Aims

This study compared the cobalt and chromium serum ion concentration of patients treated with two different metal-on-metal (MoM) hinged total knee arthroplasty (TKA) systems, as well as a titanium nitride (TiN)-coated variant.

Aims

A limited number of investigations with conflicting results have described perivascular lymphocytic infiltration (PVLI) in the setting of total knee arthroplasty (TKA). The purpose of this study was to determine if PVLI found in TKAs at the time of aseptic revision surgery was associated with worse clinical outcomes and survivorship.

Aims

The present study investigated the five-year interval changes in pseudotumours and measured serum metal ions at long-term follow-up of a previous report of 28 mm diameter metal-on-metal (MoM) total hip arthroplasty (THA).

We present a series of 35 patients (19 men and 16 women) with a mean age of 64 years (36.7 to 75.9), who underwent total hip replacement using the ESKA dual-modular short stem with metal on-polyethylene bearing surfaces. This implant has a modular neck section in addition to the modular head. Of these patients, three presented with increasing post-operative pain due to pseudotumour formation that resulted from corrosion at the modular neck-stem junction. These patients underwent further surgery and aseptic lymphocytic vaculitis associated lesions were demonstrated on histological analysis.

Retrieval analysis of two modular necks showed corrosion at the neck-stem taper. Blood cobalt and chromium levels were measured at a mean of nine months (3 to 28) following surgery. These were compared with the levels in seven control patients (three men and four women) with a mean age of 53.4 years (32.1 to 64.1), who had an identical prosthesis and articulation but with a prosthesis that had no modularity at neck-stem junction. The mean blood levels of cobalt in the study group were raised at 50.75 nmol/l (5 to 145) compared with 5.6 nmol/l (2 to 13) in control patients.

Corrosion at neck-stem tapers has been identified as an important source of metal ion release and pseudotumour formation requiring revision surgery. Finite element modelling of the dual modular stem demonstrated high stresses at the modular stem-neck junction. Dual modular cobalt-chrome hip prostheses should be used with caution due to these concerns.

Early failure associated with adverse reactions to metal debris is an emerging problem after hip resurfacing but the exact mechanism is unclear. We analysed our entire series of 660 metal-on-metal resurfacings (Articular Surface Replacement (ASR) and Birmingham Hip Resurfacing (BHR)) and large-bearing ASR total hip replacements, to establish associations with metal debris-related failures. Clinical and radiological outcomes, metal ion levels, explant studies and lymphocyte transformation tests were performed. A total of 17 patients (3.4%) were identified (all ASR bearings) with adverse reactions to metal debris, for which revision was required. This group had significantly smaller components, significantly higher acetabular component anteversion, and significantly higher whole concentrations of blood and joint chromium and cobalt ions than asymptomatic patients did (all p < 0.001). Post-revision lymphocyte transformation tests on this group showed no reactivity to chromium or cobalt ions. Explants from these revisions had greater surface wear than retrievals for uncomplicated fractures. The absence of adverse reactions to metal debris in patients with well-positioned implants usually implies high component wear.

Surgeons must consider implant design, expected component size and acetabular component positioning in order to reduce early failures when performing large-bearing metal-on-metal hip resurfacing and replacement.

We conducted a retrospective study to assess the prevalence of adverse reactions to metal debris (ARMD) in patients operated on at our institution with metal-on-metal (MoM) total hip replacements with 36 mm heads using a Pinnacle acetabular shell. A total of 326 patients (150 males, 175 hips; 176 females, 203 hips) with a mean age of 62.7 years (28 to 85) and mean follow-up of 7.5 years (0.1 to 10.8) participating in our in-depth modern MoM follow-up programme were included in the study, which involved recording whole blood cobalt and chromium ion measurements, Oxford hip scores (OHS) and plain radiographs of the hip and targeted cross-sectional imaging. Elevated blood metal ion levels (> 5 parts per billion) were seen in 32 (16.1%) of the 199 patients who underwent unilateral replacement. At 23 months after the start of our modern MoM follow-up programme, 29 new cases of ARMD had been revealed. Hence, the nine-year survival of this cohort declined from 96% (95% CI 95 to 98) with the old surveillance routine to 86% (95% CI 82 to 90) following the new protocol. Although ARMD may not be as common in 36 mm MoM THRs as in those with larger heads, these results support the Medicines and Healthcare Products Regulatory Agency guidelines on regular reviews and further investigations, and emphasise the need for specific a follow-up programme for patients with MoM THRs.

Cite this article: Bone Joint J 2014; 96-B:1610–17.

We carried out metal artefact-reduction MRI, three-dimensional CT measurement of the position of the component and inductively-coupled plasma mass spectrometry analysis of cobalt and chromium levels in whole blood on 26 patients with unexplained pain following metal-on-metal resurfacing arthroplasty.

MRI showed periprosthetic lesions around 16 hips, with 14 collections of fluid and two soft-tissue masses. The lesions were seen in both men and women and in symptomatic and asymptomatic hips. Using three-dimensional CT, the median inclination of the acetabular component was found to be 55° and its positioning was outside the Lewinnek safe zone in 13 of 16 cases. Using inductively-coupled plasma mass spectrometry, the levels of blood metal ions tended to be higher in painful compared with well-functioning metal-on-metal hips.

These three clinically useful investigations can help to determine the cause of failure of the implant, predict the need for future revision and aid the choice of revision prostheses.

We present the early clinical and radiological results of Articular Surface Replacement (ASR) resurfacings in 214 hips (192 patients) with a mean follow-up of 43 months (30 to 57). The mean age of the patients was 56 years (28 to 74) and 85 hips (40%) were in 78 women.

The mean Harris hip score improved from 52 (11 to 81) to 95 (27 to 100) at two years and the mean University of California, Los Angeles activity score from 3.9 (1 to 10) to 7.4 (2 to 10) in the same period. Narrowing of the neck (to a maximum of 9%) was noted in 124 of 209 hips (60%). There were 12 revisions (5.6%) involving four (1.9%) early fractures of the femoral neck and two (0.9%) episodes of collapse of the femoral head secondary to avascular necrosis. Six patients (2.8%) had failure related to metal wear debris. The overall survival for our series was 93% (95% confidence interval 80 to 98) and 89% (95% confidence interval 82 to 96) for hips with acetabular components smaller than 56 mm in diameter.

The ASR implant has a lower diametrical clearance and a subhemispherical acetabular component when compared with other more frequently implanted metal-on-metal hip resurfacings. These changes may contribute to the higher failure rate than in other series, compared with other designs. Given our poor results with the small components we are no longer implanting the smaller size.