Osteoarthritis (OA) is a prevalent joint disorder with inflammatory response and cartilage deterioration as its main features. Dihydrocaffeic acid (DHCA), a bioactive component extracted from natural plant ( In vitro, interleukin-1 beta (IL-1β) was used to establish the mice OA chondrocytes. Cell counting kit-8 evaluated chondrocyte viability. Western blotting analyzed the expression levels of collagen II, aggrecan, SOX9, inducible nitric oxide synthase (iNOS), IL-6, matrix metalloproteinases (MMPs: MMP1, MMP3, and MMP13), and signalling molecules associated with nuclear factor-kappa B (NF-κB) and mitogen-activated protein kinase (MAPK) pathways. Immunofluorescence analysis assessed the expression of aggrecan, collagen II, MMP13, and p-P65. In vivo, a destabilized medial meniscus (DMM) surgery was used to induce mice OA knee joints. After injection of DHCA or a vehicle into the injured joints, histological staining gauged the severity of cartilage damage.Aims
Methods
Support of appositional bone ingrowth and resistance to bacterial adhesion and biofilm formation are preferred properties for biomaterials used in spinal fusion surgery. Although polyetheretherketone (PEEK) is a widely used interbody spacer material, it exhibits poor osteoconductive and bacteriostatic properties. In contrast, monolithic silicon nitride (Si3N4) has shown enhanced osteogenic and antimicrobial behavior. Therefore, it was hypothesized that incorporation of Si3N4 into a PEEK matrix might improve upon PEEK's inherently poor ability to bond with bone and also impart resistance to biofilm formation. A PEEK polymer was melted and compounded with three different silicon nitride powders at 15% (by volume, vol.%), including: (i) Introduction
Methods
Femoral heads made from zirconia-toughened alumina (ZTA) are the most advanced bioceramic available for total hip arthroplasty. ZTA's superior mechanical properties result from the polymorphic transformation of its zirconia (ZrO2) phase in the presence of a propagating crack. BIOLOX®Introduction
Materials and Methods
Due to its remarkable stoichiometric flexibility and surface chemistry, hydroxyapatite (HAp) is the fundamental structural material in all vertebrates. Natural HAp's properties inspired an investigation into silicon nitride (Si3N4) to see if similar functionality could be engineered into this bioceramic. Biological and Four groups of Si3N4 discs, Ø12.7×1.0mm, (Amedica Corporation, Salt Lake City, UT USA) were subjected to surface treatments: (i) “As-fired;” (ii) HF-etched (5% HF solution for 45 s); (iii) Oxidized (1070°C for 7 h); and (iv) Nitrogen-annealed (1400°C for 30 min, 1.1 bar N2 gas).1 Titanium alloy discs (Ti6Al4V, ASTM F136) were used as a control group. SaOS-2 cells cultured for 24 h at 37°C were deposited (5×105 cells/ml) and incubated on the UV sterilized discs in an osteogenic medium for 7 days at 37°C. Cell proliferation was monitored using scanning electron and laser microscopy. The Receptor Activator of NF-kB Ligand (sRANKL) and the insulin growth factor 1 (IGF-1) were used to evaluate osteoclast formation and cell proliferation efficiency, respectively. Introduction
Materials and Methods