To present a surgically relevant update of trunnionosis. Systematic review performed April 2017.Aims
Materials and Methods
Tribocorrosion at the head–neck taper interface
– so-called ‘taperosis’ – may be a source of metal ions and particulate
debris in metal-on-polyethylene total hip arthroplasty (THA). We examined the effect of femoral head length on fretting and
corrosion in retrieved head–neck tapers Head length was observed to affect fretting (p = 0.03), with
28 mm + 8 mm femoral heads showing greater total fretting scores
than all other head lengths. The central zone of the femoral head
bore taper was subject to increased fretting damage (p = 0.01),
regardless of head length or stem offset. High-offset femoral stems
were associated with greater total fretting of the bore taper (p
= 0.04). Increased fretting damage is seen with longer head lengths and
high-offset femoral stems, and occurs within a central concentric
zone of the femoral head bore taper. Further investigation is required
to determine the effect of increased head size, and variations in
head–neck taper design. Cite this article:
A modular femoral head–neck junction has practical
advantages in total hip replacement. Taper fretting and corrosion
have so far been an infrequent cause of revision. The role of design
and manufacturing variables continues to be debated. Over the past
decade several changes in technology and clinical practice might
result in an increase in clinically significant taper fretting and
corrosion. Those factors include an increased usage of large diameter
(36 mm) heads, reduced femoral neck and taper dimensions, greater
variability in taper assembly with smaller incision surgery, and
higher taper stresses due to increased patient weight and/or physical
activity. Additional studies are needed to determine the role of
taper assembly compared with design, manufacturing and other implant
variables. Cite this article: