Free radicals, such as reactive oxygen species (ROS) which are released abruptly after deflation of an ischaemic tourniquet, cause reperfusion injuries. Ischaemic precondition (IPC), however, can reduce the injury. In clinical practice, the sequential application and release of tourniquets is often used in bilateral total knee replacement (TKR) to obtain a clearer operative field, but the effects on the production of free radicals and lipid peroxidation have not been studied. In this study, we have observed the production of free radicals and the subsequent lipid peroxidation in bilateral TKR with sequential application of a tourniquet to examine the effect of IPC. Patients undergoing elective TKR under intrathecal anaesthesia were studied. Blood samples were obtained after spinal anaesthesia, one minute before and five and 20 minutes after release of each tourniquet. We used the lucigenin chemiluminescence analysis and the phosphatidylcholine hydroperoxide (PCOOH) assay to measure the production of ROS and lipid peroxidation. Our results showed that production of ROS significantly increased at five and 20 minutes after release of the first tourniquet and at five minutes after release of the second tourniquet, but returned to normal at 20 minutes after the second reperfusion. The peak production of ROS was at 20 minutes after the first reperfusion; lipid peroxidation did not change significantly. We conclude that in spite of significant production of ROS after the release of tourniquet, the IPC phenomenon occurs during bilateral TKR with sequential application of a tourniquet

Secondary sterilisation of allograft bone by gamma irradiation is common, but the conditions under which it is performed vary between tissue banks. Some do so at room temperature, others while the bone is frozen. Bone is made brittle by irradiation because of the destruction of collagen alpha chains, probably mediated by free radicals generated from water molecules. Freezing reduces the mobility of water molecules and may therefore decrease the production of free radicals. We found that bone irradiated at −78°C was less brittle and had less collagen damage than when irradiated at room temperature. These findings may have implications for bone-banking

Aims

The primary outcome was investigating differences in wear, as measured by femoral head penetration, between cross-linked vitamin E-diffused polyethylene (vE-PE) and cross-linked polyethylene (XLPE) acetabular component liners and between 32 and 36 mm head sizes at the ten-year follow-up. Secondary outcomes included acetabular component migration and patient-reported outcome measures (PROMs) such as the EuroQol five-dimension questionnaire, 36-Item Short-Form Health Survey, Harris Hip Score, and University of California, Los Angeles Activity Scale (UCLA).

Bone necrosis adjacent to self-curing polymethylmethacrylate is a matter of accepted fact. Among the possible causes are mechanical and vascular damage from the preparation of the bone cavity, chemical damage from the monomer and free radicals in the cement dough, and thermal damage from the heat of polymerisation, occurring in this order. Consideration of the tissue reaction to this material, theoretical calculation of the heat output from polymerising acrylic and interface temperature proffiles, experimental observations of interface temperatures and maximal temperatures at polymerisation, together with clinical observations, all lead to the view that the bone necrosis is not a consequence of thermal damage, which is unlikely to be a cause of failure of prosthetic fixation. Temperatures recorded from within polymerising acrylic masses are related primarily to the amount of monomer polymerising and are of no clinical significance in the fixation of prostheses. Interface temperatures are related primarily to the surface area of the interface and the thermal characteristics of the cooler material

Sterilisation by gamma irradiation in the presence of air causes free radicals generated in polyethylene (PE) to react with oxygen, which could lead to loss of physical properties and reduction in fatigue strength. Tissue retrieved from failed total hip replacements often has large quantities of particulate PE and most particles associated with peri-implant osteolysis are oxidised. Consequently, an understanding of the cellular responses of oxidised PE particles may lead to clarification of the pathogenesis of osteolysis and aseptic loosening. We have used the agarose system to demonstrate the differential effects of oxidised and non-oxidised PE particles on the release of proinflammatory products such as interleukin-1β (IL-1β), IL-6, and tumour necrosis factor-α (TNF-α) from monocytes/ macrophages (M/M). Oxidised PE particles were shown to stimulate human M/M to phagocytose and to release cytokines. Oxidation may alter the surface chemistry of the particles and enhance the response to specific membrane receptors on macrophages, such as scavenger-type receptors

Aims

The aim of this study was to evaluate the performance of first-generation annealed highly cross-linked polyethylene (HXLPE) in cementless total hip arthroplasty (THA).

Aims

Vitamin E-infused highly crosslinked polyethylene (VEPE) has been introduced into total hip arthroplasty (THA) with the aim of further improving the wear characteristics of moderately and highly crosslinked polyethylenes (ModXLPE and HXLPE). There are few studies analyzing the outcomes of vitamin E-infused components in cemented arthroplasty, though early acetabular component migration has been reported. The aim of this study was to measure five-year polyethylene wear and acetabular component stability of a cemented VEPE acetabular component compared with a ModXLPE cemented acetabular component.

Aims

The most frequent indication for revision surgery in total hip arthroplasty (THA) is aseptic loosening. Aseptic loosening is associated with polyethylene liner wear, and wear may be reduced by using vitamin E-doped liners. The primary objective of this study was to compare proximal femoral head penetration into the liner between a) two cross-linked polyethylene (XLPE) liners (vitamin E-doped (vE-PE)) versus standard XLPE liners, and b) two modular femoral head diameters (32 mm and 36 mm).

Aims

We aimed to investigate if the use of the largest possible cobalt-chromium head articulating with polyethylene acetabular inserts would increase the in vivo wear rate in total hip arthroplasty.

Aims

Vitamin E-diffused, highly crosslinked polyethylene (VEPE) and porous titanium-coated (PTC) shells were introduced in total hip arthroplasty (THA) to reduce the risk of aseptic loosening. The purpose of this study was: 1) to compare the wear properties of VEPE to moderately crosslinked polyethylene; 2) to assess the stability of PTC shells; and 3) to report their clinical outcomes at seven years.

Aims

The use of vitamin E-infused highly crosslinked polyethylene (HXLPE) in total knee prostheses is controversial. In this paper we have compared the clinical and radiological results between conventional polyethylene and vitamin E-infused HXLPE inserts in total knee arthroplasty (TKA).

Aims

The aim of this study was to identify the effect of the manufacturing characteristics of polyethylene acetabular liners on the survival of cementless and hybrid total hip arthroplasty (THA).

Aims

The primary aim of this study was to compare the wear properties of vitamin E-diffused, highly crosslinked polyethylene (VEPE) and one formulation of moderately crosslinked and mechanically annealed ultra-high molecular weight polyethylene (ModXLPE) in patients five years after primary total hip arthroplasty (THA). The secondary aim was to assess the clinical results of patients treated with VEPE by evaluating patient-reported outcome measures (PROMs), radiological evidence of fixation, and the incidence of mechanical failure.

Aims

The purpose of this study is to examine six types of bearing surfaces implanted at a single institution over three decades to determine whether the reasons for revision vary among the groups and how long it takes to identify differences in survival.

Advances in polyethylene (PE) in total hip arthroplasty have led to interest and increased use of highly crosslinked PE (HXLPE) in total knee arthroplasty (TKA). Biomechanical data suggest improved wear characteristics for HXLPE inserts over conventional PE in TKA. Short-term results from registry data and few clinical trials are promising. Our aim is to present a review of the history of HXLPEs, the use of HXLPE inserts in TKA, concerns regarding potential mechanical complications, and a thorough review of the available biomechanical and clinical data.

Cite this article: Bone Joint J 2017;99-B:996–1002.

Aims

The objective of this five-year prospective, blinded, randomised controlled trial (RCT) was to compare femoral head penetration into a vitamin E diffused highly cross-linked polyethylene (HXLPE) liner with penetration into a medium cross-linked polyethylene control liner using radiostereometric analysis.

Aims

The aim of this study was to evaluate the surface damage, the density of crosslinking, and oxidation in retrieved antioxidant-stabilized highly crosslinked polyethylene (A-XLPE) tibial inserts from total knee arthroplasty (TKA), and to compare the results with a matched cohort of standard remelted highly crosslinked polyethylene (XLPE) inserts.

Aims

There is insufficient evidence to recommend the use of alternative polyethylene bearings in modular, fixed-bearing total knee arthroplasty (TKA). The purpose of this study was to compare standard polyethylene (SP) and highly crosslinked polyethylene (XLP) tibial liners in posterior-stabilized TKA, with osteolysis as the primary outcome and clinical results and the rate of re-operation as the secondary outcomes.

Polyethylene wear debris can cause osteolysis and the failure of total hip arthroplasty. We present the five-year wear rates of a highly cross-linked polyethylene (X3) bearing surface when used in conjunction with a 36 mm ceramic femoral head.

This was a prospective study of a cohort of 100 THAs in 93 patients. Pain and activity scores were measured pre- and post-operatively. Femoral head penetration was measured at two months, one year, two years and at five years using validated edge-detecting software (PolyWare Auto).

At a mean of 5.08 years (3.93 to 6.01), 85 hips in 78 patients were available for study. The mean age of these patients was 59.08 years (42 to 73, the mean age of males (n = 34) was 59.15 years, and females (n = 44) was 59.02 years). All patients had significant improvement in their functional scores (p < 0.001). The steady state two-dimensional linear wear rate was 0.109 mm/year. The steady state volumetric wear rate was 29.61 mm³/year. No significant correlation was found between rate of wear and age (p = 0.34), acetabular component size (p = 0.12) or clinical score (p = 0.74).

Our study shows low steady state wear rates at five years in X3 highly cross-linked polyethylene in conjunction with a 36 mm ceramic femoral head. The linear wear rate was almost identical to the osteolysis threshold of 0.1 mm/year recommended in the literature.

Cite this article: Bone Joint J 2015;97-B:1470–4.