remained at the ten-year follow-up. Eligible patients were randomized into one of four interventions: vE-PE acetabular liner with either 32 or 36 mm femoral head, and XLPE acetabular liner with either 32 or 36 mm femoral head. Parameters were otherwise identical except for acetabular liner material and femoral head size. Results. A total of 116 patients participated, of whom 77 were male. The median ages of the vE-PE 32 mm and 36 mm groups were 65 (interquartile range (IQR) 57 to 67) and 63 years (IQR 56 to 66), respectively, and of the XLPE 32 mm and 36 mm groups were 64 (IQR 58 to 66) and 61 years (IQR 54 to 66), respectively. Mean total head penetration was significantly lower into vE-PE acetabular liner groups than into XLPE acetabular liner groups (-0.219 mm (95% confidence interval -0.348 to -0.090); p = 0.001). There were no differences in wear according to head size, acetabular component migration, or PROMs, except for UCLA. There were no cases of aseptic loosening or failures requiring revision at long-term follow-up. Conclusion. Significantly lower wear was observed in vE-PE acetabular liners than in XLPE acetabular liners. No difference in wear was observed between different head size or PROMs except for the UCLA at ten years. Cite this article: Bone Joint J 2023;105-B(10):1052–1059