We report a systematic review and meta-analysis of the peer-reviewed literature focusing on metal sensitivity testing in patients undergoing total joint replacement (TJR). Our purpose was to assess the risk of developing metal hypersensitivity post-operatively and its relationship with outcome and to investigate the advantages of performing hypersensitivity testing. We undertook a comprehensive search of the citations quoted in PubMed and EMBASE: 22 articles (comprising 3634 patients) met the inclusion criteria. The frequency of positive tests increased after TJR, especially in patients with implant failure or a metal-on-metal coupling. The probability of developing a metal allergy was higher post-operatively (odds ratio (OR) 1.52 (95% confidence interval (CI) 1.06 to 2.31)), and the risk was further increased when failed implants were compared with stable TJRs (OR 2.76 (95% CI 1.14 to 6.70)). Hypersensitivity testing was not able to discriminate between stable and failed TJRs, as its predictive value was not statistically proven. However, it is generally thought that hypersensitivity testing should be performed in patients with a history of metal allergy and in failed TJRs, especially with metal-on-metal implants and when the cause of the loosening is doubtful

Aims

A limited number of investigations with conflicting results have described perivascular lymphocytic infiltration (PVLI) in the setting of total knee arthroplasty (TKA). The purpose of this study was to determine if PVLI found in TKAs at the time of aseptic revision surgery was associated with worse clinical outcomes and survivorship.

Aims. The treatment of patients with allergies to metal in total joint arthroplasty is an ongoing debate. Possibilities include the use of hypoallergenic prostheses, as well as the use of standard cobalt-chromium (CoCr) alloy. This non-designer study was performed to evaluate the clinical outcome and survival rates of unicondylar knee arthroplasty (UKA) using a standard CoCr alloy in patients reporting signs of a hypersensitivity to metal. Patients and Methods. A consecutive series of patients suitable for UKA were screened for symptoms of metal hypersensitivity by use of a questionnaire. A total of 82 patients out of 1737 patients suitable for medial UKA reporting cutaneous metal hypersensitivity to cobalt, chromium, or nickel were included into this study and prospectively evaluated to determine the functional outcome, possible signs of hypersensitivity, and short-term survivorship at a minimum follow-up of 1.5 years. Results. At a mean follow-up of three years (1.5 to 5.7), no local or systemic symptoms of hypersensitivity to metal were observed. One patient underwent revision surgery to a bicondylar prosthesis due to a tibial periprosthetic fracture resulting in a survival rate of 98.8% (95% confidence interval (CI) 91.7 to 99.8; number at risk, 28) at three years with the endpoint of revision for any reason and a survival rate of 97.6% (95% CI 90.6 to 99.3; number at risk, 29) for the endpoint of all reoperations. Clinical outcome was good to excellent with a mean Oxford Knee Score of 42.5 (. sd. 2.5; 37 to 48). Conclusion. This study is the first demonstrating clinical results and survival analysis of UKA using a CoCr alloy in patients with a history of metal hypersensitivity. Functional outcome and survivorship are on a high-level equivalent to those reported for UKA in patients without a history of metal hypersensitivity. No serious local or systemic symptoms of metal hypersensitivity could be detected, and no revision surgery was performed due to an adverse reaction to metal ions

We explored the literature surrounding whether allergy and hypersensitivity has a clinical basis for implant selection in total knee arthroplasty (TKA). In error, the terms hypersensitivity and allergy are often used synonymously. Although a relationship is present, we could not find any evidence of implant failure due to allergy. There is however increasing basic science that suggests a link between loosening and metal ion production. This is not an allergic response but is a potential problem. With a lack of evidence logically there can be no justification to use ‘hypoallergenic’ implants in patients who have pre-existing skin sensitivity to the metals used in TKA.

Cite this article: Bone Joint J 2016;98-B:437–41.

Aims

The primary aim of this independent prospective randomised trial was to compare serum metal ion levels for ceramic-on-metal (CoM) and metal-on-metal (MoM) bearing surfaces in total hip arthroplasty (THA). Our one-year results demonstrated elevation in metal ion levels above baseline with no significant difference between the CoM and MoM groups. This paper reviews the five-year data.

Aims

In order to evaluate the effectiveness of the Mobi-C implant in cervical disc degeneration, a randomised study was conducted, comparing the Mobi-C prosthesis arthroplasty with anterior cervical disc fusion (ACDF) in patients with single level cervical spondylosis.

A total of 219 hips in 192 patients aged between 18 and 65 years were randomised to 28-mm metal-on-metal uncemented total hip replacements (THRs, 107 hips) or hybrid hip resurfacing (HR, 112 hips). At a mean follow-up of eight years (6.6 to 9.3) there was no significant difference between the THR and HR groups regarding rate of revision (4.0% (4 of 99) vs 5.8% (6 of 104), p = 0.569) or re-operation rates without revision (5.1% (5 of 99) vs 2.9% (3 of 104), p = 0.428). In the THR group one recurrent dislocation, two late deep infections and one peri-prosthetic fracture required revision, whereas in the HR group five patients underwent revision for femoral head loosening and one for adverse reaction to metal debris. The mean University of California, Los Angeles activity scores were significantly higher in HR (7.5 (sd 1.7) vs 6.9 (sd 1.7), p = 0.035), but similar mean Western Ontario and McMaster Universities Osteoarthritis Index scores were obtained (5.8 (sd 9.5) in HR vs 5.1 (sd 8.9) in THR, p = 0.615) at the last follow-up. Osteolysis was found in 30 of 81 THR patients (37.4%), mostly in the proximal femur, compared with two of 83 HR patients (2.4%) (p < 0.001). At five years the mean metal ion levels were < 2.5 μg/l for cobalt and chromium in both groups; only titanium was significantly higher in the HR group (p = 0.001). Although revision rates and functional scores were similar in both groups at mid-term, long-term survival analysis is necessary to determine whether one procedure is more advantageous than the other.

Cite this article: Bone Joint J 2013;95-B:1464–73.

We report a case of a male patient presenting with bilateral painful but apparently well-positioned and -fixed large-diameter metal-on-metal hip replacements four years post-operatively. Multiple imaging modes revealed a thick-walled, cystic expansile mass in communication with the hip joint (a pseudotumour). Implant retrieval analysis and tissue culture eliminated high bearing wear or infection as causes for the soft-tissue reaction, but noted marked corrosion of the modular neck taper adaptor and corrosion products in the tissues. Therefore, we believe corrosion products from the taper caused by mismatch of the implant components led to pseudotumour formation requiring revision.

We report the consensus of surgical opinions of an international faculty of expert metal-on-metal hip resurfacing surgeons, with a combined experience of over 18 000 cases, covering required experience, indications, surgical technique, rehabilitation and the management of problematic cases.

In a double-blinded randomised controlled trial, 83 patients with primary osteoarthritis of the hip received either a ceramic-on-metal (CoM) or metal-on-metal (MoM) total hip replacement (THR). The implants differed only in the bearing surfaces used. The serum levels of cobalt and chromium and functional outcome scores were compared pre-operatively and at six and 12 months post-operatively.

Data were available for 41 CoM and 36 MoM THRs (four patients were lost to follow-up, two received incorrect implants). The baseline characteristics of both cohorts were similar. Femoral head size measured 36 mm in all but two patients who had 28 mm heads. The mean serum cobalt and chromium levels increased in both groups, with no difference noted between groups at six months (cobalt p = 0.67, chromium p = 0.87) and 12 months (cobalt p = 0.76, chromium p = 0.76) post-operatively. Similarly, the mean Oxford hip scores, Western Ontario and McMaster Universities Osteoarthritis index and University of California, Los Angeles activity scores showed comparable improvement at 12 months.

Our findings indicate that CoM and MoM couplings are associated with an equivalent increase in serum cobalt and chromium levels, and comparable functional outcome scores at six and 12-months follow-up.

There is widespread concern regarding the incidence of adverse soft-tissue reactions after metal-on-metal (MoM) hip replacement. Recent National Joint Registry data have shown clear differences in the rates of failure of different designs of hip resurfacing. Our aim was to update the failure rates related to metal debris for the Articular Surface Replacement (ASR). A total of 505 of these were implanted.

Kaplan-Meier analysis showed a failure rate of 25% at six years for the ASR resurfacing and of 48.8% for the ASR total hip replacement (THR). Of 257 patients with a minimum follow-up of two years, 67 (26.1%) had a serum cobalt concentration which was greater than 7 μg/l. Co-ordinate measuring machine analysis of revised components showed that all patients suffering adverse tissue reactions in the resurfacing group had abnormal wear of the bearing surfaces. Six THR patients had relatively low rates of articular wear, but were found to have considerable damage at the trunion-taper interface. Our results suggest that wear at the modular junction is an important factor in the development of adverse tissue reactions after implantation of a large-diameter MoM THR.

Metallosis is a rare cause of failure after total knee replacement and has only previously been reported when there has been abnormal metal-on-metal contact. We describe 14 patients (15 knees) whose total knee replacement required revision for a new type of early failure caused by extensive metallosis. A modification of a cementless rotating platform implant, which had previously had excellent long-term survival, had been used in each case. The change was in the form of a new porous-beaded surface on the femoral component to induce cementless fixation, which had been used successfully in the fixation of acetabular and tibial components. This modification appeared to have resulted in metallosis due to abrasive two-body wear. The component has subsequently been recalled and is no longer in use. The presentation, investigation, and findings at revision are described and a possible aetiology and its implications are discussed.

We have reviewed our experience of the removal of deep extremity orthopaedic implants in children to establish the nature, rate and risk of complications associated with this procedure. A retrospective review was performed of 801 children who had 1223 implants inserted and subsequently removed over a period of 17 years. Bivariate analysis of possible predictors including clinical factors, complications associated with implant insertion and indications for removal and the complications encountered at removal was performed. A logistical regression model was then constructed using those predictors which were significantly associated with surgical complications from the bivariate analyses. Odds ratios estimated in the logistical regression models were converted to risk ratios.

The overall rate of complications after removal of the implant was 12.5% (100 complications in 801 patients), with 48 (6.0%) major and 52 (6.5%) minor. Children with a complication after insertion of the initial implant or with a non-elective indication for removal, a neuromuscular disease associated with a seizure disorder or a neuromuscular disease in those unable to walk, had a significantly greater chance of having a major complication after removal of the implant. Children with all four of these predictors were 14.6 times more likely to have a major complication.

Despite the increasing interest and subsequent published literature on hip resurfacing arthroplasty, little is known about the prevalence of its complications and in particular the less common modes of failure. The aim of this study was to identify the prevalence of failure of hip resurfacing arthroplasty and to analyse the reasons for it.

From a multi-surgeon series (141 surgeons) of 5000 Birmingham hip resurfacings we have analysed the modes, prevalence, gender differences and times to failure of any hip requiring revision. To date 182 hips have been revised (3.6%). The most common cause for revision was a fracture of the neck of the femur (54 hips, prevalence 1.1%), followed by loosening of the acetabular component (32 hips, 0.6%), collapse of the femoral head/avascular necrosis (30 hips, 0.6%), loosening of the femoral component (19 hips, 0.4%), infection (17 hips, 0.3%), pain with aseptic lymphocytic vascular and associated lesions (ALVAL)/metallosis (15 hips, 0.3%), loosening of both components (five hips, 0.1%), dislocation (five hips, 0.1%) and malposition of the acetabular component (three hips, 0.1%). In two cases the cause of failure was unknown.

Comparing men with women, we found the prevalence of revision to be significantly higher in women (women = 5.7%; men = 2.6%, p < 0.001). When analysing the individual modes of failure women had significantly more revisions for loosening of the acetabular component, dislocation, infection and pain/ALVAL/metallosis (p < 0.001, p = 0.004, p = 0.008, p = 0.01 respectively).

The mean time to failure was 2.9 years (0.003 to 11.0) for all causes, with revision for fracture of the neck of the femur occurring earlier than other causes (mean 1.5 years, 0.02 to 11.0). There was a significantly shorter time to failure in men (mean 2.1 years, 0.4 to 8.7) compared with women (mean 3.6 years, 0.003 to 11.0) (p < 0.001).

Metal-on-metal hip resurfacing is commonly performed for osteoarthritis in young active patients. We have observed cystic or solid masses, which we have called inflammatory pseudotumours, arising around these devices. They may cause soft-tissue destruction with severe symptoms and a poor outcome after revision surgery. The aim of this study was to determine the incidence of and risk factors for pseudotumours that are serious enough to require revision surgery.

Since 1999, 1419 metal-on-metal hip resurfacings have been implanted by our group in 1224 patients; 1.8% of the patients had a revision for pseudotumour. In this series the Kaplan-Meier cumulative revision rate for pseudotumour increased progressively with time. At eight years, in all patients, it was 4% (95% confidence interval (CI) 2.2 to 5.8). Factors significantly associated with an increase in revision rate were female gender (p < 0.001), age under 40 (p = 0.003), small components (p = 0.003), and dysplasia (p = 0.019), whereas implant type was not (p = 0.156). These factors were inter-related, however, and on fitting a Cox proportional hazard model only gender (p = 0.002) and age (p = 0.024) had a significant independent influence on revision rate; size nearly reached significance (p = 0.08). Subdividing the cohort according to significant factors, we found that the revision rate for pseudotumours in men was 0.5% (95% CI 0 to 1.1) at eight years wheras in women over 40 years old it was 6% (95% CI 2.3 to 10.1) at eight years and in women under 40 years it was 13.1% at six years (95% CI 0 to 27) (p < 0.001).

We recommend that resurfacings are undertaken with caution in women, particularly those under 40 years of age but they remain a good option in young men. Further work is required to understand the aetiology of pseudotumours so that this complication can be avoided.

Early failure associated with adverse reactions to metal debris is an emerging problem after hip resurfacing but the exact mechanism is unclear. We analysed our entire series of 660 metal-on-metal resurfacings (Articular Surface Replacement (ASR) and Birmingham Hip Resurfacing (BHR)) and large-bearing ASR total hip replacements, to establish associations with metal debris-related failures. Clinical and radiological outcomes, metal ion levels, explant studies and lymphocyte transformation tests were performed. A total of 17 patients (3.4%) were identified (all ASR bearings) with adverse reactions to metal debris, for which revision was required. This group had significantly smaller components, significantly higher acetabular component anteversion, and significantly higher whole concentrations of blood and joint chromium and cobalt ions than asymptomatic patients did (all p < 0.001). Post-revision lymphocyte transformation tests on this group showed no reactivity to chromium or cobalt ions. Explants from these revisions had greater surface wear than retrievals for uncomplicated fractures. The absence of adverse reactions to metal debris in patients with well-positioned implants usually implies high component wear.

Surgeons must consider implant design, expected component size and acetabular component positioning in order to reduce early failures when performing large-bearing metal-on-metal hip resurfacing and replacement.

We have undertaken a prospective, randomised study to compare conservation of acetabular bone after total hip replacement and resurfacing arthroplasty of the hip. We randomly assigned 210 hips to one of the two treatment groups. Uncemented, press-fit acetabular components were used for both.

No significant difference was found in the mean diameter of acetabular implant inserted in the groups (54.74 mm for total hip replacement and 54.90 mm for resurfacing arthroplasty). In seven resurfacing procedures (6.8%), the surgeon used a larger size of component in order to match the corresponding diameter of the femoral component.

With resurfacing arthroplasty, conservation of bone is clearly advantageous on the femoral side. Our study has shown that, with a specific design of acetabular implant and by following a careful surgical technique, removal of bone on the acetabular side is comparable with that of total hip replacement.

We evaluated the concentrations of chromium and cobalt ions in blood after metal-on-metal surface replacement arthroplasty using a wrought-forged, high carbon content chromium-cobalt alloy implant in 64 patients. At one year, mean whole blood ion levels were 1.61 μg/L (0.4 to 5.5) for chromium and 0.67 μg/L (0.23 to 2.09) for cobalt. The pre-operative ion levels, component size, female gender and the inclination of the acetabular component were inversely proportional to the values of chromium and/or cobalt ions at one year postoperatively. Other factors, such as age and level of activity, did not correlate with the levels of metal ions. We found that the levels of the ions in the serum were 1.39 and 1.37 times higher for chromium and cobalt respectively than those in the whole blood.

The levels of metal ions obtained may be specific to the hip resurfacing implant and reflect its manufacturing process.