Aims

We sought to determine whether cobalt-chromium alloy (CoCr) femoral stem tapers (trunnions) wear more than titanium (Ti) alloy stem tapers (trunnions) when used in a large diameter (LD) metal-on-metal (MoM) hip arthroplasty system.

Aims. Several short- and mid-term studies have shown minimal liner wear of highly cross-linked polyethylene (HXLPE) in total hip arthroplasty (THA), but the safety of using thinner HXLPE liners to maximize femoral head size remains uncertain. The objective of this study was to analyze clinical survival and radiological wear rates of patients with HXLPE liners, a 36 mm femoral head, and a small acetabular component with a minimum of ten years’ follow-up. Methods. We retrospectively identified 55 patients who underwent primary THA performed at a single centre, using HXLPE liners with 36 mm cobalt-chrome heads in acetabular components with an outer diameter of 52 mm or smaller. Patient demographic details, implant details, death, and all-cause revisions were recorded. Cox regression and Kaplan-Meier survival was used to determine all-cause and liner-specific revision. Of these 55 patients, 22 had a minimum radiological follow-up of seven years and were assessed radiologically for linear and volumetric wear. Results. Overall survival rate for all-cause revision was 94.5% (95% confidence interval (CI) 81.7% to 97.2%) at a mean follow-up of 12.8 years (10.9 to 18.7). Three patients were revised, none for liner wear, fracture, or dissociation. A total of 22 patients were included in the radiological analysis (mean follow-up 9.9 years (7.5 to 13.7)). Mean linear liner wear was 0.085 mm (95% CI -0.086 to 0.257) and the volumetric wear rate was 11.097 mm. 3. /year (95% CI -6.5 to 28.7). Conclusion. Using HXLPE liners with 36 mm heads in 52 mm acetabular components or smaller is safe, with excellent survival and low rates of linear and volumetric wear at medium-term follow-up. Patients did not require revision surgery for liner complications such as fracture, dissociation, or wear. Our results suggest that the advantages of using larger heads outweigh the potential risks of using thin HXLPE liners. Cite this article: Bone Joint J 2023;105-B(1):29–34

Aims. We aimed to investigate if the use of the largest possible cobalt-chromium head articulating with polyethylene acetabular inserts would increase the in vivo wear rate in total hip arthroplasty. Methods. In a single-blinded randomized controlled trial, 96 patients (43 females), at a median age of 63 years (interquartile range (IQR) 57 to 69), were allocated to receive either the largest possible modular femoral head (36 mm to 44 mm) in the thinnest possible insert or a standard 32 mm head. All patients received a vitamin E-doped cross-linked polyethylene insert and a cobalt-chromium head. The primary outcome was proximal head penetration measured with radiostereometric analysis (RSA) at two years. Secondary outcomes were volumetric wear, periacetabular radiolucencies, and patient-reported outcomes. Results. At two years, 44 patients in each group were available for RSA assessment. The median total two-year proximal head penetration was -0.02 mm (IQR -0.09 to 0.07; p = 0.548) for the largest possible head and -0.01 mm (IQR -0.07 to 0.10; p = 0.525) for 32 mm heads. Their difference was not statistically significant (p = 0.323). Neither group demonstrated a bedding-in period. The median steady-state volumetric wear rates were 6.1 mm. 3. /year (IQR -59 to 57) and 3.5 mm. 3. /year (-21 to 34) respectively, and did not differ between the groups (p = 0.848). There were no statistically significant differences in periacetabular radiolucencies or patient-reported outcomes. Conclusion. The use of the largest possible metal head did not increase vitamin E-doped cross-linked polyethylene wear compared with 32 mm heads at two years. Linear wear was negligible and volumetric wear rates were very low in both head size groups. There was a tendency towards higher values of volumetric wear in large heads that warrants longer-term evaluation before any definite conclusions about the association between head size and wear can be drawn. Cite this article: Bone Joint J 2021;103-B(7):1206–1214

Aims. Oxidized zirconium (OxZi) and highly cross-linked polyethylene (HXLPE) were developed to minimize wear and risk of osteolysis in total hip arthroplasty (THA). However, retrieval studies have shown that scratched femoral heads may lead to runaway wear, and few reports of long-term results have been published. The purpose of this investigation is to report minimum ten-year wear rates and clinical outcomes of THA with OxZi femoral heads on HXLPE, and to compare them with a retrospective control group of cobalt chrome (CoCr) or ceramic heads on HXLPE. Methods. From 2003 to 2006, 108 THAs were performed on 96 patients using an OxZi head with a HXLPE liner with minimum ten-year follow-up. Harris Hip Scores (HHS) were collected preoperatively and at the most recent follow-up (mean 13.3 years). Linear and volumetric liner wear was measured on radiographs of 85 hips with a minimum ten-year follow-up (mean 14.5 years). This was compared to a retrospective control group of 45 THAs using ceramic or CoCr heads from October 1999 to February 2005, with a minimum of ten years’ follow-up. Results. Average HHS improved from 50.8 to 91.9 and 51.0 to 89.8 in the OxZi group and control group, respectively (p = 0.644), with no osteolysis in either group. Linear and volumetric wear rates in the OxZi group averaged 0.03 mm/year and 3.46 mm. 3. /year, respectively. There was no statistically significant difference in HHS scores, nor in linear or volumetric wear rate between the groups, and no revision for any indication. Conclusion. The radiological and clinical outcomes, and survivorship of THA with OxZi femoral heads and HXLPE liners, were excellent, and comparable to CoCr or ceramic heads at minimum ten-year follow-up. Wear rates are below what would be expected for development of osteolysis. OxZi-HXLPE is a durable bearing couple with excellent long-term outcomes. Cite this article: Bone Joint J 2024;106-B(3 Supple A):38–43

Aims. A retrospective study was conducted to measure short-term in vivo linear and volumetric wear of polyethylene (PE) inserts in 101 total knee arthroplasty (TKA) patients using model-based radiostereometric analysis (MBRSA). Patients and Methods. Nonweightbearing supine RSA exams were performed postoperatively and at six, 12, and 24 months. Weightbearing standing RSA exams were performed on select patients at 12 and 24 months. Wear was measured both linearly (joint space) and volumetrically (digital model overlap) at each available follow-up. Precision of both methods was assessed by comparing double RSA exams. Patient age, sex, body mass index, and Oxford Knee Scores were analyzed for any association with PE wear. Results. Linear wear occurred at 0.015 mm/year (supine) and 0.220 mm/year (standing). Volumetric wear occurred at 10.3 mm. 3. /year (supine) and 39.3 mm. 3. /year (standing). Wear occurred primarily on the medial side of the joint. Weightbearing imaging greatly improved the reliability of measurement. Clinical precision of volumetric wear was 34 mm. 3. No significant associations were found between patient demographics or function scores and measured wear. Conclusion. In vivo volumetric wear of TKAs can be assessed at short-term follow-up using MBRSA. Cite this article: Bone Joint J 2019;101-B:1348–1355

Aims. A retrospective longitudinal study was conducted to compare directly volumetric wear of retrieved polyethylene inserts to predicted volumetric wear modelled from individual gait mechanics of total knee arthroplasty (TKA) patients. Methods. In total, 11 retrieved polyethylene tibial inserts were matched with gait analysis testing performed on those patients. Volumetric wear on the articular surfaces was measured using a laser coordinate measure machine and autonomous reconstruction. Knee kinematics and kinetics from individual gait trials drove computational models to calculate medial and lateral tibiofemoral contact paths and forces. Sliding distance along the contact path, normal forces and implantation time were used as inputs to Archard’s equation of wear to predict volumetric wear from gait mechanics. Measured and modelled wear were compared for each component. Results. Volumetric wear rates on eight non-delaminated components measured 15.9 mm. 3. /year (standard error (SE) ± 7.7) on the total part, 11.4 mm. 3. /year (SE ± 6.4) on the medial side and 4.4 (SE ± 2.6) mm. 3. /year on the lateral side. Volumetric wear rates modelled from patient gait mechanics predicted 16.4 mm. 3. /year (SE 2.4) on the total part, 11.7 mm. 3. /year (SE 2.1) on the medial side and 4.7 mm. 3. /year (SE 0.4) on the lateral side. Measured and modelled wear volumes correlated significantly on the total part (p = 0.017) and the medial side (p = 0.012) but not on the lateral side (p = 0.154). Conclusion. In the absence of delamination, patient-specific knee mechanics during gait directly affect wear of the tibial component in TKA. Cite this article: Bone Joint J 2020;102-B(6 Supple A):129–137

Aims. We present the ten-year data of a cohort of patients, aged between 18 and 65 years (mean age 52.7 years; 19 to 64), who underwent total hip arthroplasty. Patients were randomised to be treated with a cobalt-chrome (CoCr) femoral head with an ultra-high molecular weight polyethylene (UHMWPE), highly cross-linked polyethylene (XLPE) or ceramic-on-ceramic (CoC) bearing surface. Patients and Methods. A total of 102 hips (91 patients) were randomised into the three groups. At ten years, 97 hips were available for radiological and functional follow-up. Two hips (two patients) had been revised (one with deep infection and one for periprosthetic fracture) and three were lost to follow-up. Radiological analysis was performed using a validated digital assessment programme to give linear, directional and volumetric wear of the two polyethylene groups. Results. There was a significantly reduced rate of steady-state linear wear with XLPE (0.07 mm/yr) compared with UHMWPE (0.37 mm/yr) (p = 0.001). Volumetric wear was also significantly reduced in the XLPE group (29.29 mm. 3. /yr) compared with the UHMWPE group (100.75mm. 3. /yr) (p = 0.0001). There were six patients with UHMWPE who had non-progressive osteolysis and none in the XLPE group. All three bearing groups had significant improvements in 12-item short form health survey scores, Western Ontario and McMaster Universities Osteoarthritis Index score and Harris Hip Score. However, the improvement in HSS was significantly less in the UHMWPE group (p = 0.0188) than in the other two groups. At ten years, the rates of volumetric and linear wear in the XLPE group remain low and predominantly below the estimated threshold for osteolysis (1 mm/yr). The rate of linear wear in the XLPE group was three times less than in the UHMWPE group at five-year follow-up and five times less at ten years. The rate of volumetric wear was also three times less in the XLPE group at ten years. Conclusion. While CoC also performs well, XLPE at ten years remains a safe and excellent bearing option in young patients, with low rates of wear and no evidence of osteolysis. Cite this article: Bone Joint J 2017;99-B:1590–5

Aims. Highly cross-linked polyethylene (HXLPE) has greatly improved the durability of total hip arthroplasty (THA) in young patients because of its improved wear characteristics. Few studies have followed this population into the second decade, and therefore the purpose of this investigation was to evaluate the clinical outcome for THA patients 50 years of age and younger at a minimum of 15 years postoperatively. The second purpose was to evaluate the radiological findings secondary to wear or mechanical failure of the implant. Methods. Between October 1999 and December 2005, 105 THAs were performed in 95 patients (53 female, 42 male) aged 50 years and younger (mean 42 years (20 to 50)). There were 87 patients (96 hips) that were followed for a minimum of 15 years (mean 17.3 years (15 to 21)) for analysis. Posterior approach was used with cementless fixation with a median head size of 28 mm. HXLPE was the acetabular bearing for all hips. Radiographs were evaluated for polyethylene wear, radiolucent lines, and osteolysis. Results. Clinical outcomes showed significant improvement of mean Harris Hip Scores from 52.8 (SD 13.5) preoperatively to 94.8 (SD 7.6) postoperatively. One hip was revised for recurrent instability, and there were no infections. No hips were revised for mechanical loosening or osteolysis. Mean polyethylene linear wear was 0.04 mm/year and volumetric wear was 6.22 mm. 3. /year, with no significant differences between head size or material. Osteolysis was not present in any of the hips. Conclusion. The use of HXLPE in THA for patients aged 50 years and younger has performed exceptionally well without evidence of significant wear causing mechanical loosening or necessitating revision. The radiolucent lines of the acetabular component must be followed to determine the prognostic significance. This investigation represents the longest clinical follow-up of a large, consecutive cohort of patients aged 50 years or younger with THA using HXLPE. This long-term analysis found negligible polyethylene wear, no incidence of aseptic loosening, and excellent clinical outcomes at and beyond 15 years of follow-up. Cite this article: Bone Joint J 2021;103-B(7 Supple B):78–83

We sought to establish the incidence of joint failure secondary to adverse reaction to metal debris (ARMD) following metal-on-metal hip resurfacing in a large, three surgeon, multicentre study involving 4226 hips with a follow-up of 10 to 142 months. Three implants were studied: the Articular Surface Replacement; the Birmingham Hip Resurfacing; and the Conserve Plus. Retrieved implants underwent analysis using a co-ordinate measuring machine to determine volumetric wear. There were 58 failures associated with ARMD. The median chromium and cobalt concentrations in the failed group were significantly higher than in the control group (p < 0.001). Survival analysis showed a failure rate in the patients with Articular Surface Replacement of 9.8% at five years, compared with < 1% at five years for the Conserve Plus and 1.5% at ten years for the Birmingham Hip Resurfacing. Two ARMD patients had relatively low wear of the retrieved components. Increased wear from the metal-on-metal bearing surface was associated with an increased rate of failure secondary to ARMD. However, the extent of tissue destruction at revision surgery did not appear to be dose-related to the volumetric wear

Polyethylene wear of acetabular components is a key factor in the development of periprosthetic osteolysis and wear at the articular surface has been well documented and quantified, but fewer data are available about changes which occur at the backside of the liner. At revision surgery for loosening of the femoral component we retrieved 35 conventional modular acetabular liners of the same design. Linear and volumetric articular wear, backside volumetric change and the volume of the screw-head indentations were quantified. These volumes, clinical data and the results from radiological Ein Bild Röntgen Analyse migration analysis were used to identify potential factors influencing the volumetric articular wear and backside volumetric change. The rate of backside volumetric change was found to be 2.8% of the rate of volumetric articular wear and decreased with increasing liner size. Migrated acetabular components showed significantly higher rates of backside volumetric change plus screw-head indentations than those without migration. The backside volumetric change was at least ten times larger than finite-element simulation had suggested. In a stable acetabular component with well-anchored screws, the amount of backside wear should not cause clinical problems. Impingement of the screw-heads could produce more wear particles than those generated at the liner-shell interface. Because the rate of backside volumetric change is only 2.8% of the rate of volumetric articular wear and since creep is likely to contribute a significant portion to this, the debris generated by wear at the backside of the liner may not be sufficient to create a strong osteolytic response

We conducted a systematic review and meta-analysis of randomised controlled trials comparing cross-linked with conventional polyethylene liners for total hip replacement in order to determine whether these liners reduce rates of wear, radiological evidence of osteolysis and the need for revision. The MEDLINE, EMBASE and COCHRANE databases were searched from their inception to May 2010 for all trials involving the use of cross-linked polyethylene in total hip replacement. Eligibility for inclusion in the review included the random allocation of treatments, the use of cross-linked and conventional polyethylene, and radiological wear as an outcome measure. The pooled mean differences were calculated for bedding-in, linear wear rate, three-dimensional linear wear rate, volumetric wear rate and total linear wear. Pooled risk ratios were calculated for radiological osteolysis and revision hip replacement. A search of the literature identified 194 potential studies, of which 12 met the inclusion criteria. All reported a significant reduction in radiological wear for cross-linked polyethylene. The pooled mean differences for linear rate of wear, three-dimensional linear rate of wear, volumetric wear rate and total linear wear were all significantly reduced for cross-linked polyethylene. The risk ratio for radiological osteolysis was 0.40 (95% confidence interval 0.27 to 0.58; I. 2. = 0%), favouring cross-linked polyethylene. The follow-up was not long enough to show a difference in the need for revision surgery

Wear of polyethylene is associated with aseptic loosening of orthopaedic implants and has been observed in hip and knee prostheses and anatomical implants for the shoulder. The reversed shoulder prostheses have not been assessed as yet. We investigated the volumetric polyethylene wear of the reversed and anatomical Aequalis shoulder prostheses using a mathematical musculoskeletal model. Movement and joint stability were achieved by EMG-controlled activation of the muscles. A non-constant wear factor was considered. Simulated activities of daily living were estimated from in vivo recorded data. After one year of use, the volumetric wear was 8.4 mm. 3. for the anatomical prosthesis, but 44.6 mm. 3. for the reversed version. For the anatomical prosthesis the predictions for contact pressure and wear were consistent with biomechanical and clinical data. The abrasive wear of the polyethylene in reversed prostheses should not be underestimated, and further analysis, both experimental and clinical, is required

Aims. We wished to investigate the influence of metal debris exposure on the subsequent immune response and resulting soft-tissue injury following metal-on-metal (MoM) hip arthroplasty. Some reports have suggested that debris generated from the head-neck taper junction is more destructive than equivalent doses from metal bearing surfaces. . Patients and Methods. We investigated the influence of the source and volume of metal debris on chromium (Cr) and cobalt (Co) concentrations in corresponding blood and hip synovial fluid samples and the observed agglomerated particle sizes in excised tissues using multiple regression analysis of prospectively collected data. A total of 199 explanted MoM hips (177 patients; 132 hips female) were analysed to determine rates of volumetric wear at the bearing surfaces and taper junctions. . Results. The statistical modelling suggested that a greater source contribution of metal debris from the taper junction was associated with smaller aggregated particle sizes in the local tissues and a relative reduction of Cr ion concentrations in the corresponding synovial fluid and blood samples. Metal debris generated from taper junctions appears to be of a different morphology, composition and therefore, potentially, immunogenicity to that generated from bearing surfaces. Conclusion. The differences in debris arising from the taper and the articulating surfaces may provide some understanding of the increased incidence of soft-tissue reactions reported in patients implanted with MoM total hip arthroplasties compared with patients with hip resurfacings. Cite this article: Bone Joint J 2016;98-B:925–33

Aims. There are limited published data detailing the volumetric material loss from tapers of conventional metal-on-polyethylene (MoP) total hip arthroplasties (THAs). Our aim was to address this by comparing the taper wear rates measured in an explanted cohort of the widely used Exeter THA with those measured in a group of metal-on-metal (MoM) THAs. Patients and Methods. We examined an existing retrieval database to identify all Exeter V40 and Universal MoP THAs. Volumetric wear analysis of the taper surfaces was conducted using previously validated methodology. These values were compared with those obtained from a series of MoM THAs using non-parametric statistical methodology. A number of patient and device variables were accounted for using multiple regression modelling. Results. A total of 95 Exeter MoP and 249 MoM THAs were examined. The median volumetric loss from the MoM cohort was over four times larger than that from the MoP cohort (1.01 mm. 3. vs 0.23 mm. 3. , p < 0.001), despite a significantly shorter median period in vivo for the MoM group (48 months vs 90 months, p < 0.001). Multiple regression modelling indicated that the dominant variables leading to greater female taper material loss were bearing diameter (p < 0.001), larger female taper angles (p < 0.001), and male titanium stem tapers (p < 0.001). Conclusion. Consistent with the long-term clinical success of the device, the volumetric material loss from Exeter femoral head tapers was, in general, small compared with that from larger-diameter MoM head tapers. Cite this article: Bone Joint J 2018;100-B:1310–9

We analysed 54 alumina ceramic-on-ceramic bearings from total hip replacements retrieved at one centre after a mean duration of 3.5 years (0.2 to 10.6) in situ. These implants were obtained from 54 patients (16 men and 38 women) with a mean age of 67 years (33 to 88) who underwent revision for a variety of reasons. Posterior edge loading was found in the majority of these retrievals (32 out of 54). Anterosuperior edge loading occurred less often but produced a higher rate of wear. Stripe wear on the femoral heads had a median volumetric wear rate of 0.2 mm. 3. /year (0 to 7.2). The wear volume on the femoral heads corresponded to the width of edge wear on the matching liner. Anteversion of the acetabular component was found to be a more important determinant than inclination for wear in ceramic bearings. Posterior edge loading may be considered to be a normal occurrence in ceramic-on-ceramic bearings, with minimal clinical consequences. Edge loading should be defined as either anterosuperior or posterior, as each edge loading mechanism may result in different clinical implications

Polyethylene wear debris can cause osteolysis and the failure of total hip arthroplasty. We present the five-year wear rates of a highly cross-linked polyethylene (X3) bearing surface when used in conjunction with a 36 mm ceramic femoral head. This was a prospective study of a cohort of 100 THAs in 93 patients. Pain and activity scores were measured pre- and post-operatively. Femoral head penetration was measured at two months, one year, two years and at five years using validated edge-detecting software (PolyWare Auto). At a mean of 5.08 years (3.93 to 6.01), 85 hips in 78 patients were available for study. The mean age of these patients was 59.08 years (42 to 73, the mean age of males (n = 34) was 59.15 years, and females (n = 44) was 59.02 years). All patients had significant improvement in their functional scores (p < 0.001). The steady state two-dimensional linear wear rate was 0.109 mm/year. The steady state volumetric wear rate was 29.61 mm. 3. /year. No significant correlation was found between rate of wear and age (p = 0.34), acetabular component size (p = 0.12) or clinical score (p = 0.74). Our study shows low steady state wear rates at five years in X3 highly cross-linked polyethylene in conjunction with a 36 mm ceramic femoral head. The linear wear rate was almost identical to the osteolysis threshold of 0.1 mm/year recommended in the literature. Cite this article: Bone Joint J 2015;97-B:1470–4

There are many methods for analysing wear volume in failed polyethylene acetabular components. We compared a radiological technique with three recognised ex vivo methods of measurement. We tested 18 ultra-high-molecular-weight polyethylene acetabular components revised for wear and aseptic loosening, of which 13 had pre-revision radiographs, from which the wear volume was calculated based upon the linear wear. We used a shadowgraph technique on silicone casts of all of the retrievals and a coordinate measuring method on the components directly. For these techniques, the wear vector was calculated for each component and the wear volume extrapolated using mathematical equations. The volumetric wear was also measured directly using a fluid-displacement method. The results of each technique were compared. The series had high wear volumes (mean 1385 mm. 3. ; 730 to 1850) and high wear rates (mean 205 mm. 3. /year; 92 to 363). There were wide variations in the measurements of wear volume between the radiological and the other techniques. Radiograph-derived wear volume correlated poorly with that of the fluid-displacement method, co-ordinate measuring method and shadowgraph methods, becoming less accurate as the wear increased. The mean overestimation in radiological wear volume was 47.7% of the fluid-displacement method wear volume. Fluid-displacement method, coordinate measuring method and shadowgraph determinations of wear volume were all better than that of the radiograph-derived linear measurements since they took into account the direction of wear. However, only radiological techniques can be used in vivo and remain useful for monitoring linear wear in the clinical setting. Interpretation of radiological measurements of acetabular wear must be done judiciously in the clinical setting. In vitro laboratory techniques, in particular the fluid-displacement method, remain the most accurate and reliable methods of assessing the wear of acetabular polyethylene

Polyethylene acetabular cups retrieved at revision surgery were measured by a shadowgraph technique to determine linear wear, and the values were compared with those obtained from radiographs. There was a close correlation between them, although the radiographic measurements slightly underestimated the true wear. Average linear wear rates for surface-replacement components were much greater than those for conventional prostheses with femoral heads up to 32 mm in diameter. Volumetric wear, calculated using a new formula, was found to be less than previously reported in vivo, and similar in magnitude to the results of experimental wear tests in vitro. The volumetric wear rates were greatest for the surface-replacement components and, for conventional components, were found to increase in a linear manner with component diameter

Ultra-high-molecular-weight polyethylene (UHMWPE) components for total joint replacement generate wear particles which cause adverse biological tissue reactions leading to osteolysis and loosening. Sterilisation of UHMWPE components by gamma irradiation in air causes chain scissions which initiate a long-term oxidative process that degrades the chemical and mechanical properties of the polyethylene. Using a tri-pin-on-disc tribometer we studied the effect of ageing for ten years after gamma irradiation in air on the volumetric wear, particle size distribution and the number of particles produced by UHMWPE when sliding against a stainless-steel counterface. The aged and irradiated material produced six times more volumetric wear and 34 times more wear particles per unit load per unit sliding distance than non-sterilised UHMWPE. Our findings indicate that oxidative degradation of polyethylene after gamma irradiation in air with ageing produces more wear

This multicentre study analysed 12 alumina ceramic-on-ceramic components retrieved from squeaking total hip replacements after a mean of 23 months in situ (11 to 61). The rates and patterns of wear seen in these squeaking hips were compared with those seen in matched controls using retrieval data from 33 ‘silent’ hip replacements with similar ceramic bearings. All 12 bearings showed evidence characteristic of edge-loading wear. The median rate of volumetric wear was 3.4 mm. 3. /year for the acetabular component, 2.9 mm. 3. /year on the femoral heads and 6.3 mm. 3. /year for head and insert combined. This was up to 45 times greater than that of previously reported silent ceramic-on-ceramic retrievals. The rate of wear seen in ceramic components revised for squeaking hips appears to be much greater than in that seen in retrievals from ‘silent’ hips.

Osteolysis is due to particulate wear debris and is responsible for the long-term failure of total hip replacements. It has stimulated the development of alternative joint surfaces such as metal-on-metal or ceramic-on-ceramic implants. Since 1988 the second-generation metal-on-metal implant Metasul has been used in over 60 000 hips. Analysis of 118 retrieved specimens of the head or cup showed rates of wear of approximately 25 μm for the whole articulation per year in the first year, decreasing to about 5 μm per year after the third. Metal surfaces have a ‘self-polishing’ capacity. Scratches are worn out by further joint movement. Volumetric wear was decreased some 60-fold compared with that of metal-on-polyethylene implants, suggesting that second-generation metal-on-metal prostheses may considerably reduce osteolysis

We compared and quantified the modes of failure and patterns of wear of 11 Mittelmeier and 11 Ceraver-Ostal retrieved alumina-alumina hip prostheses with reference to the corresponding clinical and radiological histories. Macroscopic wear was assessed using a three-dimensional co-ordinate measuring machine. Talysurf contacting profilometry was used to measure surface roughness on a microscopic scale and SEM to determine mechanisms of wear at the submicron level. The components were classified into one of three categories of wear: low (no visible/measurable wear), stripe (elliptical wear stripe on the heads and larger worn areas on the cups) and severe (macroscopic wear, large volumes of material lost). Overall, the volumetric wear of the alumina-alumina prostheses was substantially less than the widely used metal and ceramic-on-polyethylene combinations. By identifying and eliminating the factors which accelerate wear, it is expected that the lifetime of these devices can be further increased

In this prospective, randomised study, we have compared the wear rate of cemented, acetabular polyethylene cups articulating with either a 22 mm or a 32 mm cobalt-chromium head. We evaluated 89 patients who had a total of 484 radiographs. The mean follow-up period was 71.4 months (SD 29.1). All the radiographs were digitised and electronically measured. The linear wear rate was significantly higher during the first two years and decreased after this period to a constant value. We suggest that this is partly due to a ‘run-in’ process caused by irregularities between surfaces of the cup and head and an initial plastic deformation of the polyethylene. The mean volumetric wear was 120.3 mm. 3. /year for the 32 mm head, which was significantly higher than the 41.5 mm. 3. /year for the 22 mm heads. The mean linear wear rate was not significantly different. We were, however, unable to find radiological signs of osteolysis in the patients who had higher wear rates

Aims

The first aim of this study was to evaluate whether preoperative renal function is associated with postoperative changes in whole blood levels of metal ions in patients who have undergone a Birmingham Hip Resurfacing (BHR) arthroplasty with a metal-on-metal bearing. The second aim was to evaluate whether exposure to increased cobalt (Co) and chromium (Cr) levels for ten years adversely affected renal function.

Aims

The aim of this study was to evaluate the performance of first-generation annealed highly cross-linked polyethylene (HXLPE) in cementless total hip arthroplasty (THA).

Aims

The aim of this study was to investigate whether wear and backside deformation of polyethylene (PE) tibial inserts may influence the cement cover of tibial trays of explanted total knee arthroplasties (TKAs).

We examined radiographic polyethylene wear in 233 cemented total hip arthroplasties (201 patients) with either a metal-backed or a non-metal-backed acetabular cup. All patients had identical cemented one-piece titanium femoral stems with a femoral head diameter of 28 mm. The mean linear wear rate was 0.11 mm/yr in metal-backed sockets and 0.08 mm/yr in non-metal-backed sockets (p = 0.0002). The mean volumetric wear rate was 66.2 mm3/yr in the metal-backed sockets and 48.2 mm3/yr in the polyethylene sockets (p = 0.0002). The addition of metal backing to a cemented acetabular cup therefore resulted in a 37% increase in mean polyethylene wear rates which may partially explain the higher failure rate of cemented metal-backed cups. Linear regression analysis also implicated increased follow-up time (log), gross acetabular migration, metal backing and male gender in increasing polyethylene wear. We advocate the use of an all-polyethylene cup in cemented total hip arthroplasty. The increased polyethylene wear must also cause concern about the wear rate of uncemented metal-backed acetabular sockets

Aims

Achieving accurate implant positioning and restoring native hip biomechanics are key surgeon-controlled technical objectives in total hip arthroplasty (THA). The primary objective of this study was to compare the reproducibility of the planned preoperative centre of hip rotation (COR) in patients undergoing robotic arm-assisted THA versus conventional THA.

Aims

The aims of this study were to evaluate wear on the surface of cobalt-chromium (CoCr) femoral components used in total knee arthroplasty (TKA) and compare the wear of these components with that of ceramic femoral components.

Aims

This study reports the ten-year wear rates, incidence of osteolysis, clinical outcomes, and complications of a multicentre randomized controlled trial comparing oxidized zirconium (OxZr) versus cobalt-chrome (CoCr) femoral heads with ultra-high molecular weight polyethylene (UHMWPE) and highly cross-linked polyethylene (XLPE) liners in total hip arthroplasty (THA).

Aims

Registry studies on modified acetabular polyethylene (PE) liner designs are limited. We investigated the influence of standard and modified PE acetabular liner designs on the revision rate for mechanical complications in primary cementless total hip arthroplasty (THA).

We have reviewed 70 patients with bilateral simultaneous total hip arthroplasties to determine the rate of failure and to compare polyethylene wear and osteolysis between an implant with a cobalt-chrome head and Hylamer liner with that of a zirconia head and Hylamer liner. The mean thickness of the polyethylene liner was 11.0 mm (8.8 to 12.2) in the hip with a zirconia head and 10.7 mm (8.8 to 12.2) in that with a cobalt-chrome head. At follow-up at 6.4 years no acetabular or femoral component had been revised for aseptic loosening and no acetabular or femoral component was loose according to radiological criteria in both the cemented and cementless groups. The mean rate of linear wear and annual wear rate were highest in the 22 mm zirconia femoral head (1.25 mm (SD 1.05) and 0.21 mm (SD 0.18), respectively) and lowest in the 22 mm cobalt-chrome femoral head (0.70 mm (SD 0.39) and 0.12 mm (SD 0.07), respectively). The mean volumetric wear was highest in the 28 mm zirconia femoral head (730.79 mm. 3. ) and lowest in the 22 mm cobalt-chrome femoral head (264.67 mm. 3. ), but if the results were compared by size of the femoral head and type of material there was no statistical difference (p > 0.05). Sequential measurements of annual wear showed that the zirconia femoral head had a relatively higher rate of penetration than the cobalt-chrome head over the first three years; thereafter the rate of wear was reduced and compared favourably with that of cobalt-chrome heads. There was a statistically significant relationship between the wear of the polyethylene liner and the age of the patient, male gender and the degree of abduction angle of the cup, but not diagnosis, weight, hip score, range of movement, or amount of anteversion. Osteolysis was identified on both sides of the acetabulum in six patients (9%). Of 12 hips with acetabular osteolysis, six had a 28 mm cobalt-chrome femoral head and the remaining six a 28 mm zirconia head. Osteolysis was observed in zones 1A and 7A of the femur in two hips (3%) with a 28 mm zirconia head (cemented hip) and in four (6%) with a 28 mm cobalt-chrome femoral head (cementless hip). Our findings suggest that although the performance of a zirconia femoral head with a Hylamer liner was not statistically different from that of a cobalt-chrome femoral head and Hylamer liner, there was a trend for the zirconia head to be worse than the cobalt-chrome femoral head

Aims

Vitamin E-infused highly cross-linked polyethylene (E1) has recently been introduced in total knee arthroplasty (TKA). An in vitro wear simulator study showed that E1 reduced polyethylene wear. However there is no published information regarding in vivo wear. Previous reports suggest that newly introduced materials which reduce in vitro polyethylene wear do not necessarily reduce in vivo polyethylene wear. To assist in the evaluation of the newly introduced material before widespread use, we established an in vivo polyethylene wear particle analysis for TKA. The aim of this study was to compare in vivo polyethylene wear particle generation between E1 and conventional polyethylene (ArCom) in TKA.

Aims

This study compared the cobalt and chromium serum ion concentration of patients treated with two different metal-on-metal (MoM) hinged total knee arthroplasty (TKA) systems, as well as a titanium nitride (TiN)-coated variant.

Aims

The most frequent indication for revision surgery in total hip arthroplasty (THA) is aseptic loosening. Aseptic loosening is associated with polyethylene liner wear, and wear may be reduced by using vitamin E-doped liners. The primary objective of this study was to compare proximal femoral head penetration into the liner between a) two cross-linked polyethylene (XLPE) liners (vitamin E-doped (vE-PE)) versus standard XLPE liners, and b) two modular femoral head diameters (32 mm and 36 mm).

Aims

Adverse local tissue reactions associated with abnormal wear considerably slowed down the general use of metal-on-metal (MoM) hip resurfacing arthroplasty (HRA), now limited to a few specialized centres. In this study, we provide the clinical results of 400 consecutive MoM HRAs implanted more than 20 years ago in one such centre.

Aims

In the 1990s, a bioactive bone cement (BABC) containing apatite-wollastonite glass-ceramic (AW-GC) powder and bisphenol-a-glycidyl methacrylate resin was developed at our hospital. In 1996, we used BABC to fix the acetabular component in primary total hip arthroplasty (THA) in 20 patients as part of a clinical trial. The purpose of this study was to investigate the long-term results of primary THA using BABC.

Aims

The purpose of this study is to examine six types of bearing surfaces implanted at a single institution over three decades to determine whether the reasons for revision vary among the groups and how long it takes to identify differences in survival.

Aims

The aim of this study was to investigate whether the use of antibiotic-loaded bone cement influenced the risk of revision surgery after primary total hip arthroplasty (THA) for osteoarthritis.

We have studied the influence of weight-bearing on the measurement of wear of the polyethylene acetabular component in total hip arthroplasty using two techniques. The measured vertical wear was significantly greater when radiographs were taken weight-bearing rather than with the patient supine (p = 0.001, method 1; p = 0.007, method 2). Calculations of rates of linear wear of the acetabular component were significantly underestimated (p < 0.05) when radiographs were taken supine. There are two reasons for this. First, a change in pelvic orientation when bearing weight ensures that the thinnest polyethylene is brought into relief, and secondly, the head of the femoral component assumes the position of maximal displacement along its wear path. Interpretation of previous studies on both linear and volumetric polyethylene wear in total hip arthroplasty should be reassessed in the light of these findings

Aims

Dual mobility (DM) bearings are an attractive treatment option to obtain hip stability during challenging primary and revision total hip arthroplasty (THA) cases. The purpose of this study was to analyze data submitted to the American Joint Replacement Registry (AJRR) to characterize utilization trends of DM bearings in the USA.

Aims

In previous studies, we identified multiple factors influencing the survivorship of hip resurfacing arthroplasties (HRAs), such as initial anatomical conditions and surgical technique. In addition, the University of California, Los Angeles (UCLA) activity score presents a ceiling effect, so a better quantification of activity is important to determine which activities may be advisable or detrimental to the recovered patient. We aimed to determine the effect of specific groups of sporting activities on the survivorship free of aseptic failure of a large series of HRA.

Aims

Instability continues to be a troublesome complication after total hip arthroplasty (THA). Patient-related risk factors associated with a higher dislocation risk include the preoperative diagnosis, an age of 75 years or older, high body mass index (BMI), a history of alcohol abuse, and neurodegenerative diseases. The goal of this study was to assess the dislocation rate, radiographic outcomes, and complications of patients stratified as high-risk for dislocation who received a dual mobility (DM) bearing in a primary THA at a minimum follow-up of two years.

Aims

Our aim in this study was to describe a continuing review of 11 total hip arthroplasties using 22.225 mm Alumina ceramic femoral heads on a Charnley flanged femoral component, articulating against a silane crosslinked polyethylene.

We reviewed the literature on the currently available choices of bearing surface in total hip replacement (THR). We present a detailed description of the properties of articulating surfaces review the understanding of the advantages and disadvantages of existing bearing couples. Recent technological developments in the field of polyethylene and ceramics have altered the risk of fracture and the rate of wear, although the use of metal-on-metal bearings has largely fallen out of favour, owing to concerns about reactions to metal debris. As expected, all bearing surface combinations have advantages and disadvantages. A patient-based approach is recommended, balancing the risks of different options against an individual’s functional demands.

Cite this article: Bone Joint J 2014;96-B:147–56.

Aims

We sought to establish whether an oxidised zirconium (OxZr) femoral component causes less loss of polyethylene volume than a cobalt alloy (CoCr) femoral component in total knee arthroplasty.

Advances in polyethylene (PE) in total hip arthroplasty have led to interest and increased use of highly crosslinked PE (HXLPE) in total knee arthroplasty (TKA). Biomechanical data suggest improved wear characteristics for HXLPE inserts over conventional PE in TKA. Short-term results from registry data and few clinical trials are promising. Our aim is to present a review of the history of HXLPEs, the use of HXLPE inserts in TKA, concerns regarding potential mechanical complications, and a thorough review of the available biomechanical and clinical data.

Cite this article: Bone Joint J 2017;99-B:996–1002.

Aims

The aim of this study was to determine whether there is a difference in the rate of wear between acetabular components positioned within and outside the ‘safe zones’ of anteversion and inclination angle.

Aims

For this retrospective cohort study, patients aged ≤ 30 years (very young) who underwent total hip arthroplasty (THA) were compared with patients aged ≥ 60 years (elderly) to evaluate the rate of revision arthroplasty, implant survival, the indications for revision, the complications, and the patient-reported outcomes.

The use of large-diameter metal-on-metal (MoM) components in total hip arthroplasty (THA) is associated with an increased risk of early failure due to adverse local tissue reaction to metal debris (ARMD) in response to the release of metal ions from the bearing couple and/or head-neck taper corrosion. The aim of this paper was to present a review of the incidence and natural history of ARMD and the forms of treatment, with a focus on the need for and extent of resection or debulking of the pseudotumour. An illustrative case report is presented of a patient with an intra-pelvic pseudotumour associated with a large diameter MoM THA, which was treated successfully with revision of the bearing surface to a dual mobility couple and retention of the well-fixed acetabular and femoral components. The pseudotumour was left in situ. Resolution of the intra-pelvic mass and normalisation of metal ion levels was observed seven months post-operatively.

Cite this article: Bone Joint J 2016;98-B:736–40.

Aims

To present a surgically relevant update of trunnionosis.

The leading indication for revision total hip arthroplasty (THA) remains aseptic loosening owing to wear. The younger, more active patients currently undergoing THA present unprecedented demands on the bearings. Ceramic-on-ceramic (CoC) bearings have consistently shown the lowest rates of wear. The recent advances, especially involving alumina/zirconia composite ceramic, have led to substantial improvements and good results in vitro.

Alumina/zirconia composite ceramics are extremely hard, scratch resistant and biocompatible. They offer a low co-efficient of friction and superior lubrication and lower rates of wear compared with other bearings. The major disadvantage is the risk of fracture of the ceramic. The new composite ceramic has reduced the risk of fracture of the femoral head to 0.002%. The risk of fracture of the liner is slightly higher (0.02%).

Assuming that the components are introduced without impingement, CoC bearings have major advantages over other bearings. Owing to the superior hardness, they produce less third body wear and are less vulnerable to intra-operative damage.

The improved tribology means that CoC bearings are an excellent choice for young, active patients requiring THA.

Cite this article: Bone Joint J 2016;98-B(1 Suppl A):14–17.

There is widespread concern regarding the incidence of adverse soft-tissue reactions after metal-on-metal (MoM) hip replacement. Recent National Joint Registry data have shown clear differences in the rates of failure of different designs of hip resurfacing. Our aim was to update the failure rates related to metal debris for the Articular Surface Replacement (ASR). A total of 505 of these were implanted.

Kaplan-Meier analysis showed a failure rate of 25% at six years for the ASR resurfacing and of 48.8% for the ASR total hip replacement (THR). Of 257 patients with a minimum follow-up of two years, 67 (26.1%) had a serum cobalt concentration which was greater than 7 μg/l. Co-ordinate measuring machine analysis of revised components showed that all patients suffering adverse tissue reactions in the resurfacing group had abnormal wear of the bearing surfaces. Six THR patients had relatively low rates of articular wear, but were found to have considerable damage at the trunion-taper interface. Our results suggest that wear at the modular junction is an important factor in the development of adverse tissue reactions after implantation of a large-diameter MoM THR.

Large femoral heads have been used with increasing frequency over the last decade. The prime reason is likely the effect of large heads on stability. The larger head neck ratio, combined with the increased jump distance of larger heads result in a greater arc of impingement free motion, and greater resistance to dislocation in a provocative position. Multiple studies have demonstrated clear clinical efficacy in diminishing dislocation rates with the use of large femoral heads. With crosslinked polyethylene, wear has been shown to be equivalent between larger and smaller heads. However, the stability advantages of increasing diameter beyond 38 mm have not been clearly demonstrated. More importantly, recent data implicates large heads in the increasing prevalence of groin pain and psoas impingement. There are clear benefits with larger femoral head diameters, but the advantages of diameters beyond 38 mm have not yet been demonstrated clinically.

We studied prospectively the long-term results of the Charnley Elite-Plus femoral stem in 184 consecutive young patients (194 hips). There were 130 men and 54 women with a mean age of 49.1 years (21 to 60). The predominant diagnosis was osteonecrosis of the femoral head (63.6%, 117 patients). Clinical and radiological evaluation was undertaken at each follow-up. The mean follow-up was 11.2 years (10 to 12).

The mean pre-operative Harris hip score was 43.4 (12 to 49) which improved to 91 (59 to 100) at the final follow-up. The survival of the femoral stem at 12 years was 99% with revision as the end-point. The mean annual linear wear of the polyethylene liner was 0.17 mm (0.13 to 0.22). The prevalence of acetabular osteolysis was 10.8% (21 hips) and osteolysis of the calcar femorale 12.9% (25 hips).

A third-generation cementing technique, accurate alignment of the stem and the use of a 22 mm zirconia head were important factors in the prevention of aseptic loosening of the Elite Plus femoral stem in these high-risk young patients.

Aims

The aim of this systematic review was to report the rate of dislocation following the use of dual mobility (DM) acetabular components in primary and revision total hip arthroplasty (THA).

Despite a lack of long-term follow-up, there is an increasing trend towards using femoral heads of large diameter in total hip replacement (THR), partly because of the perceived advantage of lower rates of dislocation. However, increasing the size of the femoral head is not the only way to reduce the rate of dislocation; optimal alignment of the components and repair of the posterior capsule could achieve a similar effect.

In this prospective study of 512 cemented unilateral THRs (Male:Female 230:282) performed between 2004 and 2011, we aimed to determine the rate of dislocation in patients who received a 22 mm head on a 9/10 Morse taper through a posterior approach with capsular repair and using the transverse acetabular ligament (TAL) as a guide for the alignment of the acetabular component. The mean age of the patients at operation was 67 years (35 to 89). The mean follow-up was 2.8 years (0.5 to 6.6). Pre- and post-operative assessment included Oxford hip, Short Form-12 and modified University of California Los Angeles and Merle D’Aubigne scores. The angles of inclination and anteversion of the acetabular components were measured using radiological software. There were four dislocations (0.78%), all of which were anterior.

In conclusion, THR with a 22 mm diameter head performed through a posterior approach with capsular repair and using the TAL as a guide for the alignment of the acetabular component was associated with a low rate of dislocation.

Cite this article: Bone Joint J 2014;96-B:1202–6.

Aims

One goal of total hip arthroplasty is to restore normal hip anatomy. The aim of this study was to compare displacement of the centre of rotation (COR) using a standard reaming technique with a technique in which the acetabulum was reamed immediately peripherally and referenced off the rim.

The ideal bearing surface for young patients undergoing total hip replacement (THR) remains controversial. We report the five-year results of a randomised controlled trial comparing the clinical and radiological outcomes of 102 THRs in 91 patients who were <  65 years of age. These patients were randomised to receive a cobalt–chrome on ultra-high-molecular-weight polyethylene, cobalt–chrome on highly cross-linked polyethylene, or a ceramic-on-ceramic bearing. In all, 97 hip replacements in 87 patients were available for review at five years. Two hips had been revised, one for infection and one for peri-prosthetic fracture.

At the final follow-up there were no significant differences between the groups for the mean Western Ontario and McMaster Universities osteoarthritis index (pain, p = 0.543; function, p = 0.10; stiffness, p = 0.99), Short Form-12 (physical component, p = 0.878; mental component, p = 0.818) or Harris hip scores (p = 0.22). Radiological outcomes revealed no significant wear in the ceramic group.

Comparison of standard and highly cross-linked polyethylene, however, revealed an almost threefold difference in the mean annual linear wear rates (0.151 mm/year versus 0.059 mm/year, respectively) (p < 0.001).

We investigated the rate of polyethylene wear of a cementless acetabular component at different periods of follow-up in order to test the hypothesis than an irrecoverable deformation process (creep) was followed by an initially low, but gradually increasing wear rate. We studied prospectively 93 uncemented total hip arthroplasties in 83 patients (mean age 50 years (22 to 63)) with a mean follow-up of 8.2 years (3 to 12). We measured the penetration of the femoral head from radiographs taken immediately after surgery at three, six and nine years, or at the latest follow-up.

The median wear rate was 0.17 mm per year in the first three years, a finding which we considered to be caused by creep. Thereafter, the rate of wear declined to 0.07 mm per year (four- to six-year period) and then increased to 0.17 mm per year (seven to nine years) and 0.27 mm per year (more than nine years), which we considered to be a reflection of genuine polyethylene wear. After the nine-year follow-up the wear rates were higher in patients with marked osteolysis. We found no relationship between the inclination angle of the acetabular component or femoral head orientation and the rate of wear. No acetabular component required revision.

We have examined the outcome of 400 consecutive patients who underwent total knee replacement with the Low Contact Stress mobile-bearing system between 1993 and 1994 and were followed up for a minimum of ten years. All operations were performed by surgeons in Christchurch, New Zealand, who used no other knee prosthesis during the study time.

At ten years after operation 238 patients (244 knees) remained for independent clinical and radiological assessment. There was a significant improvement (p < 0.001) in the postoperative knee scores at one, three, seven and ten years, although a slight deterioration in the score occurred between seven and ten years which did not reach statistical significance. The survival for polyethylene wear or loosening was 97% (95% CI 96 to 98) and survival using reoperation for any cause was 92% (95% CI 90 to 94) at 12 years. Polyethylene wear was more common in the meniscal-bearing component, with five knees requiring revision and a further eight demonstrating early wear. Osteolysis was not seen in the rotating platform component, but was present in three of the meniscal-bearing knees.

There was no association between the radiological alignment at one year and those knees that subsequently required revision. However, there was an association between the overall limb alignment and the Western Ontario McMasters University score (p < 0.001).

The Low Contact Stress mobile-bearing total knee replacement has proved to be a reliable implant at ten years when used in primary knee replacement irrespective of the deformity and diagnosis.

This study reports on ceramic-on-metal (CoM) bearings in total hip replacement. Whole blood metal ion levels were measured. The median increase in chromium and cobalt at 12 months was 0.08 μg/1 and 0.22 μg/1, respectively, in CoM bearings. Comparable values for metal-on-metal (MoM) were 0.48 μg/1 and 0.32 μg/1. The chromium levels were significantly lower in CoM than in MoM bearings (p = 0.02). The cobalt levels were lower, but the difference was not significant. Examination of two explanted ceramic heads revealed areas of thin metal transfer. CoM bearings (one explanted head and acetabular component, one explanted head and new acetabular component, and three new heads and acetabular components) were tested in a hip joint simulator. The explanted head and acetabular component had higher bedding-in. However, after one million cycles all the wear rates were the same and an order of magnitude less than that reported for MoM bearings. There were four outliers in each clinical group, primarily related to component malposition.

Oxidised zirconium (OxZi) has been developed as an alternative bearing surface for femoral heads in total hip arthroplasty (THA). This study has investigated polyethylene wear, functional outcomes and complications, comparing OxZi and cobalt–chrome (CoCr) as part of a three-arm, multicentre randomised controlled trial. Patients undergoing THA from four institutions were prospectively randomised into three groups. Group A received a CoCr femoral head and highly cross-linked polyethylene (XLPE) liner; Group B received an OxZi femoral head and XLPE liner; Group C received an OxZi femoral head and ultra-high molecular weight polyethylene (UHMWPE) liner. At five years, 368 patients had no statistically significant differences in short-form-36 (p = 0.176 mental, p = 0.756 physical), Western Ontario and McMaster Universities Osteoarthritis Index (p = 0.847), pain scores (p = 0.458) or complications. The mean rate of linear wear was 0.028 mm/year (standard deviation (sd) 0.010) for Group A, 0.023 mm/year (sd 0.010) for Group B, and 0.09 mm/year (sd 0.045) for Group C. Penetration was significantly higher in the UHMWPE liner group compared with both XLPE liner groups (p < 0.001) but no significant difference was noted between CoCr and OxZi when articulating with XLPE (p = 0.153). In this, the largest randomised study of this bearing surface, it appears that using a XLPE acetabular liner is more important in reducing THA component wear than the choice of femoral head bearing, at mid-term follow-up. There is a non-significant trend towards lower wear, coupling OxZi rather than CoCr with XLPE but long-term analysis is required to see if this observation changes with time and becomes significant.

Cite this article: Bone Joint J 2015;97-B:883–9.

Dislocation remains among the most common complications of, and reasons for, revision of both primary and revision total hip replacements (THR). Hence, there is great interest in maximising stability to prevent this complication. Head size has been recognised to have a strong influence on the risk of dislocation post-operatively. As femoral head size increases, stability is augmented, secondary to an increase in impingement-free range of movement. Larger head sizes also greatly increase the ‘jump distance’ required for the head to dislocate in an appropriately positioned cup. Level-one studies support the use of larger diameter heads as they decrease the risk of dislocation following primary and revision THR. Highly cross-linked polyethylene has allowed us to increase femoral head size, without a marked increase in wear. However, the thin polyethylene liners necessary to accommodate larger heads may increase the risk of liner fracture and larger heads have also been implicated in causing soft-tissue impingement resulting in groin pain. Larger diameter heads also impart larger forces on the femoral trunnion, which may contribute to corrosion, metal release, and adverse local tissue reactions. Alternative large bearings including large ceramic heads and dual mobility bearings may mitigate some of these risks, and several of these devices have been used with clinical success.

Cite this article: Bone Joint J 2014;96-B(11 Suppl A):23–6.

Tribocorrosion at the head–neck taper interface – so-called ‘taperosis’ – may be a source of metal ions and particulate debris in metal-on-polyethylene total hip arthroplasty (THA).

We examined the effect of femoral head length on fretting and corrosion in retrieved head–neck tapers in vivo for a minimum of two years (mean 8.7 years; 2.6 to 15.9). A total of 56 femoral heads ranging from 28 mm to 3 mm to 28 mm + 8 mm, and 17 femoral stems featuring a single taper design were included in the study. Fretting and corrosion were scored in three horizontally oriented concentric zones of each taper by stereomicroscopy.

Head length was observed to affect fretting (p = 0.03), with 28 mm + 8 mm femoral heads showing greater total fretting scores than all other head lengths. The central zone of the femoral head bore taper was subject to increased fretting damage (p = 0.01), regardless of head length or stem offset. High-offset femoral stems were associated with greater total fretting of the bore taper (p = 0.04).

Increased fretting damage is seen with longer head lengths and high-offset femoral stems, and occurs within a central concentric zone of the femoral head bore taper. Further investigation is required to determine the effect of increased head size, and variations in head–neck taper design.

Cite this article: Bone Joint J 2015; 97-B:911–16.

The long term biological effects of wear products following total hip arthroplasty (THA) are unclear. However, the indications for THA are expanding, with increasingly younger patients undergoing the procedure.

This prospective, randomised study compared two groups of patients undergoing THA after being randomised to receive one of two different bearing surfaces: metal-on-polyethylene (MoP) n = 22 and metal-on-metal (MoM) n = 23. We investigated the relationship between three variables: bearing surface (MoP vs MoM), whole blood levels of chromium (Cr) and cobalt (Co) and chromosomal aberrations in peripheral lymphocyte pre-operatively and at one, two and five years post-surgery.

Our results demonstrated significantly higher mean cobalt and chromium (Co and Cr) blood levels in the MoM group at all follow-up points following surgery (p < 0.01), but there were no significant differences in the chromosomal aberration indices between MoM and MoP at two or five years (two years: p = 0.56, p = 0.08, p = 0.91, p = 0.51 and five years: p = 0.086, p = 0.73, p = 0.06, p = 0.34) for translocations, breaks, loss and gain of chromosomes respectively. Regression analysis showed a strong linear relationship between Cr levels and the total chromosomal aberration indices in the MoM group (R² = 0.90016), but this was not as strong for Co (R² = 0.68991). In the MoP group, the analysis revealed a poor relationship between Cr levels and the total chromosomal aberration indices (R² = 0.23908) but a slightly stronger relationship for Co (R² = 0.64292). Across both groups, Spearman’s correlation detected no overall association between Co and Cr levels and each of the studied chromosomal aberrations. There remains no clear indication which THA bearing couple is the most biocompatible, especially in young active patients. While THA continues to be very successful at alleviating pain and restoring function, the long-term biological implications of the procedure still require further scrutiny.

Cite this article: Bone Joint J 2015;97-B:1183–91.

The purpose of this study was to evaluate whether concerns about the release of metal ions in metal-on-metal total hip replacements (THR) should be extended to patients with metal-bearing total disc replacements (TDR).

Cobalt and chromium levels in whole blood and serum were measured in ten patients with a single-level TDR after a mean follow-up of 34.5 months (13 to 61) using inductively-coupled plasma mass spectrometry. These metal ion levels were compared with pre-operative control levels in 81 patients and with metal ion levels 12 months after metal-on-metal THR (n = 21) and resurfacing hip replacement (n = 36). Flexion-extension radiographs were used to verify movement of the TDR.

Cobalt levels in whole blood and serum were significantly lower in the TDR group than in either the THR (p = 0.007) or the resurfacing group (p < 0.001). Both chromium levels were also significantly lower after TDR versus hip resurfacing (p < 0.001), whereas compared with THR this difference was only significant for serum levels (p = 0.008). All metal ion levels in the THR and resurfacing groups were significantly higher than in the control group (p < 0.001). In the TDR group only cobalt in whole blood appeared to be significantly higher (p < 0.001). The median range of movement of the TDR was 15.5° (10° to 22°).

These results suggest that there is minimal cause for concern about high metal ion concentrations after TDR, as the levels appear to be only moderately elevated. However, spinal surgeons using a metal-on-metal TDR should still be aware of concerns expressed in the hip replacement literature about toxicity from elevated metal ion levels, and inform their patients appropriately.

This study reports the mid-term results of a large-bearing hybrid metal-on-metal total hip replacement in 199 hips (185 patients) with a mean follow-up of 62 months (32 to 83).

Two patients died of unrelated causes and 13 were lost to follow-up. In all, 17 hips (8.5%) have undergone revision, and a further 14 are awaiting surgery. All revisions were symptomatic. Of the revision cases, 14 hips showed evidence of adverse reactions to metal debris. The patients revised or awaiting revision had significantly higher whole blood cobalt ion levels (p = 0.001), but no significant difference in acetabular component size or position compared with the unrevised patients. Wear analysis (n = 5) showed increased wear at the trunnion-head interface, normal levels of wear at the articulating surfaces and evidence of corrosion on the surface of the stem.

The cumulative survival rate, with revision for any reason, was 92.4% (95% confidence interval 87.4 to 95.4) at five years. Including those awaiting surgery, the revision rate would be 15.1% with a cumulative survival at five years of 89.6% (95% confidence interval 83.9 to 93.4).

This hybrid metal-on-metal total hip replacement series has shown an unacceptably high rate of failure, with evidence of high wear at the trunnion-head interface and passive corrosion of the stem surface. This raises concerns about the use of large heads on conventional 12/14 tapers.

The survivorship of contemporary resurfacing arthroplasty of the hip using metal-on-metal bearings is better than that of first generation designs, but short-term failures still occur. The most common reasons for failure are fracture of the femoral neck, loosening of the component, osteonecrosis of the femoral head, reaction to metal debris and malpositioning of the component. In 2008 the Australian National Joint Registry reported an inverse relationship between the size of the head component and the risk of revision in resurfacing hip arthroplasty. Hips with a femoral component size of ≤ 44 mm have a fivefold increased risk of revision than those with femoral components of ≥ 55 mm irrespective of gender. We have reviewed the literature to explore this observation and to identify possible reasons including the design of the implant, loading of the femoral neck, the orientation of the component, the production of wear debris and the effects of metal ions, penetration of cement and vascularity of the femoral head. Our conclusion is that although multifactorial, the most important contributors to failure in resurfacing arthroplasty of the hip are likely to be the design and geometry of the component and the orientation of the acetabular component.

Large ceramic femoral heads offer several advantages that are potentially advantageous to patients undergoing both primary and revision total hip replacement. Many high-quality studies have demonstrated the benefit of large femoral heads in reducing post-operative instability. Ceramic femoral heads may also offer an advantage in reducing polyethylene wear that has been reported in vitro and is starting to become clinically apparent in mid-term clinical outcome studies. Additionally, the risk of taper corrosion at a ceramic femoral head–neck junction is clearly lower than when using a metal femoral head. With improvements in the material properties of both modern ceramic femoral heads and polyethylene acetabular liners that have reduced the risk of mechanical complications, large ceramic heads have gained popularity in recent years.

Cite this article: Bone Joint J 2013;95-B, Supple A:63–6.

The Oxford Unicompartmental Knee replacement (UKR) was introduced as a design to reduce polyethylene wear. There has been one previous retrieval study involving this implant, which reported very low rates of wear in some specimens but abnormal patterns of wear in others. There has been no further investigation of these abnormal patterns. The bearings were retrieved from 47 patients who had received a medial Oxford UKR for anteromedial osteoarthritis of the knee. None had been studied previously. The mean time to revision was 8.4 years (sd 4.1), with 20 having been implanted for over ten years. The macroscopic pattern of polyethylene wear and the linear penetration were recorded for each bearing. The mean rate of linear penetration was 0.07 mm/year. The patterns of wear fell into three categories, each with a different rate of linear penetration; 1) no abnormal macroscopic wear and a normal articular surface, n = 16 (linear penetration rate = 0.01 mm/year); 2) abnormal macroscopic wear and normal articular surfaces with extra-articular impingement, n = 16 (linear penetration rate = 0.05 mm/year); 3) abnormal macroscopic wear and abnormal articular surfaces with intra-articular impingement +/− signs of non-congruous articulation, n = 15 (linear penetration rate = 0.12 mm/year). The differences in linear penetration rate were statistically significant (p < 0.001).

These results show that very low rates of polyethylene wear are possible if the device functions normally. However, if the bearing displays suboptimal function (extra-articular, intra-articular impingement or incongruous articulation) the rates of wear increase significantly.

Alumina–alumina bearings are among the most resistant to wear in total hip replacement. Examination of their surfaces is one way of comparing damage caused by wear of hip joints simulated in vitro to that seen in explanted bearings. The aim of this study was to determine whether second-generation ceramic bearings exhibited a better pattern of wear than those reported in the literature for first-generation bearings. We considered both macro- and microscopic findings.

We found that long-term alumina wear in association with a loose acetabular component could be categorised into three groups. Of 20 specimens, four had ‘low wear’, eight ‘crescent wear’ and eight ‘severe wear’, which was characterised by a change in the physical shape of the bearing and a loss of volume. This suggests that the wear in alumina–alumina bearings in association with a loose acetabular component may be variable in pattern, and may explain, in part, why the wear of a ceramic head in vivo may be greater than that seen after in vitro testing.

Radiological assessment of total and unicompartmental knee replacement remains an essential part of routine care and follow-up. Appreciation of the various measurements that can be identified radiologically is important. It is likely that routine plain radiographs will continue to be used, although there has been a trend towards using newer technologies such as CT, especially in a failing knee, where it provides more detailed information, albeit with a higher radiation exposure.

The purpose of this paper is to outline the radiological parameters used to evaluate knee replacements, describe how these are measured or classified, and review the current literature to determine their efficacy where possible.

We report a case of a male patient presenting with bilateral painful but apparently well-positioned and -fixed large-diameter metal-on-metal hip replacements four years post-operatively. Multiple imaging modes revealed a thick-walled, cystic expansile mass in communication with the hip joint (a pseudotumour). Implant retrieval analysis and tissue culture eliminated high bearing wear or infection as causes for the soft-tissue reaction, but noted marked corrosion of the modular neck taper adaptor and corrosion products in the tissues. Therefore, we believe corrosion products from the taper caused by mismatch of the implant components led to pseudotumour formation requiring revision.

Increased femoral head size may reduce dislocation rates following total hip replacement. The National Joint Registry for England and Wales has highlighted a statistically significant increase in the use of femoral heads ≥ 36 mm in diameter from 5% in 2005 to 26% in 2009, together with an increase in the use of the posterior approach. The aim of this study was to determine whether rates of dislocation have fallen over the same period. National data for England for 247 546 procedures were analysed in order to determine trends in the rate of dislocation at three, six, 12 and 18 months after operation during this time. The 18-month revision rates were also examined.

Between 2005 and 2009 there were significant decreases in cumulative dislocations at three months (1.12% to 0.86%), six months (1.25% to 0.96%) and 12 months (1.42% to 1.11%) (all p < 0.001), and at 18 months (1.56% to 1.31%) for the period 2005 to 2008 (p < 0.001). The 18-month revision rates did not significantly change during the study period (1.26% to 1.39%, odds ratio 1.10 (95% confidence interval 0.98 to 1.24), p = 0.118). There was no evidence of changes in the coding of dislocations during this time.

These data have revealed a significant reduction in dislocations associated with the use of large femoral head sizes, with no change in the 18-month revision rate.

Complications involving the patellofemoral joint, caused by malrotation of the femoral component during total knee replacement, are an important cause of persistent pain and failure leading to revision surgery. The aim of this study was to determine and quantify the influence of femoral component malrotation on patellofemoral wear, and to determine whether or not there is a difference in the rate of wear of the patellar component when articulated against oxidised zirconium (OxZr) and cobalt-chrome (CoCr) components. An in vitro method was used to simulate patellar maltracking for both materials. Both rates of wear and changes in height on the patellar articular surface were measured. The mean rates of wear measured were very small compared to standard tibiofemoral wear rates. When data for each femoral component material were pooled, the mean rate of wear was 0.19 mm³/Mcycle (sd 0.21) for OxZr and 0.34 mm³/Mcycle (sd 0.335) for CoCr. The largest change in height on each patella varied from -0.05 mm to -0.33 mm over the different configurations.

The results suggest that patellar maltracking due to an internally rotated femoral component leads to an increased mean patellar wear. Although not statistically significant, the mean wear production may be lower for OxZr than for CoCr components.

We present a case of early retrieval of an Oxinium femoral head and corresponding polyethylene liner where there was significant surface damage to the head and polyethylene. The implants were retrieved at the time of revision surgery to correct leg-length discrepancy just 48 hours after the primary hip replacement. Appropriate analysis of the retrieved femoral head demonstrated loss of the Oxinium layer with exposure of the underlying substrate and transfer of titanium from the acetabular shell at the time of a reduction of the index total hip replacement. In addition, the level of damage to the polyethylene was extensive despite only 48 hours in situ.

The purpose of this report is to highlight the care that is required at the time of reduction, especially with these hard femoral counter-faces such as Oxinium. To our knowledge, the damage occurring at the time of reduction has not been previously reported following the retrieval of an otherwise well-functioning hip replacement.

The aim of this study was to investigate the possible benefit of large-head metal-on-metal bearing on a stem for primary hip replacement compared with a 28 mm diameter conventional metal-on-polyethylene bearing in a prospective randomised controlled trial. We investigated cemented stem behaviour between these two different bearings using Einzel-Bild-Röntgen-Analyse, clinical and patient reported measures (Harris hip score, Western Ontario and McMaster Universities osteoarthritis index, Short Form-36 and satisfaction) and whole blood metal ion levels at two years. A power study indicated that 50 hips were needed in each group to detect subsidence of > 5 mm at two years with a p-value of < 0.05.

Significant improvement (p < 0.001) was found in the mean clinical and patient reported outcomes at two years for both groups. Comparison of outcomes between the groups at two years showed no statistically significant difference for mean stem migration, clinical and patient reported outcomes; except overall patient satisfaction which was higher for metal-on-metal group (p = 0.05). Metal ion levels were raised above the Medicines and Healthcare products Regulatory Agency advised safety level (7 µg per litre) in 20% of the metal-on-metal group and in one patient in metal-on-polyethylene group (who had a metal-on-metal implant on the contralateral side). Two patients in the metal-on-metal group were revised, one for pseudotumour and one for peri-prosthetic fracture.

Use of large modular heads is associated with a risk of raised whole blood metal ion levels despite using a proven bearing from resurfacing. The head-neck junction or excess stem micromotion are possibly the weak links warranting further research.

We measured the orientation of the acetabular and femoral components in 45 patients (33 men, 12 women) with a mean age of 53.4 years (30 to 74) who had undergone revision of metal-on-metal hip resurfacings. Three-dimensional CT was used to measure the inclination and version of the acetabular component, femoral version and the horizontal femoral offset, and the linear wear of the removed acetabular components was measured using a roundness machine.

We found that acetabular version and combined version of the acetabular and femoral components were weakly positively correlated with the rate of wear. The acetabular inclination angle was strongly positively correlated with the rate of wear. Femoral version was weakly negatively correlated with the rate of wear. Application of a threshold of > 5 μm/year for the rate of wear in order to separate the revisions into low or high wearing groups showed that more high wearing components were implanted outside Lewinnek’s safe zone, but that this was mainly due to the inclination of the acetabular component, which was the only parameter that significantly differed between the groups.

We were unable to show that excess version of the acetabular component alone or combined with femoral version was associated with an increase in the rate of wear based on our assessment of version using CT.

There have been comparatively few studies of the incidence of osteolysis and the survival of hybrid and cementless total hip replacements (THRs) in patients younger than 50 years of age. We prospectively reviewed 78 patients (109 hips) with a hybrid THR having a mean age of 43.4 years (21 to 50) and 79 patients (110 hips) with a cementless THR with a mean age of 46.8 years (21 to 49). The patients were evaluated clinically using the Harris hip score, the Western Ontario and McMaster Universities (WOMAC) osteoarthritis score and the University of California, Los Angeles (UCLA) activity score. Radiographs and CT scans were assessed for loosening and osteolysis. The mean follow-up was for 18.4 years (16 to 19) in both groups.

The mean post-operative Harris hip scores (91 points versus 90 points), the mean WOMAC scores (11 points versus 13 points) and UCLA activity scores (6.9 points versus 7.1 points) were similar in both groups. The revision rates of the acetabular component (13% versus 16%) and the femoral component (3% versus 4%), and the survival of the acetabular component (87% versus 84%) and the femoral component (97% versus 96%) were similar in both groups.

Although the long-term fixation of the acetabular metallic shell and the cemented and cementless femoral components was outstanding, wear and peri-acetabular osteolysis constitute the major challenges of THR in young patients.

The Articular Surface Replacement (ASR) hip resurfacing arthroplasty has a failure rate of 12.0% at five years, compared with 4.3% for the Birmingham Hip Resurfacing (BHR). We analysed 66 ASR and 64 BHR explanted metal-on-metal hip replacements with the aim of understanding their mechanisms of failure. We measured the linear wear rates of the acetabular and femoral components and analysed the clinical cause of failure, pre-revision blood metal ion levels and orientation of the acetabular component.

There was no significant difference in metal ion levels (chromium, p = 0.82; cobalt, p = 0.40) or head wear rate (p = 0.14) between the two groups. The ASR had a significantly increased rate of wear of the acetabular component (p = 0.03) and a significantly increased occurrence of edge loading (p < 0.005), which can be attributed to differences in design between the ASR and BHR. The effects of differences in design on the in vivo wear rates are discussed: these may provide an explanation as to why the ASR is more sensitive to suboptimal positioning than the BHR.

As metal-on-metal arthroplasty becomes more widespread, concerns are being raised about the potential dangers of metal particulate debris. We present the case of a benign psoas mass secondary to the presence of such particles. The mass was excised and the hip resurfacing subsequently revised to a total hip replacement.

Components from 73 failed knee replacements (TKRs) consisting of rotating-platform, mobile-bearing and fixed-bearing implants were examined to assess the patterns of wear. The patterns were divided into low-grade (burnishing, abrasion and cold flow) and high-grade (scratching, pitting/metal embedding and delamination) to assess the severity of the wear of polyethylene.

The rotating-platform group had a higher incidence of low-grade wear on the upper surface compared with the fixed-bearing group. By contrast, high-grade wear comprising scratching, pitting and third-body embedding was seen on the lower surface. Linear regression analysis showed a significant correlation of the wear scores between the upper and lower surfaces of the tibial insert (R² = 0.29, p = 0.04) for the rotating-platform group, but no significant correlation was found for the fixed-bearing counterpart.

This suggests that high-grade wear patterns on the upper surface are reduced with the rotating-platform design. However, the incidence of burnishing, pitting/third-body embedding and scratching wear patterns on the lower surface was higher compared with that in the fixed-bearing knee.

Metal-on-metal bearings for total hip replacement (THR) are becoming increasingly popular. Improved wear characteristics mean that these articulations are being inserted into younger patients in the form of THR and resurfacing procedures. This has led to concerns regarding potential carcinogenicity because of the increased exposure to metal ions that the procedure brings.

We have studied the serum cobalt and chromium concentrations in patients who had primary, well-fixed Ring metal-on-metal THRs for more than 30 years. The levels of cobalt and chromium were elevated by five and three times, respectively compared with those in our reference groups. Metal-on-metal articulations appear to be the source of metal ions throughout the life of the prosthesis. In three patients who had undergone revision of a previous metal-on-metal THR to a metal-on-polyethylene replacement the levels of metal ions were within the normal range. The elevations of cobalt and chromium ions seen in our study were comparable with those in patients with modern metal-on-metal THRs.

We present the early clinical and radiological results of Articular Surface Replacement (ASR) resurfacings in 214 hips (192 patients) with a mean follow-up of 43 months (30 to 57). The mean age of the patients was 56 years (28 to 74) and 85 hips (40%) were in 78 women.

The mean Harris hip score improved from 52 (11 to 81) to 95 (27 to 100) at two years and the mean University of California, Los Angeles activity score from 3.9 (1 to 10) to 7.4 (2 to 10) in the same period. Narrowing of the neck (to a maximum of 9%) was noted in 124 of 209 hips (60%). There were 12 revisions (5.6%) involving four (1.9%) early fractures of the femoral neck and two (0.9%) episodes of collapse of the femoral head secondary to avascular necrosis. Six patients (2.8%) had failure related to metal wear debris. The overall survival for our series was 93% (95% confidence interval 80 to 98) and 89% (95% confidence interval 82 to 96) for hips with acetabular components smaller than 56 mm in diameter.

The ASR implant has a lower diametrical clearance and a subhemispherical acetabular component when compared with other more frequently implanted metal-on-metal hip resurfacings. These changes may contribute to the higher failure rate than in other series, compared with other designs. Given our poor results with the small components we are no longer implanting the smaller size.

We have compared four computer-assisted methods to measure penetration of the femoral head into the acetabular component in total hip replacement. These were the Martell Hip Analysis suite 7.14, Rogan HyperOrtho, Rogan View Pro-X and Roman v1.70. The images used for the investigation comprised 24 anteroposterior digital radiographs and 24 conventional acetate radiographs which were scanned to provide digital images. These radiographs were acquired from 24 patients with an uncemented total hip replacement with a follow-up of approximately eight years (mean 8.1; 6.3 to 9.1). Each image was measured twice by two blinded observers. The mean annual rates of penetration of the femoral head measured in the eight-year single image analysis were: Martell, 0.24 (SD 0.19); HyperOrtho, 0.12 (SD 0.08); View Pro-X, 0.12 (SD 0.06); Roman, 0.12 (SD 0.07). In paired analysis of the six-month and eight-year radiographs: Martell, 0.35 (SD 0.22); HyperOrtho, 0.15 (SD 0.13); View Pro-X, 0.11 (SD 0.06); Roman, 0.11 (SD 0.07). The intra- and inter-observer variability for the paired analysis was best for View Pro-X and Roman software, with intraclass correlations of 0.97, 0.87 and 0.96, 0.87, respectively, and worst for HyperOrtho and Martell, with intraclass correlations of 0.46, 0.13 and 0.33, 0.39, respectively.

The Roman method proved the most precise and the most easy to use in clinical practice and the software is available free of charge. The Martell method showed the lowest precision, indicating a problem with its edge detection algorithm on digital images.

A reduced femoral offset in total hip replacement has been thought to be disadvantageous. We reviewed the results of 54 consecutive primary total hip replacements in 49 patients (mean age of 68 years) performed between August 1990 and December 1994, with a mean follow-up of 8.8 years (sd 2.1). The mean pre-operative femoral offset for these hips was 41 mm (sd 7.4). All patients received a low-offset Charnley stem and a polyethylene cup inserted by a single surgeon.

At their latest follow-up, surviving patients had a significant improvement in the performance of their hip. Three had undergone revision, one each for deep infection, recurrent dislocation and late pain with subluxation. No hips had been revised, or were at risk of revision, for aseptic loosening. The mean annual linear rate of wear was 0.2 mm (sd 0.08) for the whole group. There was no correlation between the pre-operative femoral offset and the post-operative rate of wear. Our survivorship estimate was 91% when revision for any reason was taken as an end-point, but 100% if aseptic loosening was considered as the end-point. Our study demonstrates that a low-offset femoral stem can produce good, medium-term results.

The long-term effects of metal-on-metal arthroplasty are currently under scrutiny because of the potential biological effects of metal wear debris. This review summarises data describing the release, dissemination, uptake, biological activity, and potential toxicity of metal wear debris released from alloys currently used in modern orthopaedics. The introduction of risk assessment for the evaluation of metal alloys and their use in arthroplasty patients is discussed and this should include potential harmful effects on immunity, reproduction, the kidney, developmental toxicity, the nervous system and carcinogenesis.