Aims. This study compared the cobalt and chromium serum ion concentration of patients treated with two different metal-on-metal (MoM) hinged total knee arthroplasty (TKA) systems, as well as a titanium nitride (TiN)-coated variant. Methods. A total of 63 patients (65 implants) were treated using either a MoM-coated (n = 29) or TiN-coated (n = 7) hinged TKA (GenuX mobile bearing, MUTARS; Implantcast, Germany) versus the BPKS (Brehm, Germany) hinged TKA (n = 27), in which the weight placed on the MoM hinge is diffused through a polyethylene (PE) inlay, reducing the direct load on the MoM hinge. Serum cobalt and chromium ion concentrations were assessed after minimum follow-up of 12 months, as well as functional outcome and quality of life. Results. No differences in mean age (69 years, 40 to 86), mean age adapted Charlson Comorbidity Index (3.1 (SD 1.4)), mean BMI (29.2 kg/m. 2. (SD 5.8)), or number of other implants were observed between groups. Significant improvements in outcome scores and pain levels were achieved for all groups, and there was no difference in quality of life (12-Item Short-Form Health Survey questionnaire (SF-12)). Mean cobalt and chromium ion levels were significantly higher for the GenuX versus the BPKS hinged TKA (GenuX vs BPKS: cobalt: 16.3 vs 9.4 µg/l; chromium: 9.5 vs 5.2 µg/l). The TiN-coated implants did not appear to confer improvement in the metal ion levels. Metal ion concentrations above 7 µg/l were detected in 81%(29/36) of GenuX patients versus 41% (11/27) in the BPKS group. No GenuX patients had normal levels under 2 µg/l, versus 22% of BPKS patients. No significant reduction in outcome scores was observed regardless of the metal ion levels, whereas higher work-related activity was correlated with higher chromium concentrations. Conclusion. Hinged TKA, using MoM hinges, resulted in critically high cobalt and chromium ion concentrations. The BPKS hinged TKA showed significantly lower metal ion concentrations compared with the GenuX TKA. No benefits were observed using TiN coating. The different weightbearing mechanics might influence the wear of the component materials. Higher workloads and physical activity could influence chromium levels. Cite this article: Bone Joint J 2022;104-B(3):376–385

Aims

A limited number of investigations with conflicting results have described perivascular lymphocytic infiltration (PVLI) in the setting of total knee arthroplasty (TKA). The purpose of this study was to determine if PVLI found in TKAs at the time of aseptic revision surgery was associated with worse clinical outcomes and survivorship.

Aims

The management of periprosthetic joint infection (PJI) after total knee arthroplasty (TKA) is challenging. The correct antibiotic management remains elusive due to differences in epidemiology and resistance between countries, and reports in the literature. Before the efficacy of surgical treatment is investigated, it is crucial to analyze the bacterial strains causing PJI, especially for patients in whom no organisms are grown.

Metallosis is a rare cause of failure after total knee replacement and has only previously been reported when there has been abnormal metal-on-metal contact. We describe 14 patients (15 knees) whose total knee replacement required revision for a new type of early failure caused by extensive metallosis. A modification of a cementless rotating platform implant, which had previously had excellent long-term survival, had been used in each case. The change was in the form of a new porous-beaded surface on the femoral component to induce cementless fixation, which had been used successfully in the fixation of acetabular and tibial components. This modification appeared to have resulted in metallosis due to abrasive two-body wear. The component has subsequently been recalled and is no longer in use. The presentation, investigation, and findings at revision are described and a possible aetiology and its implications are discussed.