We exposed human macrophages isolated from the peripheral blood of healthy donors to metal and bone-cement particles from 0.2 to 10 μm in size. Zymography showed that macrophages exposed to titanium alloy and polymethylmethacrylate (PMMA) particles released a 92- and 72-kDa gelatinase in a dose- and time-dependent manner. Western immunoblotting confirmed that the 92- and 72-kDa gelatinolytic activities corresponded to matrix metalloproteinase-9 and matrix metalloproteinase-2 (MMP-9, MMP-2), respectively. Western immunoblotting also indicated that titanium alloy and PMMA particles increased the release of MMP-1. Northern blotting showed elevated mRNA signal levels for MMP-1, MMP-2, and MMP-9 after exposure to both types of particle. Collagenolytic activity also increased in the macrophage culture medium in response to both types of particle. Our findings support the hypothesis that macrophages release MMPs in proportion to the amount of particulate debris within periprosthetic tissues

We used a rat model in vivo to study the effects of particulate bone cements at the bone-implant interface. A ceramic pin was implanted into the tibiae of 48 rats. Three types of particle of clinically relevant size were produced from one bone-cement base without radio-opacifier, with zirconium dioxide (ZrO. 2. ) and with barium sulphate (BaSO. 4. ). The rats were randomly assigned to four groups to receive one of the three bone cements or normal saline with 2% v/v Sprague-Dawley serum as the control. A total of 10. 9. particles was injected into the knee at 8, 10 and 12 weeks after the original surgery. The animals were killed at 14 weeks and the tibiae processed for histomorphometry. The area of fibrous tissue and the gap between the implant and bone were measured using image analysis. All three types of particle were associated with a larger area of bone resorption than the control. Only in the case of the BaSO. 4. -containing cement did this reach statistical significance (p = 0.01). Particles of bone cement appear to promote osteolysis at the bone-implant interface and this effect is most marked when BaSO. 4. is used as the radiopaque agent

Clinical experience indicates the beneficial effects of antibiotic-loaded bone cement. Although in vitro studies have shown the formation of a biofilm on its surface they have not considered the gap between the cement and the bone. We have investigated bacterial survival in that gap. Samples with gaps 200 μm wide were made of different bone cements. These were stored dry (‘pre-elution’) or submersed in phosphate-buffered saline to simulate the initial release of gentamicin (‘post-elution’). The gaps were subsequently inoculated with bacteria, which had been isolated from infected orthopaedic prostheses and assessed for their sensitivity to gentamicin. Bacterial survival was measured 24 hours after inoculation. All the strains survived in plain cements. In the pre-elution gentamicin-loaded cements only the most gentamicin-resistant strain, CN5115, survived, but in post-elution samples more strains did so, depending on the cement tested. Although high concentrations of gentamicin were demonstrated in the gaps only the gentamicin-sensitive strains were killed. This could explain the increased prevalence of gentamicin-resistant infections which are seen clinically.