We measured the proximal migration of 265 acetabular cups over seven years and correlated the findings with clinical outcome and acetabular revision for aseptic loosening. Cups which eventually became aseptically loose were shown to migrate more rapidly than successful cups. The average proximal migration at two years postoperatively for four groups of cups showed a monotonic relationship to the acetabular revision rate for aseptic loosening at 6.5 years. We conclude that acetabular cups which develop aseptic loosening as evidenced by pain, revision or screw fracture show increased proximal migration by one year, and that the 'migration rate' at two years can be used to predict the acetabular revision rate from aseptic loosening at 6.5 years

In laboratory tests, the ultra-high molecular weight polyethylene used for the acetabular cups of Charnley hip prostheses has a very low wear rate against steel. In the body radiographic measurements indicate that the polyethylene wears more rapidly. In order to investigate this higher wear rate, the sockets of acetabular cups removed at post-mortem have been examined using optical and electron microscopy. It has been shown that a socket wears predominantly on its superior part and that this is a direct consequence of the orientation of the cup in the body and the direction of loading of the hip. In the worn region the femoral head in effect bores out a new socket for itself, a process which is visible with the naked eye after approximately eight years. Electron microscopy shows that the predominant wear mechanism is adhesion, but after about eight years the appearance of surface cracks suggests that surface fatigue is taking place in addition to this. Laboratory wear tests have shown that pure surface fatigue is not sufficient to account for the high clinical wear rate. Other deformation processes are suggested and discussed with regard to the higher clinical wear rate

We examined radiographic polyethylene wear in 233 cemented total hip arthroplasties (201 patients) with either a metal-backed or a non-metal-backed acetabular cup. All patients had identical cemented one-piece titanium femoral stems with a femoral head diameter of 28 mm. The mean linear wear rate was 0.11 mm/yr in metal-backed sockets and 0.08 mm/yr in non-metal-backed sockets (p = 0.0002). The mean volumetric wear rate was 66.2 mm3/yr in the metal-backed sockets and 48.2 mm3/yr in the polyethylene sockets (p = 0.0002). The addition of metal backing to a cemented acetabular cup therefore resulted in a 37% increase in mean polyethylene wear rates which may partially explain the higher failure rate of cemented metal-backed cups. Linear regression analysis also implicated increased follow-up time (log), gross acetabular migration, metal backing and male gender in increasing polyethylene wear. We advocate the use of an all-polyethylene cup in cemented total hip arthroplasty. The increased polyethylene wear must also cause concern about the wear rate of uncemented metal-backed acetabular sockets

Between March 1990 and May 1991 we performed 85 primary total hip replacements in 74 patients using the Landos Atoll hydroxyapatite (HA)-coated cup and the Corail HA-coated stem. The patients were followed up for a mean of ten years. Of the 85 cups, 26 (31%) have already been revised and a further six are radiologically unstable and awaiting revision. Two femoral stems have been revised for infection without loosening. The retrieved acetabular cups were studied by SEM and image-processing techniques to quantify the amount of residual HA on the cup. This was correlated with the clinical variables and modes of failure. The residual HA (as a percentage of the surface) on the loose cups correlated negatively with the duration of implantation (r = −0.732, p < 0.001). Six cups were stable at revision and had more residual HA coating than those which were loose (p < 0.01). The rate of failure of the Landos Atoll HA-coated, smooth hemispherical cup with screw fixation is unacceptably high. Resorption of the HA coating is markedly increased in loose cups compared with stable cups. HA coating cannot substitute for stable mechanical fixation

Fracture of the polyethylene acetabular cup is a rare late complication of total hip replacement. Five cases are reported. In each one this followed a fall, and involved a Muller arthroplasty which had previously been symptomless. It is postulated that ridges or other irregularities of bone, produced by keying holes, could lead to areas of thin cement and potential weakness of support for the cup

1. Prosthetic acetabular cups of the Charnley and McKee-Farrar designs were cemented into cadaveric pelves using different procedures for preparing the acetabulum. 2. The torsional moments needed to loosen these cups were measured. 3. The torsional moments so measured were found to be from about four to more than twenty times higher than the frictional moments measured in independent tests on the two designs of prosthesis. 4. It is argued that late looseness of the acetabular component after total hip replacement, in the absence of infection, seems most likely to be due to thermal damage to the bone occurring at the time of polymerisation of the cement, and to subsequent bone resorption. 5. Surgical preparation of the acetabulum should include removal of all the articular cartilage and cleaning of the acetabular fossa, but the drilling of additional holes in the floor of the acetabulum seems unimportant. 6. The possibility of fatigue fracture in bone as a factor contributing to late loosening is an argument in favour of metal-on-polyethylene prostheses with their lower frictional moments, although the importance of this factor cannot be estimated

Laboratory wear testing of ultra high molecular weight polyethylene from 12 Charnley acetabular cups, removed after periods of up to 17.5 years showed that the large patient-to-patient variations in clinical penetration rate cannot be explained by batch-to-batch variation in the wear resistance of the material. Nor was there any evidence of a time-dependent degradation in wear resistance of the material

We report the long-term radiological results of 58 total hip arthroplasties (THA) using the Charnley offset-bore acetabular socket. Wear was measured at four sites and radiolucent lines and possible migration were recorded. Four cups were retrieved at revision and were examined using light microscopy, SEM and X-ray microanalysis. At a mean follow-up of seven years the mean wear in the DeLee and Charnley zone I was 0.4 mm and in zone II 0.26 mm. The wear rate was 0.06 and 0.04 mm/year, respectively. Progression of radiolucent lines was seen in five cases (8.6%). Three sockets (5.2%) were revised because of aseptic migration at a mean follow-up of 9.8 years and one socket for infection at two years. The offset-bore acetabular cup had excellent wear behaviour and a low migration and revision rate. We recommend that it should be considered in THA since the use of small cups is increasing, particularly in revision cases

We describe a new method for the accurate measurement of the angle of anteversion of an acetabular cup from standard anteroposterior radiographs, and provide the conversion tables required. The effect of the centering of the radiograph is discussed and a method of distinguishing between anteversion and retroversion by using a caudally directed x-ray beam is described

Failure of an acetabular cup is uncommon and has been attributed to wear or creep, trauma or bony irregularities in the acetabulum. We report ten cases in which fracture of the cup occurred at the site of drill holes used to anchor the marker wire. The role of such indentations as stress raisers has not been previously reported; we suggest that deep indentations or grooves should not be placed in the most highly stressed areas and that the cup thickness should allow for predicted wear rates

Ten acetabular cups coated with hydroxyapatite (HA) had originally been inserted in five primary and five revision total hip replacements. The thickness of the HA was 155 ± 35 μm. The cups, which were well-fixed, were retrieved, with their adherent tissue, at reoperation after 0.3 to 5.8 years because of infection (five hips), wear of polyethylene (three hips), and instability (two hips). Undecalcified sections showed a direct contact between bone and osteoid-like tissue which had formed directly onto the HA coating. The area within the threads and their mirror images, as well as the implant-tissue interfaces consisted of similar amounts of bone and soft tissue. Degradation of HA was seen in all hips. The mean thickness of the remaining HA coating was 97 μm (95% CI 94 to 101). The metal interface comprised 66% HA. The HA-tissue interface contained more bone than soft tissue (p = 0.001), whereas the metal-tissue interface included more soft tissue than bone (p = 0.019). Soft tissue at the implant interface and poor replacement of HA by bone may interfere with long-term fixation

We describe a simple, retroperitoneal approach for the removal of acetabular components that have migrated into the pelvis. The dense fibrous tissue layer which surrounds the implant protects the iliac vessels during removal of the cup by this method.

We reviewed 264 consecutive primary total hip replacements in 244 patients in which the Harris-Galante I porous-coated acetabular component had been used. The mean follow-up was 95 months (69 to 132). In 221 arthroplasties a 32 mm ceramic head had been used, and in the other 43 one of cobalt-chrome alloy. There were 124 women and 120 men with a mean age at operation of 56.8 years (21 to 83).

Survival analysis of the acetabular components was performed using the following definitions of failure: 1) infection; 2) removal because of aseptic loosening; 3) removal for any cause; and 4) a worst-case analysis including removal of the cup or infection or loss to follow-up.

Two well-fixed cups had been removed because of deep infection and three, similarly sound cups had been exchanged at the time of femoral revision. None of the acetabular components had required revision for aseptic loosening. After 11 years survival was 97.7% using the worst-case criterion. Radiological analysis of 187 acetabular components at a mean of 82 months (41 to 132) revealed no case of aseptic loosening. Pelvic osteolysis was seen in only one patient, but was not progressive and showed signs of regression.

The results using these acetabular components are encouraging but the need for regular follow-up remains since complications such as significant wear of the liner, massive osteolysis of the pelvis, aseptic loosening and late infection may increase in the second decade.

We report a high rate of failure of the Ring polyethylene cementless cup caused largely by granulomatous osteolysis. We have reviewed 126 prostheses inserted from 1986 to 1992 at from 11 to 90 months after surgery. There was radiological evidence of osteolytic granulomas adjacent to the external surface of the cup in 32%, appearing on average at three years from operation. In a subgroup of 59 prostheses followed for at least four years the incidence of such changes was 54%. A total of 27 cups (22%) have required revision, 21 for granulomatous loosening at an average follow-up of five years. In the retrieved prostheses there was obvious polyethylene abrasion and histological examination confirmed the presence of polyethylene wear debris. We found no significant correlation of osteolysis with cup size, although smaller cups were predominant among those having revision.

We studied wear in the ultra-high-molecular-weight polyethylene offset bore socket in 54 hips which had had Charnley low-friction arthroplasty. At an average follow-up of 8.1 years, the mean penetration rate was 0.04 mm per year. Correlation between the depth of socket penetration and the incidence of socket migration was confirmed, but socket migration occurred with lower penetration than had been previously reported.

We performed thermal analysis of polyethylene samples obtained from 73 new cups of the Weller hip prosthesis. There were marked individual differences in the degree of their crystallinity, ranging from 37.8% to 67.2% with a mean of 53%. Analysis of polyethylene from removed cups also showed differences in crystallinity in individual cups, with the mean value being higher in the removed implants than in the new ones. This difference in crystallinity between the groups was statistically significant. Marked individual differences in the degree of cup wear may result from these changes.

We have compared the survival of two hydroxyapatite (HA)-coated cups, 1208 Atoll hemispheric and 2641 Tropic threaded, with cemented Charnley all-polyethylene cups (16 021) using the Cox regression model.

The Tropic cup used in combination with an alumina ceramic femoral head, had good results, similar to those of the Charnley cup. When used in combination with a stainless-steel head, however, the risk of revision beyond four years was increased 3.4 times for the Tropic cup compared with the Charnley cup (p < 0.001). Over the same period, the Atoll cup had an increased risk of revision of 3.8 times when used with the alumina heads (p < 0.001) and an increased risk of 6.1 times when used with stainless-steel heads (p < 0.001). Revision because of wear and osteolysis was more common with both types of HA-coated cup than with the Charnley cup. The rate of revision of the Atoll cup because of aseptic loosening was also increased.

We found that HA-coated cups did not perform better than the Charnley cup.

In total hip replacement, orientation of the cup is critical to the stability of the prosthesis. A new method to determine the angle of planar anteversion is described. A simple mathematical formula uses the measurements taken from anteroposterior radiographs to calculate the planar anteversion without reference to tables or charts.

An experimental study in vitro has shown the efficacy of the formula in giving results which are within a clinically acceptable range.

One concern about the fixation of HA-coated implants is the possible disintegration of the surface, with the migration of HA granules into the joint space, producing third-body wear.

We report a study of six revisions of HA-coated polyethylene RM cups at 9 to 14 years after successful primary arthroplasty. In all six hips, we found HA granules embedded in the articulating surface of the polyethylene, with abrasive wear of the cup and the metal femoral head. The cup had loosened in four hips and three showed severe osteolysis of the proximal femur.

Third-body wear due to HA particles from implant coating may produce severe clinical problems with few early warning signs. Further clinical, radiological and histological observations are needed to determine the possible incidence of this late complication in the various types of coating of a variety of substrates.

Aims. Pelvic reconstruction after the resection of a tumour around the acetabulum is a challenging procedure due to the complex anatomy and biomechanics. Several pelvic endoprostheses have been introduced, but the rates of complication remain high. Our aim was to review the use of a stemmed acetabular pedestal cup in the management of these patients. Patients and Methods. The study involved 48 patients who underwent periacetabular reconstruction using a stemmed pedestal cup (Schoellner cup; Zimmer Biomet Inc., Warsaw, Indiana) between 2000 and 2013. The indications for treatment included a primary bone tumour in 27 patients and metastatic disease in 21 patients. The mean age of the patients at the time of surgery was 52 years (16 to 83). Results. At a median follow-up of 6.6 years (95% confidence interval 4.6 to 8.2), local control was achieved in all patients; 19 patients had died (16 of disease). Complications occurred in 19 patients (40%), of which deep infection was the most common, affecting eight patients (17%). Seven patients (15%) had a dislocation of the hip. Aseptic loosening was found in three patients (6%). Two (4%) underwent hindquarter amputation for non-oncological reasons. The risk of revision, with death being treated as a competing event, was 28% at one year, 39% at five years and 48% at ten years post-operatively. The mean Musculoskeletal Tumour Society Score at final follow-up was 71% (27% to 93%). Conclusion. This type of reconstruction is a satisfactory option for the treatment of patients with a periacetabular tumour. There remains, however, a high rate of complication, which may be reduced by future modifications of the device such as silver coating and tripolar articulation. Cite this article: Bone Joint J 2017;99-B:841–8

Aims

Pelvic discontinuity is a challenging acetabular defect without a consensus on surgical management. Cup-cage reconstruction is an increasingly used treatment strategy. The present study evaluated implant survival, clinical and radiological outcomes, and complications associated with the cup-cage construct.

Aims

Oxidized zirconium (OxZi) and highly cross-linked polyethylene (HXLPE) were developed to minimize wear and risk of osteolysis in total hip arthroplasty (THA). However, retrieval studies have shown that scratched femoral heads may lead to runaway wear, and few reports of long-term results have been published. The purpose of this investigation is to report minimum ten-year wear rates and clinical outcomes of THA with OxZi femoral heads on HXLPE, and to compare them with a retrospective control group of cobalt chrome (CoCr) or ceramic heads on HXLPE.

Aims

Mechanical impingement of the iliopsoas (IP) tendon accounts for 2% to 6% of persistent postoperative pain after total hip arthroplasty (THA). The most common initiator is anterior acetabular component protrusion, where the anterior margin is not covered by anterior acetabular wall. A CT scan can be used to identify and measure this overhang; however, no threshold exists for determining symptomatic anterior IP impingement due to overhang. A case-control study was conducted in which CT scan measurements were used to define a threshold that differentiates patients with IP impingement from asymptomatic patients after THA.

We analysed in-vivo migration and wear over a long period of all-polyethylene acetabular cups which had not been affected by mechanical loosening. The selection criteria of regular radiological follow-up, good clinical outcome (Charnley score of 5 or 6), continued walking without crutches and no radiological signs of loosening of the acetabular cups were fulfilled by 25 Charnley total hip arthroplasties. Mean migration, measured by the Nunn method, was 0.6 mm in the medial and 0.2 mm in the cranial direction. The mean yearly rate of wear was 0.05 mm and 0.04 mm, with six and two cups having no detectable wear, as measured by the Livermore and Charnley-Cupic methods, respectively. The maximal detected wear was 3.7 mm. There were no changes in the rate of wear with time. Computerised Ein Bild Röntgen Analyse (single-image radiological analysis) measurements of 20 hips indicated plastic deformation of the cups. We conclude that long-term successful cups do not migrate and have a very low rate of wear which was not affected by ageing of the polyethylene. There was no evidence that polyethylene wear alone caused mechanical loosening of the cup but high rates of wear seem to have an adverse prognostic value in terms of the long-term survival of the prosthesis

Aims

Isolated acetabular liner exchange with a highly crosslinked polyethylene (HXLPE) component is an option to address polyethylene wear and osteolysis following total hip arthroplasty (THA) in the presence of a well-fixed acetabular shell. The liner can be fixed either with the original locking mechanism or by being cemented within the acetabular component. Whether the method used for fixation of the HXLPE liner has any bearing on the long-term outcomes is still unclear.

Aims

The primary objective of this study was to develop a validated classification system for assessing iatrogenic bone trauma and soft-tissue injury during total hip arthroplasty (THA). The secondary objective was to compare macroscopic bone trauma and soft-tissues injury in conventional THA (CO THA) versus robotic arm-assisted THA (RO THA) using this classification system.

Literature surrounding artificial intelligence (AI)-related applications for hip and knee arthroplasty has proliferated. However, meaningful advances that fundamentally transform the practice and delivery of joint arthroplasty are yet to be realized, despite the broad range of applications as we continue to search for meaningful and appropriate use of AI. AI literature in hip and knee arthroplasty between 2018 and 2021 regarding image-based analyses, value-based care, remote patient monitoring, and augmented reality was reviewed. Concerns surrounding meaningful use and appropriate methodological approaches of AI in joint arthroplasty research are summarized. Of the 233 AI-related orthopaedics articles published, 178 (76%) constituted original research, while the rest consisted of editorials or reviews. A total of 52% of original AI-related research concerns hip and knee arthroplasty (n = 92), and a narrative review is described. Three studies were externally validated. Pitfalls surrounding present-day research include conflating vernacular (“AI/machine learning”), repackaging limited registry data, prematurely releasing internally validated prediction models, appraising model architecture instead of inputted data, withholding code, and evaluating studies using antiquated regression-based guidelines. While AI has been applied to a variety of hip and knee arthroplasty applications with limited clinical impact, the future remains promising if the question is meaningful, the methodology is rigorous and transparent, the data are rich, and the model is externally validated. Simple checkpoints for meaningful AI adoption include ensuring applications focus on: administrative support over clinical evaluation and management; necessity of the advanced model; and the novelty of the question being answered.

Cite this article: Bone Joint J 2022;104-B(12):1292–1303.

Severe leg pain in a patient after total hip replacement was found to be caused by compression of the sciatic nerve by methylmethacrylate cement which had leaked from the acetabulum during fixation of the acetabular cup. The pain persisted for six years but was immediately relieved by removal of the cement mass

We report a case of late dissociation of a one-piece metal-backed acetabular component, associated with a prolific soft-tissue reaction to the polyethylene debris. The polyethylene liner was not visible on the radiographs. The metal-backed shell could not be removed because of bone ingrowth. We recommend that modular systems be utilised in cementless arthroplasty of the hip and that radiographic markers be incorporated in the polyethylene of the acetabular cup

A new method to reconstruct major acetabular floor defects is described. It relies on the placement of special nails into each of the three bones of the hemipelvis. Curved lugs attached to the nails are coalesced using bone cement forming a platform onto which a standard acetabular prosthesis is located. Forty-seven cases are reported with a mean follow-up of 4.4 years (1 to 8). No loosening of an acetabular cup or migration of the device has occurred

Four en-bloc resections for malignant tumours of the hip, the peri-acetabular region and the iliac wing were reconstructed using an irradiated hemipelvic allograft together with a total hip prosthesis. Technical aspects include the use of an anterior Enneking approach which excises the previous biopsy site, division and re-attachment of the iliac crest and fixation of the prosthesis using a modified acetabular cup and three polypropylene artificial ligaments to increase the stability of the joint. Weight-bearing was allowed at three months. The oncological and clinical results were satisfactory after a mean follow-up of 19 months, with walking distances of 500 metres to two kilometres without pain

The Wroblewski golf ball acetabular cup was introduced by surgeons using the trochanteric osteotomy approach for revision total hip replacement (THR) in order to reduce the rate of dislocation. We have routinely used the Ogee long posterior wall (Ogee LPW) and the Wroblewski angle bore cups in THR. Although the new Wroblewski golf ball cup performed well there was a significant early rate of dislocation of 20%. Our rate of dislocation over a period of ten years using the Ogee LPW and Wroblewski angle bore cups had been 0.52%. We present our findings and an investigation as to why the new cup has such a high rate of dislocation when used with the posterior approach. We show that a relatively small change in the design of the acetabular component resulted in significant adverse clinical results

We implanted 203 smooth-stemmed femoral components before January 1988. The femoral component used was anatomically shaped, fluted and made of titanium. Thirty-two hips were revised due to mid-thigh pain, and the femoral implant was found to be loose in all. In the 157 patients with a two-year follow-up, the Merle d'Aubigne and pain scores for completely cementless arthroplasties were similar to those for hybrid prostheses (cemented acetabular cup and cementless femoral stem). Of the 145 cases with two-year radiographic follow-up, 59 had extensive radiolucencies and 22 were unstable. The five-year cumulative survival rate was 77%. Implantation of this stem should be restricted to patients in whom cement fixation is contra-indicated

We selected randomly a consecutive series of 162 patients requiring hip replacement to receive either a cementless, hemispherical, modular, titanium acetabular cup or a cemented, all-polyethylene cup. These replacements were performed by two surgeons in four general hospitals. The same surgical technique was used and a 26 mm metal-head femoral component was used in every case. After exclusions, 115 hips were studied for differences in rates of wear and osteolysis. The mean clinical follow-up was eight years and the mean radiological follow-up, 6.5 years. The cementless cups wore at a mean rate of 0.15 mm per year and the cemented cups at 0.07 mm per year. This difference was significant (p < 0.0001). Our findings in this mid-term study suggest that cementless cups wear more than cemented cups

Polyethylene acetabular cups retrieved at revision surgery were measured by a shadowgraph technique to determine linear wear, and the values were compared with those obtained from radiographs. There was a close correlation between them, although the radiographic measurements slightly underestimated the true wear. Average linear wear rates for surface-replacement components were much greater than those for conventional prostheses with femoral heads up to 32 mm in diameter. Volumetric wear, calculated using a new formula, was found to be less than previously reported in vivo, and similar in magnitude to the results of experimental wear tests in vitro. The volumetric wear rates were greatest for the surface-replacement components and, for conventional components, were found to increase in a linear manner with component diameter

Between February 1975 and August 1976, 195 total hip replacements using Stanmore components were performed; of these, 146 were in 135 patients who had not had previous hip surgery. At review 52 had died, but none of the others was lost to follow-up. Of the 52, two had had a second operation, one for infection and one for recurrent dislocation. In the remaining 83 patients (92 hips) five revisions were necessary: four for aseptic loosening, and one for stem fracture. The remaining 78 patients had little or no pain and little restriction of activity. After a follow-up period of at least nine years, the survival rate of the prosthesis was 95%. There had been migration of the femoral component in five cases and migration of the acetabular cup in one case, but no wear of the acetabular component could be demonstrated

We measured polyethylene wear in 231 porous-coated uncemented acetabular cups. We divided the hips into two groups according to the fixation of the femoral component, by cementing (n = 97) or press-fit (n = 134). Follow-up was from three to five years. The patients in two sub-groups were matched for weight, diagnosis, sex, age and length of follow-up. The linear wear rate of cups articulated with uncemented femoral components (0.22 mm/year) was significantly higher than the wear rate (0.15 mm/year) of cups articulated within cemented femoral components (p < 0.05). These results can be compared with previously reported wear rates of 0.08 mm/year for cemented all-polyethylene cups and 0.11 mm/year for cemented metal-backed cups. The higher wear rates of uncemented arthroplasties could jeopardize the long-term results of this type of hip replacement

We prospectively studied 217 patients who underwent 234 Elite Plus total hip arthroplasties. At a mean of 6.4 (SD 0.7) years post-operatively, 39 patients had died and 22 were either lost to follow-up or had no radiographs available. Clinical (Oxford hip score) and radiological assessments were performed on 156 patients (168 hip arthroplasties) who had a mean age of 67.7 (SD 9.7) years at operation. In the assessed group, 26 of 159 (16.4%) of femoral stems which had not already been revised and 19 of 159 (11.9%) of acetabular cups were definitely loose. In total, 52 of 168 (31%) of hips had either been revised or had definite evidence of loosening of a component. We could not establish any relationship between clinical and radiological outcomes. Despite the fact that the clinical outcome and rate of revision for the Elite Plus appeared to meet international standards, our findings give us cause for concern. We believe that joint registries should include radiological surveillance in order to provide reliable information about medium-term outcomes for hip prostheses

We reviewed the radiographs of 864 Charnley and STH (Zimmer) cemented total hip arthroplasties with a mean follow-up of seven years (maximum 16 years). Survivorship analysis was used to assess the correlation between radiographic performance and the bony containment or the coronal orientation of the acetabular cup. The cup orientation and containment were interrelated; all vertically oriented cups were completely contained, whereas 25% of more horizontal cups were only partially contained. Completely contained cups had significantly lower incidences of complete cement-bone radiolucency (p = 0.02) and of wear (p = 0.09). Vertically oriented cups had a lower incidence of continuous radiolucency than neutrally oriented cups, but this was not statistically significant (p = 0.25). Our results confirm the importance of complete bony containment, and also indicate that it is better to accept vertical orientation and obtain full bony coverage than to have a more horizontal orientation with partial containment

An analysis of 142 dislocations from a multicentre study of 6774 total hip replacements is reported. The incidence of dislocation was 2.1 per cent. Patients with neuromuscular disorder, those in a confused mental state, and those undergoing revision operations are at special risk. The commonest surgical error, present in nearly half the patients, was placing the acetabular cup too vertically or too anteverted. A less common fault was placing the femoral component too anteverted. Neither the original pathology nor the approach to the hip appeared to affect the likelihood of dislocation. The dislocations were divided into early and late, single and recurrent, and the success rate of treatment is described in these groups. One hundred and eleven patients (78.2 per cent) eventually obtained stability. Of those with a single dislocation, 62 per cent remained stable after a single manipulation. Thirty-four per cent of the patients required an open operation to achieve stability and it is suggested that, in many cases, open reduction alone is not enough; the mechanical fault needs to be corrected

We examined stainless-steel, cobalt-chrome, titanium and alumina and zirconia ceramic femoral heads retrieved at revision surgery. All the heads had articulated against ultra-high-molecular-weight-polyethylene (UHMWPE) acetabular cups. We studied the simulation of third-body damage and the wear of UHMWPE against the various materials used for the heads. The surfaces of the retrieved heads were analysed using a two-dimensional contacting profilometer. Third-body damage was characterised by the mean height of the scratches above the mean line (R. pm. ). The alumina ceramic and zirconia ceramic retrieved heads were found to have significantly less damage. In laboratory studies the ceramics were also more resistant to simulated third-body damage than the metal alloys. We studied the wear of UHMWPE against the damaged counterfaces in simple configuration tests. The damaged ceramics produced less polyethylene wear than the damaged metal counterfaces. The wear factor of UHMWPE against the damaged materials was dependent on the amount of damage to the counterface (R. p. ). Our study has shown the benefit of using the harder and more damage-resistant ceramic materials for femoral heads

We analysed revised Mathys isoelastic polyacetal femoral stems with stainless-steel heads and polyethylene acetabular cups from eight patients in order to differentiate various types of particle of wear debris. Loosening of isoelastic femoral stems is associated with the formation of polyacetal wear particles as well as those of polyethylene and metal. All three types of particle were isolated simultaneously by tissue digestion followed by sucrose gradient centrifugation. Polyacetal particles were either elongated, ranging from 10 to 150 μm in size, or shred-like and up to 100 μm in size. Polyethylene particles were elongated or granules, and were typically submicron or micronsized. Polyacetal and polyethylene polymer particles were differentiated by the presence of BaSO. 4. , which is added as a radiopaque agent to polyacetal but not to polyethylene. This was easily detectable by back-scattered SEM analysis and verified by energy dispersive x-ray analysis. Two types of foreign-body giant cell (FBGC) were recognised in the histological specimens. Extremely large FBGCs with irregular polygonal particles showing an uneven, spotty birefringence in polarised light were ascribed to polyacetal debris. Smaller FBGCs with slender elongated particles shining uniformly brightly in polarisation were related to polyethylene. Mononucleated histiocytes containing both types of particle were also present. Our findings offer a better understanding of the processes involved in the loosening of polyacetal stems and indicate why the idea of ‘isoelasticity’ proved to be unsuccessful in clinical practice

We report the findings from independent prospective clinical and laboratory-based joint-simulator studies of the performance of ceramic femoral heads of 22.225 mm diameter in cross-linked polyethylene (XLP) acetabular cups. We found remarkable qualitative and quantitative agreement between the clinical and simulator results for the wear characteristics with time, and confirmed that ceramic femoral heads penetrate the XLP cups at only about half the rate of otherwise comparable metal heads. In the clinical study, 19 hips in 17 patients were followed for an average of 77 months. In the hip-joint simulator a similar prosthesis was tested for 7.3 million cycles. Both clinical and simulator results showed relatively high rates of penetration over the first 18 months or 1.5 million cycles, followed by a very much lower wear thereafter. Once an initial bedding-in of 0.2 mm to 0.4 mm had taken place the subsequent rates of penetration were very small. The initial clinical wear during bedding-in averaged 0.29 mm/year; subsequent progression was an order of magnitude lower at about 0.022 mm/year, lower than the 0.07 mm/year in metal-to-UHMWP Charnley LFAs. Our results show the excellent tribological features of alumina-ceramic-to-XLP implants, and also confirm the value of well-designed joint simulators for the evaluation of total joint replacements