Aims. We have previously demonstrated raised cobalt and chromium levels in patients with larger diameter femoral heads, following metal-on-polyethylene uncemented total hip arthroplasty. Further data have been collected, to see whether these associations have altered with time and to determine the long-term implications for these patients and our practice. Methods. Patients from our previous study who underwent Trident-Accolade primary total hip arthroplasties using a metal-on-polyethylene bearing in 2009 were reviewed. Patients were invited to have their cobalt and chromium levels retested, and were provided an Oxford Hip Score. Serum ion levels were then compared between groups (28 mm, 36 mm, and 40 mm heads) and over time. Results. Metal ion levels were repeated in 33 patients. When comparing the results of serum metal ion levels over time, regardless of head size, there was a significant increase in both cobalt and chromium levels (p < 0.001). Two patients with larger head sizes had undergone revision arthroplasty with evidence of trunnion damage at surgery. Two patients within the 40 mm subgroup had metal ion levels above the MHRA (Medicines and Healthcare Products Regulatory Agency) threshold for detailed investigation. The increase in cobalt and chromium, when comparing the 36 mm and 40 mm groups with those of the 28 mm group, was not significant (36 mm vs 28 mm; p = 0.092/p = 0.191; 40 mm vs 28 mm; p = 0.200/p = 0.091, respectively). There was no difference, between femoral head sizes, when comparing outcome as measured by the Oxford Hip Score. Conclusion. This study shows an increase in cobalt and chromium levels over time for all modular femoral head sizes in patients with metal-on-polyethylene bearings, with two patients demonstrating ion levels above the MHRA threshold for failure, and a further two patients requiring revision surgery. These results may have clinical implications regarding longer term follow-up of patients and future implant choice, particularly among younger patients. Cite this article: Bone Joint J 2020;102-B(7):832–837

Aims. To report our experience with trunnion corrosion following metal-on-polyethylene total hip arthroplasty, in particular to report the spectrum of presentation and determine the mean time to presentation. Patients and Methods. We report the presenting symptoms and signs, intraoperative findings, and early results and complications of operative treatment in nine patients with a mean age of 74 years (60 to 86). The onset of symptoms was at a mean of seven years (3 to 18) after index surgery. Results. Patients presented with a variety of symptoms including pain, limp and rash. The preoperative mean serum cobalt level was 7.1 ppb (2.2 to 12.8) and mean serum chromium level was 2.2 ppb (0.5 to 5.2). Metal artifact reduction sequence (MARS) MRI showed fluid collection and possible pseudotumour formation in five hips, fluid collection in two hips, and synovitis/debris in one hip, with no MRI in one patient. Acetabular revision was performed in three patients, six patients underwent liner and head exchange only. The postoperative metal levels decreased in all patients: mean cobalt 0.5 ppb (0 to 1.8) and mean chromium 0.9 ppb (0 to 2.6) at a mean of five months (3 to 8) postoperatively. Seven patients had good pain relief and no complications at one year. There were two major complications requiring reoperation: acute infection at six weeks, for which the patient required two-stage reimplantation; and recurrent dislocation, for which the patient was revised to a dual mobility component. Conclusion. Trunnion corrosion in metal-on-polyethylene THA has a range of presenting symptoms, and may present later than previously described. A high index of suspicion is warranted, and serum cobalt and chromium levels are recommended for diagnosis. Patients should be counselled about possible postoperative complications. Cite this article: Bone Joint J 2018;100-B:898–902

Aims. In metal-on-polyethylene (MoP) total hip arthroplasty (THA), large metal femoral heads have been used to increase stability and reduce the risk of dislocation. The increased size of the femoral head can, however, lead to increased taper corrosion, with the release of metal ions and adverse reactions. The aim of this study was to investigate the relationship between the size of the femoral head and the levels of metal ions in the blood in these patients. Methods. A total of 96 patients were enrolled at two centres and randomized to undergo MoP THA using either a 32 mm metal head or a femoral head of between 36 mm and 44 mm in size, being the largest possible to fit the thinnest available polyethylene insert. The levels of metal ions and patient-reported outcome measures (Oxford Hip Score, University of California, Los Angeles Activity Scale) were recorded at two and five years postoperatively. Results. At five years, the median levels of chromium, cobalt, and titanium were 0.5 μg/l (interquartile range (IQR) 0.50 to 0.62), 0.24 μg/l (IQR 0.18 to 0.30), and 1.16 μg/l (IQR 1.0 to 1.68) for the 32 mm group, and 0.5 μg/l (IQR 0.5 to 0.54), 0.23 μg/l (IQR 0.17 to 0.39), and 1.30 μg/l (IQR 1 to 2.05) for the 36 mm to 44 mm group, with no significant difference between the groups (p = 0.825, p = 1.000, p = 0.558). There were increased levels of metal ions at two years postoperatively in seven patients in the 32 mm group, compared with four in the 36 mm to 44 mm group, and at five years postoperatively in six patients in the 32 mm group, compared with seven in the 36 mm to 44 mm group. There was no significant difference in either the OHS (p = 0.665) or UCLA (p = 0.831) scores between patients with or without an increased level of metal ions. Conclusion. In patients who underwent MoP THA, we found no differences in the levels of metal ions five years postoperatively between those with a femoral head of 32 mm and those with a femoral head of between 36 mm and 44 mm, and no corrosion-related revisions. As taper corrosion can start after five years, there remains a need for longer-term studies investigating the relationship between the size of the femoral head size and corrosion in patients undergoing MoP THA. Cite this article: Bone Joint J 2024;106-B(3 Supple A):31–37

The long term biological effects of wear products following total hip arthroplasty (THA) are unclear. However, the indications for THA are expanding, with increasingly younger patients undergoing the procedure. This prospective, randomised study compared two groups of patients undergoing THA after being randomised to receive one of two different bearing surfaces: metal-on-polyethylene (MoP) n = 22 and metal-on-metal (MoM) n = 23. We investigated the relationship between three variables: bearing surface (MoP vs MoM), whole blood levels of chromium (Cr) and cobalt (Co) and chromosomal aberrations in peripheral lymphocyte pre-operatively and at one, two and five years post-surgery. Our results demonstrated significantly higher mean cobalt and chromium (Co and Cr) blood levels in the MoM group at all follow-up points following surgery (p < 0.01), but there were no significant differences in the chromosomal aberration indices between MoM and MoP at two or five years (two years: p = 0.56, p = 0.08, p = 0.91, p = 0.51 and five years: p = 0.086, p = 0.73, p = 0.06, p = 0.34) for translocations, breaks, loss and gain of chromosomes respectively. Regression analysis showed a strong linear relationship between Cr levels and the total chromosomal aberration indices in the MoM group (R. 2.  = 0.90016), but this was not as strong for Co (R. 2. = 0.68991). In the MoP group, the analysis revealed a poor relationship between Cr levels and the total chromosomal aberration indices (R. 2. = 0.23908) but a slightly stronger relationship for Co (R. 2. = 0.64292). Across both groups, Spearman’s correlation detected no overall association between Co and Cr levels and each of the studied chromosomal aberrations. There remains no clear indication which THA bearing couple is the most biocompatible, especially in young active patients. While THA continues to be very successful at alleviating pain and restoring function, the long-term biological implications of the procedure still require further scrutiny. Cite this article: Bone Joint J 2015;97-B:1183–91

The aim of this study was to investigate the possible benefit of large-head metal-on-metal bearing on a stem for primary hip replacement compared with a 28 mm diameter conventional metal-on-polyethylene bearing in a prospective randomised controlled trial. We investigated cemented stem behaviour between these two different bearings using Einzel-Bild-Röntgen-Analyse, clinical and patient reported measures (Harris hip score, Western Ontario and McMaster Universities osteoarthritis index, Short Form-36 and satisfaction) and whole blood metal ion levels at two years. A power study indicated that 50 hips were needed in each group to detect subsidence of > 5 mm at two years with a p-value of < 0.05. . Significant improvement (p < 0.001) was found in the mean clinical and patient reported outcomes at two years for both groups. Comparison of outcomes between the groups at two years showed no statistically significant difference for mean stem migration, clinical and patient reported outcomes; except overall patient satisfaction which was higher for metal-on-metal group (p = 0.05). Metal ion levels were raised above the Medicines and Healthcare products Regulatory Agency advised safety level (7 µg per litre) in 20% of the metal-on-metal group and in one patient in metal-on-polyethylene group (who had a metal-on-metal implant on the contralateral side). Two patients in the metal-on-metal group were revised, one for pseudotumour and one for peri-prosthetic fracture. . Use of large modular heads is associated with a risk of raised whole blood metal ion levels despite using a proven bearing from resurfacing. The head-neck junction or excess stem micromotion are possibly the weak links warranting further research

A 70-year-old man with an uncemented metal-on-polyethylene total hip prosthesis underwent revision arthroplasty 33 months later because of pain, swelling and recurrent dislocation. There appeared to be corrosion and metal release from the prosthetic head, resulting in pseudotumour formation and severe local soft-tissue destruction. The corrosion occurred at the junction between the titanium-molybdenum-zirconium-iron taper and the cobalt-chrome-molybdenum head, but the mechanism was unproven.

Aims. To analyze the short-term outcome of two types of total wrist arthroplasty (TWA) in terms of wrist function, migration, and periprosthetic bone behaviour. Methods. A total of 40 patients suffering from non-rheumatoid wrist arthritis were enrolled in a randomized controlled trial comparing the ReMotion and Motec TWAs. Patient-rated and functional outcomes, radiological changes, blood metal ion levels, migration measured by model-based radiostereometric analysis (RSA), bone mineral density (BMD) measured by dual-energy X-ray absorptiometry (DXA), complications, loosening, and revision rates at two years were compared. Results. Patient-Rated Wrist and Hand Evaluation (PRWHE) scores, abbreviated version of the Disabilities of the Arm, Shoulder and Hand questionnaire (QuickDASH) scores, and pain improved similarly and significantly in both groups. Wrist motion improved significantly in the Motec group only, and forearm rotation in the ReMotion group only. Cobalt (Co) and chromium (Cr) blood ion levels were significantly higher in the metal-on-metal (MoM) Motec group than in the metal-on-polyethylene (MoP) ReMotion group. Mean total translation was 0.65 mm (95% confidence interval (CI) 0.26 to 1.12) and 0.27 mm (95% CI 0.14 to 0.47) for the ReMotion carpal and radial components, and 0.32 mm (95% CI 0.22 to 0.45) and 0.26 mm (95% CI 0.20 to 0.34) for the Motec metacarpal and radial components, respectively. Apart from dorsal and volar tilts, which were significantly higher for the radial ReMotion than for the Motec component, no significant differences in absolute migration occurred. BMD around the radial components never returned to baseline. Almost one-third of patients required reoperation due to complications. Two ReMotion implants were revised to Motec TWAs due to carpal component loosening, and three Motec MoM articulations were revised to metal-on-polyether ether ketone due to painful synovitis. Conclusion. Both implants provided matched function and were stable at short-term follow-up, but with a high complication rate. This procedure should be restricted to specialist centres undertaking prospective analysis until its role is clarified. Cite this article: Bone Joint J 2022;104-B(10):1132–1141

The biological significance of cobalt-chromium wear particles from metal-on-metal hip replacements may be different to the effects of the constituent metal ions in solution. Bacteria may be able to discriminate between particulate and ionic forms of these metals because of a transmembrane nickel/cobalt-permease. It is not known whether wear particles are bacteriocidal. We compared the doubling time of coagulase negative staphylococcus, Staphylococcus aureus and methicillin resistant S. aureus when cultured in either wear particles from a metal-on-metal hip simulator, wear particles from a metal-on-polyethylene hip simulator, metal ions in solution or a control. Doubling time halved in metal-on-metal (p = 0.003) and metal-on-polyethylene (p = 0.131) particulate debris compared with the control. Bacterial nickel/cobalt-transporters allow metal ions but not wear particles to cross bacterial membranes. This may be useful for testing the biological characteristics of different wear debris. This experiment also shows that metal-on-metal hip wear debris is not bacteriocidal

We have studied the relationship between metal ion levels and lymphocyte counts in patients with metal-on-metal hip resurfacings. Peripheral blood samples were analysed for lymphocyte subtypes and whole blood cobalt and chromium ion levels in 68 patients (34 with metal-on-metal hip resurfacings and 34 with standard metal-on-polyethylene total hip replacements). All hip components were radiologically well-fixed and the patients were asymptomatic. Cobalt and chromium levels were significantly elevated in the patients with metal-on-metal hip resurfacings, compared with the patients with standard metal-on-polyethylene designs (p < 0.0001). There was a statistically significant decrease in the level of CD8. +. cells (T-cytotoxic/suppressor) (p = 0.005) in the metal-on-metal hip resurfacing group. A threshold level of blood cobalt and chromium ions was associated with reduced CD8. +. T-cell counts. We have no evidence that our patients suffered as a result of this reduced level of CD8. +. T-cells

Dislocation is a common reason for revision following total hip replacement. This study investigated the relationship between the bearing surface and the risk of revision due to dislocation. It was based on 110 239 primary total hip replacements with a diagnosis of osteoarthritis collected by the Australian Orthopaedic Association National Joint Replacement Registry between September 1999 and December 2007. A total of 862 (0.78%) were revised because of dislocation. Ceramic-on-ceramic bearing surfaces had a lower risk of requiring revision due to dislocation than did metal-on-polyethylene and ceramic-on-polyethylene surfaces, with a follow-up of up to seven years. However, ceramic-on-ceramic implants were more likely to have larger prosthetic heads and to have been implanted in younger patients. The size of the head of the femoral component and age are known to be independent predictors of dislocation. Therefore, the outcomes were stratified by the size of the head and age. There is a significantly higher rate of revision for dislocation in ceramic-on-ceramic bearing surfaces than in metal-on-polyethylene implants when smaller sizes (≤ 28 mm) of the head were used in younger patients (< 65 years) (hazard ratio = 1.53, p = 0.041) and also with larger (> 28 mm) and in older patients (≥ 65 years) (hazard ratio = 1.73, p = 0.016)

Previous research has shown an increase in chromosomal aberrations in patients with worn implants. The type of aberration depended on the type of metal alloy in the prosthesis. We have investigated the metal-specific difference in the level of DNA damage (DNA stand breaks and alkali labile sites) induced by culturing human fibroblasts in synovial fluid retrieved at revision arthroplasty. All six samples from revision cobalt-chromium metal-on-metal and four of six samples from cobalt-chromium metal-on-polyethylene prostheses caused DNA damage. By contrast, none of six samples from revision stainless-steel metal-on-polyethylene prostheses caused significant damage. Samples of cobalt-chromium alloy left to corrode in phosphate-buffered saline also caused DNA damage and this depended on a synergistic effect between the cobalt and chromium ions. Our results further emphasise that epidemiological studies of orthopaedic implants should take account of the type of metal alloy used

Aims. There are limited published data detailing the volumetric material loss from tapers of conventional metal-on-polyethylene (MoP) total hip arthroplasties (THAs). Our aim was to address this by comparing the taper wear rates measured in an explanted cohort of the widely used Exeter THA with those measured in a group of metal-on-metal (MoM) THAs. Patients and Methods. We examined an existing retrieval database to identify all Exeter V40 and Universal MoP THAs. Volumetric wear analysis of the taper surfaces was conducted using previously validated methodology. These values were compared with those obtained from a series of MoM THAs using non-parametric statistical methodology. A number of patient and device variables were accounted for using multiple regression modelling. Results. A total of 95 Exeter MoP and 249 MoM THAs were examined. The median volumetric loss from the MoM cohort was over four times larger than that from the MoP cohort (1.01 mm. 3. vs 0.23 mm. 3. , p < 0.001), despite a significantly shorter median period in vivo for the MoM group (48 months vs 90 months, p < 0.001). Multiple regression modelling indicated that the dominant variables leading to greater female taper material loss were bearing diameter (p < 0.001), larger female taper angles (p < 0.001), and male titanium stem tapers (p < 0.001). Conclusion. Consistent with the long-term clinical success of the device, the volumetric material loss from Exeter femoral head tapers was, in general, small compared with that from larger-diameter MoM head tapers. Cite this article: Bone Joint J 2018;100-B:1310–9

Aims. The aim of this study was to describe temporal trends and survivorship of total hip arthroplasty (THA) in very young patients, aged ≤ 20 years. Patients and Methods. A descriptive observational study was undertaken using data from the National Joint Registry (NJR) for England, Wales, Northern Ireland and the Isle of Man between April 2003 and March 2017. All patients aged ≤ 20 years at the time of THA were included and the primary outcome was revision surgery. Descriptive statistics were used to summarize the data and Kaplan–Meier estimates calculated for the cumulative implant survival. Results. A total of 769 THAs were performed in 703 patients. The median follow-up was 5.1 years (interquartile range (IQR) 2.6 to 7.8). Eight patients died and 35 THAs were revised. The use of metal-on-metal (MoM) bearings and resurfacing procedures declined after 2008. The most frequently recorded indications for revision were loosening (20%) and infection (20%), although the absolute risk of these events occurring was low (0.9%). Factors associated with lower implant survival were MoM and metal-on-polyethylene (MoP) bearings and resurfacing arthroplasty (vs ceramic-on-polyethylene (CoP) and ceramic-on-ceramic (CoC) bearings, p = 0.002), and operations performed by surgeons who undertook few THAs in this age group as recorded in the NJR (vs those with five or more recorded operations, p = 0.030). Kaplan–Meier estimates showed 96% (95% confidence interval (CI) 94% to 98%) survivorship of implants at five years. Conclusion. Within the NJR, the overall survival for very young patients undergoing THA exceeded 96% during the first five postoperative years. In the absence of studies that can better account for differences in the characteristics of the patients, surgeons should consider the association between early revision and the type of implant, the number of THAs performed in these patients, and the bearing surface when performing THA in very young patients. Cite this article: Bone Joint J 2018;100-B:1320–9

Aims. Periprosthetic joint infection (PJI) is a serious complication of total hip arthroplasty (THA). Different bearing surface materials have different surface properties and it has been suggested that the choice of bearing surface may influence the risk of PJI after THA. The objective of this meta-analysis was to compare the rate of PJI between metal-on-polyethylene (MoP), ceramic-on-polyethylene (CoP), and ceramic-on-ceramic (CoC) bearings. Patients and Methods. Electronic databases (Medline, Embase, Cochrane library, Web of Science, and Cumulative Index of Nursing and Allied Health Literature) were searched for comparative randomized and observational studies that reported the incidence of PJI for different bearing surfaces. Two investigators independently reviewed studies for eligibility, evaluated risk of bias, and performed data extraction. Meta-analysis was performed using the Mantel–Haenzel method and random-effects model in accordance with methods of the Cochrane group. Results. Our search strategy revealed 2272 studies, of which 17 met the inclusion criteria and were analyzed. These comprised 11 randomized controlled trials and six observational studies. The overall quality of included studies was high but the observational studies were at high risk of bias due to inadequate adjustment for confounding factors. The overall cumulative incidence of PJI across all studies was 0.78% (1514/193 378). For each bearing combination, the overall incidence was as follows: MoP 0.85% (1353/158 430); CoP 0.38% (67/17 489); and CoC 0.53% (94/17 459). The meta-analysis showed no significant difference between the three bearing combinations in terms of risk of PJI. Conclusion. On the basis of the clinical studies available, there is no evidence that bearing choice influences the risk of PJI. Future research, including basic science studies and large, adequately controlled registry studies, may be helpful in determining whether implant materials play a role in determining the risk of PJI following arthroplasty surgery. Cite this article: Bone Joint J 2018;100-B:134–42

Aims. Fretting and corrosion at the modular head/neck junction, known as trunnionosis, in total hip arthroplasty (THA) is a cause of adverse reaction to metal debris (ARMD). We describe the outcome of revision of metal-on-polyethylene (MoP) THA for ARMD due to trunnionosis with emphasis on the risk of major complications. Patients and Methods. A total of 36 patients with a MoP THA who underwent revision for ARMD due to trunnionosis were identified. Three were excluded as their revision had been to another metal head. The remaining 33 were revised to a ceramic head with a titanium sleeve. We describe the presentation, revision findings, and risk of complications in these patients. Results. The patients presented with pain, swelling, stiffness, or instability and an inflammatory mass was confirmed radiologically. Macroscopic material deposition on the trunnion was seen in all patients, associated with ARMD. Following revision, six (18.2%) dislocated, requiring further revision in four. Three (9.1%) developed a deep infection and six (18.2%) had significant persistent pain without an obvious cause. One developed a femoral artery thrombosis after excision of an iliofemoral pseudotumor, requiring a thrombectomy. Conclusion. The risk of serious complications following revision MoP THA for ARMD associated with trunnionosis is high. In the presence of extensive tissue damage, a constrained liner or dual mobility construct is recommended in these patients. Cite this article: Bone Joint J 2018;100-B:720–4

Symptomatic cobalt toxicity from a failed total hip replacement is a rare but devastating complication. It has been reported following revision of fractured ceramic components, as well as in patients with failed metal-on-metal articulations. Potential clinical findings include fatigue, weakness, hypothyroidism, cardiomyopathy, polycythaemia, visual and hearing impairment, cognitive dysfunction, and neuropathy. We report a case of an otherwise healthy 46-year-old patient, who developed progressively worsening symptoms of cobalt toxicity beginning approximately six months following synovectomy and revision of a fractured ceramic-on-ceramic total hip replacement to a metal-on-polyethylene bearing. The whole blood cobalt levels peaked at 6521 µg/l. The patient died from cobalt-induced cardiomyopathy. Implant retrieval analysis confirmed a loss of 28.3 g mass of the cobalt–chromium femoral head as a result of severe abrasive wear by ceramic particles embedded in the revision polyethylene liner. Autopsy findings were consistent with heavy metal-induced cardiomyopathy. We recommend using new ceramics at revision to minimise the risk of wear-related cobalt toxicity following breakage of ceramic components. Cite this article: Bone Joint J 2013;95-B:31–7

Aims. We present a case series of ten metal-on-polyethylene total hip arthroplasties (MoP THAs) with delayed dislocation associated with unrecognised adverse local tissue reaction due to corrosion at the trunnion and pseudotumour formation. . Methods. The diagnosis was not suspected in nine of the ten patients (six female/four male; mean age 66 years), despite treatment in a specialist unit (mean time from index surgery to revision was 58 months, 36 to 84). It was identified at revision surgery and subsequently confirmed by histological examination of resected tissue. Pre-operative assessment and culture results ruled out infection. A variety of treatment strategies were used, including resection of the pseudotumour and efforts to avoid recurrent dislocation. . Results. The rate of complications was high and included three deep infections, two patients with recurrent dislocation, and one recurrent pseudotumour. . Conclusion. This series (mean follow-up of 76 months following index procedure and 19 months following revision THA) demonstrates that pseudotumour is an infrequent but important contributor to delayed instability following MoP THA. It is easy to overlook in the differential diagnosis, especially if the alignment of the components is less than optimal, leading to an assumption that malalignment is the cause of the dislocation. The instability is likely to be multifactorial and the revision surgery is complex. Take home message: Due to the high complication rate associated with revision in this cohort, the diagnosis should be borne in mind when counselling patients regarding the risks of revision surgery. . Cite this article: Bone Joint J 2016;98-B:187–93

We compared the incidence of pseudotumours after large head metal-on-metal (MoM) total hip arthroplasty (THA) with that after conventional metal-on-polyethylene (MoP) THA and assessed the predisposing factors to pseudotumour formation. . From a previous randomised controlled trial which compared large head (38 mm to 60 mm) cementless MoM THA with conventional head (28 mm) cementless MoP THA, 93 patients (96 THAs: 41 MoM (21 males, 20 females, mean age of 64 years, standard deviation (. sd. ) 4) and 55 MoP (25 males, 30 females, mean age of 65 years, . sd. 5) were recruited after a mean follow-up of 50 months (36 to 64). . The incidence of pseudotumours, measured using a standardised CT protocol was 22 (53.7%) after MoM THA and 12 (21.8%) after MoP THA. Women with a MoM THA were more likely to develop a pseudotumour than those with a MoP THA (15 vs 7, odds ratio (OR) = 13.4, p < 0.001). There was a similar incidence of pseudotumours in men with MoM THAs and those with MoP THAs (7 vs 5, OR = 2.1, p = 0.30). Elevated cobalt levels (≥ 5 microgram/L) were only associated with pseudotumours in women with a MoM THA. There was no difference in mean Oxford and Harris hip scores between patients with a pseudotumour and those without. . Contrary to popular belief, pseudotumours occur frequently around MoP THAs. Women with a MoM THA and an elevated cobalt level are at greatest risk. In this study, pseudotumours had no effect on the functional outcome after either large head MoM or conventional MoP THA. Cite this article: Bone Joint J 2015;97-B:1481–7

We carried out a cross-sectional study with analysis of the demographic, clinical and laboratory characteristics of patients with metal-on-metal hip resurfacing, ceramic-on-ceramic and metal-on-polyethylene hip replacements. Our aim was to evaluate the relationship between metal-on-metal replacements, the levels of cobalt and chromium ions in whole blood and the absolute numbers of circulating lymphocytes. We recruited 164 patients (101 men and 63 women) with hip replacements, 106 with metal-on-metal hips and 58 with non-metal-on-metal hips, aged < 65 years, with a pre-operative diagnosis of osteoarthritis and no pre-existing immunological disorders. Laboratory-defined T-cell lymphopenia was present in13 patients (15%) (CD8. +. lymphopenia) and 11 patients (13%) (CD3. +. lymphopenia) with unilateral metal-on-metal hips. There were significant differences in the absolute CD8. +. lymphocyte subset counts for the metal-on-metal groups compared with each control group (p-values ranging between 0.024 and 0.046). Statistical modelling with analysis of covariance using age, gender, type of hip replacement, smoking and circulating metal ion levels, showed that circulating levels of metal ions, especially cobalt, explained the variation in absolute lymphocyte counts for almost all lymphocyte subsets

Aims

Metal and ceramic humeral head bearing surfaces are available choices in anatomical shoulder arthroplasties. Wear studies have shown superior performance of ceramic heads, however comparison of clinical outcomes according to bearing surface in total shoulder arthroplasty (TSA) and hemiarthroplasty (HA) is limited. This study aimed to compare the rates of revision and reoperation following metal and ceramic humeral head TSA and HA using data from the National Joint Registry (NJR), which collects data from England, Wales, Northern Ireland, Isle of Man and the States of Guernsey.

Metal-on-metal bearings for total hip replacement (THR) are becoming increasingly popular. Improved wear characteristics mean that these articulations are being inserted into younger patients in the form of THR and resurfacing procedures. This has led to concerns regarding potential carcinogenicity because of the increased exposure to metal ions that the procedure brings. We have studied the serum cobalt and chromium concentrations in patients who had primary, well-fixed Ring metal-on-metal THRs for more than 30 years. The levels of cobalt and chromium were elevated by five and three times, respectively compared with those in our reference groups. Metal-on-metal articulations appear to be the source of metal ions throughout the life of the prosthesis. In three patients who had undergone revision of a previous metal-on-metal THR to a metal-on-polyethylene replacement the levels of metal ions were within the normal range. The elevations of cobalt and chromium ions seen in our study were comparable with those in patients with modern metal-on-metal THRs

Metal-on-metal hip bearings are being implanted into younger patients. The consequence of elevated levels of potentially carcinogenic metal ions is therefore a cause for concern. We have determined the levels of cobalt (Co), chromium (Cr), titanium (Ti) and vanadium (Va) in the urine and whole blood of patients who had had metal-on-metal and metal-on-polyethylene articulations in situ for more than 30 years. We compared these with each other and with the levels for a control group of subjects. We found significantly elevated levels of whole blood Ti, Va and urinary Cr in all arthroplasty groups. The whole blood and urine levels of Co were grossly elevated, by a factor of 50 and 300 times respectively in patients with loose metal-on-metal articulations when compared with the control group. Stable metal-on-metal articulations showed much lower levels. Elevated levels of whole blood or urinary Co may be useful in identifying metal-on-metal articulations which are loose

Aims

Modular dual-mobility (DM) articulations are increasingly used during total hip arthroplasty (THA). However, concerns remain regarding the metal liner modularity. This study aims to correlate metal artifact reduction sequence (MARS)-MRI abnormalities with serum metal ion levels in patients with DM articulations.

Tribocorrosion at the head–neck taper interface – so-called ‘taperosis’ – may be a source of metal ions and particulate debris in metal-on-polyethylene total hip arthroplasty (THA). We examined the effect of femoral head length on fretting and corrosion in retrieved head–neck tapers in vivo for a minimum of two years (mean 8.7 years; 2.6 to 15.9). A total of 56 femoral heads ranging from 28 mm to 3 mm to 28 mm + 8 mm, and 17 femoral stems featuring a single taper design were included in the study. Fretting and corrosion were scored in three horizontally oriented concentric zones of each taper by stereomicroscopy. Head length was observed to affect fretting (p = 0.03), with 28 mm + 8 mm femoral heads showing greater total fretting scores than all other head lengths. The central zone of the femoral head bore taper was subject to increased fretting damage (p = 0.01), regardless of head length or stem offset. High-offset femoral stems were associated with greater total fretting of the bore taper (p = 0.04). Increased fretting damage is seen with longer head lengths and high-offset femoral stems, and occurs within a central concentric zone of the femoral head bore taper. Further investigation is required to determine the effect of increased head size, and variations in head–neck taper design. Cite this article: Bone Joint J 2015; 97-B:911–16

The purpose of this study was to establish if the Bateman prosthesis functions as a bipolar device moving primarily at the inner metal-on-polyethylene bearing as originally proposed, or as a unipolar hemiarthroplasty moving at the outer metal-on-cartilage surface as has recently been suggested. One hundred hips were examined at one year follow-up; 78 were examined again at two to four years. The replacement was performed for arthritis in 76 hips and for femoral neck fracture in 24. Movement was assessed both with and without weight-bearing. In 80% of the arthritis group the prosthesis functioned as a bipolar hip replacement with movement occurring primarily at the inner metal-on-polyethylene surface. By contrast, in 75% of the fracture group the prosthesis functioned largely as a unipolar device with movement occurring primarily at the outer metal-on-cartilage surface. In all cases examined serially the movement pattern was the same at two to four years as it has been at one year. Clearly, the action of the prosthesis depends on the condition of the acetabular cartilage

We aimed to assess whether the immunological abnormalities which have been observed in patients with loose total hip replacements (THRs) are present in patients with a well-fixed prosthesis. We examined blood samples from 39 healthy donors, 22 patients before THR and 41 with well-fixed THRs of different types (15 metal-on-metal, 13 metal-on-polyethylene, 13 ceramic-on-ceramic). Before THR, the patients showed a decrease in leukocytes and myeloid cells in comparison with healthy donors, and a prevalence of type-1 T lymphocytes, which was confirmed by the increase in ratio of interferon-γ to interleukin 4. Moreover, patients with metal-on-metal or metal-on-polyethylene implants showed a significant decrease in the number of T lymphocytes and a significant increase in the serum level of chromium and cobalt, although no significant correlation was observed with the immunological changes. In the ceramic-on-ceramic group, leukocytes and lymphocyte subsets were not significantly changed, but a significant increase in type-2 cytokines restored the ratio of interferon-γ to interleukin 4 to normal values. We conclude that abnormalities of the cell-mediated immune response may be present in patients with a well-fixed THR, and that the immunological changes are more evident in those who have at least one metal component in the articular coupling

Hip simulators have been used for ten years to determine the tribological performance of large-head metal-on-metal devices using traditional test conditions. However, the hip simulator protocols were originally developed to test metal-on-polyethylene devices. We have used patient activity data to develop a more physiologically relevant test protocol for metal-on-metal devices. This includes stop/start motion, a more appropriate walking frequency, and alternating kinetic and kinematic profiles. There has been considerable discussion about the effect of heat treatments on the wear of metal-on-metal cobalt chromium molybdenum (CoCrMo) devices. Clinical studies have shown a higher rate of wear, levels of metal ions and rates of failure for the heat-treated metal compared to the as-cast metal CoCrMo devices. However, hip simulator studies in vitro under traditional testing conditions have thus far not been able to demonstrate a difference between the wear performance of these implants. Using a physiologically relevant test protocol, we have shown that heat treatment of metal-on-metal CoCrMo devices adversely affects their wear performance and generates significantly higher wear rates and levels of metal ions than in as-cast metal implants

Aims

Oxidized zirconium (OxZi) and highly cross-linked polyethylene (HXLPE) were developed to minimize wear and risk of osteolysis in total hip arthroplasty (THA). However, retrieval studies have shown that scratched femoral heads may lead to runaway wear, and few reports of long-term results have been published. The purpose of this investigation is to report minimum ten-year wear rates and clinical outcomes of THA with OxZi femoral heads on HXLPE, and to compare them with a retrospective control group of cobalt chrome (CoCr) or ceramic heads on HXLPE.

Aims

The aim of this study was to report the long-term follow-up of cemented short Exeter femoral components when used in primary total hip arthroplasty (THA).

Aims

Accurate diagnosis of chronic periprosthetic joint infection (PJI) presents a significant challenge for hip surgeons. Preoperative diagnosis is not always easy to establish, making the intraoperative decision-making process crucial in deciding between one- and two-stage revision total hip arthroplasty (THA). Calprotectin is a promising point-of-care novel biomarker that has displayed high accuracy in detecting PJI. We aimed to evaluate the utility of intraoperative calprotectin lateral flow immunoassay (LFI) in THA patients with suspected chronic PJI.

Aims

Mechanical impingement of the iliopsoas (IP) tendon accounts for 2% to 6% of persistent postoperative pain after total hip arthroplasty (THA). The most common initiator is anterior acetabular component protrusion, where the anterior margin is not covered by anterior acetabular wall. A CT scan can be used to identify and measure this overhang; however, no threshold exists for determining symptomatic anterior IP impingement due to overhang. A case-control study was conducted in which CT scan measurements were used to define a threshold that differentiates patients with IP impingement from asymptomatic patients after THA.

The issues surrounding raised levels of metal ions in the blood following large head metal-on-metal total hip replacement (THR), such as cobalt and chromium, have been well documented. Despite the national popularity of uncemented metal-on-polyethylene (MoP) THR using a large-diameter femoral head, few papers have reported the levels of metal ions in the blood following this combination. Following an isolated failure of a 44 mm Trident–Accolade uncemented THR associated with severe wear between the femoral head and the trunnion in the presence of markedly elevated levels of cobalt ions in the blood, we investigated the relationship between modular femoral head diameter and the levels of cobalt and chromium ions in the blood following this THR. A total of 69 patients received an uncemented Trident–Accolade MoP THR in 2009. Of these, 43 patients (23 men and 20 women, mean age 67.0 years) were recruited and had levels of cobalt and chromium ions in the blood measured between May and June 2012. The patients were then divided into three groups according to the diameter of the femoral head used: 12 patients in the 28 mm group (controls), 18 patients in the 36 mm group and 13 patients in the 40 mm group. A total of four patients had identical bilateral prostheses in situ at phlebotomy: one each in the 28 mm and 36 mm groups and two in the 40 mm group. There was a significant increase in the mean levels of cobalt ions in the blood in those with a 36 mm diameter femoral head compared with those with a 28 mm diameter head (p = 0.013). The levels of cobalt ions in the blood were raised in those with a 40 mm diameter head but there was no statistically significant difference between this group and the control group (p = 0.152). The levels of chromium ions in the blood were normal in all patients. The clinical significance of this finding is unclear, but we have stopped using femoral heads with a diameter of ≤ 36 mm, and await further larger studies to clarify whether, for instance, this issue particularly affects this combination of components. Cite this article: Bone Joint J 2014;96-B:43–7

Aims

Professional dancers represent a unique patient population in the setting of hip arthroplasty, given the high degree of hip strength and mobility required by their profession. We sought to determine the clinical outcomes and ability to return to professional dance after total hip arthroplasty (THA) or hip resurfacing arthroplasty (HRA).

Aims

The Birmingham Hip Resurfacing (BHR) was introduced in 1997 to address the needs of young active patients using a historically proven large-diameter metal-on-metal (MoM) bearing. A single designer surgeon’s consecutive series of 130 patients (144 hips) was previously reported at five and ten years, reporting three and ten failures, respectively. The aim of this study was to extend the follow-up of this original cohort at 25 years.

Aims

Elevated blood cobalt levels secondary to metal-on-metal (MoM) hip arthroplasties are a suggested risk factor for developing cardiovascular complications including cardiomyopathy. Clinical studies assessing patients with MoM hips using left ventricular ejection fraction (LVEF) have found conflicting evidence of cobalt-induced cardiomyopathy. Global longitudinal strain (GLS) is an echocardiography measurement known to be more sensitive than LVEF when diagnosing early cardiomyopathies. The extent of cardiovascular injury, as measured by GLS, in patients with elevated blood cobalt levels has not previously been examined.

Aims

This study aims to assess the relationship between history of pseudotumour formation secondary to metal-on-metal (MoM) implants and periprosthetic joint infection (PJI) rate, as well as establish ESR and CRP thresholds that are suggestive of infection in these patients. We hypothesized that patients with a pseudotumour were at increased risk of infection.

United Kingdom National Institute for Health and Clinical Excellence guidelines recommend the use of total hip replacement (THR) for displaced intracapsular fractures of the femoral neck in cognitively intact patients, who were independently mobile prior to the injury. This study aimed to analyse the risk factors associated with revision of the implant and mortality following THR, and to quantify risk. National Joint Registry data recording a THR performed for acute fracture of the femoral neck between 2003 and 2010 were analysed. Cox proportional hazards models were used to investigate the extent to which risk of revision was related to specific covariates. Multivariable logistic regression was used to analyse factors affecting peri-operative mortality (< 90 days). A total of 4323 procedures were studied. There were 80 patients who had undergone revision surgery at the time of censoring (five-year revision rate 3.25%, 95% confidence interval 2.44 to 4.07) and 137 patients (3.2%) patients died within 90 days. After adjusting for patient and surgeon characteristics, an increased risk of revision was associated with the use of cementless prostheses compared with cemented (hazard ratio (HR) 1.33, p = 0.021). Revision was independent of bearing surface and head size. The risk of mortality within 90 days was significantly increased with higher American Society of Anesthesiologists (ASA) grade (grade 3: odds ratio (OR) 4.04, p < 0.001; grade 4/5: OR 20.26, p < 0.001; both compared with grades 1/2) and older age (≥ 75 years: OR 1.65, p = 0.025), but reduced over the study period (9% relative risk reduction per year). THR is a good option in patients aged < 75 years and with ASA 1/2. Cementation of the femoral component does not adversely affect peri-operative mortality but improves survival of the implant in the mid-term when compared with cementless femoral components. There are no benefits of using head sizes > 28 mm or bearings other than metal-on-polyethylene. More research is required to determine the benefits of THR over hemiarthroplasty in older patients and those with ASA grades > 2

Craig P, Bancroft G, Burton A, Collier S, Shaylor P, Sinha A. Raised levels of metal ions in the blood in patients who have undergone uncemented metal-on-polyethylene Trident–Accolade total hip replacement. Bone Joint J 2014;96-B:43–47

Aims

Head-taper corrosion is a cause of failure in total hip arthroplasty (THA). Recent reports have described an increasing number of V40 taper failures with adverse local tissue reaction (ALTR). However, the real incidence of V40 taper damage and its cause remain unknown. The aim of this study was to evaluate the long-term incidence of ALTR in a consecutive series of THAs using a V40 taper and identify potentially related factors.

Aims

Total hip arthroplasty (THA) is a very successful and cost-effective operation, yet debate continues about the optimum fixation philosophy in different age groups. The concept of the 'cementless paradox' and the UK 'Getting it Right First Time' initiative encourage increased use of cemented fixation due to purported lower revision rates, especially in elderly patients, and decreased cost.

Aims

Total hip arthroplasties (THAs) are performed by surgeons at various stages in training with varying levels of supervision, but we do not know if this is safe practice with comparable outcomes to consultant-performed THA. Our aim was to examine the association between surgeon grade, the senior supervision of trainees, and the risk of revision following THA.

Aims

A recent report from France suggested an association between the use of cobalt-chrome (CoCr) femoral heads in total hip arthroplasties (THAs) and an increased risk of dilated cardiomyopathy and heart failure. CoCr is a commonly used material in orthopaedic implants. If the reported association is causal, the consequences would be significant given the millions of joint arthroplasties and other orthopaedic procedures in which CoCr is used annually. We examined whether CoCr-containing THAs were associated with an increased risk of all-cause mortality, heart outcomes, cancer, and neurodegenerative disorders in a large national database.

Aims

The aim of this study was to evaluate the performance of first-generation annealed highly cross-linked polyethylene (HXLPE) in cementless total hip arthroplasty (THA).

Aims

Proximal femoral endoprosthetic replacements (PFEPRs) are the most common reconstruction option for osseous defects following primary and metastatic tumour resection. This study aimed to compare the rate of implant failure between PFEPRs with monopolar and bipolar hemiarthroplasties and acetabular arthroplasties, and determine the optimum articulation for revision PFEPRs.

Aims

This study compared the cobalt and chromium serum ion concentration of patients treated with two different metal-on-metal (MoM) hinged total knee arthroplasty (TKA) systems, as well as a titanium nitride (TiN)-coated variant.

Between 1988 and 1998 we implanted 318 total hip replacements (THRs) in 287 patients using the Plasmacup (B. Braun Ltd, Sheffield, United Kingdom) and a conventional metal-on-polyethylene articulation. The main indications for THR were primary or secondary osteoarthritis. At follow-up after a mean 11.6 years (7.6 to 18.4) 17 patients had died and 20 could not be traced leaving a final series of 280 THRs in 250 patients. There were 62 revisions (22.1%) in 59 patients. A total of 43 acetabular shells (15.4%) had been revised and 13 (4.6%) had undergone exchange of the liner. The most frequent indications for revision were osteolysis and aseptic loosening, followed by polyethylene wear. The mean Kaplan-Meier survival of the Plasmacup was 91% at ten years and 58% at 14 years. Osteolysis was found around 36 (17.1%) of the 211 surviving shells. The median annual rate of linear wear in the surviving shells was 0.12 mm/year and 0.25 mm/year in those which had been revised (p < 0.001). Polyethylene wear was a strong independent risk factor for osteolysis and aseptic loosening. The percentage of patients with osteolysis increased proportionately with each quintile of wear-rate. There is a high late rate of failure of the Plasmacup. Patients with the combination of this prosthesis and bearing should be closely monitored after ten years

Osteolysis is due to particulate wear debris and is responsible for the long-term failure of total hip replacements. It has stimulated the development of alternative joint surfaces such as metal-on-metal or ceramic-on-ceramic implants. Since 1988 the second-generation metal-on-metal implant Metasul has been used in over 60 000 hips. Analysis of 118 retrieved specimens of the head or cup showed rates of wear of approximately 25 μm for the whole articulation per year in the first year, decreasing to about 5 μm per year after the third. Metal surfaces have a ‘self-polishing’ capacity. Scratches are worn out by further joint movement. Volumetric wear was decreased some 60-fold compared with that of metal-on-polyethylene implants, suggesting that second-generation metal-on-metal prostheses may considerably reduce osteolysis

1. Prosthetic acetabular cups of the Charnley and McKee-Farrar designs were cemented into cadaveric pelves using different procedures for preparing the acetabulum. 2. The torsional moments needed to loosen these cups were measured. 3. The torsional moments so measured were found to be from about four to more than twenty times higher than the frictional moments measured in independent tests on the two designs of prosthesis. 4. It is argued that late looseness of the acetabular component after total hip replacement, in the absence of infection, seems most likely to be due to thermal damage to the bone occurring at the time of polymerisation of the cement, and to subsequent bone resorption. 5. Surgical preparation of the acetabulum should include removal of all the articular cartilage and cleaning of the acetabular fossa, but the drilling of additional holes in the floor of the acetabulum seems unimportant. 6. The possibility of fatigue fracture in bone as a factor contributing to late loosening is an argument in favour of metal-on-polyethylene prostheses with their lower frictional moments, although the importance of this factor cannot be estimated

Aims

Dual mobility (DM) implants have been shown to reduce the dislocation rate after total hip arthroplasty (THA), but there remain concerns about the use of cobalt chrome liners inserted into titanium shells. The aim of this study was to assess the clinical outcomes, metal ion levels, and periprosthetic femoral bone mineral density (BMD) at mid-term follow-up in young, active patients receiving a modular DM THA.