Aims. The Birmingham Hip Resurfacing (BHR) was introduced in 1997 to address the needs of young active patients using a historically proven large-diameter metal-on-metal (MoM) bearing. A single designer surgeon’s consecutive series of 130 patients (144 hips) was previously reported at five and ten years, reporting three and ten failures, respectively. The aim of this study was to extend the follow-up of this original cohort at 25 years. Methods. The study extends the reporting on the first consecutive 144 resurfacing procedures in 130 patients for all indications. All operations were undertaken between August 1997 and May 1998. The mean age at operation was 52.1 years (SD 9.93; 17 to 76), and included 37 female patients (28.5%). Failure was defined as revision of either component for any reason. Kaplan-Meier survival analysis was performed. Routine follow-up with serum metal ion levels, radiographs, and Oxford Hip Scores (OHSs) was undertaken. Results. Overall implant survival was 83.50% (95% confidence interval (CI) 0.79 to 0.90) at 25 years, and the number at risk was 79. Survival in male patients at 25 years was 89.5% (95% CI 0.83 to 0.96) compared to 66.9% for female patients (95% CI 0.51 to 0.83). Ten additional failures occurred in the period of ten to 25 years. These involved an adverse reaction to metal debris in four patients, a periprosthetic femoral neck fracture affecting five patients, and aseptic loosening in one patient. The median chromium levels were 49.50 nmol/l (interquartile range (IQR) 34 to 70), and the median cobalt serum levels were 42 nmol/l (IQR 24.50 to 71.25). The median OHS at last follow-up was 35 (IQR 10 to 48). During the 25-year study period, 29 patients died. Patient survival at 25 years was 75.10% (95% CI 0.67 to 0.83). Conclusion. This study demonstrates that MoM hip resurfacing using the BHR provides a durable alternative to total hip arthroplasty (THA), particularly in younger male patients with osteoarthritis wishing to maintain a high level of function. These results compare favourably to the best results for THAs. Cite this article: Bone Joint J 2024;106-B(6):540–547

The aim of this study was to establish the natural course of unrevised asymptomatic pseudotumours after metal-on-metal (MoM) hip resurfacing during a six- to 12-month follow-up period. We used repeated metal artefact reduction sequence (MARS)-magnetic resonance imaging (MRI), serum metal ion analysis and clinical examination to study 14 unrevised hips (mean patient age 52.7 years, 46 to 68, 5 female, 7 male) with a pseudotumour and 23 hips (mean patient age 52.8 years, 38 to 69, 7 female, 16 male) without a pseudotumour. The mean post-operative time to the first MARS-MRI scan was 4.3 years (2.2 to 8.3), and mean time between the first and second MARS-MRI scan was eight months (6 to 12). At the second MRI scan, the grade of severity of the pseudotumour had not changed in 35 hips. One new pseudotumour (Anderson C2 score, moderate) was observed, and one pseudotumour was downgraded from C2 (moderate) to C1 (mild). In general, the characteristics of the pseudotumours hardly changed. Repeated MARS-MRI scans within one year in patients with asymptomatic pseudotumours after MoM hip resurfacing showed little or no variation. In 23 patients without pseudotumour, one new asymptomatic pseudotumour was detected. This is the first longitudinal study on the natural history of pseudotumours using MARS-MRI scans in hip resurfacing, and mirrors recent results for 28 mm diameter MoM total hip replacement. Cite this article: Bone Joint J 2013;95-B:1626–31

Aims

We investigated whether blood metal ion levels could effectively identify patients with bilateral Birmingham Hip Resurfacing (BHR) implants who have adverse reactions to metal debris (ARMD).

Aims

Cardiac magnetic resonance (CMR) was used to assess whether cardiac function or tissue composition was affected in patients with well-functioning metal-on-metal hip resurfacing arthroplasties (MoMHRA) when compared with a group of controls, and to assess if metal ion levels correlated with any of the functional or structural parameters studied.

The presence of pseudotumours, which are soft-tissue masses relating to the hip, after metal-on-metal hip resurfacing arthroplasty has been associated with elevated levels of metal ions in serum, suggesting that pseudotumours occur when there is increased wear. We aimed to quantify the wear in vivo of implants revised for pseudotumours (eight) and of a control group of implants (22) revised for other reasons of failure.

We found that the implant group with pseudotumours had a significantly higher rate of median linear wear of the femoral component at 8.1 μm/year (2.75 to 25.4) than the 1.79 μm/year (0.82 to 4.15; p = 0.002) of the non-pseudotumour group. For the acetabular component a significantly higher rate of median linear wear of 7.36 μm/year (1.61 to 24.9) was observed in the pseudotumour group compared with 1.28 μm/year (0.81 to 3.33, p = 0.001) in the other group. Wear of the acetabular component in the pseudotumour group always involved the edge of the implant, indicating that edge-loading had occurred.

Our findings are the first direct evidence that pseudotumour is associated with increased wear at the metal-on-metal articulation. Furthermore, edge-loading with the loss of fluid-film lubrication may be an important mechanism of generation of wear in patients with a pseudotumour.

In this paper, we will consider the current role of metal-on-metal bearings by looking at three subtypes of MoM hip arthroplasty separately: Hip resurfacing, large head (> 36 mm) MoM THA and MoM THA with traditional femoral head sizes.

We undertook a retrospective cohort study to determine clinical outcomes following the revision of metal-on-metal (MoM) hip replacements for adverse reaction to metal debris (ARMD), and to identify predictors of time to revision and outcomes following revision. Between 1998 and 2012 a total of 64 MoM hips (mean age at revision of 57.8 years; 46 (72%) female; 46 (72%) hip resurfacings and 18 (28%) total hip replacements) were revised for ARMD at one specialist centre. At a mean follow-up of 4.5 years (1.0 to 14.6) from revision for ARMD there were 13 hips (20.3%) with post-operative complications and eight (12.5%) requiring re-revision.

The Kaplan–Meier five-year survival rate for ARMD revision was 87.9% (95% confidence interval 78.9 to 98.0; 19 hips at risk). Excluding re-revisions, the median absolute Oxford hip score (OHS) following ARMD revision using the percentage method (0% best outcome and 100% worst outcome) was 18.8% (interquartile range (IQR) 7.8% to 48.3%), which is equivalent to 39/48 (IQR 24.8/48 to 44.3/48) when using the modified OHS. Histopathological response did not affect time to revision for ARMD (p = 0.334) or the subsequent risk of re-revision (p = 0.879). Similarly, the presence or absence of a contralateral MoM hip bearing did not affect time to revision for ARMD (p = 0.066) or the subsequent risk of re-revision (p = 0.178).

Patients revised to MoM bearings had higher rates of re-revision (five of 16 MoM hips re-revised; p = 0.046), but those not requiring re-revision had good functional results (median absolute OHS 14.6% or 41.0/48). Short-term morbidity following revision for ARMD was comparable with previous reports. Caution should be exercised when choosing bearing surfaces for ARMD revisions.

Cite this article: Bone Joint J 2014;96-B:1600–9.

We measured the orientation of the acetabular and femoral components in 45 patients (33 men, 12 women) with a mean age of 53.4 years (30 to 74) who had undergone revision of metal-on-metal hip resurfacings. Three-dimensional CT was used to measure the inclination and version of the acetabular component, femoral version and the horizontal femoral offset, and the linear wear of the removed acetabular components was measured using a roundness machine.

We found that acetabular version and combined version of the acetabular and femoral components were weakly positively correlated with the rate of wear. The acetabular inclination angle was strongly positively correlated with the rate of wear. Femoral version was weakly negatively correlated with the rate of wear. Application of a threshold of > 5 μm/year for the rate of wear in order to separate the revisions into low or high wearing groups showed that more high wearing components were implanted outside Lewinnek’s safe zone, but that this was mainly due to the inclination of the acetabular component, which was the only parameter that significantly differed between the groups.

We were unable to show that excess version of the acetabular component alone or combined with femoral version was associated with an increase in the rate of wear based on our assessment of version using CT.

Aims

Our first aim was to determine whether there are significant changes in the level of metal ions in the blood at mid-term follow-up, in patients with an Articular Surface Replacement (ASR) arthroplasty. Secondly, we sought to identify risk factors for any increases.

Aims

To determine ten-year failure rates following 36 mm metal-on-metal (MoM) Pinnacle total hip arthroplasty (THA), and identify predictors of failure.

We sought to establish the incidence of joint failure secondary to adverse reaction to metal debris (ARMD) following metal-on-metal hip resurfacing in a large, three surgeon, multicentre study involving 4226 hips with a follow-up of 10 to 142 months. Three implants were studied: the Articular Surface Replacement; the Birmingham Hip Resurfacing; and the Conserve Plus. Retrieved implants underwent analysis using a co-ordinate measuring machine to determine volumetric wear. There were 58 failures associated with ARMD. The median chromium and cobalt concentrations in the failed group were significantly higher than in the control group (p < 0.001). Survival analysis showed a failure rate in the patients with Articular Surface Replacement of 9.8% at five years, compared with < 1% at five years for the Conserve Plus and 1.5% at ten years for the Birmingham Hip Resurfacing. Two ARMD patients had relatively low wear of the retrieved components. Increased wear from the metal-on-metal bearing surface was associated with an increased rate of failure secondary to ARMD. However, the extent of tissue destruction at revision surgery did not appear to be dose-related to the volumetric wear.

Aims

The aims of this study were to compare the diagnostic test characteristics of ultrasound alone, metal artefact reduction sequence MRI (MARS-MRI) alone, and ultrasound combined with MARS-MRI for identifying intra-operative pseudotumours in metal-on-metal hip resurfacing (MoMHR) patients undergoing revision surgery.

Plasma levels of cobalt and chromium ions and Metal Artefact Reduction Sequence (MARS)-MRI scans were performed on patients with 209 consecutive, unilateral, symptomatic metal-on-metal (MoM) hip arthroplasties. There was wide variation in plasma cobalt and chromium levels, and MARS-MRI scans were positive for adverse reaction to metal debris (ARMD) in 84 hips (40%). There was a significant difference in the median plasma cobalt and chromium levels between those with positive and negative MARS-MRI scans (p < 0.001). Compared with MARS-MRI as the potential reference standard for the diagnosis of ARMD, the sensitivity of metal ion analysis for cobalt or chromium with a cut-off of > 7 µg/l was 57%. The specificity was 65%, positive predictive value was 52% and the negative predictive value was 69% in symptomatic patients. A lowered threshold of > 3.5 µg/l for cobalt and chromium ion levels improved the sensitivity and negative predictive value to 86% and 74% but at the expense of specificity (27%) and positive predictive value (44%).

Metal ion analysis is not recommended as a sole indirect screening test in the surveillance of symptomatic patients with a MoM arthroplasty. The investigating clinicians should have a low threshold for obtaining cross-sectional imaging in these patients, even in the presence of low plasma metal ion levels.

Persistent groin pain after seemingly successful total hip replacement (THR) appears to have become more common. Recent studies have indicated a high incidence after metal-on-polyethylene and metal-on-metal conventional THR and it has been documented in up to 18% of patients after metal-on-metal resurfacing. There are many causes, including acetabular loosening, stress fracture, and iliopsoas tendonitis and impingement. The evaluation of this problem requires a careful history and examination, plain radiographs and an algorithmic approach to special diagnostic imaging and tests. Non-operative treatment is not usually successful. Specific operative treatment depending on the cause of the pain usually involves revision of the acetabular component, iliopsoas tenotomy or other procedures, and is usually successful. Here, an appropriate algorithm is described.

This study compared component wear rates and pre-revision blood metal ions levels in two groups of failed metal-on-metal hip arthroplasties: hip resurfacing and modular total hip replacement (THR).

There was no significant difference in the median rate of linear wear between the groups for both acetabular (p = 0.4633) and femoral (p = 0.0872) components. There was also no significant difference in the median linear wear rates when failed hip resurfacing and modular THR hips of the same type (ASR and Birmingham hip resurfacing (BHR)) were compared.

Unlike other studies of well-functioning hips, there was no significant difference in pre-revision blood metal ion levels between hip resurfacing and modular THR.

Edge loading was common in both groups, but more common in the resurfacing group (67%) than in the modular group (57%). However, this was not significant (p = 0.3479). We attribute this difference to retention of the neck in resurfacing of the hip, leading to impingement-type edge loading. This was supported by visual evidence of impingement on the femur.

These findings show that failed metal-on-metal hip resurfacing and modular THRs have similar component wear rates and are both associated with raised pre-revision blood levels of metal ions.

We retrospectively analysed concentrations of chromium and cobalt ions in samples of synovial fluid and whole blood taken from a group of 92 patients with failed current-generation metal-on-metal hip replacements. We applied acid oxidative digestion to our trace metal analysis protocol, which found significantly higher levels of metal ion concentrations in blood and synovial fluid than a non-digestive method. Patients were subcategorised by mode of failure as either ‘unexplained pain’ or ‘defined causes’. Using this classification, chromium and cobalt ion levels were present over a wider range in synovial fluid and not as strongly correlated with blood ion levels as previously reported. There was no significant difference between metal ion concentrations and manufacturer of the implant, nor femoral head size below or above 50 mm. There was a moderately positive correlation between metal ion levels and acetabular component inclination angle as measured on three-dimensional CT imaging.

Our results suggest that acid digestion of samples of synovial fluid samples is necessary to determine metal ion concentrations accurately so that meaningful comparisons can be made between studies.

Lately, concerns have arisen following the use of large metal-on-metal bearings in hip replacements owing to reports of catastrophic soft-tissue reactions resulting in implant failure and associated complications. This review examines the literature and contemporary presentations on current clinical dilemmas in metal-on-metal hip replacement.

We carried out metal artefact-reduction MRI, three-dimensional CT measurement of the position of the component and inductively-coupled plasma mass spectrometry analysis of cobalt and chromium levels in whole blood on 26 patients with unexplained pain following metal-on-metal resurfacing arthroplasty.

MRI showed periprosthetic lesions around 16 hips, with 14 collections of fluid and two soft-tissue masses. The lesions were seen in both men and women and in symptomatic and asymptomatic hips. Using three-dimensional CT, the median inclination of the acetabular component was found to be 55° and its positioning was outside the Lewinnek safe zone in 13 of 16 cases. Using inductively-coupled plasma mass spectrometry, the levels of blood metal ions tended to be higher in painful compared with well-functioning metal-on-metal hips.

These three clinically useful investigations can help to determine the cause of failure of the implant, predict the need for future revision and aid the choice of revision prostheses.

Metal-on-metal total hip replacement has been targeted at younger patients with anticipated long-term survival, but the effect of the production of metal ions is a concern because of their possible toxicity to cells. We have reviewed the results of the use of the Ultima hybrid metal-on-metal total hip replacement, with a cemented polished tapered femoral component with a 28 mm diameter and a cobalt-chrome (CoCr) modular head, articulating with a 28 mm CoCr acetabular bearing surface secured in a titanium alloy uncemented shell.

Between 1997 and 2004, 545 patients with 652 affected hips underwent replacement using this system. Up to 31 January 2008, 90 (13.8%) hips in 82 patients had been revised. Pain was the sole reason for revision in 44 hips (48.9%) of which 35 had normal plain radiographs. Peri-prosthetic fractures occurred in 17 hips (18.9%) with early dislocation in three (3.3%) and late dislocation in 16 (17.8%). Infection was found in nine hips (10.0%).

At operation, a range of changes was noted including cavities containing cloudy fluid under pressure, necrotic soft tissues with avulsed tendons and denuded osteonecrotic upper femora. Corrosion was frequently observed on the retrieved cemented part of the femoral component. Typically, the peri-operative findings confirmed those found on pre-operative metal artefact reduction sequence MRI and histological examination showed severe necrosis.

Metal artefact reduction sequence MRI proved to be useful when investigating these patients with pain in the absence of adverse plain radiological features.