Orthopaedic Proceedings
Vol. 103-B, Issue SUPP_4 | Pages 79 - 79
1 Mar 2021
Doodkorte R Roth A van Rietbergen B Arts J Lataster L van Rhijn L Willems P
Full Access

Complications after spinal fusion surgery are common, with implant loosening occurring in up to 50% of osteoporotic patients. Pedicle screw fixation strength reduces as a result of decreased trabecular bone density, whereas sublaminar wiring is less affected by these changes. Therefore, pedicle screw augmentation with radiopaque sublaminar wires (made with Dyneema Purity® Radiapque fibers, DSM Biomedical, Geleen, the Netherlands) may improve fixation strength. Furthermore, sublaminar tape could result in a gradual motion transition to distribute stress over multiple levels and thereby reduce implant loosening. The objective of this study is to test this hypothesis in a novel experimental setup in which a cantilever bending moment is applied to individual human vertebrae.

Thirty-eight human cadaver vertebrae were stratified into four different groups: ultra-high molecular weight polyethylene sublaminar tape (ST), pedicle screw (PS), metal sublaminar wire (SW) and pedicle screw reinforced with sublaminar tape (PS+ST). The vertebrae were individually embedded in resin, and a cantilever bending moment was applied bilaterally through the spinal rods using a universal material testing machine. This cantilever bending setup closely resembles the loading of fixators at transitional levels of spinal instrumentation.

The pull-out strength of the ST (3563 ± 476N) was not significantly different compared to PS, SW or PS+ST. The PS+ST group had a significantly higher pull-out strength (4522 ± 826N) compared to PS (2678 ± 292N) as well as SW (2931 ± 250N).

The higher failure strength of PS + ST compared to PS indicates that PS augmentation with ST may be an effective measure to reduce the incidence of screw pullout, even in osteoporotic vertebrae. Moreover, the lower stiffness of sublaminar fixation techniques and the absence of damage to the cortices in the ST group suggest that ST as a stand-alone fixation technique in adult spinal deformity surgery may also be clinically feasible and offer clinical benefits.


Orthopaedic Proceedings
Vol. 103-B, Issue SUPP_4 | Pages 80 - 80
1 Mar 2021
van Gestel N Kleuskens M Wanders D Ito K Arts J van Rietbergen B Hofmann S
Full Access

Novel biomaterials are being developed and studied, intended to be applied as bone graft substitute materials. Typically, these materials are being tested in in vitro setups, where among others their cytotoxicity and alkaline phosphatase activity (as a marker for osteoblastic differentiation) are being evaluated. However, it has been reported that in vitro tests correlate poorly with in vivo results and therefore many promising biomaterials may not reach the clinic as a bone graft substitute product. One of the reasons for the poor correlation, may be the minimal complexity of the in vitro tests, as compared to the in vivo environment. Ex vivo models, mimicking the natural tissue environment whilst maintaining control of culture parameters, may be a promising alternative to assess biomaterials for bone formation. Assess the possibility of an ex vivo culture platform to test biomaterials on their potential to stimulate new bone formation. Osteochondral plugs (cylinders n=10, Ø 10 mm, height 15 mm) were drilled from fresh porcine knees, from the slaughterhouse. A bone defect (Ø 6 mm) was created and which was filled with a biomaterial graft (S53P4 bioactive glass (n=3); collagen sponges loaded with BMP-2 (n=3, as positive control)) or kept empty (n=4). The explants were cultured in custom-made two-chamber bioreactors for six weeks (LifeTec Group BV). Cartilage and bone were physically separated, similar to the in vivo situation, by a sealing ring. The two tissues were cultured in separate compartments, allowing for specific culture medium for each tissue. Medium was changed every 2–3 days and weekly micro computed tomography (µCT) images were obtained to longitudinally monitor the formation of new bone. An MTT assay was performed on half of the samples after six weeks of culture. The other samples were fixed for histology, to determine which cells were present after six weeks. The MTT metabolic assay showed that a number of cells in the bone were viable after six weeks. The further away from the border, the fewer living cells were observed. The cells in the cartilage also survived. No significant bone formation was observed with µCT in either of groups, even though abundant bone formation was expected in the BMP-2 group. Explanations of the negative results of the positive group might be that too few viable cells remain after six weeks, or that the cells that are still present are not able to form bone. No significant bone formation was observed in the bone defects in osteochondral explants that were cultured with, or without, biomaterials for six weeks. However, the platform showed that it is capable to successfully culture osteochondral explants for six weeks.

Histology needs to be performed to evaluate which cells were present at the end of the culture and this will be compared to the cells present directly after drilling the explants.


Orthopaedic Proceedings
Vol. 103-B, Issue SUPP_4 | Pages 81 - 81
1 Mar 2021
Roth AK Willem PC van Rhijn LW Arts JJ Ito K van Rietbergen B
Full Access

Currently, between 17% of patients undergoing surgery for adult spinal deformity experience severe instrumentation related problems such as screw pullout or proximal junctional failure necessitating revision surgery. Cables may be used to reinforce pedicle screw fixation as an additive measure or may provide less rigid fixation at the construct end levels in order to prevent junctional level problems. The purpose of this study is to provide insight into the maximum expected load during flexion in UHMWPE cable in constructs intended for correction of adult spine deformity (degenerative scoliosis) in the PoSTuRe first-in-man clinical trial.

Following the concept of toppinoff, a new construct is proposed with screw/cable fixation of rods at the lower levels and standalone UHMWPE cables at the upper level (T11). A parametric FE model of the instrumented thoracolumbar spine, which has been previously validated, was used to represent the construct. Pedicle screws are modeled by assigning a rigid tie constraint between the rod and the lamina of the corresponding spinal level. Cables are modeled using linear elastic line elements, fixing the rod to the lamina medially at the cranial laminar end and laterally at the caudal laminar end. A Youngs modulus was assigned such that the stiffness of the line element was the same as that of the cable. An 8 Nm flexion moment was applied to the cranial endplate.

The maximum value of the force in the wire (80 N) is found at the T11 (upper) level. At the other levels, forces in the cable are very small because most of the force is carried by the screw (T12) or because the wires are force shielded by the contralateral and adjacent level pedicle screws (L2, L3).

The model provides first estimates of the forces that can be expected in the UHMWPE cables in constructs for kyphosis correction during movement. It is expected that this approach can help in defining the number of wires for optimal treatment.


Orthopaedic Proceedings
Vol. 100-B, Issue SUPP_3 | Pages 88 - 88
1 Apr 2018
Jeuken R Roth A Peters M van Rietbergen B Emans P
Full Access

INTRODUCTION

Adequate osseointegration of knee resurfacing implants for the treatment of focal cartilage defects is an important prerequisite for good clinical outcomes. Inadequate initial fixation and sustained micromotion may lead to osteolysis and ultimately implant failure. PET/CT with the bone seeking tracer 18F-sodium fluoride (18F-NaF) allows for localisation and quantification of abnormalities in bone metabolism. 18F-NaF PET/CT has been shown to correlate with loosening of implants in the hip and spine. Here, we asses osseointegration of the knee resurfacing implants using micro-computed tomography (µCT) and correlate µCT parameters to 18F-NaF uptake on PET/CT scans taken 3 and 12 weeks after surgery. We hypothesize that 18F-NaF uptake at 12 weeks and its relative decrease between 3 and 12 weeks correlates with osseointegration at 12 weeks postoperatively. Polymer implants with Young”s moduli approximately equal to- and below the Young's modulus of bone, with- and without surface modification were used in this study next to a control metal implant.

METHODS

Five different osteochondral implants were implanted bilaterally in critically-sized osteochondral defects in 16 goats. At 3 and 12 weeks postoperatively, a 10-minute static PET/CT-scan (Philips, Gemini TF PET/CT) was made 60 minutes after intravenous injection of 18F-NaF. Image processing resulted in an overall bone metabolism parameter, i.e. standardized uptake value (SUV). A cylindrical region of interest was drawn around each implant to obtain the maximum SUV (SUVmax). Bone quality parameters were quantified in a cylinder surrounding the implant using µCT after sacrifice as a measure for osseointegration. The in vivo 18F-NaF PET/CT uptake parameters were correlated to the bone quality parameters.


Orthopaedic Proceedings
Vol. 100-B, Issue SUPP_3 | Pages 21 - 21
1 Apr 2018
Caron M Castermans T van Rietbergen B Haartmans M van Rhijn L Witlox A Welting T
Full Access

INTRODUCTION

Endochondral ossification in the growth plate is directly responsible for skeletal growth and its de novo bone-generating activity. Growth plates are vulnerable to disturbances that may lead to abnormal skeletal development. Non-steroidal anti-inflammatory drugs (NSAIDs) are widely used analgesics but have been reported to impair endochondral ossification-driven fracture healing. Despite the general awareness that NSAIDs affect endochondral ossification, the consequences of NSAIDs on skeletal development are unknown. We hypothesise that the NSAID celecoxib leads to impaired growth plate development and consequently impairs skeletal development.

METHODS

Healthy skeletally immature (5 weeks old) C57BL/6 mice were treated for ten weeks with celecoxib (daily oral administration 10 mg/kg) or placebo (water) (institutional approval 2013–094) (n=12 per group). At 15 weeks postnatally, total growth plate thickness, the thickness of specific growth plate zones, (immuno)histological analysis of extracellular matrix composition in the growth plate, cell number and cell size, longitudinal bone growth and bone micro-architecture by micro-CT were analysed. Inhibition of COX-2 activity was confirmed by determining PGE2 levels in plasma using an ELISA.


Orthopaedic Proceedings
Vol. 100-B, Issue SUPP_3 | Pages 40 - 40
1 Apr 2018
Roth A van der Meer R Willems P van Rhijn L Arts J Ito K van Rietbergen B
Full Access

INTRODUCTION

Growth-guidance constructs are an alternative to growing rods for the surgical treatment of early onset scoliosis (EOS). In growth-guidance systems, free-sliding anchors preserve longitudinal spinal growth, thereby eliminating the need for surgical lengthening procedures. Non-segmental constructs containing ultra-high molecular weight polyethylene (UHMWPE) sublaminar wires have been proposed as an improvement to the traditional Luque trolley. In such a construct, UHMWPE sublaminar wires, secured by means of a knot, serve as sliding anchors at the proximal and distal ends of a construct, while pedicle screws at the apex prevent rod migration and enable curve derotation. Ideally, a construct with the optimal UHMWPE sublaminar wire density, offering the best balance between providing adequate spinal fixation and minimizing surgical exposure, is designed preoperatively for each individual patient. In a previous study, we developed a parametric finite element (FE) model that potentially enables preoperative patient-specific planning of this type of spinal surgery. The objective of this study is to investigate if this model can capture the decrease in range of motion (ROM) after spinal fixation as measured in an experimental study.

MATERIALS AND METHODS

In a previous in vitro study, the ROM of an 8-segment porcine spine was measured before and after instrumentation, using different instrumentation constructs with a sequentally decreasing number of wire fixation points. In the current study, the parametric FE model of the thoracolumbar spine was first validated relative to ROM values reported in the literature. The rods, screws, and sublaminar wires were implemented, and the model was subsequently used to replicate the in vitro tests. The experimental and simulated ROM”s for the different instrumentation conditions were compared.


Orthopaedic Proceedings
Vol. 99-B, Issue SUPP_9 | Pages 73 - 73
1 May 2017
van Gestel N Arts J Hulsen D Geurts J Ito K van Rietbergen B
Full Access

Background

Bio-Active Glass (BAG) is a promising bone graft substitute for large bone defect reconstruction because of its favourable osteoconductive, antibacterial and angiogenic properties. Potentially, it could also mechanically reinforce the defect, thus making it suitable for load-bearing defects. However, the mechanical properties of the reconstructive layer consisting of BAG/bone allograft mixtures are unknown. The goals of this study therefore were, first, to measure the mechanical properties of different BAG/bone graft mixtures and, second, to investigate to what extent such mixtures could reinforce distal tibial defects using micro-FE analysis and high-resolution CT scans.

Materials and Methods

Four different BAG/bone graft mixtures were impacted in a cylindrical holder, mechanically tested in confined compression and scanned with micro-CT. From these images, bone graft material and glass were segmented using two different threshold values. The interface between bone and BAG was modelled separately by dilating the glass phase. Micro-Finite-Element (FE) models of the composites were made using a Young's modulus of 2.5 GPa for bone and 35 GPa for BAG. The Young's modulus for the interface region was determined by fitting experimental and micro-FE results for the same specimens. (82 μm resolution) CT scans of a 9 mm region of the distal tibia of 3 subjects were used. Micro-FE models of this region were made to determine its stiffness in the original state, with a simulated cortical defect and after a mixture of BAG/bone was modelled in the defect.


Orthopaedic Proceedings
Vol. 99-B, Issue SUPP_8 | Pages 43 - 43
1 Apr 2017
Arts J Marangalou JH Meijer G Ito K van Rietbergen B Homminga J
Full Access

Background

Finite element (FE) models have become a standard pre-clinical tool to study biomechanics of spine and are used to simulate and evaluate different strategies in scoliosis treatment: examine their efficacy as well as the effect of different implant design parameters. The goal of this study is to investigate, in a system of rods and laminar wires, the effect of the number of wires and their pre-stress on whole spine stiffness.

Methods

A generic FE model was developed to represent a full human spine, including vertebrae, intervertebral discs, ligaments, facet and costovertebral joints, and ribcage. Intervertebral discs were modeled with 3D rebar elements with linear elastic material properties. Vertebrae, ribs, sternum, facet joints, cartilage and endplates were modeled with brick elements, and costal muscles with shell elements with linear elastic properties. Furthermore, ligaments were modeled with truss elements with nonlinear hypo-elastic properties. The spine model was instrumented from T7 to T12 with rods and wires modeled as titanium. Nonlinear contact properties were defined for rib neck-vertebra, transverse processes-rib and facet joint sets. The FE model was loaded in flexion and the whole spine instantaneous stiffness was calculated for different wire pre-stressing levels (0.1 to 2 MPa). Similar analyses were performed with changed numbers of wires and whole spine stiffness was calculated.