The creep and wear behaviour of highly cross-linked polyethylene and standard polyethylene liners were examined in a prospective, double-blind randomised, controlled trial using radiostereometric analysis. We randomised 54 patients to receive hip replacements with either highly cross-linked polyethylene or standard liners and determined the three-dimensional penetration of the liners over three years. After three years the mean total penetration was 0.35 mm (SD 0.14) for the highly cross-linked polyethylene group and 0.45 mm (SD 0.19) for the standard group. The difference was statistically significant (p = 0.0184). From the pattern of penetration it was possible to discriminate creep from wear. Most (95%) of the creep occurred within six months of implantation and nearly all within the first year. There was no difference in the mean degree of creep between the two types of polyethylene (highly cross-linked polyethylene 0.26 mm, SD 0.17; standard 0.27 mm, SD 0.2; p = 0.83). There was, however, a significant difference (p = 0.012) in the mean wear rate (highly cross-linked polyethylene 0.03 mm/yr, SD 0.06; standard 0.07 mm/yr, SD 0.05). Creep and wear occurred in significantly different directions (p = 0.01); creep was predominantly proximal whereas wear was anterior, proximal and medial. We conclude that penetration in the first six months is creep-dominated, but after one year virtually all penetration is due to wear. Highly cross-linked polyethylene has a 60% lower rate of wear than standard polyethylene and therefore will probably perform better in the long term

Aims. Highly cross-linked polyethylene (HXLPE) has greatly improved the durability of total hip arthroplasty (THA) in young patients because of its improved wear characteristics. Few studies have followed this population into the second decade, and therefore the purpose of this investigation was to evaluate the clinical outcome for THA patients 50 years of age and younger at a minimum of 15 years postoperatively. The second purpose was to evaluate the radiological findings secondary to wear or mechanical failure of the implant. Methods. Between October 1999 and December 2005, 105 THAs were performed in 95 patients (53 female, 42 male) aged 50 years and younger (mean 42 years (20 to 50)). There were 87 patients (96 hips) that were followed for a minimum of 15 years (mean 17.3 years (15 to 21)) for analysis. Posterior approach was used with cementless fixation with a median head size of 28 mm. HXLPE was the acetabular bearing for all hips. Radiographs were evaluated for polyethylene wear, radiolucent lines, and osteolysis. Results. Clinical outcomes showed significant improvement of mean Harris Hip Scores from 52.8 (SD 13.5) preoperatively to 94.8 (SD 7.6) postoperatively. One hip was revised for recurrent instability, and there were no infections. No hips were revised for mechanical loosening or osteolysis. Mean polyethylene linear wear was 0.04 mm/year and volumetric wear was 6.22 mm. 3. /year, with no significant differences between head size or material. Osteolysis was not present in any of the hips. Conclusion. The use of HXLPE in THA for patients aged 50 years and younger has performed exceptionally well without evidence of significant wear causing mechanical loosening or necessitating revision. The radiolucent lines of the acetabular component must be followed to determine the prognostic significance. This investigation represents the longest clinical follow-up of a large, consecutive cohort of patients aged 50 years or younger with THA using HXLPE. This long-term analysis found negligible polyethylene wear, no incidence of aseptic loosening, and excellent clinical outcomes at and beyond 15 years of follow-up. Cite this article: Bone Joint J 2021;103-B(7 Supple B):78–83

Aims. We aimed to evaluate the long-term outcome of highly cross-linked polyethylene (HXLPE) cemented acetabular components and assess whether any radiolucent lines (RLLs) which arose were progressive. Methods. We retrospectively reviewed 170 patients who underwent 187 total hip arthroplasties at two hospitals with a minimum follow-up of ten years. All interventions were performed using the same combination of HXLPE cemented acetabular components with femoral stems made of titanium alloy. Kaplan-Meier survival analysis was performed for the primary endpoint of acetabular component revision surgery for any reason and secondary endpoint of the appearance of RLLs. RLLs that had appeared once were observed over time. We statistically assessed potential relationships between RLLs and a number of factors, including the technique of femoral head autografting and the Japanese Orthopaedic Association score. Results. The mean follow-up period was 13.0 years (10.0 to 16.3). Femoral head autografting was performed on 135 hips (72.2%). One acetabular component was retrieved because of deep infection. No revision was performed for the aseptic acetabular loosening. The Kaplan-Meier survival curve for the primary and secondary endpoints were 98.2% (95% confidence interval (CI) 88.6% to 99.8%) and 79.3% (95% CI 72.8% to 84.6%), respectively. RLLs were detected in 38 hips (21.2%), at a mean of 1.7 years (1 month to 6 years) postoperatively. None of the RLLs were progressive, and the presence of RLLs did not show a significant association with the survival and clinical score. RLLs were more frequently observed in hips without femoral head autografts than in those with autografts. Conclusion. The use of HXLPE cemented acetabular components in total hip arthroplasty demonstrated excellent clinical outcomes after ten years, and no RLLs were progressive, and their presence did not affect the outcome. Femoral head autografting did not negatively impact the acetabular component survival or the appearance of RLLs. Cite this article: Bone Joint J 2021;103-B(10):1604–1610

Aims. Several short- and mid-term studies have shown minimal liner wear of highly cross-linked polyethylene (HXLPE) in total hip arthroplasty (THA), but the safety of using thinner HXLPE liners to maximize femoral head size remains uncertain. The objective of this study was to analyze clinical survival and radiological wear rates of patients with HXLPE liners, a 36 mm femoral head, and a small acetabular component with a minimum of ten years’ follow-up. Methods. We retrospectively identified 55 patients who underwent primary THA performed at a single centre, using HXLPE liners with 36 mm cobalt-chrome heads in acetabular components with an outer diameter of 52 mm or smaller. Patient demographic details, implant details, death, and all-cause revisions were recorded. Cox regression and Kaplan-Meier survival was used to determine all-cause and liner-specific revision. Of these 55 patients, 22 had a minimum radiological follow-up of seven years and were assessed radiologically for linear and volumetric wear. Results. Overall survival rate for all-cause revision was 94.5% (95% confidence interval (CI) 81.7% to 97.2%) at a mean follow-up of 12.8 years (10.9 to 18.7). Three patients were revised, none for liner wear, fracture, or dissociation. A total of 22 patients were included in the radiological analysis (mean follow-up 9.9 years (7.5 to 13.7)). Mean linear liner wear was 0.085 mm (95% CI -0.086 to 0.257) and the volumetric wear rate was 11.097 mm. 3. /year (95% CI -6.5 to 28.7). Conclusion. Using HXLPE liners with 36 mm heads in 52 mm acetabular components or smaller is safe, with excellent survival and low rates of linear and volumetric wear at medium-term follow-up. Patients did not require revision surgery for liner complications such as fracture, dissociation, or wear. Our results suggest that the advantages of using larger heads outweigh the potential risks of using thin HXLPE liners. Cite this article: Bone Joint J 2023;105-B(1):29–34

Aims

The purpose of this study was to compare the long-term results of primary total hip arthroplasty (THA) in young patients using either a conventional (CPE) or a highly cross-linked (HXLPE) polyethylene liner in terms of functional outcome, incidence of osteolysis, radiological wear and rate of revision.

Two Durasul highly crosslinked polyethylene liners were exchanged during revision surgery four and five years after implantation, respectively. The retrieved liners were evaluated macroscopically and surface analysis was performed using optical and electron microscopy. A sample of each liner was used to determine the oxidation of the material by Fourier transform infrared spectroscopy. Samples of the capsule were examined histologically.

The annual wear rate was found to be 0.010 and 0.015 mm/year, respectively. Surface analysis showed very little loss of material caused by wear. Histological evaluation revealed a continuous neosynovial lining with single multinucleated foreign-body giant cells. Our findings showed no unexpected patterns of wear on the articulating surfaces up to five years after implantation and no obvious failure of material.

Aims

The most frequent indication for revision surgery in total hip arthroplasty (THA) is aseptic loosening. Aseptic loosening is associated with polyethylene liner wear, and wear may be reduced by using vitamin E-doped liners. The primary objective of this study was to compare proximal femoral head penetration into the liner between a) two cross-linked polyethylene (XLPE) liners (vitamin E-doped (vE-PE)) versus standard XLPE liners, and b) two modular femoral head diameters (32 mm and 36 mm).

Aims. The aim of this study was to evaluate the performance of first-generation annealed highly cross-linked polyethylene (HXLPE) in cementless total hip arthroplasty (THA). Methods. We retrospectively evaluated 29 patients (35 hips) who underwent THA between December 2000 and February 2002. The survival rate was estimated using the Kaplan-Meier method. Hip joint function was evaluated using the Japanese Orthopaedic Association (JOA) score. Two-dimensional polyethylene wear was estimated using Martell’s Hip Analysis Suite. We calculated the wear rates between years 1 and 5, 5 and 10, 10 and 15, and 15 and final follow-up. Results. The mean follow-up period was 19.1 years (SD 0.6; 17.3 to 20.1). The 19-year overall survival rate with the end point of all-cause revision was 97.0% (95% confidence interval (CI) 91 to 100). The mean JOA score improved from 43.2 (SD 10.6; 30 to 76) before surgery to 90.2 (SD 6.4; 76 to 98) at the final follow-up (p < 0.001). There was no osteolysis or loosening of the acetabular or femoral components. The overall steady-state wear rate was 0.013 mm/year (SD 0.012). There was no hip with a steady-state wear rate of > 0.1 mm/year. There was no significant difference in wear rates for each period. We found no significant correlation between the wear rate and age, body weight, BMI, or cup inclination. Conclusion. First-generation annealed HXLPE shows excellent wear resistance and no acceleration of wear for approximately 20 years, with low all-cause revision rates. Cite this article: Bone Joint J 2022;104-B(2):200–205

We report the five-year outcome of a randomised controlled trial which used radiostereometric analysis (RSA) to assess the influence of surface oxidised zirconium (OxZr, Oxinium) on polyethylene wear in vivo.

A total of 120 patients, 85 women and 35 men with a mean age of 70 years (59 to 80) who were scheduled for primary cemented total hip arthroplasty were randomly allocated to four study groups. Patients were blinded to their group assignment and received either a conventional polyethylene (CPE) or a highly cross-linked (HXL) acetabular component of identical design. On the femoral side patients received a 28 mm head made of either cobalt-chromium (CoCr) or OxZr.

The proximal head penetration (wear) was measured with repeated RSA examinations over five years. Clinical outcome was measured using the Harris hip score.

There was no difference in polyethylene wear between the two head materials when used with either of the two types of acetabular component (p = 0.3 to 0.6). When comparing the two types of polyethylene there was a significant difference in favour of HXLPE, regardless of the head material used (p < 0.001).

In conclusion, we found no advantage of OxZr over CoCr in terms of polyethylene wear after five years of follow-up. Our findings do not support laboratory results which have shown a reduced rate of wear with OxZr. They do however add to the evidence on the better resistance to wear of HXLPE over CPE.

Cite this article: Bone Joint J 2015;97-B:1463–9.

The ideal bearing surface for young patients undergoing total hip replacement (THR) remains controversial. We report the five-year results of a randomised controlled trial comparing the clinical and radiological outcomes of 102 THRs in 91 patients who were <  65 years of age. These patients were randomised to receive a cobalt–chrome on ultra-high-molecular-weight polyethylene, cobalt–chrome on highly cross-linked polyethylene, or a ceramic-on-ceramic bearing. In all, 97 hip replacements in 87 patients were available for review at five years. Two hips had been revised, one for infection and one for peri-prosthetic fracture. At the final follow-up there were no significant differences between the groups for the mean Western Ontario and McMaster Universities osteoarthritis index (pain, p = 0.543; function, p = 0.10; stiffness, p = 0.99), Short Form-12 (physical component, p = 0.878; mental component, p = 0.818) or Harris hip scores (p = 0.22). Radiological outcomes revealed no significant wear in the ceramic group. Comparison of standard and highly cross-linked polyethylene, however, revealed an almost threefold difference in the mean annual linear wear rates (0.151 mm/year versus 0.059 mm/year, respectively) (p < 0.001)

Aims. A significant reduction in wear at five and ten years was previously reported when comparing Durasul highly cross-linked polyethylene with nitrogen-sterilized Sulene polyethylene in total hip arthroplasty (THA). We investigated whether the improvement observed at the earlier follow-up continued, resulting in decreased osteolysis and revision surgery rates over the second decade. Methods. Between January 1999 and December 2001, 90 patients underwent surgery using the same acetabular and femoral components with a 28 mm metallic femoral head and either a Durasul or Sulene liner. A total of 66 hips of this prospective randomized study were available for a minimum follow-up of 20 years. The linear femoral head penetration rate was measured at six weeks, one year, and annually thereafter, using the Dorr method on digitized radiographs with a software package. Results. In the Durasul group, no patients underwent revision due to loosening or showed radiological evidence of osteolysis. In the Sulene group, four patients (four hips) were revised due to femoral component loosening. The 20-year cumulative failure incidence in the presence of the competing event of death for revision surgery was 4.5% (95% confidence interval (CI) 0.8 to 13.6) in the Durasul group, and 8.9% (95% CI 2.8 to 19.5) in the Sulene group. The mean wear one year after surgery was 0.09 mm (SD 0.007) in the Durasul group and 0.24 (SD 0.015) in the Sulene group (p < 0.001). From one to 20 years after surgery, the mean total penetration was 0.32 mm (SD 0.045) in the Durasul group and 1.07 mm (SD 0.13) in the Sulene group (p < 0.001). Mean femoral head penetration at 20 years was approximately 70.0% less in the Durasul group than the Sulene group. Conclusion. The significant reduction in femoral head penetration obtained with the Durasul compared with Sulene in uncemented THA resulted in lower osteolysis and revision rates after 20 years. Cite this article: Bone Joint J 2022;104-B(9):1032–1038

Aims. This study reports the ten-year wear rates, incidence of osteolysis, clinical outcomes, and complications of a multicentre randomized controlled trial comparing oxidized zirconium (OxZr) versus cobalt-chrome (CoCr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) and highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA). Methods. Patients undergoing primary THA were recruited from four institutions and prospectively allocated to the following treatment groups: Group A, CoCr femoral head with XLPE liner; Group B, OxZr femoral head with XLPE liner; and Group C, OxZr femoral head with UHMWPE liner. All study patients and assessors recording outcomes were blinded to the treatment groups. The outcomes of 262 study patients were analyzed at ten years’ follow-up. Results. Patients in Group C were associated with increased mean liner wear rates compared to patients in Group A (0.133 mm/yr (SD 0.21) vs 0.031 mm/yr (SD 0.07), respectively; p < 0.001) and Group B (0.133 mm/yr (SD 0.21) vs 0.022 mm/yr (SD 0.05), respectively; p < 0.001) at ten years’ follow-up. Patients in Group C were also associated with increased risk of osteolysis and aseptic loosening requiring revision surgery, compared with patients in Group A (7/133 vs 0/133, respectively; p = 0.007) and Group B (7/133 vs 0/135, respectively; p = 0.007). There was a non-statistically significant trend towards increased mean liner wear rates in Group A compared with Group B (0.031 mm/yr (SD 0.07) vs 0.022 mm/yr (SD 0.05), respectively; p = 0.128). All three groups were statistically comparable preoperatively and at ten years’ follow-up when measuring normalized Western Ontario and McMaster Universities Osteoarthritis Index (p = 0.410), 36-Item Short Form Health Survey (p = 0.465 mental, p = 0.713 physical), and pain scale scores (p = 0.451). Conclusion. The use of UHMWPE was associated with progressively increased annual liner wear rates after THA compared to XLPE. At ten years’ follow-up, the group receiving UHMWPE demonstrated an increased incidence of osteolysis and aseptic loosening requiring revision surgery compared to XLPE. Femoral heads composed of OxZr were associated with trend towards reduced wear rates compared to CoCr, but this did not reach statistical significance and did not translate to any differences in osteolysis, functional outcomes, or revision surgery between the two femoral head components. Cite this article: Bone Joint J 2022;104-B(7):833–843

Aims. Contemporary outcomes of primary total hip arthroplasties (THAs) with highly cross-linked polyethylene (HXLPE) liners in patients with inflammatory arthritis have not been well studied. This study examined the implant survivorship, complications, radiological results, and clinical outcomes of THA in patients with inflammatory arthritis. Methods. We identified 418 hips (350 patients) with a primary diagnosis of inflammatory arthritis who underwent primary THA with HXLPE liners from January 2000 to December 2017. Of these hips, 68% had rheumatoid arthritis (n = 286), 13% ankylosing spondylitis (n = 53), 7% juvenile rheumatoid arthritis (n = 29), 6% psoriatic arthritis (n = 24), 5% systemic lupus erythematosus (n = 23), and 1% scleroderma (n = 3). Mean age was 58 years (SD 14.8), 66.3% were female (n = 277), and mean BMI was 29 kg/m. 2. (SD 7). Uncemented femoral components were used in 77% of cases (n = 320). Uncemented acetabular components were used in all patients. Competing risk analysis was used accounting for death. Mean follow-up was 4.5 years (2 to 18). Results. The ten-year cumulative incidence of any revision was 3%, and was highest in psoriatic arthritis patients (16%). The most common indications for the 15 revisions were dislocations (n = 8) and periprosthetic joint infections (PJI; n = 4, all on disease-modifying antirheumatic drugs (DMARDs)). The ten-year cumulative incidence of reoperation was 6.1%, with the most common indications being wound infections (six cases, four on DMARDs) and postoperative periprosthetic femur fractures (two cases, both uncemented femoral components). The ten-year cumulative incidence of complications not requiring reoperation was 13.1%, with the most common being intraoperative periprosthetic femur fracture (15 cases, 14 uncemented femoral components; p = 0.13). Radiological evidence of early femoral component subsidence was observed in six cases (all uncemented). Only one femoral component ultimately developed aseptic loosening. Harris Hip Scores substantially improved (p < 0.001). Conclusion. Contemporary primary THAs with HXLPE in patients with inflammatory arthritis had excellent survivorship and good functional outcomes regardless of fixation method. Dislocation, PJI, and periprosthetic fracture were the most common complications in this cohort with inflammatory arthritis. Cite this article: Bone Joint J 2023;105-B(7):768–774

Polyethylene wear debris can cause osteolysis and the failure of total hip arthroplasty. We present the five-year wear rates of a highly cross-linked polyethylene (X3) bearing surface when used in conjunction with a 36 mm ceramic femoral head. This was a prospective study of a cohort of 100 THAs in 93 patients. Pain and activity scores were measured pre- and post-operatively. Femoral head penetration was measured at two months, one year, two years and at five years using validated edge-detecting software (PolyWare Auto). At a mean of 5.08 years (3.93 to 6.01), 85 hips in 78 patients were available for study. The mean age of these patients was 59.08 years (42 to 73, the mean age of males (n = 34) was 59.15 years, and females (n = 44) was 59.02 years). All patients had significant improvement in their functional scores (p < 0.001). The steady state two-dimensional linear wear rate was 0.109 mm/year. The steady state volumetric wear rate was 29.61 mm. 3. /year. No significant correlation was found between rate of wear and age (p = 0.34), acetabular component size (p = 0.12) or clinical score (p = 0.74). Our study shows low steady state wear rates at five years in X3 highly cross-linked polyethylene in conjunction with a 36 mm ceramic femoral head. The linear wear rate was almost identical to the osteolysis threshold of 0.1 mm/year recommended in the literature. Cite this article: Bone Joint J 2015;97-B:1470–4

Aims. We present the ten-year data of a cohort of patients, aged between 18 and 65 years (mean age 52.7 years; 19 to 64), who underwent total hip arthroplasty. Patients were randomised to be treated with a cobalt-chrome (CoCr) femoral head with an ultra-high molecular weight polyethylene (UHMWPE), highly cross-linked polyethylene (XLPE) or ceramic-on-ceramic (CoC) bearing surface. Patients and Methods. A total of 102 hips (91 patients) were randomised into the three groups. At ten years, 97 hips were available for radiological and functional follow-up. Two hips (two patients) had been revised (one with deep infection and one for periprosthetic fracture) and three were lost to follow-up. Radiological analysis was performed using a validated digital assessment programme to give linear, directional and volumetric wear of the two polyethylene groups. Results. There was a significantly reduced rate of steady-state linear wear with XLPE (0.07 mm/yr) compared with UHMWPE (0.37 mm/yr) (p = 0.001). Volumetric wear was also significantly reduced in the XLPE group (29.29 mm. 3. /yr) compared with the UHMWPE group (100.75mm. 3. /yr) (p = 0.0001). There were six patients with UHMWPE who had non-progressive osteolysis and none in the XLPE group. All three bearing groups had significant improvements in 12-item short form health survey scores, Western Ontario and McMaster Universities Osteoarthritis Index score and Harris Hip Score. However, the improvement in HSS was significantly less in the UHMWPE group (p = 0.0188) than in the other two groups. At ten years, the rates of volumetric and linear wear in the XLPE group remain low and predominantly below the estimated threshold for osteolysis (1 mm/yr). The rate of linear wear in the XLPE group was three times less than in the UHMWPE group at five-year follow-up and five times less at ten years. The rate of volumetric wear was also three times less in the XLPE group at ten years. Conclusion. While CoC also performs well, XLPE at ten years remains a safe and excellent bearing option in young patients, with low rates of wear and no evidence of osteolysis. Cite this article: Bone Joint J 2017;99-B:1590–5

We describe our technique and rationale using hybrid fixation for primary total hip arthroplasty (THA) at the Hospital for Special Surgery. Modern uncemented acetabular components have few screw holes, or no holes, polished inner surfaces, improved locking mechanisms, and maximised thickness and shell-liner conformity. Uncemented sockets can be combined with highly cross-linked polyethylene liners, which have demonstrated very low wear and osteolysis rates after ten to 15 years of implantation. The results of cement fixation with a smooth or polished surface finished stem have been excellent, virtually eliminating complications seen with cementless fixation like peri-operative femoral fractures and thigh pain. Although mid-term results of modern cementless stems are encouraging, the long-term data do not show reduced revision rates for cementless stems compared with cemented smooth stems. In this paper we review the conduct of a hybrid THA, with emphasis on pre-operative planning, surgical technique, hypotensive epidural anaesthesia, and intra-operative physiology. Cite this article: Bone Joint J 2016;98-B(1 Suppl A):54–9

Aims. Dual mobility (DM) implants have been shown to reduce the dislocation rate after total hip arthroplasty (THA), but there remain concerns about the use of cobalt chrome liners inserted into titanium shells. The aim of this study was to assess the clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) at mid-term follow-up in young, active patients receiving a modular DM THA. Methods. This was a prospective study involving patients aged < 65 years, with a BMI of < 35 kg/m. 2. , and University of California, Los Angeles activity score of > 6 who underwent primary THA with a modular cobalt chrome acetabular liner, highly cross-linked polyethylene mobile bearing, and a cementless titanium femoral stem. Patient-reported outcome measures, whole blood metal ion levels (μg/l), and periprosthetic femoral BMD were measured at baseline and at one, two, and five years postoperatively. The results two years postoperatively for this cohort have been previously reported. Results. A total of 43 patients were enrolled. At minimum follow-up of five years, 23 (53.4%) returned for clinical and radiological review, 25 (58.1%) had metal ion analysis performed, 19 (44.2%) underwent dual energy x-ray absorptiometry scans, and 25 (58%) completed a pain-drawing questionnaire. The mean modified Harris Hip Scores improved significantly from 54.8 (SD 19) preoperatively to 93.08 (SD 10.5) five years postoperatively (p < 0.001). One patient was revised for aseptic acetabular loosening. The mean cobalt levels increased from 0.065 μg/l (SD 0.03) to 0.08 (SD 0.05) and the mean titanium levels increased from 0.35 (SD 0.13) to 0.78 (SD 0.29). The femoral BMD ratio decreased in Gruen Zone 1 (91.9%) at five years postoperatively compared with the baseline scores at six weeks potoperatively. The femoral BMD ratio was maintained in Gruen zones 2 to 7. Conclusion. The use of a modular DM component and a cementless, tapered femoral stem shows excellent mid-term survivorship with minimal concerns for corrosion and metal ion release in a cohort of young, active patients undergoing primary THA. Cite this article: Bone Joint J 2021;103-B(7 Supple B):73–77

In this prospective study we studied the effect of the inclination angle of the acetabular component on polyethylene wear and component migration in cemented acetabular sockets using radiostereometric analysis. A total of 120 patients received either a cemented Reflection All-Poly ultra-high-molecular-weight polyethylene or a cemented Reflection All-Poly highly cross-linked polyethylene acetabular component, combined with either cobalt–chrome or Oxinium femoral heads. Femoral head penetration and migration of the acetabular component were assessed with repeated radiostereometric analysis for two years. The inclination angle was measured on a standard post-operative anteroposterior pelvic radiograph. Linear regression analysis was used to determine the relationship between the inclination angle and femoral head penetration and migration of the acetabular component. We found no relationship between the inclination angle and penetration of the femoral head at two years’ follow-up (p = 0.9). Similarly, our data failed to reveal any statistically significant correlation between inclination angle and migration of these cemented acetabular components (p = 0.07 to p = 0.9)

Oxidised zirconium (OxZi) has been developed as an alternative bearing surface for femoral heads in total hip arthroplasty (THA). This study has investigated polyethylene wear, functional outcomes and complications, comparing OxZi and cobalt–chrome (CoCr) as part of a three-arm, multicentre randomised controlled trial. Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and highly cross-linked polyethylene (XLPE) liner; Group B received an OxZi femoral head and XLPE liner; Group C received an OxZi femoral head and ultra-high molecular weight polyethylene (UHMWPE) liner. At five years, 368 patients had no statistically significant differences in short-form-36 (p = 0.176 mental, p = 0.756 physical), Western Ontario and McMaster Universities Osteoarthritis Index (p = 0.847), pain scores (p = 0.458) or complications. The mean rate of linear wear was 0.028 mm/year (standard deviation (. sd) 0.010). for Group A, 0.023 mm/year (. sd. 0.010) for Group B, and 0.09 mm/year (. sd. 0.045) for Group C. Penetration was significantly higher in the UHMWPE liner group compared with both XLPE liner groups (p < 0.001) but no significant difference was noted between CoCr and OxZi when articulating with XLPE (p = 0.153). In this, the largest randomised study of this bearing surface, it appears that using a XLPE acetabular liner is more important in reducing THA component wear than the choice of femoral head bearing, at mid-term follow-up. There is a non-significant trend towards lower wear, coupling OxZi rather than CoCr with XLPE but long-term analysis is required to see if this observation changes with time and becomes significant. Cite this article: Bone Joint J 2015;97-B:883–9

Ultra-high-molecular-weight polyethylene sterilised in the absence of air and highly cross-linked polyethylene have been used to avoid osteolysis and loosening in total hip replacement. Our prospective randomised study has assessed the results using two different polyethylenes associated with the same prosthetic design. We assessed 45 Allofit acetabular components with a Sulene-polyethylene liner of conventional polyethylene gamma sterilised with nitrogen and 45 Allofit acetabular components with a Durasul-polyethylene liner sterilised in ethylene oxide, both matched with an Alloclassic stem with a 28 mm modular femoral head. The prostheses were implanted between May 1999 and December 2001. The mean follow-up was for 66.3 months (60 to 92). The linear penetration of the femoral head was estimated at 6 weeks, at 6 and 12 months and annually thereafter from standardised digitised radiographs using image-analysis software. There was no loosening of any prosthetic component. There were no radiolucent lines or osteolysis. The mean rate of penetration calculated from regression analysis during the first five years was 38 μm/year (. sd. 2) for the Sulene group and 6 μm/year (. sd. 1) for the Durasul group (p = 0.00002). The rate of penetration of the Durasul group was 15.7% of that of the Sulene group